CN110003581A - A kind of novel XPS plastic extrusion heated board and preparation method thereof - Google Patents
A kind of novel XPS plastic extrusion heated board and preparation method thereof Download PDFInfo
- Publication number
- CN110003581A CN110003581A CN201910326705.5A CN201910326705A CN110003581A CN 110003581 A CN110003581 A CN 110003581A CN 201910326705 A CN201910326705 A CN 201910326705A CN 110003581 A CN110003581 A CN 110003581A
- Authority
- CN
- China
- Prior art keywords
- fire
- particle
- heated board
- plastic extrusion
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of novel XPS plastic extrusion heated board, and ingredient includes: ps particle, fire-retardant particle, fire retardant, nucleating agent, master batch;Specific formula is made of the raw material of following weight: ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg, master batch 5kg.The reasonable combination of each substance in the present invention can make product have preferable thermal insulation, higher crushing resistance.
Description
Technical field
The present invention relates to insulation board technical field, specially a kind of novel XPS plastic extrusion heated board and preparation method thereof.
Background technique
XPS plastic extrusion heated board is to add various processing aids and foaming agent using polystyrene as primary raw material, by squeezing
Molding is made out.XPS extruded sheet major applications are in fields such as civil buildings exterior insulation, roof heat insulations currently on the market,
XPS plastic extrusion heated board makes it have preferable thermal insulation, higher crushing resistance, longer use with its closed foam structure
Phase.
Summary of the invention
Technical problem solved by the invention is to provide a kind of novel XPS plastic extrusion heated board and preparation method thereof, with solution
The problems in certainly above-mentioned background technique.
Technical problem solved by the invention realizes a kind of novel XPS plastic extrusion heated board using following technical scheme,
Ingredient includes: ps particle, fire-retardant particle, fire retardant, nucleating agent, master batch;Specific formula is made of the raw material of following weight: ps
Grain 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg, master batch 5kg.
Further, the fire-retardant particle is the fire-retardant particle of halogen system.
Further, the nucleating agent is talcum powder, calcium carbonate, silica, alum, titanium dioxide, calcium oxide, oxidation
One or more of magnesium, carbon black, mica etc..
A kind of novel XPS plastic extrusion heated board preparation method, specifically includes the following steps:
Step 1: according to: ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg, master batch 5kg
Weight item is put into hopper and is sufficiently mixed;
Step 2: mixed material is fed by feeder work unit, by heating, conveying in work unit, plasticizing, be kneaded,
It injects co2 (carbon dioxide);
Step 3: being delivered to work unit by net-changing device connector under the promotion of screw rod when raw material is at viscous state, pass through
Second time of foaming;
Step 4: due to being filled with co2 carbon dioxide in unit while cooperating foaming agent and nucleating agent, passing through work unit
The stirring of screw rod forms a large amount of nuclei of bubbles, is being extruded machine extrusion die mouth in a flash, is being influenced by atmospheric pressure, shape
At independent bubble one by one, surrounding materials at this time bulge, and the material to bulge are flattened by planisher, shaping is finally led
Draw machine to involve;
Step 5: finally debugging out the product needed by specification, most using trimming, plucking, fluting, cutting and packaging
After make finished product.
Further, second time of foaming temperature is 125 DEG C in the step 3.
Further, the extruder in the step 4 is single order parallel dual-screw and second order single screw extrusion machine.
Further, the foaming agent in the step 4 is AC foaming agent.
It is compared to open technology, there are following advantages by the present invention: the reasonable combination of each substance in the present invention, but product
With preferable thermal insulation, higher crushing resistance, ground heating heat insulation, air-conditioning heat insulation pipe, Water Cube engineering etc. can be applicable to.
Specific embodiment
In order to make, technological means of the invention, creation characteristic, workflow, application method reach purpose and effect is easy to bright
White understanding, below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of novel XPS plastic extrusion heated board, ingredient include: ps particle, fire-retardant particle, fire retardant, nucleating agent, master batch;
Specific formula is made of the raw material of following weight: ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg,
Master batch 5kg.
Further, the fire-retardant particle is the fire-retardant particle of halogen system.
Further, the nucleating agent is talcum powder, calcium carbonate, silica, alum, titanium dioxide, calcium oxide, oxidation
One or more of magnesium, carbon black, mica etc..
A kind of novel XPS plastic extrusion heated board preparation method, specifically includes the following steps:
Step 1: according to: ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg, master batch 5kg
Weight item is put into hopper and is sufficiently mixed;
Step 2: mixed material is fed by feeder work unit, by heating, conveying in work unit, plasticizing, be kneaded,
It injects co2 (carbon dioxide);
Step 3: being delivered to work unit by net-changing device connector under the promotion of screw rod when raw material is at viscous state, pass through
Second time of foaming;
Step 4: due to being filled with co2 carbon dioxide in unit while cooperating foaming agent and nucleating agent, passing through work unit
The stirring of screw rod forms a large amount of nuclei of bubbles, is being extruded machine extrusion die mouth in a flash, is being influenced by atmospheric pressure, shape
At independent bubble one by one, surrounding materials at this time bulge, and the material to bulge are flattened by planisher, shaping is finally led
Draw machine to involve;
Step 5: finally debugging out the product needed by specification, most using trimming, plucking, fluting, cutting and packaging
After make finished product.
Further, second time of foaming temperature is 125 DEG C in the step 3.
Further, the extruder in the step 4 is single order parallel dual-screw and second order single screw extrusion machine.
Further, the foaming agent in the step 4 is AC foaming agent.
The reasonable combination of each substance in the present invention, but product has preferable thermal insulation, higher crushing resistance, can apply
In ground heating heat insulation, air-conditioning heat insulation pipe, Water Cube engineering etc..
The above shows and describes the basic principle, main features and advantages of the invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.Claimed range of the invention by appended claims and
Its equivalent thereof.
Claims (7)
1. a kind of novel XPS plastic extrusion heated board, it is characterised in that: its ingredient includes: ps particle, fire-retardant particle, fire retardant, nucleation
Agent, master batch;Specific formula is made of the raw material of following weight: ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, at
Core agent 10kg, master batch 5kg.
2. a kind of novel XPS plastic extrusion heated board according to claim 1, it is characterised in that: the fire-retardant particle is halogen system
Fire-retardant particle.
3. a kind of novel XPS plastic extrusion heated board according to claim 1 and preparation method thereof, it is characterised in that: it is described at
Core agent is one in talcum powder, calcium carbonate, silica, alum, titanium dioxide, calcium oxide, magnesia, carbon black, mica etc.
Or it is multiple.
4. a kind of novel XPS plastic extrusion heated board and preparation method thereof, it is characterised in that: specifically includes the following steps:
Step 1: according to: the weight of ps particle 150kg, fire-retardant particle 150kg, fire retardant 20kg, nucleating agent 10kg, master batch 5kg
Ingredient is put into hopper and is sufficiently mixed;
Step 2: mixed material being fed by feeder work unit, by heating, conveying in work unit, plasticizing, be kneaded, injection
Co2 (carbon dioxide);
Step 3: being delivered to work unit by net-changing device connector under the promotion of screw rod when raw material is at viscous state, process is secondary
Foaming;
Step 4: due to being filled with co2 carbon dioxide in unit while cooperating foaming agent and nucleating agent, passing through work unit screw rod
Stirring form a large amount of nuclei of bubbles, be extruded machine extrusion die mouth in a flash, influenced by atmospheric pressure, formed one
Each and every one independent bubble, surrounding materials at this time bulge, and the material to bulge are flattened by planisher, shaping is finally by dragger
It involves;
Step 5: finally debugging out the product needed by specification, finally done using trimming, plucking, fluting, cutting and packaging
Finished product out.
5. a kind of novel XPS plastic extrusion heated board preparation method according to claim 4, it is characterised in that: the step 3
Middle second time of foaming temperature is 125 DEG C.
6. a kind of novel XPS plastic extrusion heated board preparation method according to claim 4, it is characterised in that: the step 4
In extruder be single order parallel dual-screw and second order single screw extrusion machine.
7. a kind of novel XPS plastic extrusion heated board preparation method according to claim 4, it is characterised in that: the step 4
In foaming agent be AC foaming agent.