CN109972264A - The processing method of wide cut element crepe-back satin fabric - Google Patents
The processing method of wide cut element crepe-back satin fabric Download PDFInfo
- Publication number
- CN109972264A CN109972264A CN201910054266.7A CN201910054266A CN109972264A CN 109972264 A CN109972264 A CN 109972264A CN 201910054266 A CN201910054266 A CN 201910054266A CN 109972264 A CN109972264 A CN 109972264A
- Authority
- CN
- China
- Prior art keywords
- warp
- weft
- silk
- mulberry silk
- wide cut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing methods of wide cut element crepe-back satin fabric, including sorting, it impregnates, reeling is rough clearly, double twisting sizing, lead through, power knits these making steps, the White Steam Filature Yarns that quality is good is used when sorting, organizine and tram are impregnated respectively again, it dries, it is rough clearly carrying out reeling to warp and weft, double twisting is formed and is led through in the process, pay attention to the tension force to each process, it reduces and wide anxious warp or scalelike mark occurs during power is knitted, make the fabric woven under the premise of the index request of satietin crepe-back satin silk fabrics, Uneven Width width is bigger, quality is more preferable, before processing, mulberry silk swabbing is given with collagen in advance, since mulberry silk is protein thread, it is fine with collagen compatibility, the structural strength of mulberry silk can be greatly improved using collagen as mulberry silk swabbing, play fabulous reinforcing effect.
Description
Technical field
The present invention relates to a kind of processing methods of satin face, more specifically, it relates to which a kind of wide cut element crepe-back satin fabric adds
Work method.
Background technique
Conventional fabric in plain crepe-back satin category silk fabrics, feature are that fabric sheen sense is strong, and feel is smooth, soft glutinous sagging, rich
It is flexible, it organizes closely knit；Satin face is more smooth than the sense of touch of reverse side.By these characteristics that plain crepe-back satin has, plain crepe-back satin is special
It is not suitble to be made into nightwear and bed necessaries, contacts it directly with human skin, brings silk wiping sense beyond imagination for skin.Element
Crepe-back satin be using mulberry silk as raw material, in weaving usual warp do not twist, weft heavy twist (usually 2600 twist more than), by five
The institutional framework weaving of piece satin.The thickness of traditional plain crepe-back satin is mostly 12 mommes, 16 mommes, 19 mommes these specifications, and door width is more
For 90 centimetres, 114 centimetres, 140 centimetres of these specifications, these width are generally adapted production scarf and clothes, to make bed
Bed linens then need to weave the plain crepe-back satin of wider door width.Due to the increase of plain crepe-back satin door width, traditional weaving process cannot
The Uneven Width width enough woven is more than 240 centimetres of plain crepe-back satin.Therefore, in order to meet people to the use demand of plain crepe-back satin, urgently
Wait invent a kind of method for weaving that can weave wide cut element crepe-back satin silk fabrics.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of processing of wide cut element crepe-back satin fabric
Method.
To achieve the above object, the present invention adopts the following technical scheme: a kind of processing method of wide cut element crepe-back satin fabric,
Including following weaving step:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used for 1:4 solution,
Mulberry silk is impregnated and back and forth swiped 50~60 weeks in the collagen solution of 1:4, mulberry silk, room are taken out after the completion of swabbing
Temperature is protected from light standing and dries in the shade；
(3) along silk: mulberry silk suspension 150~180min of standing that swabbing is completed and dried in the shade, make silk thread naturally droop from
And keep wire more suitable；
(4) it impregnates: along mulberry silk being distributed organizine after the completion of silk and tram is respectively put into and is placed with the immersion liquid of assistant for immersing
Middle immersion after a certain period of time, will complete the organizine after impregnating and tram picks up obtain warp and weft after drying respectively；
(5) reeling is rough clearly: reeling is carried out to the warp and weft for completing to impregnate respectively, to the good warp and weft of network point
Not Yong clear rough device remove rough point, after removing rough point, respectively with the both ends of oscillator clamping warp and weft, with 0.7rad/s's
Revolving speed rotation concussion mulberry silk；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes
Line is tangled between mulberry silk, to obtain bigger structural strength；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete to lead through warp and weft be individually positioned in the warp beam and latitude axis of rapier loom and carry out power
It knits, the breadth that power is knitted is 2.5~2.6 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
Preferably, the mulberry silk selected in step (1) is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns.
Preferably, impregnating organizine 2~4 hours in step (4), tram impregnates 7~8 hours.
Preferably, the Winding Tension of step (5) middle longitude is 7G, the Winding Tension of weft is 7G.
Preferably, the yarn-doubling tension of warp is 9G, the yarn-doubling tension of weft is 9G.
Preferably, times twist of step (6) middle longitude is 1800 twirls, times twist of weft is 2500 twirls.
Preferably, the collagen type v albumen selected in step (2).
The present invention is compared compared with the prior art using the White Steam Filature Yarns that quality is good when having the advantage that sorting, then by organizine
It impregnates, dries respectively with tram, clear rough, the double twisting sizing of reeling is being carried out to warp and weft and is being led through in the process, paying attention to every
The tension force of one process reduces and wide anxious warp or scalelike mark occurs during power is knitted, makes the fabric woven in satietin crape
Under the premise of the index request of satin silk fabrics, Uneven Width width is bigger, quality is more preferable, before processing, is given in advance with collagen
Mulberry silk swabbing, it is fine with collagen compatibility since mulberry silk is protein thread, using collagen as mulberry silk swabbing
The structural strength of mulberry silk can be greatly improved, play fabulous reinforcing effect.
Specific embodiment
The processing method embodiment of wide cut element crepe-back satin fabric of the present invention is described further below.
A kind of processing method of wide cut element crepe-back satin fabric, including following weaving step:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting, selection
Mulberry silk is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used for 1:4 solution,
Mulberry silk is impregnated and back and forth swiped 50~60 weeks in the collagen solution of 1:4, mulberry silk, room are taken out after the completion of swabbing
Temperature is protected from light standing and dries in the shade, and collagen selects collagen type v albumen；
(3) along silk: mulberry silk suspension 150~180min of standing that swabbing is completed and dried in the shade, make silk thread naturally droop from
And keep wire more suitable；
(4) it impregnates: along mulberry silk being distributed organizine after the completion of silk and tram is respectively put into and is placed with the immersion liquid of assistant for immersing
Middle immersion impregnates organizine 2~4 hours, and tram impregnates 7~8 hours, will complete the organizine after impregnating and tram picks up respectively
Warp and weft are obtained after drying；
(5) reeling is rough clearly: carrying out reeling to the warp and weft for completing to impregnate respectively, the Winding Tension of warp is 7G, latitude
The Winding Tension of line is 7G, rough point is removed with clear rough device respectively to the good warp and weft of network, after removing rough point, respectively with vibration
The both ends of device clamping warp and weft are swung, with the revolving speed rotation concussion mulberry silk of 0.7rad/s, the yarn-doubling tension of warp is 9G,
The yarn-doubling tension of weft is 9G；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes
Line is tangled between mulberry silk, to obtain bigger structural strength, times twist of warp is 1800 twirls, times twist of weft
It is twisted for 2500；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete to lead through warp and weft be individually positioned in the warp beam and latitude axis of rapier loom and carry out power
It knits, the breadth that power is knitted is 2.5~2.6 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
Embodiment 1:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting, selection
Mulberry silk is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used for 1:4 solution,
Mulberry silk is impregnated and back and forth swiped 50~60 weeks in the collagen solution of 1:4, mulberry silk, room are taken out after the completion of swabbing
Temperature is protected from light standing and dries in the shade, and collagen selects collagen type v albumen；
(3) along silk: the mulberry silk suspension that swabbing is completed and dried in the shade stands 150min, naturally droops silk thread to make
Wire is more suitable；
(4) it impregnates: along mulberry silk being distributed organizine after the completion of silk and tram is respectively put into and is placed with the immersion liquid of assistant for immersing
Middle immersion impregnates organizine 2 hours, and tram impregnates 7 hours, will complete the organizine after impregnating and tram is picked up respectively after drying
Obtain warp and weft；
(5) reeling is rough clearly: carrying out reeling to the warp and weft for completing to impregnate respectively, the Winding Tension of warp is 7G, latitude
The Winding Tension of line is 7G, rough point is removed with clear rough device respectively to the good warp and weft of network, after removing rough point, respectively with vibration
The both ends of device clamping warp and weft are swung, with the revolving speed rotation concussion mulberry silk of 0.7rad/s, the yarn-doubling tension of warp is 9G,
The yarn-doubling tension of weft is 9G；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes
Line is tangled between mulberry silk, to obtain bigger structural strength, times twist of warp is 1800 twirls, times twist of weft
It is twisted for 2500；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete to lead through warp and weft be individually positioned in the warp beam and latitude axis of rapier loom and carry out power
It knits, the breadth that power is knitted is 2.5 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
Embodiment 2:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting, selection
Mulberry silk is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used for 1:4 solution,
Mulberry silk is impregnated and back and forth swiped 50~60 weeks in the collagen solution of 1:4, mulberry silk, room are taken out after the completion of swabbing
Temperature is protected from light standing and dries in the shade, and collagen selects collagen type v albumen；
(3) along silk: the mulberry silk suspension that swabbing is completed and dried in the shade stands 180min, naturally droops silk thread to make
Wire is more suitable；
(4) it impregnates: along mulberry silk being distributed organizine after the completion of silk and tram is respectively put into and is placed with the immersion liquid of assistant for immersing
Middle immersion soaks organizine 2~4 hours, and tram impregnates 8 hours, will complete the organizine after impregnating and tram is picked up respectively after drying
Obtain warp and weft；
(5) reeling is rough clearly: carrying out reeling to the warp and weft for completing to impregnate respectively, the Winding Tension of warp is 7G, latitude
The Winding Tension of line is 7G, rough point is removed with clear rough device respectively to the good warp and weft of network, after removing rough point, respectively with vibration
The both ends of device clamping warp and weft are swung, with the revolving speed rotation concussion mulberry silk of 0.7rad/s, the yarn-doubling tension of warp is 9G,
The yarn-doubling tension of weft is 9G；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes
Line is tangled between mulberry silk, to obtain bigger structural strength, times twist of warp is 1800 twirls, times twist of weft
It is twisted for 2500；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete to lead through warp and weft be individually positioned in the warp beam and latitude axis of rapier loom and carry out power
It knits, the breadth that power is knitted is 2.6 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
Embodiment 3:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting, selection
Mulberry silk is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used for 1:4 solution,
Mulberry silk is impregnated and back and forth swiped 50~60 weeks in the collagen solution of 1:4, mulberry silk, room are taken out after the completion of swabbing
Temperature is protected from light standing and dries in the shade, and collagen selects collagen type v albumen；
(3) along silk: the mulberry silk suspension that swabbing is completed and dried in the shade stands 166min, naturally droops silk thread to make
Wire is more suitable；
(4) it impregnates: along mulberry silk being distributed organizine after the completion of silk and tram is respectively put into and is placed with the immersion liquid of assistant for immersing
Middle immersion impregnates organizine 3 hours, and tram impregnates 7.4 hours, will complete the organizine after impregnating and tram picks up dry respectively
Warp and weft are obtained afterwards；
(5) reeling is rough clearly: carrying out reeling to the warp and weft for completing to impregnate respectively, the Winding Tension of warp is 7G, latitude
The Winding Tension of line is 7G, rough point is removed with clear rough device respectively to the good warp and weft of network, after removing rough point, respectively with vibration
The both ends of device clamping warp and weft are swung, with the revolving speed rotation concussion mulberry silk of 0.7rad/s, the yarn-doubling tension of warp is 9G,
The yarn-doubling tension of weft is 9G；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes
Line is tangled between mulberry silk, to obtain bigger structural strength, times twist of warp is 1800 twirls, times twist of weft
It is twisted for 2500；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete to lead through warp and weft be individually positioned in the warp beam and latitude axis of rapier loom and carry out power
It knits, the breadth that power is knitted is 2.56 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned reality
Example is applied, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention, it is noted that for this technology
For the those of ordinary skill in field, several improvements and modifications without departing from the principles of the present invention, these are improved and profit
Decorations also should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of processing method of wide cut element crepe-back satin fabric, it is characterised in that: including following weaving step:
(1) sorting: selecting the mulberry silk of high-quality, attentional selection difference in length lesser mulberry silk when selecting；
(2) pre-process: by the mulberry silk selected with collagen liquid swabbing, the collagen liquid used is 1:4 solution, by silkworm
Silk is impregnated in the collagen solution of 1:4 and is back and forth swiped 50~60 weeks, takes out mulberry silk after the completion of swabbing, room temperature is protected from light quiet
It sets and dries in the shade；
(3) along silk: the mulberry silk suspension that swabbing is completed and dried in the shade stands 150~180min, naturally droops silk thread to make
Wire is more suitable；
(4) it impregnates: mulberry silk being distributed into organizine after the completion along silk and tram is respectively put into the immersion liquid for be placed with assistant for immersing and soaks
Bubble after a certain period of time, will complete the organizine after impregnating and tram picks up obtain warp and weft after drying respectively；
(5) reeling is rough clearly: carrying out reeling to the warp and weft for completing to impregnate respectively, uses respectively clearly the good warp and weft of network
Rough device removes rough point, after removing rough point, respectively with the both ends of oscillator clamping warp and weft, is rotated with the revolving speed of 0.7rad/s
Shake mulberry silk；
(6) double twisting is formed: the good warp and weft of network being carried out double twisting respectively, double twisting while carries out rotation twisting, makes silkworm
Line is tangled between silk, to obtain bigger structural strength；
(7) lead through: by the warp and weft after double twisting lead through；
(8) power is knitted: by complete lead through warp and weft be individually positioned in rapier loom warp beam and latitude axis on carry out power knit, power
The breadth knitted is 2.5~2.6 meters, and power obtains wide cut element crepe-back satin silk fabrics after knitting.
2. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: selected in step (1)
Mulberry silk is not less than 6A grades of 20/22 or 40/44 White Steam Filature Yarns.
3. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: by organizine in step (4)
It impregnates 2~4 hours, tram impregnates 7~8 hours.
4. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: step (5) middle longitude
Winding Tension is 7G, and the Winding Tension of weft is 7G.
5. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: the yarn-doubling tension of warp is
9G, the yarn-doubling tension of weft are 9G.
6. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: step (6) middle longitude
Times twist is 1800 to twist, and times twist of weft is 2500 to twist.
7. the processing method of wide cut element crepe-back satin fabric according to claim 1, it is characterised in that: the V selected in step (2)
Collagen type.