CN109971310A - A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect and preparation method thereof - Google Patents
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect and preparation method thereof Download PDFInfo
- Publication number
- CN109971310A CN109971310A CN201910184407.7A CN201910184407A CN109971310A CN 109971310 A CN109971310 A CN 109971310A CN 201910184407 A CN201910184407 A CN 201910184407A CN 109971310 A CN109971310 A CN 109971310A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- self
- contained
- line effect
- orange
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aqueous double-component epoxy orange-peel paints of a kind of self-contained tangerine line effect and preparation method thereof, the aqueous double-component epoxy orange-peel paint of the self-contained tangerine line effect by weight percentage following group is grouped as: aqueous epoxy emulsion 50-59%, environmentally friendly solvent 3-5%, substrate wetting agents 0.1-0.2%, defoaming agent 0.2-0.4%, deionized water 15-25%, modified lithium magnesium silicate 0.2-0.5%, bentonite 0.2-0.5%, aqueous anti-flash rusting agent 0.5-1%, aqueous association type modified polyurethane thickener 1-2%, make mill base 10-15% by oneself, aqueous epoxy curing agent 10-15%.Present invention reduces costs, and improve application property, are no longer influenced by environment and construction factor, and superpower antiseptic property is provided with.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect and its
Preparation method.
Background technique
Orange-peel paint is a kind of relatively new novelty finish, in recent years, the industries such as lathe are very popular.So-called orange-peel paint is
Paint film outer surface has the decorative pattern as orange peel, therefore claims orange-peel paint.Orange-peel paint is chiefly used in machining, numerically-controlled machine tool, instrument
The coating of device, instrument etc. makes it seem more graceful, beautiful.Currently, orange-peel paint is mostly solvent based product, now, advocated in country
It leads under the situation of health environment-friendly, the center of gravity that environmentally friendly machine becomes to study instantly.
Existing product needs to solve to paint VOC content height, seriously polluted and existing product reflected light based on solvent type
Color is single, is not easy to identification problem；
Existing aqueous orange-peel paint product is all used as finishing coat to use, and needs mating epoxy primer, therefore cause construction cost far high
In solvent based product；And tangerine line auxiliary agent is influenced too greatly, to cause tangerine line effect unstable, affect product by environment, construction factor
Popularization.
Currently, lack it is a kind of at low cost, the aqueous double-component epoxy orange-peel paint of the good self-contained tangerine line effect of antiseptic property and
Preparation method.
Summary of the invention
The object of the present invention is to provide a kind of at low cost, aqueous double-component epoxies of the good self-contained tangerine line effect of antiseptic property
Orange-peel paint and preparation method thereof.
The purpose of the present invention is what is realized by following technical proposal: aqueous pair of a kind of self-contained tangerine line effect of the invention
Component epoxy orange-peel paint, the following component of the aqueous double-component epoxy orange-peel paint of the self-contained tangerine line effect by weight percentage
Composition:
Further, the aqueous epoxy emulsion is the non-ionic aqueous epoxy emulsion 6520-WH- of Hexion
53；The environmentally friendly cosolvent is K-FLEX 975P.
Further, the defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, institute
The mass ratio of the BYK-024 of Tego901W and the Bi Ke chemistry for the Digao stated is 1:1；The substrate wetting agents are Digao
Tego510。
Further, the modification lithium magnesium silicate is the Luvogel W2N of Germany Lei Fusi；The swelling
Soil is this BENTONE DE of hamming；The aqueous association type modified polyurethane thickener is RM-8W and the sea of ROHM AND HAAS
This mass ratio of Rheolate 299 of this bright Rheolate 299, the RM-8W and hamming of the ROHM AND HAAS is 1:1.
Further, the aqueous anti-flash rusting agent is this ED617F of hamming.
Further, the aqueous epoxy curing agent is that half hydrophilic fatty amine type curing agent and polyamide type are solid
The mass ratio of two kinds of mixtures of agent, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 4:1-
1:1。
The preparation method of the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the present invention, including walk as follows
It is rapid:
Aqueous epoxy emulsion is added in stock pot, according to the raw material proportioning with 500-600r/min's by step a
Speed stirs 3-5 minutes；Then the mixture of the deionized water of 50% mass fraction and environmentally friendly solvent is added in stock pot,
The speed of 600-800r/min stirs 10 minutes；Then successively by whole defoaming agent, modified lithium magnesium silicate, bentonite, aqueous
Anti- flash rusting agent, water-based thickener and self-control mill base are added in paint mixing tank, the speed stirring of 900-1000r/min 20 minutes, i.e.,
For component A；
Step b mixes the deionized water of aqueous epoxy curing agent and 50% mass fraction equal according to the raw material proportioning
It is even, as B component；
Step c, two kinds of components of above-mentioned A, B, which are mixed in proportion, can be used, and the aqueous of self-contained tangerine line effect is made
Two-component epoxy orange-peel paint.
The utility model has the advantages that the present invention substitutes tangerine line auxiliary agent with epoxy hardener, not only reduce costs, and improve construction
Property, it is no longer influenced by environment and construction factor, convenient for construction, and is provided with superpower antiseptic property as paint for priming paint and top lacquer.
Compared with prior art, the present invention has the advantage that
(1) aqueous epoxy curing agent selected is half hydrophilic fatty amine type curing agent and polyamide type curing agent two
The mass ratio of kind mixture, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 4:1-1:1.
(2) curing agent is contained using half hydrophilic 100% admittedly, acts as the function of tangerine line auxiliary agent to a certain extent.By
Multiple producers, a variety of trade mark curing agent screening test, it is final determine Qing Te chemical company, aerochemistry company certain prepare
Curing agent can satisfy the requirement of epoxy orange-peel paint.According to fatty amine type and polyamide type curing agent different mixing proportion, table
It is different to reveal the paint film tangerine line effect come, while guaranteeing convenient construction using fatty amine type curing agent quick-drying, utilizes polyamides
The superpower antiseptic property of amine type curing agent guarantees paint film anti-corrosive properties.
(3) aqueous epoxy emulsion selected is the non-ionic aqueous epoxy emulsion 6520-WH-53 of Hexion.(epoxy
Lotion, the collocation selection of epoxy hardener are most important to tangerine line effect, because the compatibility of different lotions, different curing agent has
Difference, admixture have difference, have very big difference from what paint film levelling, tangerine line effect.Select aqueous epoxy emulsion and curing agent
Self-contained lines is reduced costs instead of tangerine line auxiliary agent, optimizes workability, largely avoid construction environment and
The influence of construction factor.The aqueous epoxy curing agent of selection is that half hydrophilic fatty amine type curing agent and polyamide type solidify
Two kinds of mixtures of agent are provided with quick-drying and two kinds of characteristics of anti-corrosion, not only ensure that application property, but also be provided with excellent antiseptic property.
Specific embodiment
By following embodiment, present invention be described in more detail, but should be noted that the scope of the present invention is not implemented by these
Any restrictions of example.
Embodiment 1
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the invention, the water of the self-contained tangerine line effect
Property two-component epoxy orange-peel paint by weight percentage following group is grouped as:
The aqueous epoxy emulsion is the non-ionic aqueous epoxy emulsion 6520-WH-53 of Hexion；The ring
Guarantor's cosolvent is K-FLEX 975P.
The defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, the Digao
Tego901W and Bi Ke chemistry BYK-024 mass ratio be 1:1；The substrate wetting agents are the Tego510 of Digao.
The modification lithium magnesium silicate is the Luvogel W2N of Germany Lei Fusi；The bentonite be hamming this
BENTONE DE；The aqueous association type modified polyurethane thickener be ROHM AND HAAS RM-8W and hamming this
This mass ratio of Rheolate 299 of Rheolate 299, the RM-8W and hamming of the ROHM AND HAAS is 1:1.
The aqueous anti-flash rusting agent is this ED617F of hamming.
The aqueous epoxy curing agent is half hydrophilic fatty amine type curing agent and two kinds of polyamide type curing agent
The mass ratio of mixture, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 3:1.
The preparation method of the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the present invention, including walk as follows
It is rapid:
Aqueous epoxy emulsion is added in stock pot, according to the raw material proportioning with the speed of 600r/min by step a
Stirring 3 minutes；Then the mixture of the deionized water of 50% mass fraction and environmentally friendly solvent is added in stock pot, 800r/
The speed of min stirs 10 minutes；Then successively by whole defoaming agents, modified lithium magnesium silicate, bentonite, aqueous anti-flash rusting agent,
Water-based thickener and self-control mill base are added in paint mixing tank, and the speed of 950r/min stirs 20 minutes, as component A；
Step b mixes the deionized water of aqueous epoxy curing agent and 50% mass fraction equal according to the raw material proportioning
It is even, as B component；
Step c, two kinds of components of above-mentioned A, B, which are mixed in proportion, can be used, and the aqueous of self-contained tangerine line effect is made
Two-component epoxy orange-peel paint.
Embodiment 2
Embodiment 2 the difference from embodiment 1 is that:
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the invention, the water of the self-contained tangerine line effect
Property two-component epoxy orange-peel paint by weight percentage following group is grouped as:
The aqueous epoxy emulsion is the non-ionic aqueous epoxy emulsion 6520-WH-53 of Hexion；The ring
Guarantor's cosolvent is K-FLEX 975P.
The defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, the Digao
Tego901W and Bi Ke chemistry BYK-024 mass ratio be 1:1；The substrate wetting agents are the Tego510 of Digao.
The modification lithium magnesium silicate is the Luvogel W2N of Germany Lei Fusi；The bentonite be hamming this
BENTONE DE；The aqueous association type modified polyurethane thickener be ROHM AND HAAS RM-8W and hamming this
This mass ratio of Rheolate 299 of Rheolate 299, the RM-8W and hamming of the ROHM AND HAAS is 1:1.
The aqueous anti-flash rusting agent is this ED617F of hamming.
The aqueous epoxy curing agent is half hydrophilic fatty amine type curing agent and two kinds of polyamide type curing agent
The mass ratio of mixture, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 1:1.
The preparation method of the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the present invention, including walk as follows
It is rapid:
Aqueous epoxy emulsion is added in stock pot, according to the raw material proportioning with the speed of 560r/min by step a
Stirring 5 minutes；Then the mixture of the deionized water of 50% mass fraction and environmentally friendly solvent is added in stock pot, 600r/
The speed of min stirs 10 minutes；Then successively by whole defoaming agents, modified lithium magnesium silicate, bentonite, aqueous anti-flash rusting agent,
Water-based thickener and self-control mill base are added in paint mixing tank, and the speed of 1000r/min stirs 20 minutes, as component A.
Embodiment 3
Embodiment 3 the difference from embodiment 1 is that:
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the invention, the water of the self-contained tangerine line effect
Property two-component epoxy orange-peel paint by weight percentage following group is grouped as:
The aqueous epoxy emulsion is the non-ionic aqueous epoxy emulsion 6520-WH-53 of Hexion；The ring
Guarantor's cosolvent is K-FLEX 975P.
The defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, the Digao
Tego901W and Bi Ke chemistry BYK-024 mass ratio be 1:1；The substrate wetting agents are the Tego510 of Digao.
The modification lithium magnesium silicate is the Luvogel W2N of Germany Lei Fusi；The bentonite be hamming this
BENTONE DE；The aqueous association type modified polyurethane thickener be ROHM AND HAAS RM-8W and hamming this
This mass ratio of Rheolate 299 of Rheolate 299, the RM-8W and hamming of the ROHM AND HAAS is 1:1.
The aqueous anti-flash rusting agent is this ED617F of hamming.
The aqueous epoxy curing agent is half hydrophilic fatty amine type curing agent and two kinds of polyamide type curing agent
The mass ratio of mixture, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 4:1.
The preparation method of the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the present invention, including walk as follows
It is rapid:
Aqueous epoxy emulsion is added in stock pot, according to the raw material proportioning with the speed of 500r/min by step a
Stirring 4 minutes；Then the mixture of the deionized water of 50% mass fraction and environmentally friendly solvent is added in stock pot, 700r/
The speed of min stirs 10 minutes；Then successively by whole defoaming agents, modified lithium magnesium silicate, bentonite, aqueous anti-flash rusting agent,
Water-based thickener and self-control mill base are added in paint mixing tank, and the speed of 900r/min stirs 20 minutes, as component A；
Step b mixes the deionized water of aqueous epoxy curing agent and 50% mass fraction equal according to the raw material proportioning
It is even, as B component；
Step c, two kinds of components of above-mentioned A, B, which are mixed in proportion, can be used, and the aqueous of self-contained tangerine line effect is made
Two-component epoxy orange-peel paint.
Embodiment 4
Embodiment 4 the difference from embodiment 1 is that:
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the invention, the water of the self-contained tangerine line effect
Property two-component epoxy orange-peel paint by weight percentage following group is grouped as:
The defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, the Digao
Tego901W and Bi Ke chemistry BYK-024 mass ratio be 1:1；The substrate wetting agents are the Tego510 of Digao.
The modification lithium magnesium silicate is the Luvogel W2N of Germany Lei Fusi；The bentonite be hamming this
BENTONE DE；The aqueous association type modified polyurethane thickener be ROHM AND HAAS RM-8W and hamming this
This mass ratio of Rheolate 299 of Rheolate 299, the RM-8W and hamming of the ROHM AND HAAS is 1:1.
The aqueous anti-flash rusting agent is this ED617F of hamming.
The aqueous epoxy curing agent is half hydrophilic fatty amine type curing agent and two kinds of polyamide type curing agent
The mass ratio of mixture, the half hydrophilic fatty amine type curing agent and polyamide type curing agent is 1:1.
Embodiment 5
Embodiment 4 the difference from embodiment 1 is that:
A kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect of the invention, the water of the self-contained tangerine line effect
Property two-component epoxy orange-peel paint by weight percentage following group is grouped as:
Test 1
The embodiment of the present invention 1 to embodiment 5 is detected, following effect data is obtained:
1 effect of embodiment: antiseptic property is worst in embodiment 1, have most fast rate of drying, minimum glossiness, compared with
Good tangerine line effect, pencil hardness is 2H to room temperature for 24 hours.
2 effect of embodiment: antiseptic property is most strong in embodiment 2, have most slow rate of drying, highest glossiness, compared with
Good tangerine line effect, pencil hardness is HB to room temperature for 24 hours.
3 effect of embodiment: antiseptic property is moderate in embodiment 3, have good rate of drying, moderate glossiness, compared with
Good tangerine line effect, pencil hardness is 2H to room temperature for 24 hours.
4 effect of embodiment: antiseptic property is moderate in embodiment 4, have good rate of drying, moderate glossiness, most
Good tangerine line effect, pencil hardness is H to room temperature for 24 hours.
5 effect of embodiment: antiseptic property is moderate in embodiment 5, have good rate of drying, moderate glossiness, compared with
Good tangerine line effect, pencil hardness is 2H to room temperature for 24 hours.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, the present invention
Claimed range is delineated by the appended claims, the specification and equivalents thereof from the appended claims.
Claims (7)
1. a kind of aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect, it is characterised in that: the self-contained tangerine line effect
Aqueous double-component epoxy orange-peel paint by weight percentage following group is grouped as:
2. the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect according to claim 1, it is characterised in that: described
Aqueous epoxy emulsion is the non-ionic aqueous epoxy emulsion 6520-WH-53 of Hexion；The environmentally friendly cosolvent is K-
FLEX 975P。
3. the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect according to claim 1, it is characterised in that: described
Defoaming agent is two kinds of mixtures of BYK-024 of Tego901W and the Bi Ke chemistry of Digao, the Tego901W of the Digao and complete
The mass ratio of gram chemical BYK-024 is 1:1；The substrate wetting agents are the Tego510 of Digao.
4. the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect according to claim 3, it is characterised in that: described
The Luvogel W2N that modified lithium magnesium silicate is Germany Lei Fusi；The bentonite is this BENTONE DE of hamming；Institute
The aqueous association type modified polyurethane thickener stated is the RM-8W and hamming this Rheolate 299 of ROHM AND HAAS, described
The RM-8W and hamming of ROHM AND HAAS this Rheolate 299 mass ratio be 1:1.
5. the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect according to claim 1, it is characterised in that: described
Aqueous anti-flash rusting agent is this ED617F of hamming.
6. the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect according to claim 5, it is characterised in that: described
Aqueous epoxy curing agent is half hydrophilic fatty amine type curing agent and two kinds of mixtures of polyamide type curing agent, described half
The mass ratio of hydrophilic fatty amine type curing agent and polyamide type curing agent is 4:1-1:1.
7. the preparation method of the aqueous double-component epoxy orange-peel paint of self-contained tangerine line effect described in claim 5, it is characterised in that
Include the following steps:
Aqueous epoxy emulsion is added in stock pot, according to the raw material proportioning with the speed of 500-600r/min by step a
Stirring 3-5 minutes；Then the mixture of the deionized water of 50% mass fraction and environmentally friendly solvent is added in stock pot, 600-
The speed of 800r/min stirs 10 minutes；Then successively by whole defoaming agents, modified lithium magnesium silicate, bentonite, aqueous anti-sudden strain of a muscle
It becomes rusty in agent, water-based thickener and self-control mill base addition paint mixing tank, the speed of 900-1000r/min stirs 20 minutes, as A group
Point；
The deionized water of aqueous epoxy curing agent and 50% mass fraction is uniformly mixed by step b according to the raw material proportioning,
As B component；
Step c, two kinds of components of above-mentioned A, B, which are mixed in proportion, can be used, and aqueous double groups of self-contained tangerine line effect are made
Part epoxy orange-peel paint.