CN110003738A - A kind of inner wall of building sustained release flowers coating and preparation method thereof - Google Patents
A kind of inner wall of building sustained release flowers coating and preparation method thereof Download PDFInfo
- Publication number
- CN110003738A CN110003738A CN201910153154.7A CN201910153154A CN110003738A CN 110003738 A CN110003738 A CN 110003738A CN 201910153154 A CN201910153154 A CN 201910153154A CN 110003738 A CN110003738 A CN 110003738A
- Authority
- CN
- China
- Prior art keywords
- pollen
- wall
- flowers
- coating
- sustained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of inner wall of building sustained release flowers coating and preparation method thereof, the coating includes the raw material of following mass percentage content: active superfine pollen Nano capsule 0.1-0.3%, adsorbent diatomite 1.5-2.2%, binder polyvinyl alcohol 1.2-2.5%, dispersing agent cellulose 0.6-1.2%, stabilizer xanthan gum 0.3-1.2%, filming emulsion 75-80%, remaining be water, wherein, the active superfine pollen Nano capsule is to be coated on Nano capsule by active superfine pollen to be made.Compared with prior art, the present invention has the function of that nature is sustained flowers.
Description
Technical field
The invention belongs to the indoor coating of building decoration area, more particularly, to a kind of inner wall of building be sustained flowers coating and
Preparation method.
Background technique
Currently, the mankind are especially deeply concerned to the air regime for living in the earth, and real-life household, working environment
In, all kinds of wood furnitures can more or less release some formaldehyde and harmful substance, and be easy that the sense of some respiratory tracts can be caused
Dye and disease, meanwhile, the use of a large amount of mobile phone, office computer, printer, scanner produces many electromagnetic radiation, to people
Nervous system, cardiovascular system, eyes of body etc. produce serious harm.
How air conditions are effectively improved, and coating is as a kind of construction material for directly contacting room air, ecology
Environmental protection becomes the Research Points of the novel environment friendly building materials field of public demand.And use the environmental protection coating material of plant fiber class in patent
It is upper to have been reported that more, but how to play the coating or blank for adjusting human nerve balance.
Patent CN106995628A discloses a kind of dope for inner wall of architecture and preparation method thereof, the dope for inner wall of architecture
It is made of following raw material components and mass ratio: dope for inner wall of architecture active ingredient 3-5%, adsorbent diatomite 1-2%, binder
Polyvinyl alcohol 1-2%, dispersing agent cellulose 0.5-1%, stabilizer 0.5-1%, filming emulsion 70-80%, water 9%-24%;It builds
Build interior wall coating preparation method be by each component according to the proportion, be put into reaction kettle, ground stirring obtains uniformly mixed
Dope for inner wall of architecture, the active ingredient of the interior wall coating be containing titanium dioxide, hafnium oxide, zinc oxide, graphene oxide,
The composite material of sodium naphthalene sulfonate and glucose, synthesizes through chemical method, but the invention can not adjust human nerve balance, and not have
Except formaldehyde, sterilizing deodoring, the anti-radiation and functions such as ageing-resistant.
Summary of the invention
The purpose of the present invention is to solve the above-mentioned problems and provides a kind of inner wall of building sustained release flowers coating and its system
Preparation Method.
The purpose of the present invention is achieved through the following technical solutions:
A kind of inner wall of building sustained release flowers coating, which includes the raw material of following mass percentage content: active superfine
Pollen Nano capsule 0.1-0.3%, adsorbent diatomite 1.5-2.2%, binder polyvinyl alcohol 1.2-2.5%, dispersing agent are fine
Tie up element 0.6-1.2%, stabilizer xanthan gum 0.3-1.2%, filming emulsion 75-80%, remaining be water, wherein it is described activity surpass
Thin pollen Nano capsule is to be coated on Nano capsule by active superfine pollen to be made, and there is slow release to be sustained flowers function naturally
Energy.
Preferably, the active superfine pollen Nano capsule is made by following steps:
(1) flower is acquired during flowers full blossom, and is dehydrated in drying plant, and first dryer heats up, then feeds intake
Successively progress high temperature dehydration is dry, cooling eases back and low temperature dewatering, and the flower of dehydration and drying is put into the grinding of ultrafine plant powder body
Machine is ground, and active superfine pollen is obtained;
(2) using sodium alginate as wall material, using active superfine pollen as core material, active superfine flower is prepared using emulsion polymerization method
Powder Nano capsule.
Preferably, dryer is warming up to 60 DEG C of stabilizations in step (1), then carries out the drying that feeds intake;High temperature dehydration drying process
Temperature be 60 DEG C, the flower residence time be 50-70min;The temperature for the process that eases back that cools down is 10-20 DEG C, the flower residence time
For 10-30min, the temperature of low temperature dewatering process is 35-40 DEG C, flower residence time 60-80min.
Preferably, step (2) specific steps are as follows: sodium alginate is dissolved in the aqueous solution containing emulsifier, then plus
Enter active superfine pollen, keeps active superfine pollen evenly dispersed in the solution through mechanical stirring, add calcium chloride and pass through gel
Reaction forms Nano capsule.
Preferably, the active superfine pollen uses the superfine powder of 800-1000 mesh.
Preferably, the adsorbent diatomite uses the diatomite of 100-300 mesh, for adsorbing the toxic gas in air
And electromagnetic radiation, the binder polyvinyl alcohol, for bonding active constituent, diatomite, dispersing agent, stabilizer and lotion.
Preferably, the dispersing agent cellulose is in hydroxymethyl cellulose, hydroxyethyl cellulose or hydroxypropyl cellulose
It is one or more.
Preferably, the filming emulsion be selected from acrylic emulsion, styrene-acrylic emulsion, silicone acrylic emulsion or acrylate and vinyl acetate emulsion one kind or
It is a variety of.
Preferably, the stabilizer xanthan gum can play emulsification and stabilization, for active constituent and diatomite in cream
Stability in liquid plays an important role, and the filming emulsion plays protection wall.
A kind of preparation method of inner wall of building sustained release flowers coating, this method are as follows: weigh by mass percentage filming emulsion,
Water, adsorbent diatomite, binder polyvinyl alcohol, dispersing agent cellulose, stabilizer xanthan gum and active superfine pollen nanometre glue
Capsule, and be added sequentially in reaction kettle, temperature control grinding stirring obtains uniformly mixed dope for inner wall of architecture.Temperature control range is 40-
65 DEG C, grinding mixing time is 8-12h.
In the present invention, during preparing active superfine pollen, excessively mated formation set equably flower is placed on it is stainless
In steel mesh belt, flower is brought into the high temperature drying area of drying machine by mesh belt, and the hot dry air that wet flower and hot-blast stove are sent carries out
Convective heat exchange.During carrying out heat exchange, the moisture on flower surface and the Free water included are evaporated discharge.In high temperature
In dry section, the moisture of flower 75%-80% is evaporated out.Then, flower enters the cooling tempering section that eases back, in this area
In section, the flower reduced is transported to the upper of drying machine by the air-flow of air-cooler (air-cooler with certain outlet pressure)
Another exit in side.For flower during being conveyed by air-cooler, temperature decline, this process is known as tempering phenomenon.Pass through cooling
Tempering, the internal junction Heshui of flower, which can be shifted soon to extexine, to spread, and creates condition for next step low temperature drying.Slow
During Soviet Union, the moisture of flower can reduce 3% or so.Flower eases back after dehydration by cooling, into low temperature drying section, this
Zone temperatures are controlled at 35-40 DEG C or so, and flower internal junction Heshui will further be extracted evaporation, and in this section, flower is
It is conveyed by one group of reciprocating sieve, is dehydrated 5%-8%, keeps flower up to standard and be discharged, which helps to maintain the activity and perfume of flowers
Gas.
Active superfine pollen Nano capsule, active superfine pollen Nano capsule and adsorbent silicon is added in the present invention in coating
The compounding such as diatomaceous earth, binder polyvinyl alcohol, dispersing agent cellulose, stabilizer xanthan gum and filming emulsion, coating tool obtained
There are nature sustained release flowers, except formaldehyde, antimycotic antiseptic eliminate the unusual smell, anti-radiation, ageing-resistant and stain resistant function.Active superfine pollen
It is coated by Nano capsule, sodium alginate is dissolved in the aqueous solution containing emulsifier, active superfine pollen is then added, through machine
Tool stirring keeps active superfine pollen evenly dispersed in the solution, adds calcium chloride by gel reaction and forms Nano capsule, this
Kind facilitates the slow release of flowers active constituent and fragrance by way of by active superfine pollen Nano capsule cladding, long
Up to several months or several years, coating still has certain floral odor.
Specific embodiment
The present invention is described in detail combined with specific embodiments below, but should be in no way restrictive.
Embodiment 1
A kind of inner wall of building sustained release flowers coating, the raw material including following mass percentage content: active superfine pollen is received
Rice glue capsule 0.1%, adsorbent diatomite 1.5%, binder polyvinyl alcohol 1.2%, dispersing agent cellulose 0.6%, stabilizer are yellow
Virgin rubber 0.3%, filming emulsion 75%, remaining be water, wherein active superfine pollen Nano capsule is coated by active superfine pollen
It is made in Nano capsule.
Above-mentioned inner wall of building sustained release flowers coating is prepared in accordance with the following methods:
In reaction kettle, 60 DEG C of water-bath temperature control, the adsorbent silicon of filming emulsion acrylic emulsion, water, 100 mesh is sequentially added
Diatomaceous earth, binder polyvinyl alcohol, dispersing agent hydroxyethyl cellulose and stabilizer xanthan gum, active superfine pollen Nano capsule, warp
Grinding stirring 8h, obtains uniformly mixed dope for inner wall of architecture.
Wherein, active superfine pollen Nano capsule is made by the following method:
(1) picking flowers are collected: the shaking spray during flowers full blossom, and ground spreads colour bar film and accepts to acquire flower,
It prevents soil, impurity to be mixed into, and picks up the leaf in flower clearly, and be sent to drying plant dehydration and drying in the same day.
(2) it dehydrates:
Dryer temperature-rise period: first preheating drying machine before feeding intake, and built-in temperature stabilization is made to start to feed intake at 60 DEG C
It is dry.
High temperature dehydration drying process: temperature is 60 DEG C, and the flower residence time is about 50min.
Cool down the process that eases back: temperature is 10 DEG C.
Low temperature dewatering process: temperature is 35 DEG C, flower residence time 60min, is conveyed by one group of reciprocating sieve.
(3) extra-fine grinding: by the flower of dehydration and drying, it is put into ultrafine plant powder body grinder (QLMA-10 air-flow crushing
Machine, QLFD-300 gas flow sizing machine, Germany is through glad board), active superfine pollen is obtained, major ingredient fineness can pack standby in 800 mesh
With.
(4) sodium alginate is dissolved in the aqueous solution containing Tween 80, active superfine pollen is then added, is stirred through machinery
Mixing keeps active superfine pollen evenly dispersed in the solution, adds a small amount of calcium chloride by gel reaction and forms Nano capsule,
In, sodium alginate concentration 0.6mg/ml, emulsification times 5min, ultrasonic time 15min, stirring rate 1200rmp, stirring when
Between be 30min, Nano capsule partial size be 15-20 μm.
Embodiment 2
A kind of inner wall of building sustained release flowers coating, the raw material including following mass percentage content: active superfine pollen is received
Rice glue capsule 0.21%, adsorbent diatomite 1.9%, binder polyvinyl alcohol 1.8%, dispersing agent cellulose 0.9%, stabilizer are yellow
Virgin rubber 0.9%, filming emulsion 80%, remaining be water, wherein active superfine pollen Nano capsule is coated by active superfine pollen
It is made in Nano capsule.
Above-mentioned inner wall of building sustained release flowers coating is prepared in accordance with the following methods:
In reaction kettle, 55 DEG C of water-bath temperature control, the adsorbent diatom of filming emulsion styrene-acrylic emulsion, water, 100 mesh is sequentially added
Soil, binder polyvinyl alcohol, dispersing agent hydroxymethyl cellulose and stabilizer xanthan gum, active superfine pollen Nano capsule, through grinding
Mill stirring 10h, obtains uniformly mixed dope for inner wall of architecture.
Wherein, active superfine pollen Nano capsule is made by the following method:
(1) picking flowers are collected: the shaking spray during flowers full blossom, and ground spreads colour bar film and accepts to acquire flower,
It prevents soil, impurity to be mixed into, and picks up the leaf in flower clearly, and be sent to drying plant dehydration and drying in the same day.
(2) it dehydrates:
Dryer temperature-rise period: first preheating drying machine before feeding intake, and built-in temperature stabilization is made to start to feed intake at 60 DEG C
It is dry.
High temperature dehydration drying process: temperature is 60 DEG C, and the flower residence time is about 50min.
Cool down the process that eases back: temperature is 10 DEG C.
Low temperature dewatering process: temperature is 35 DEG C, flower residence time 65min, is conveyed by one group of reciprocating sieve.
(3) extra-fine grinding: by the flower of dehydration and drying, it is put into ultrafine plant powder body grinder (QLMA-10 air-flow crushing
Machine, QLFD-300 gas flow sizing machine, Germany is through glad board), active superfine pollen is obtained, major ingredient fineness can pack standby in 800 mesh
With.
(4) sodium alginate is dissolved in the aqueous solution containing Tween 80, active superfine pollen is then added, is stirred through machinery
Mixing keeps active superfine pollen evenly dispersed in the solution, adds a small amount of calcium chloride by gel reaction and forms Nano capsule,
In, sodium alginate concentration 0.65mg/ml, emulsification times 8min, ultrasonic time 10min, stirring rate 1200rmp, stirring
Time is 30min, and Nano capsule partial size is 15-20 μm.
Embodiment 3
A kind of inner wall of building sustained release flowers coating, the raw material including following mass percentage content: active superfine pollen is received
Rice glue capsule 0.3%, adsorbent diatomite 2.2%, binder polyvinyl alcohol 2.5%, dispersing agent cellulose 1.2%, stabilizer are yellow
Virgin rubber 1.2%, filming emulsion 80%, remaining be water, wherein active superfine pollen Nano capsule is coated by active superfine pollen
It is made in Nano capsule.
Above-mentioned inner wall of building sustained release flowers coating is prepared in accordance with the following methods:
In reaction kettle, 60 DEG C of water-bath temperature control, the adsorbent diatom of filming emulsion styrene-acrylic emulsion, water, 100 mesh is sequentially added
Soil, binder polyvinyl alcohol, dispersing agent hydroxypropyl cellulose and stabilizer xanthan gum, active superfine pollen Nano capsule, through grinding
Mill stirring 12h, obtains uniformly mixed dope for inner wall of architecture.
Wherein, active superfine pollen Nano capsule is made by the following method:
(1) picking flowers are collected: the shaking spray during flowers full blossom, and ground spreads colour bar film and accepts to acquire flower,
It prevents soil, impurity to be mixed into, and picks up the leaf in flower clearly, and be sent to drying plant dehydration and drying in the same day.
(2) it dehydrates:
Dryer temperature-rise period: first preheating drying machine before feeding intake, and built-in temperature stabilization is made to start to feed intake at 60 DEG C
It is dry.
High temperature dehydration drying process: temperature is 60 DEG C, and the flower residence time is about 50min.
Cool down the process that eases back: temperature is 10 DEG C.
Low temperature dewatering process: temperature is 35 DEG C, flower residence time 70min, is conveyed by one group of reciprocating sieve.
(3) extra-fine grinding: by the flower of dehydration and drying, it is put into ultrafine plant powder body grinder (QLMA-10 air-flow crushing
Machine, QLFD-300 gas flow sizing machine, Germany is through glad board), active superfine pollen is obtained, major ingredient fineness can pack standby in 800 mesh
With.
(4) sodium alginate is dissolved in the aqueous solution containing Tween 80, active superfine pollen is then added, is stirred through machinery
Mixing keeps active superfine pollen evenly dispersed in the solution, adds a small amount of calcium chloride by gel reaction and forms Nano capsule,
In, sodium alginate concentration 0.65mg/ml, emulsification times 8min, ultrasonic time 10min, stirring rate 1200rmp, stirring
Time is 30min, and Nano capsule partial size is 15-20 μm.
By coating material made from embodiment 1-3 in wall, in 25 DEG C of dry and ventilated environment, when test fragrance retains
Between, table 1 is test result, other indexs also all comply with standard JG/T24-2000, and has except formaldehyde, antimycotic antiseptic and resistance to be stained with
Dirty function.
1 test result of table
Number | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Time (moon) | 15.5 | 16.8 | 18.3 |
The above description of the embodiments is intended to facilitate ordinary skill in the art to understand and use the invention.
Person skilled in the art obviously easily can make various modifications to these embodiments, and described herein general
Principle is applied in other embodiments without having to go through creative labor.Therefore, the present invention is not limited to the above embodiments, ability
Field technique personnel announcement according to the present invention, improvement and modification made without departing from the scope of the present invention all should be of the invention
Within protection scope.
Claims (10)
1. a kind of inner wall of building is sustained flowers coating, which is characterized in that the coating includes the raw material of following mass percentage content:
Active superfine pollen Nano capsule 0.1-0.3%, adsorbent diatomite 1.5-2.2%, binder polyvinyl alcohol 1.2-2.5%,
Dispersing agent cellulose 0.6-1.2%, stabilizer xanthan gum 0.3-1.2%, filming emulsion 75-80%, remaining be water, wherein institute
Stating active superfine pollen Nano capsule is to be coated on Nano capsule by active superfine pollen to be made.
2. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that the active superfine pollen
Nano capsule is made by following steps:
(1) flower is acquired during flowers full blossom, and is dehydrated in drying plant, and first dryer heats up, then feeds intake successively
Progress high temperature dehydration is dry, cooling eases back and low temperature dewatering, and the flower of dehydration and drying is put into ultrafine plant powder body grinder, into
Row grinding, obtains active superfine pollen;
(2) using sodium alginate as wall material, using active superfine pollen as core material, active superfine pollen is prepared using emulsion polymerization method and is received
Rice glue capsule.
3. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that dryer in step (1)
60 DEG C of stabilizations are warming up to, then carry out the drying that feeds intake;The temperature of high temperature dehydration drying process is 60 DEG C, and the flower residence time is 50-
70min;The temperature for the process that eases back that cools down is 10-20 DEG C, and the flower residence time is 10-30min, and the temperature of low temperature dewatering process is
35-40 DEG C, flower residence time 60-80min.
4. a kind of inner wall of building according to claim 2 is sustained flowers coating, which is characterized in that step (2) specific steps
Are as follows: sodium alginate is dissolved in the aqueous solution containing emulsifier, active superfine pollen is then added, makes activity through mechanical stirring
Ultra-fine pollen is evenly dispersed in the solution, adds calcium chloride by gel reaction and forms Nano capsule.
5. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that the active superfine pollen
Using the superfine powder of 800-1000 mesh.
6. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that the adsorbent diatomite
Using the diatomite of 100-300 mesh.
7. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that the dispersing agent cellulose
Selected from one of hydroxymethyl cellulose, hydroxyethyl cellulose or hydroxypropyl cellulose or a variety of.
8. a kind of inner wall of building according to claim 1 is sustained flowers coating, which is characterized in that the filming emulsion is selected from
Acrylic emulsion, styrene-acrylic emulsion, silicone acrylic emulsion or acrylate and vinyl acetate emulsion it is one or more.
9. such as a kind of described in any item preparation methods of inner wall of building sustained release flowers coating of claim 1-8, which is characterized in that
This method are as follows: weigh filming emulsion, water, adsorbent diatomite, binder polyvinyl alcohol, dispersing agent fiber by mass percentage
Element, stabilizer xanthan gum and active superfine pollen Nano capsule, and be added sequentially in reaction kettle, temperature control grinding stirring obtains
Uniformly mixed dope for inner wall of architecture.
10. a kind of preparation method of inner wall of building sustained release flowers coating according to claim 9, which is characterized in that temperature control
Range is 40-65 DEG C, and grinding mixing time is 8-12h.