CN110000071A - A kind of production technology of X-ray film - Google Patents
A kind of production technology of X-ray film Download PDFInfo
- Publication number
- CN110000071A CN110000071A CN201910286185.XA CN201910286185A CN110000071A CN 110000071 A CN110000071 A CN 110000071A CN 201910286185 A CN201910286185 A CN 201910286185A CN 110000071 A CN110000071 A CN 110000071A
- Authority
- CN
- China
- Prior art keywords
- added
- agent
- production
- deionized water
- silver nitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technology of X-ray film, the percentage of the raw material composition are as follows: resin 8%~45%, crosslinking agent 0.8%~7.5%, polymethyl methacrylate 0.3%~3%, matting agent 2%~15%, nonionic surface active agent 3%~5%, polyacrylic acid 2%~5%, antistatic agent 4%~10%, polyvinyl alcohol 5%~55%, deionized water 80%~90%, gel 10%~20%, potassium bromide 30%~40%, potassium iodide 1%~2%, silver nitrate 40%~50%, titanium dioxide 1%~3%, antioxidant 2%~3%.Compared with other X-ray films, invention in the backing layer coating of production chip base by being added antistatic agent and antioxidant, so that the chip base made has good antistatic property, oxidative phenomena will not occur easily in use, be conducive to save the information of film face, the film face of production is smooth, so that adhesion during film printing, and simple production process.
Description
Technical field
The invention belongs to X-ray film technical fields, and in particular to a kind of production technology of X-ray film.
Background technique
X-ray film is that the shooting of confession under directions X-ray uses, and has and is coated with emulsion on the two sides of chip base to improve the direct of sensitivity
Film for shooting, and the indirect film (35 millimeters, 56*84 millimeters) for shooting by X-ray shooting fluorescent picture.It is indirectly for shooting
Film, in addition to radiograph, in terms of the photographic recording for being also used to cathode-ray tube oscillograph etc.,
Existing X-ray film when in use, since surface is not smooth enough, is easy to happen adhesion, and X-ray in printing use
For film after long-term place, the contents on surface are easy to happen oxidation, so that information is lost, for this purpose, it is proposed that a kind of X-ray
The production technology of film.
Summary of the invention
It is an object of the invention to overcome the deficiencies of existing technologies, a kind of production technology of X-ray film of proposition, by
It makes and antistatic agent and antioxidant is added in the backing layer coating of chip base, so that the chip base made is with good antistatic
Property, and oxidative phenomena will not occur easily in use, be conducive to the information for saving film face, the glue that the present invention makes
Piece smooth surface, so that adhesion during film printing, crosses machine, and simple production process with good.
To achieve the goals above, technical scheme is as follows:
A kind of production technology of X-ray film, it is characterised in that: the percentage of the raw material composition are as follows:
Resin 8%~45%, crosslinking agent 0.8%~7.5%, polymethyl methacrylate 0.3%~3%, matting agent 2%
~15%, nonionic surface active agent 3%~5%, polyacrylic acid 2%~5%, antistatic agent 4%~10%, polyvinyl alcohol
5%~55%, deionized water 80%~90%, gel 10%~20%, potassium bromide 30%~40%, potassium iodide 1%~2%,
Silver nitrate 40%~50%, titanium dioxide 1%~3%, antioxidant 2%~3%;
S1, production bottom coating: it is stirred standing by deionized water is added in nonionic surface active agent, then will
Deionized water is added after mixing evenly after polyvinyl alcohol and polymethyl methacrylate mixing, by nonionic surface active agent and
The mixing liquid of deionized water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, bottom coating is obtained;
S2, production backing layer coating: then resin and deionized water agitation and dilution mix deionized water with polyacrylic acid
It stirs afterwards 4 minutes, antistatic agent and antioxidant is then divided into 3 times and are added thereto and stir evenly standing 2 minutes, then will
The mixed liquor of deionized water and resin pours into wherein, while crosslinking agent is added, and be sufficiently stirred, and obtains backing layer coating;
S3, production chip base: backing layer coating and bottom coating are applied on film respectively, and stand 15 minutes, after dry
For use;
S4, production emulsion: the warm distilled water that appropriate gel is added dissolves, and potassium bromide and potassium iodide are put into gel
It in solution, and constantly stirs until dissolution, then silver nitrate will be put into dissolution in distilled water and form silver nitrate solution, then will
Titanium dioxide pours into dissolution in distilled water and forms titania solution, and silver nitrate solution and titania solution are slowly poured into
In above-mentioned steps in solution obtained, after mixing, the temperature of mixed liquor is maintained at 55 DEG C, continues 10 minutes, then make
It is cooled to 40 DEG C, and stands 12h, forms gelatin, then warm distilled water is added in gelatin and is softened, and by the gel after softening
Stirring and dissolving in silver nitrate solution is poured into, cooling is stood, is then repeatedly washed, heated after washing, is heated to
It 55 DEG C, cools down after heating time at 40 DEG C, obtains emulsion.
S5, production film: emulsion is uniformly applied to the surface of chip base, then will smear the chip base of emulsion
It places dry with recessed shady place.
Preferred: the antistatic agent uses fatty alcohol polyoxyethylene ether.
Preferred: the antioxidant uses metal ion chelation agent.
Technical effect and advantage of the invention:
The present invention in the backing layer coating of production chip base by being added antistatic agent and antioxidant, so that the piece made
Base has good antistatic property, and oxidative phenomena will not occur easily in use, is conducive to save film face
Information, the film face that the present invention makes is smooth, so that adhesion during film printing, crosses machine with good, and raw
Production. art is simple.
Specific embodiment
The present invention is described in further details below with reference to embodiment.
Embodiment 1:
Resin 8%, crosslinking agent 0.8%, polymethyl methacrylate 0.3%, matting agent 2%, non-ionic surfactant
Agent 3%, polyacrylic acid 2%, antistatic agent 4%, polyvinyl alcohol 5%, deionized water 80%, gel 10%, potassium bromide 30%, iodine
Change potassium 1%, silver nitrate 43%, titanium dioxide 1%, antioxidant 2%.
The preparation method comprises the following steps: production bottom coating: will in nonionic surface active agent be added deionized water be stirred it is quiet
It sets, deionized water is added after mixing evenly after then mixing polyvinyl alcohol and polymethyl methacrylate, by non-ionic table
The mixing liquid of face activating agent and deionized water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, is obtained
To bottom coating;By resin and deionized water agitation and dilution, stirred 4 minutes after then mixing deionized water with polyacrylic acid,
Then antistatic agent and antioxidant are divided into 3 times and are added thereto and stir evenly standing 2 minutes, then by deionized water and tree
The mixed liquor of rouge pours into wherein, while crosslinking agent is added, and is sufficiently stirred, and obtains backing layer coating, and backing layer coating and bottom are applied
Material is applied on film respectively, and stands 15 minutes, after dry stand-by, the warm distilled water that appropriate gel is added dissolves, by bromine
Change potassium and potassium iodide is put into gel solution, and constantly stirs until dissolution, then silver nitrate will be put into molten in distilled water
Solution forms silver nitrate solution, and titanium dioxide is then poured into dissolution in distilled water and forms titania solution, by silver nitrate solution
It slowly pours into titania solution in above-mentioned steps in solution obtained, after mixing, the temperature of mixed liquor is kept
At 55 DEG C, continue 10 minutes, be then allowed to cool to 40 DEG C, and stand 12h, forms gelatin, then warm distilled water is added in gelatin
Softened, and the gel after softening poured into stirring and dissolving in silver nitrate solution, stood cooling, then repeatedly washed,
It is heated after washing, is heated to 55 DEG C, cooled down after heating time at 40 DEG C, obtain emulsion, emulsion is equal
Then the even surface for being applied to chip base places the chip base for having smeared emulsion dry with recessed shady place.
Embodiment 2:
Resin 15%, crosslinking agent 3%, polymethyl methacrylate 1%, matting agent 5%, nonionic surface active agent
3.5%, polyacrylic acid 3%, antistatic agent 5%, polyvinyl alcohol 20%, deionized water 83%, gel 14%, potassium bromide 32%,
Potassium iodide 1.4%, silver nitrate 44%, titanium dioxide 1.5%, antioxidant 2.2%.
The preparation method comprises the following steps: production bottom coating: will in nonionic surface active agent be added deionized water be stirred it is quiet
It sets, deionized water is added after mixing evenly after then mixing polyvinyl alcohol and polymethyl methacrylate, by non-ionic table
The mixing liquid of face activating agent and deionized water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, is obtained
To bottom coating;By resin and deionized water agitation and dilution, stirred 4 minutes after then mixing deionized water with polyacrylic acid,
Then antistatic agent and antioxidant are divided into 3 times and are added thereto and stir evenly standing 2 minutes, then by deionized water and tree
The mixed liquor of rouge pours into wherein, while crosslinking agent is added, and is sufficiently stirred, and obtains backing layer coating, and backing layer coating and bottom are applied
Material is applied on film respectively, and stands 15 minutes, after dry stand-by, the warm distilled water that appropriate gel is added dissolves, by bromine
Change potassium and potassium iodide is put into gel solution, and constantly stirs until dissolution, then silver nitrate will be put into molten in distilled water
Solution forms silver nitrate solution, and titanium dioxide is then poured into dissolution in distilled water and forms titania solution, by silver nitrate solution
It slowly pours into titania solution in above-mentioned steps in solution obtained, after mixing, the temperature of mixed liquor is kept
At 55 DEG C, continue 10 minutes, be then allowed to cool to 40 DEG C, and stand 12h, forms gelatin, then warm distilled water is added in gelatin
Softened, and the gel after softening poured into stirring and dissolving in silver nitrate solution, stood cooling, then repeatedly washed,
It is heated after washing, is heated to 55 DEG C, cooled down after heating time at 40 DEG C, obtain emulsion, emulsion is equal
Then the even surface for being applied to chip base places the chip base for having smeared emulsion dry with recessed shady place.
Embodiment 3:
Resin 30%, crosslinking agent 6%, polymethyl methacrylate 2%, matting agent 12%, nonionic surface active agent
4%, polyacrylic acid 4%, antistatic agent 8%, polyvinyl alcohol 45%, deionized water 87%, gel 18%, potassium bromide 38%, iodine
Change potassium 1.8%, silver nitrate 47%, titanium dioxide 2.5%, antioxidant 2.8%.
The preparation method comprises the following steps: production bottom coating: will in nonionic surface active agent be added deionized water be stirred it is quiet
It sets, deionized water is added after mixing evenly after then mixing polyvinyl alcohol and polymethyl methacrylate, by non-ionic table
The mixing liquid of face activating agent and deionized water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, is obtained
To bottom coating;By resin and deionized water agitation and dilution, stirred 4 minutes after then mixing deionized water with polyacrylic acid,
Then antistatic agent and antioxidant are divided into 3 times and are added thereto and stir evenly standing 2 minutes, then by deionized water and tree
The mixed liquor of rouge pours into wherein, while crosslinking agent is added, and is sufficiently stirred, and obtains backing layer coating, and backing layer coating and bottom are applied
Material is applied on film respectively, and stands 15 minutes, after dry stand-by, the warm distilled water that appropriate gel is added dissolves, by bromine
Change potassium and potassium iodide is put into gel solution, and constantly stirs until dissolution, then silver nitrate will be put into molten in distilled water
Solution forms silver nitrate solution, and titanium dioxide is then poured into dissolution in distilled water and forms titania solution, by silver nitrate solution
It slowly pours into titania solution in above-mentioned steps in solution obtained, after mixing, the temperature of mixed liquor is kept
At 55 DEG C, continue 10 minutes, be then allowed to cool to 40 DEG C, and stand 12h, forms gelatin, then warm distilled water is added in gelatin
Softened, and the gel after softening poured into stirring and dissolving in silver nitrate solution, stood cooling, then repeatedly washed,
It is heated after washing, is heated to 55 DEG C, cooled down after heating time at 40 DEG C, obtain emulsion, emulsion is equal
Then the even surface for being applied to chip base places the chip base for having smeared emulsion dry with recessed shady place.
Embodiment 4:
Resin 45%, crosslinking agent 7.5%, polymethyl methacrylate 3%, matting agent 15%, non-ionic surfactant
Agent 5%, polyacrylic acid 5%, antistatic agent 10%, polyvinyl alcohol 55%, deionized water 90%, gel 20%, potassium bromide 40%,
Potassium iodide 2%, silver nitrate 50%, titanium dioxide 3%, antioxidant 3%.
The preparation method comprises the following steps: production bottom coating: will in nonionic surface active agent be added deionized water be stirred it is quiet
It sets, deionized water is added after mixing evenly after then mixing polyvinyl alcohol and polymethyl methacrylate, by non-ionic table
The mixing liquid of face activating agent and deionized water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, is obtained
To bottom coating;By resin and deionized water agitation and dilution, stirred 4 minutes after then mixing deionized water with polyacrylic acid,
Then antistatic agent and antioxidant are divided into 3 times and are added thereto and stir evenly standing 2 minutes, then by deionized water and tree
The mixed liquor of rouge pours into wherein, while crosslinking agent is added, and is sufficiently stirred, and obtains backing layer coating, and backing layer coating and bottom are applied
Material is applied on film respectively, and stands 15 minutes, after dry stand-by, the warm distilled water that appropriate gel is added dissolves, by bromine
Change potassium and potassium iodide is put into gel solution, and constantly stirs until dissolution, then silver nitrate will be put into molten in distilled water
Solution forms silver nitrate solution, and titanium dioxide is then poured into dissolution in distilled water and forms titania solution, by silver nitrate solution
It slowly pours into titania solution in above-mentioned steps in solution obtained, after mixing, the temperature of mixed liquor is kept
At 55 DEG C, continue 10 minutes, be then allowed to cool to 40 DEG C, and stand 12h, forms gelatin, then warm distilled water is added in gelatin
Softened, and the gel after softening poured into stirring and dissolving in silver nitrate solution, stood cooling, then repeatedly washed,
It is heated after washing, is heated to 55 DEG C, cooled down after heating time at 40 DEG C, obtain emulsion, emulsion is equal
Then the even surface for being applied to chip base places the chip base for having smeared emulsion dry with recessed shady place.
Claims (3)
1. a kind of production technology of X-ray film, it is characterised in that: the percentage of the raw material composition are as follows:
Resin 8%~45%, crosslinking agent 0.8%~7.5%, polymethyl methacrylate 0.3%~3%, matting agent 2%~
15%, nonionic surface active agent 3%~5%, polyacrylic acid 2%~5%, antistatic agent 4%~10%, polyvinyl alcohol
5%~55%, deionized water 80%~90%, gel 10%~20%, potassium bromide 30%~40%, potassium iodide 1%~2%,
Silver nitrate 40%~50%, titanium dioxide 1%~3%, antioxidant 2%~3%;
S1, production bottom coating: it is stirred standing by deionized water is added in nonionic surface active agent, then by poly- second
Enol and polymethyl methacrylate mixing after be added deionized water after mixing evenly, by nonionic surface active agent and go from
The mixing liquid of sub- water is poured slowly into, and after stirring, crosslinking agent is added, is again stirring for, bottom coating is obtained;
S2, production backing layer coating: resin and deionized water agitation and dilution stir after then mixing deionized water with polyacrylic acid
Mix 4 minutes, antistatic agent and antioxidant be then divided into 3 times and are added thereto and stir evenly standing 2 minutes, then will go from
The mixed liquor of sub- water and resin pours into wherein, while crosslinking agent is added, and be sufficiently stirred, and obtains backing layer coating;
S3, production chip base: backing layer coating and bottom coating being applied on film respectively, and stand 15 minutes, after dry it is stand-by;
S4, production emulsion: the warm distilled water that appropriate gel is added dissolves, and potassium bromide and potassium iodide are put into gel solution
In, and constantly stir until dissolution, then silver nitrate will be put into dissolution in distilled water and form silver nitrate solution, then by dioxy
Change titanium pours into dissolution in distilled water and forms titania solution, silver nitrate solution and titania solution is slowly poured into above-mentioned
In step in solution obtained, after mixing, the temperature of mixed liquor is maintained at 55 DEG C, continues 10 minutes, then make its cold
But to 40 DEG C, and 12h is stood, forms gelatin, then warm distilled water is added in gelatin and is softened, and the gel after softening is poured into
Stirring and dissolving in silver nitrate solution stands cooling, is then repeatedly washed, heated after washing, be heated to 55 DEG C,
It cools down after heating time at 40 DEG C, obtains emulsion;
Emulsion: being uniformly applied to the surface of chip base by S5, production film, then places the chip base for having smeared emulsion
It is dry with recessed shady place.
2. a kind of production technology of X-ray film as described in claim 1, which is characterized in that the antistatic agent is using fat
Alcohol polyoxyethylene ether.
3. a kind of production technology of X-ray film as described in claim 1, it is characterised in that: the antioxidant uses metal
Ion chelating agent.