CN109988511A - Water plugged by grouting glue and preparation method thereof - Google Patents
Water plugged by grouting glue and preparation method thereof Download PDFInfo
- Publication number
- CN109988511A CN109988511A CN201811597869.3A CN201811597869A CN109988511A CN 109988511 A CN109988511 A CN 109988511A CN 201811597869 A CN201811597869 A CN 201811597869A CN 109988511 A CN109988511 A CN 109988511A
- Authority
- CN
- China
- Prior art keywords
- component
- water
- plugged
- grouting glue
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water plugged by grouting glue and preparation method thereof, the mass ratio including component A and B component is (10-40): 1;Component A includes polyacrylate 25-60%;Monohydrate lithium hydroxide 0.1-3%;Surfactant 0.1-2%;Silica 5-25%;Acrylamide 10-40%;Polymerization inhibitor 0.01-0.5%;Excess water;B component includes ammonium sulfate 0.01-0.5%;Sodium pyrosulfite 0.01-0.5%;Excess water.The present invention, which restores to cause by bi-component, generates gel, is poured into gap and expansion joint, thus leak stopping sealing, since gap and expansion joint are there are water, product can allow water to thicken rapidly, there is the expansion rate of 150-500% after solidifying water depletion fluidity, colloid;Form changes with crack, and colloid shape is not collapsed under long-term wet environment.The wet body of remaining flexible property is solid-state like after plastic, has fabulous elasticity and stretching force and adhesive strength, and gel time is adjustable, has excellent concrete castability, is suitble to machinery mud jacking or the manual cementation of fissures and water blockoff.
Description
Technical field
The present invention relates to building materials field fields, and in particular to a kind of filling elastomeric as prepared by based on polyacrylate
Starch water blockoff glue and preparation method thereof.
Background technique
Currently, buildings waterproof plugging material such as polyurathamc, the appearance such as epoxy resin largely repeat to leak, be all because
There is no plasticity after material solidification, cannot be with seasonal building tear, concrete stress, leak environment etc. changes and becomes
Change, extreme loss and significant wastage is caused to construction party and owner, the reason is that these materials are linear material, molecular weight mostly
Greatly, viscosity is high, and concrete castability is poor, and leak stopping is poor.Epoxy resin its viscosity after processing is 60-80s (applying -4 glasss of viscosmeters), water
Property polyurethane or polyurathamc it is attainable it is ultimate attainment be also 40-120s.In addition, existing linear material is poor except leak stopping, effect
It is bad outer, it is easily aoxidized at dark humidity for a long time, quickly, the service life is very short for performance degradation.
Summary of the invention
The invention proposes a kind of water plugged by grouting glue and preparation method thereof, the application property initial viscosity for solving material is high
Problem, not oxidizable and material has self-healing property under dark wet environment, and water-swellable has stronger bonding force and attached
Put forth effort.
To achieve the goals above, the present invention is achieved through the following technical solutions:
The mass ratio of a kind of water plugged by grouting glue, including component A and B component, the component A and B component is (10-40): 1;
The component A includes following components, by weight percent are as follows: polyacrylate 25-60%;Monohydrate lithium hydroxide
0.1-3%;Surfactant 0.1-2%;Silica 5-25%;Acrylamide 10-40%;Polymerization inhibitor 0.01-0.5%;It is remaining
Measure water;
The B component includes following components, by weight percent are as follows: ammonium sulfate 0.01-0.5%;Sodium pyrosulfite 0.01-
0.5%;Excess water.
Preferably, the component A includes following components, by weight percent are as follows: polyacrylate 30-50%;Single water hydrogen
Lithia 0.1-2%;Surfactant 0.1-1%;Silica 1 0-25%;Acrylamide 15-35%;Polymerization inhibitor 0.01-
0.3%;Excess water.
Preferably, the component A includes following components, by weight percent are as follows: polyacrylate 35-45%;Single water hydrogen
Lithia 0.1-1%;Surfactant 0.1-0.9%;Silica 1 0-20%;Acrylamide 20-30%;Polymerization inhibitor 0.01-
0.1%;Excess water.
Preferably, the B component includes following components, by weight percent are as follows: ammonium sulfate 0.01-0.2%;Pyrosulfurous acid
Sodium 0.01-0.2%;Excess water.
Preferably, the B component includes following components, by weight percent are as follows: ammonium sulfate 0.01-0.1%;Pyrosulfurous acid
Sodium 0.01-0.1%;Excess water.
Surfactant described above is fluorocarbon surfactant.
Polymerization inhibitor described above is 2- tert-butyl hydroquinone, in 2,5- tert-butyl hydroquinone, p-hydroxyanisole
Any one.
The preparation method of water plugged by grouting glue, it is characterised in that: the following steps are included:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, propylene
After amide and polymerization inhibitor mix at normal temperature, water is added, mixed liquor A is obtained;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is obtained
To mixed liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B are mixed, and rapidly after mixing evenly, fracture faces can be poured into,
And it is used in 4h.
Water plugged by grouting glue of the present invention and preparation method thereof, the beneficial effect is that:
(1) it restores to cause by bi-component and generates gel, be poured into gap and expansion joint, thus leak stopping sealing, due to seam
There are water, product can allow water to thicken rapidly for gap and expansion joint, there is that 150-500%'s is swollen after solidifying water depletion fluidity, colloid
Swollen rate;Form changes with crack, and colloid shape is not collapsed under long-term wet environment.
(2) the wet body of remaining flexible property is solid-state like after plastic, has fabulous elasticity and stretching force and adhesive strength, coagulates
The glue time is adjustable, has excellent concrete castability, is suitble to machinery mud jacking or the manual cementation of fissures and water blockoff.
It (3) is 10s with initial viscosity after glue, the cementation of fissures is rapid, and crack closure is good, and construction method is simple, especially has in humidity
It can be used in the environment of water.
Specific embodiment
It is next combined with specific embodiments below that present invention be described in more detail.
Embodiment 1
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 35:1,
Component A includes following components, by weight percent are as follows: polyacrylate 25%;Monohydrate lithium hydroxide 0.1%;Fluorine
Carbon surface active agent 0.1%;Silica 5%;Acrylamide 10%;2- tert-butyl hydroquinone 0.01%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.01%;Sodium pyrosulfite 0.01;Excess water;
The preparation method of water plugged by grouting glue, comprising the following steps:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, propylene
After amide and polymerization inhibitor mix at normal temperature, water is added, mixed liquor A is obtained;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is obtained
To mixed liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B are mixed, and rapidly after mixing evenly, fracture faces can be poured into,
And it is used in 4h.
Embodiment 2
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 15:1,
Component A includes following components, by weight percent are as follows: polyacrylate 60%;Monohydrate lithium hydroxide 0.3%;Fluorine
Carbon surface active agent 0.2%;Silica 5%;Acrylamide 25%;2- tert-butyl hydroquinone 0.5%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.5%;Sodium pyrosulfite 0.5;Excess water;
The preparation method of water plugged by grouting glue, comprising the following steps:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, propylene
After amide and polymerization inhibitor mix at normal temperature, water is added, mixed liquor A is obtained;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is obtained
To mixed liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B are mixed, and rapidly after mixing evenly, fracture faces can be poured into,
And it is used in 4h.
Embodiment 3
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 25:1,
Component A includes following components, by weight percent are as follows: polyacrylate 30%;Monohydrate lithium hydroxide 2%;Fluorine carbon
Surfactant 1%;Silica 1 0%;Acrylamide 15%;2- tert-butyl hydroquinone 0.3%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.2%;Sodium pyrosulfite 0.2;Excess water;
The preparation method of water plugged by grouting glue, comprising the following steps:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, propylene
After amide and polymerization inhibitor mix at normal temperature, water is added, mixed liquor A is obtained;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is obtained
To mixed liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B are mixed, and rapidly after mixing evenly, fracture faces can be poured into,
And it is used in 4h.
Embodiment 4
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 40:1,
Component A includes following components, by weight percent are as follows: polyacrylate 50%;Monohydrate lithium hydroxide 2%;Fluorine carbon
Surfactant 1%;Silica 25%;Acrylamide 35%;2- tert-butyl hydroquinone 0.3%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.2%;Sodium pyrosulfite 0.2;Excess water;
The preparation method of water plugged by grouting glue, comprising the following steps:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, propylene
After amide and polymerization inhibitor mix at normal temperature, water is added, mixed liquor A is obtained;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is obtained
To mixed liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B are mixed, and rapidly after mixing evenly, fracture faces can be poured into,
And it is used in 4h.
Embodiment 5
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 30:1,
Component A includes following components, by weight percent are as follows: polyacrylate 35%;Monohydrate lithium hydroxide 1%;Fluorine carbon
Surfactant 0.9%;Silica 20%;Acrylamide 20%;2- tert-butyl hydroquinone 0.1%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.1%;Sodium pyrosulfite 0.1;Excess water;
Embodiment 6
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 20:1,
Component A includes following components, by weight percent are as follows: polyacrylate 45%;Monohydrate lithium hydroxide 0.5%;Fluorine
Carbon surface active agent 0.5%;Silica 1 0%;Acrylamide 30%;2- tert-butyl hydroquinone 0.05%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.05%;Sodium pyrosulfite 0.02;Excess water;
Embodiment 7
A kind of water plugged by grouting glue: including component A and B component, the mass ratio including component A and B component is 10:1,
Component A includes following components, by weight percent are as follows: polyacrylate 45%;Monohydrate lithium hydroxide 0.5%;Fluorine
Carbon surface active agent 0.5%;Silica 1 5%;Acrylamide 25%;2- tert-butyl hydroquinone 0.02%;Excess water;
B component includes following components, by weight percent are as follows: ammonium sulfate 0.03%;Sodium pyrosulfite 0.01;Excess water.
The application method of embodiment 1-7 are as follows:
One, basic crack surface is cleaned up
Two, component A and B component are slightly stirred and pours into fracture faces at once.Make in 4 hours after component A and B component mixing
It is finished, time-out can be reduced using properties of product.
Three, after gel, the extra gel of fracture faces is rooted out, criticizes and scrapes 0.5-1.0cm thickness acrylamide sand grout as protective layer.
Four, temperature has larger impact to curing rate, and usual temperature is at 25 DEG C or less;If temperature is at 30 DEG C or more, B component
Dosage accordingly to reduce.
It is provided for the embodiments of the invention technical solution above to be described in detail, specific case used herein
The principle and embodiment of the embodiment of the present invention are expounded, the explanation of above embodiments is only applicable to help to understand this
The principle of inventive embodiments;At the same time, for those skilled in the art, according to an embodiment of the present invention, in specific embodiment party
There will be changes in formula and application range, in conclusion the contents of this specification are not to be construed as limiting the invention.
Claims (8)
1. a kind of water plugged by grouting glue, it is characterised in that: including component A and B component, the mass ratio of the component A and B component is
(10-40): 1;
The component A includes following components, by weight percent are as follows: polyacrylate 25-60%;Monohydrate lithium hydroxide 0.1-
3%;Surfactant 0.1-2%;Silica 5-25%;Acrylamide 10-40%;Polymerization inhibitor 0.01-0.5%;Excess water;
The B component includes following components, by weight percent are as follows: ammonium sulfate 0.01-0.5%;Sodium pyrosulfite 0.01-
0.5%;Excess water.
2. water plugged by grouting glue according to claim 1, it is characterised in that: the component A includes following components, by quality percentage
Number are as follows: polyacrylate 30-50%;Monohydrate lithium hydroxide 0.1-2%;Surfactant 0.1-1%;Silica 1 0-25%;
Acrylamide 15-35%;Polymerization inhibitor 0.01-0.3%;Excess water.
3. water plugged by grouting glue according to claim 1, it is characterised in that: the component A includes following components, by quality percentage
Number are as follows: polyacrylate 35-45%;Monohydrate lithium hydroxide 0.1-1%;Surfactant 0.1-0.9%;Silica 1 0-
20%;Acrylamide 20-30%;Polymerization inhibitor 0.01-0.1%;Excess water.
4. water plugged by grouting glue according to claim 1, it is characterised in that: the B component includes following components, by quality percentage
Number are as follows: ammonium sulfate 0.01-0.2%;Sodium pyrosulfite 0.01-0.2%;Excess water.
5. water plugged by grouting glue according to claim 1, it is characterised in that: the B component includes following components, by quality percentage
Number are as follows: ammonium sulfate 0.01-0.1%;Sodium pyrosulfite 0.01-0.1%;Excess water.
6. water plugged by grouting glue according to claim 1, it is characterised in that: the surfactant is fluorocarbon surfactant.
7. water plugged by grouting glue according to claim 1, it is characterised in that: the polymerization inhibitor be 2- tert-butyl hydroquinone, 2,
Any one in 5- tert-butyl hydroquinone, p-hydroxyanisole.
8. the preparation method of water plugged by grouting glue described in -7 Arbitrary Terms according to claim 1, it is characterised in that: including following step
It is rapid:
(1) preparation method of component A: by polyacrylate, monohydrate lithium hydroxide, surfactant, silica, acrylamide
After mixing at normal temperature with polymerization inhibitor, water is added, obtains mixed liquor A;
(2) preparation method of B component: after ammonium sulfate and sodium pyrosulfite are mixed, the water that surplus is added is mixed, and is mixed
Close liquid B;
(3) i.e. with i.e. use: mixed liquor A and mixed liquid B being mixed, and rapidly after mixing evenly, fracture faces, and 4h can be poured into
Inside use.