CN109987863A - Frosting laminated glass and preparation method thereof - Google Patents
Frosting laminated glass and preparation method thereof Download PDFInfo
- Publication number
- CN109987863A CN109987863A CN201910265386.1A CN201910265386A CN109987863A CN 109987863 A CN109987863 A CN 109987863A CN 201910265386 A CN201910265386 A CN 201910265386A CN 109987863 A CN109987863 A CN 109987863A
- Authority
- CN
- China
- Prior art keywords
- layer
- frosting
- basal layer
- film
- laminated glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of frosting laminated glass, it includes at least two basal layer, at least two basal layer overlaps setting, and overlaps at least two basal layer being arranged, and is smooth surface positioned at the upper surface of the basal layer of top layer and positioned at the lower surface of undermost basal layer；At least one frosted layer；The corresponding surface for being prepared in basal layer of frosted layer；At least one film plating layer；The corresponding surface for being covered in frosted layer of film plating layer；At least one adhesive film；Adhesive film is for the connection between two neighboring basal layer；Present invention further teaches a kind of preparation methods of frosting laminated glass.The frosting laminated glass of the application, by carrying out coating film treatment on frosting face, so that frosting face still keeps frosted finish effect under the high-temperature process of doubling；In addition, the preparation method of the application is simple, industrialized production can be carried out.
Description
Technical field
The present invention relates to glass technology fields, and in particular, to a kind of frosting laminated glass and preparation method thereof.
Background technique
All glass by frosting processing can be known as mat glass, mat glass as dim art glass,
Aesthetic feeling is added for spatial decoration, is the new lover of art glass.With the development and growth of decoration industry, mat glass is being filled
It is nearly ubiquitous in decorations space, it is widely used on the finishing such as wall, partition, door and window, glass tea table.Mat glass is very
Good is organically combined together indoor with scenery external by artistic decoration.When monolithic mat glass uses in the prior art
The disadvantages of that there are surfaces is not easy to clean, broken safety is insufficient；And mat glass doubling product is exposed to air due to frosting face
In, surface is not also easy to clean；If frosting face is placed on the inside of laminated glass, and because glue film is in the high-temperature process of doubling technique
The problem of there is down mobility, frosting face is made to lose frosted finish effect.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of frosting laminated glass and preparation method thereof.
A kind of frosting laminated glass disclosed by the invention includes:
At least two basal layer, at least two basal layer overlaps setting, and overlaps at least two substrate of setting
It is smooth surface positioned at the upper surface of the basal layer of top layer and positioned at the lower surface of undermost basal layer in layer；
At least one frosted layer；The corresponding surface for being prepared in basal layer of frosted layer；
At least one film plating layer；The corresponding surface for being covered in frosted layer of film plating layer；
At least one adhesive film；Adhesive film is for the connection between two neighboring basal layer.
According to an embodiment of the present invention, basal layer is transparent glass.
According to an embodiment of the present invention, basal layer is in plate glass, tempered glass, heat-bending glass and coated glass
It is one or more.
According to an embodiment of the present invention, adhesive film is XIR composite membrane, PVB film, SGP film, EVA film and PU glue
One of piece is a variety of.
According to an embodiment of the present invention, film plating layer is transparent nano film layer.
The preparation method of frosting laminated glass disclosed by the invention, comprising the following steps:
At least one basal layer is by frosting process, after tempering, obtains the basal layer at least one frosted layer；
Frosted layer is handled by coating process, and film plating layer is covered in the surface of frosted layer；
At least two basal layer overlaps setting, wherein two neighboring basal layer carries out doubling process, forms glue film
Layer, and positioned at the upper surface of the basal layer of top layer and be smooth surface positioned at the lower surface of undermost basal layer.
According to an embodiment of the present invention, frosting process uses chemical frost method or physics sand-blast.
According to an embodiment of the present invention, chemical frost method refers to is acted on basal layer by frosting cream, after tempering, is obtained
There must be the basal layer of frosted layer.
According to an embodiment of the present invention, coating process processing uses physical coating method or electroless plating.
According to an embodiment of the present invention, doubling technique is dry lamination technique.
Present invention, by carrying out coating film treatment on frosting face, so that under the high-temperature process of doubling, frosting face
Frosted finish effect is still kept, the frosting face for avoiding single layer mat glass or frosting doubling glass exposes in air, is not easy
The problem of cleaning；In addition, the preparation method of the application is simple, industrialized production can be carried out, in combination with the works such as colored glaze, hollow
Skill, breaks that mat glass dicoration is excessively single, reaches the diversification of product.
Detailed description of the invention
The drawings described herein are used to provide a further understanding of the present application, constitutes part of this application, this Shen
Illustrative embodiments and their description please are not constituted an undue limitation on the present application for explaining the application.In the accompanying drawings:
Fig. 1 is the structural schematic diagram of frosting laminated glass in embodiment 2；
Fig. 2 is the structural schematic diagram of frosting laminated glass in embodiment 3；
Fig. 3 is the structural schematic diagram of frosting laminated glass in embodiment 4.
Specific embodiment
Multiple embodiments of the invention will be disclosed with schema below, as clearly stated, the details in many practices
It will be explained in the following description.It should be appreciated, however, that the details in these practices is not applied to limit the present invention.Also
It is to say, in some embodiments of the invention, the details in these practices is non-essential.In addition, for the sake of simplifying schema,
Some known usual structures and component will be painted it in the drawings in simply illustrative mode.
It is to be appreciated that the directional instruction such as up, down, left, right, before and after ... of institute is only used in the embodiment of the present invention
Relative positional relationship, the motion conditions etc. in the case where a certain particular pose is as shown in the picture between each component are explained, if this is specific
When posture changes, then directionality instruction also correspondingly changes correspondingly.
In addition, the description for being such as related to " first ", " second " in the present invention is used for description purposes only, not especially censure
The meaning of order or cis-position, also non-to limit the present invention, the component described just for the sake of difference with same technique term
Or operation, it is not understood to indicate or imply its relative importance or implicitly indicates the number of indicated technical characteristic
Amount." first " is defined as a result, the feature of " second " can explicitly or implicitly include at least one of the features.In addition, each
Technical solution between a embodiment can be combined with each other, but must can be implemented as base with those of ordinary skill in the art
Plinth will be understood that the combination of this technical solution is not present when conflicting or cannot achieve when occurs in the combination of technical solution,
Also not the present invention claims protection scope within.
In order to further understand the content, features and effects of the present invention, the following examples are hereby given, and cooperate attached drawing
Detailed description are as follows:
Embodiment 1:
Frosting laminated glass in the present embodiment includes basal layer 1, frosted layer 2, film plating layer 3 and adhesive film 4.Wherein, until
Few two basal layers 1, at least two basal layer 1 overlaps setting, and overlaps at least two basal layer 1 being arranged, position
It is smooth surface in the upper surface of the basal layer 1 of top layer and positioned at the lower surface of undermost basal layer 1.Preferably, base
Bottom 1 is transparent glass.This set can make smooth surface in outermost, can be to avoid frosting face outside, and it is inconvenient to clean.Extremely
A few frosted layer 2, the corresponding surface for being prepared in basal layer 1 of frosted layer 2.At least one film plating layer 3, the corresponding covering of film plating layer 3
In the surface of frosted layer 2, this set can make under the high-temperature process of doubling, and frosting face still keeps frosted finish effect.It is preferred that
, film plating layer 3 is transparent nano film layer.At least one adhesive film 4, adhesive film 4 is for the company between two neighboring basal layer 1
It connects.
In the present embodiment basal layer 1 can be used one of plate glass, tempered glass, heat-bending glass and coated glass or
It is a variety of, by the matched combined between different plates, so that frosting laminated glass obtained has the characteristic of various materials.Substrate
The size of layer 1 can design according to actual needs.
Adhesive film 4 in the present embodiment can be in XIR composite membrane, PVB film, SGP film, EVA film and PU film
It is one or more, can be selected according to the basal layer 1 of different characteristics material, guarantee adhesive effect between multiple basal layers 1.
Embodiment 2:
Referring to Fig.1, Fig. 1 is the structural schematic diagram of the present embodiment frosting laminated glass.Frosting interlayer glass in the present embodiment
Glass difference from example 1 is that comprising two film plating layers 3 of frosted layer 2, one of basal layer 1, one and a glue film
Layer 4.
Embodiment 3:
It is the structural schematic diagram of the present embodiment frosting laminated glass referring to Fig. 2, Fig. 2.Frosting interlayer glass in the present embodiment
Glass difference from example 1 is that comprising two film plating layers 3 of frosted layer 2, two of basal layer 1, two and a glue film
Layer 4.
Embodiment 4:
It is the structural schematic diagram of the present embodiment frosting laminated glass referring to Fig. 3, Fig. 3.Frosting interlayer glass in the present embodiment
Glass difference from example 1 is that comprising three film plating layers 3 of frosted layer 2, two of basal layer 1, two and two glue films
Layer 4.
Embodiment 5:
In the present embodiment frosting laminated glass preparation method the following steps are included:
S1, at least one basal layer 1 is by frosting process, after tempering, obtains the base at least one frosted layer 2
Bottom 1.Frosting technique is sandblasted method using chemical frost method or physics, specifically, chemical frost method refers to commercially available frosting cream
First stirring evenly, for the amount of taking fully frosting cream on 100-200 mesh nylon monofilament screen cloth, silk screen and basal layer 1 keep 2-4mm spacing,
So that silk screen can bounce off rapidly 1 surface of basal layer after silk-screen, with polyurethane scraper plate, by frosting cream uniformly at full tilt silk-screen in substrate
Layer 1 allows frosting cream to rest on 1 surface of basal layer and reacts 10-60 seconds, then cleans 1 surface of basal layer with clear water, after drying i.e.
It can；Physics sand-blast, which refers to, is sprayed onto 1 surface of basal layer with diamond dust mixing water high speed, causes physics to corrode on 1 surface of basal layer；
The present embodiment is using chemical frost method.Physical toughened method or chemical tempering process can be used in tempering, specifically, physical toughened
Method refers to will be heated to softening temperature (600 close to basal layer 1 by the basal layer 1 after frosting process in heating furnace
DEG C) when, stress is eliminated by the deformation of itself, basal layer 1 is then removed into heating furnace, then with bull nozzle by high pressure cold air
The two sides for blowing to basal layer 1, is cooled to room temperature it rapidly and uniformly；Chemical tempering process refers to the surface by changing glass
Chemical composition improve the intensity of glass, usually carry out tempering using ion-exchange, method is will to contain alkali metal
The silicate-base bottom 1 of ion, is immersed in the lithium salts of molten condition, makes the sodium ion or potassium ion and lithium on 1 surface layer of basal layer
Ion exchanges, and surface forms lithium ion exchanged layer, since the coefficient of expansion of lithium ion is less than sodium ion and potassium ion, thus
It causes outer layer to shrink smaller and internal layer in cooling procedure and shrinks larger, after being cooled to room temperature, glass is just similarly in internal layer
Tension, the state that outer layer is pressurized, effect are similar to physical toughened method；The present embodiment is using physical toughened method.Through tempering
Treated, and 1 intensity of basal layer greatly improves, and treated that the broken fractionlet of basal layer 1 does not have sharp corners for tempering,
It is not easy to hurt sb.'s feelings, safety is relatively high.
S2, frosted layer 2 carry out coating process processing, and film plating layer 3 is covered in the surface of frosted layer 2.Coating process processing is adopted
With physical coating method or electroless plating；Electroless plating is commonly collosol and gel coating method and chemical vapor deposition plated film
Method；Physical coating method is commonly vacuum evaporatation and vacuum magnetron sputtering coating film method.The present embodiment is using vacuum
Basal layer 1 with film plating layer 3 is placed in vacuum chamber, reaction gas is passed through in vacuum chamber, when right by magnetron sputtering embrane method
When sputter cathode is powered, under the action of electric field, electron ion hits metallic, and basal layer can be deposited on by forming charged particle
Film is formed on 1.There is film layer securely and uniformly using vacuum magnetron sputtering coating film method plated film, stable chemical performance, and capable of obtaining
The advantages that obtaining a variety of ideal optical properties.
S3, at least two basal layer 1 overlap setting, wherein two neighboring basal layer 1 carries out doubling process, shape
It at adhesive film 4, and positioned at the upper surface of the basal layer 1 of top layer and is light positioned at the lower surface of undermost basal layer 1
Face cleaning.Specifically, refer among two panels or the above basal layer 1 of two panels use the pre- conjunction precompressed such as PVB film or EVA film,
It is then sent to bubble of the autoclave among constant temperature and pressure processing, the adhesive film 4 that pressurizes out, so that adhesive film 4 and basal layer 1 are good
Bond together.After doubling process, laminated glass penetration ability is strong, can also prevent fragment from stabbing and penetrating
Event occurs.
To sum up, the frosting laminated glass of the application on frosting face by carrying out coating film treatment, so that in the high temperature of doubling
Under processing, frosting face still keeps frosted finish effect, avoids the frosting face exposure of single layer mat glass or frosting doubling glass
In air, it is not easy the problem of cleaning；In addition, the preparation method of the application is simple, industrialized production can be carried out, in combination with color
The techniques such as glaze, hollow, break that mat glass dicoration is excessively single, reach the diversification of product, while improving the peace of product
Quan Xing.
Upper is only embodiments of the present invention, is not intended to restrict the invention.To those skilled in the art,
The invention may be variously modified and varied.All any modifications made in spirit and principles of the present invention, equivalent replacement,
Improve etc., it should all be included within scope of the presently claimed invention.
Claims (10)
1. a kind of frosting laminated glass characterized by comprising
At least two basal layer (1), at least two basal layer (1) overlaps setting, and overlaps at least two of setting
The basal layer (1) in, positioned at the basal layer (1) of top layer upper surface and be located at undermost basal layer (1) under
Surface is smooth surface；
At least one frosted layer (2)；The corresponding surface for being prepared in the basal layer (1) of the frosted layer (2)；
At least one film plating layer (3)；The corresponding surface for being covered in the frosted layer (2) of the film plating layer (3)；And
At least one adhesive film (4)；The adhesive film (4) is for the connection between the two neighboring basal layer (1).
2. frosting laminated glass according to claim 1, which is characterized in that the basal layer (1) is transparent glass.
3. frosting laminated glass according to claim 2, which is characterized in that the basal layer (1) is plate glass, tempering
One of glass, heat-bending glass and coated glass are a variety of.
4. frosting laminated glass according to claim 1, which is characterized in that the adhesive film (3) is XIR composite membrane, PVB
One of film, SGP film, EVA film and PU film are a variety of.
5. frosting laminated glass according to claim 1, which is characterized in that the film plating layer (3) is transparent nano film layer.
6. a kind of preparation method of frosting laminated glass as described in claim 1, which comprises the following steps:
At least one basal layer (1) is by frosting process, after tempering, obtains the substrate at least one frosted layer (2)
Layer (1)；
The frosted layer (2) is handled by coating process, and film plating layer (3) is covered in the surface of frosted layer (2)；
At least two basal layer (1) overlaps setting, wherein the two neighboring basal layer (1) carries out at doubling technique
Reason is formed adhesive film (4), and is located at the upper surface of the basal layer (1) of top layer and is located under undermost basal layer (1)
Surface is smooth surface.
7. the preparation method of frosting laminated glass according to claim 6, which is characterized in that the frosting technique useization
Learn frosting method or physics sand-blast.
8. the preparation method of frosting laminated glass according to claim 7, which is characterized in that the chemical frost method refers to
It is acted on the basal layer (1) by frosting cream, after tempering, obtains the basal layer (1) with frosted layer (2).
9. the preparation method of frosting laminated glass according to claim 6, which is characterized in that the coating process uses object
Manage coating method or electroless plating.
10. the preparation method of frosting laminated glass according to claim 6, which is characterized in that the doubling technique is dry
Method doubling technique.