CN1099679A - Method of continous casting die casted wheel and die casting machine - Google Patents
Method of continous casting die casted wheel and die casting machine Download PDFInfo
- Publication number
- CN1099679A CN1099679A CN 94109333 CN94109333A CN1099679A CN 1099679 A CN1099679 A CN 1099679A CN 94109333 CN94109333 CN 94109333 CN 94109333 A CN94109333 A CN 94109333A CN 1099679 A CN1099679 A CN 1099679A
- Authority
- CN
- China
- Prior art keywords
- mould
- metal
- metal pattern
- die
- movable disk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A continuous casting method for a die casting wheel and the die casting machine. This die casting machine includes a fixed board 12 provided with a semi-movable metallic mold 16 provided so as to be contactable and separable to and from a main body part 20 side, and a movable board 14 for moving forward and backward in the direction of this fixed board. Also, this die casting machine contains a process in which when the movable board executes a mold opening operation after a molten metal is force-fitted into a metallic mold cavity 10, a semi- movable metallic mold is moved in the mold opening direction by allowing it to synchronize with the mold opening operation of the movable board by necessary driving force, the movable and the semi-movable metallic mold are stopped in a middle position before reaching a mold full opening position of the movable board, and its state, a sprue runner part 50 continued to a product is subjected to shearing. Therefore, the die casting wheel with a high quality is manufactured, and also, the whole die casting casting cycle time can be shortened remarkably.
Description
The present invention relates to utilize and to be pressed into motlten metal metal pattern, to produce die wheel continuous casing and the die casting machine that the die casting machine of cast product carries out continuously.
Past, for example aspect the casting method of the light metal alloy of two-wheel vehicle wheel, aspect the gravitation casting method and low pressure casting method of low speed, low pressure casting, owing to must trimming process after the casting, allowance is big, working position is also many, therefore comes a large amount of production high accuracy casting product, also extensive use casting die in the metal mold for motlten metal is pressed into.
Figure 10 shows the pressure casting method that uses traditional die casting machine to make light metal alloy wheel etc., and it makes movable disk 102 move to fixed disk 101 directions, by the matched moulds of fixing metal mould 103 and movable metal pattern 104, forms metal pattern die cavity 105.Be pressed into its inside with the plunger handle motlten metal from down gate sleeve pipe 106 again.
When taking turns the casting of goods etc. with the casting die in past, owing to must cut off the runner gate portion 107 that forms when in die cavity 105, being pressed into motlten metal, therefore not that fixing metal mould 103 is fixed on fixed disk 101 sides, only make the movable metal pattern 104 of movable disk 102 do to advance and retreat mobile facing to that fixing metal mould 103, but also will be shown in Figure 10,11, make moving part 108 can leave open-ended of down gate sleeve pipe, make advance and retreat from the base side of this fixed disk 101 to movable disk 102 sides and move.When making this moving part 108 carry out compression casting discretely with fixed disk 101, (moving part 108 and fixed disk 101 tight contact conditions under the matched moulds state, and be the state that movable disk 102 engages with the left side of moving part 108), when plunger is driven, when motlten metal is extruded in the die cavity 105, will form cast gate and runner gate portion 107 in the coupling part of die cavity 105 and down gate sleeve pipe 106.Therefore after being pressed into motlten metal, moving part has formed the state of seizing on both sides by the arms as by metal pattern die cavity, the cast gate that becomes the L shape and runner gate portion.In this state, if movable disk 102 is moved into die opening state (moving to the figure left), because the power of clasping of these goods, moving part also is moved to the left (state that Figure 11 represents this stage) simultaneously.And reset to fixed disk 101 sides when movable disk 102, when moving closer to fixed disk 101 sides, similarly this moving part 108 is finished above-mentioned mould assembling action to right-hand pushing.
In addition, make the motlten metal that has been pressed into moulding when the metal pattern die cavity is separated, must be coated with the operation of parting compound in the inner wall surface of metal pattern.Always be manual operations, be coated with operation with the hairbrush coating or with sprayings such as spray guns.
But the past, when movable disk was shifted to die opening state, in order to shorten casting cycle, moving part also moved thereupon after above-mentioned motlten metal is pressed into.In this moving process, runner gate portion is cut off by not shown cutoff tool driving mechanism.Therefore, since the delicate time deviation of each member of formation, the very easy generation defective of goods.For goods in enormous quantities, especially can bring about great losses.
In addition, moving part is only transmitting movable disk and is moving with the clasping power of motlten metal goods, so because tractive force, the cast gate place can produce released part, gate part branch fracture is opened mold if therefore movable mold is shifted to left under with the state of this moving part tying, produces cast gate remnants in this gate part branch so, so that not only goods after this all become substandard products, even casting itself also is difficult to proceed down.
In addition, be used for the parting compound coating operation that metal pattern separates with goods and mainly rely on manual operations, therefore irregular for fear of coating, operation is just very time-consuming, and operating efficiency is just poor, and this has just hindered the shortening of casting cycle.
In view of the above-mentioned problem that exists in the past, the objective of the invention is to, provide can prevent with die cavity in the generation of the gate portions fracture accident that is communicated with, and can guarantee the die wheel continuous casing of quality of item substantially fully, provide simultaneously parting compound coating operation is evenly finished, can shorten the shortening in whole die-cast cycle significantly.
In view of the above-mentioned problem that exists in the past, the objective of the invention is to, provide can prevent with die cavity in the generation of the gate portions fracture accident that is communicated with, and can guarantee the die wheel continuous casing of quality of item substantially fully, provide simultaneously parting compound coating operation is evenly finished, can shorten the die casting machine in whole die-cast cycle significantly.
For achieving the above object, the continuous casing of the described die wheel of the present invention's the 1st scheme, its device therefor comprises the fixed disk with the half live metal mould that can separate with the body side contacts, and have a live metal mould relative with half live metal mould of this fixed disk, and can be to the mobile movable disk of above-mentioned fixed disk direction advance and retreat, its operation comprises: when movable disk is made the mould breakdown action after motlten metal is pressed in the metal pattern die cavity, mould breakdown action with required driving force half live metal mould and movable disk synchronously moves to the mould opening direction, during centre position before movable disk arrives the mould fully open position movable disk and half live metal mould are stopped, cut off the runner gate portion that is connected with goods under this state, this later half live metal mould moves and resets to the body side.
The continuous casing of the die wheel that the present invention's the 2nd scheme provides, its device therefor comprises the fixed disk with the half live metal mould that can separate with the body side contacts, and have a live metal mould relative with half live metal mould of this fixed disk, and can be to the mobile movable disk of above-mentioned fixed disk direction advance and retreat, its operation comprises: before in motlten metal is pressed into the metal pattern die cavity, when in this metal pattern die cavity, supplying with the charged powder parting compound, make the inner pressure relief of metal pattern die cavity, make this powder parting compound electro-deposition on the metal pattern inwall, after this carry out the operation that is pressed into of motlten metal again.
The die casting machine that the present invention's the 3rd scheme provides, comprise fixed disk with the half live metal mould that can separate with the body side contacts, and have the live metal mould relative, and the movable disk that can move to above-mentioned fixed disk direction advance and retreat with half live metal mould of this fixed disk, also have the down gate sleeve pipe that is communicated with and is provided with inlet with the metal pattern die cavity of above-mentioned two metal patterns under the matched moulds state.On this down gate sleeve pipe, centre position in inlet and metal pattern, side, be provided with in above-mentioned metal pattern chamber and supply with the powder feeding mouth that parting compound is used, and the Charging system and supply with the powder parting compound feedway that the powder parting compound is used of interlinking on this powder feeding mouth then.
In the continuous casing and die casting machine of aforesaid die wheel, after motlten metal is pressed into the metal pattern die cavity, when movable disk is made the mould breakdown action,, the mould breakdown action of half live metal mould and movable disk is synchronously moved to the mould opening direction with required driving force.Centre position before movable disk arrives the mould fully open position stops movable disk and half live metal mould, in this state, cuts off the runner gate portion that is connected with goods.After this, half live metal mould moves and resets to the body side.Make middle moving part be independent of moving to the movable disk direction alone drivingly of movable disk with oil pressure actuated portion.And make same moved further by itself and movable disk are moved, and can guarantee the reliability of moving to prevent cast gate remnants, keep the stable of goods precision, improve whole die wheel continuous casting operating efficiency.
In addition, in motlten metal is pressed into the metal pattern die cavity before, in this metal pattern die cavity, supply with the charged powder parting compound, meanwhile, make the inner pressure relief of metal pattern die cavity, make this powder parting compound electro-deposition on the metal pattern inwall, after this be pressed into operation through motlten metal again.Thereby can carry out operation at a high speed to metal pattern inner surface coating parting compound.
The simple declaration of accompanying drawing
Fig. 1 is major part side illustration figure.State behind the die casting machine matched moulds that its explanation embodiment of the invention relates to.
Fig. 2 is that the A-A of following Fig. 5 is to view.Can see the body side of moving part in the middle of the die casting machine that embodiment relates among Fig. 5.
Fig. 3 is that the B-B of Fig. 5 is to view.
Fig. 4 is that diagram makes the mediate side illustration figure of halted state of movable disk and middle moving part.
Fig. 5 is the side illustration figure of diagram movable disk full-gear.
Fig. 6 is a key diagram of seeing the face that contacts with the body of middle moving part on the movable disk side direction.
Fig. 7 is the major part summary cross sectional illustration figure of sliding-type core box structure.
Fig. 8 is the major part approximate three-dimensional map of sliding-type core box structure.
Fig. 9 is the general principal view of sliding-type core box structure.
Figure 10 is the major part diagrammatic illustration figure of casting die in the past.
Figure 11 is the major part diagrammatic illustration figure of casting die in the past.
Preferred embodiment of the present invention below is described with reference to the accompanying drawings.
Fig. 1 shows the major part of the horizontal cold house formula die casting machine that die wheel continuous casing embodiment of the present invention relates to.It among the figure state behind the metal pattern matched moulds.
Partly form metal pattern die cavity 10 in substantial middle among the figure, fixed disk 12 is set, movable disk 14 is set in the left side simultaneously on the right side of this metal pattern die cavity 10.
Fixed disk 12 comprises the half live metal mould 16 that is arranged on end side, and movable disk 14 has with this half live metal mould 16 and is close to separable live metal mould 18 with the face fit-state simultaneously.Constitute metal pattern by this half live metal mould 16 with live metal mould 18.The metal pattern die cavity 10 that forms during their fluid-tight engagement has just formed the shape of products of wanting.
Half live metal mould 16 can relative fixed dishes 12 body 20 move as horizontal direction.Moving part 22 is configured to move by the advance and retreat that guide rod is done on the horizontal direction relative to body 20 promptly.On the position relative that 16 of half live metal moulds are arranged on moving part 22 in the middle of this with above-mentioned live metal mould 18.As described below, moving part 22 can be independent of movable disk 14 ground and move to the movable disk direction alone by drive unit in the middle of this, and can be independently moves to body 20 directions of fixed disk and reset.
As also illustrating among Fig. 2,3, do the slip of detaching direction in opposite directions with pull bar 24 bootable fixed disks 12 and movable disk 14 and move.
The face of half live metal mould, 16 sides of moving part 22 in the middle of Fig. 2 illustrates.4 pull bars 24 penetrate four angle parts that roughly are foursquare body 20 that become background side.Its private side is the face shape and partly is moving part 22 in the middle of this, core of moving part 22 in the middle of this, and for example setting-in half live metal mould 16 of colyliform in the base station of middle moving part 22.This metal pattern for example shown in Japanese Utility Model open nineteen ninety No. 1535, adopts the sliding die structure of 3 amalgamations.Cast out the complicated shape of wheel with core.That is, be provided with in Fig. 2 from 3 directions facing to 3 pairs of fitting projection 26 of center side, locate through this movable mold direct of travel it and the chimeric recess co-operating of following live metal mould 18.The 28th, when carrying out matched moulds, be located at the receiving orifice of the decompressor of movable disk 14 sides with movable disk 14 butts.
Secondly, body 20 sides of this middle moving part 22 form platen surface among Fig. 6.Except that passing the pull bar 24 that said fixing dish 12 and movable disk 14, boot activity dish move horizontally, the end of moving part also is embedded with 4 drive rods 30 in the middle of this.Therefore the matched moulds except movable disk 14 sides drives the driving force of sliding.Moving part 22 also passes through in addition independently oil pressure actuated portion 32 in the middle of this, does near leaving moving of body 20.
In addition, as Fig. 4, shown in Figure 6, middle moving part 22 with body 20 contact-making surfaces one side above be provided with cutting mechanism 34, promptly above middle moving part 22, be provided with support 36, be equipped with to cut and cut with oil cylinder 38.Make cutoff tool 40 knee-actions that are arranged on the bottom by oil pressure actuated etc.
In addition, the approximate centre portion at middle moving part 22 is provided with cast gate 42 in the horizontal direction, and it is communicated with metal pattern die cavity 10 from half live metal mould, 16 inwall sides, and runs through the sidepiece of middle moving part 22.
In addition, as shown in Figure 4, at body 20, down gate sleeve pipe 44 is facing to middle moving part 22 side direction settings.Plunger rod 46 can be configured in down gate sleeve pipe 44 inside on the horizontal direction in the drawings with being free to slide.With not shown drive device for hydraulic, promote to be arranged on by being pressed into slide block that this post puts bar 46 ends extrudes slide block 48, the motlten metal that is dropped in its place ahead one side is pressed in the metal pattern die cavity 10.
In Fig. 1, the inlet 42a with body 20 contact-making surfaces one side of moving part 22 above-mentioned cast gate 42, middle is provided with to such an extent that be higher than down gate sleeve pipe 44 and middle moving part 22 contact-making surfaces one side end.For under the matched moulds state, upwards form path from down gate sleeve pipe 44, be communicated with the inlet 42a of this cast gate, form the runner gate portion 50 that is the recess shape in the end side of the down gate sleeve pipe 44 of body 20.
Therefore when motlten metal is molded in the metal pattern die cavity 10, reach at cast gate 42 that the filling motlten metal becomes the L shape by extruding in the runner gate portion 50 that slide block forms also.Then, the cutoff tool 40 of above-mentioned cutting mechanism 34 is descended, cut off this runner gate portion 50.
In addition, in Fig. 1, down gate sleeve pipe 44 forms cylindric, at the upside of its base portion side, is provided with and drops into the inlet 52 that required motlten metal is used.
One of feature of the present invention is to be provided with the inlet 52 of this down gate sleeve pipe 44 and the powder feeding mouth 54 that the supply parting compound is used in metal pattern die cavity 10 is being set on the centre position of metal pattern side.
These powder feeding mouth 54 openings are at the upside of down gate sleeve pipe 44, by conduit 56, Charging system 58 and powder parting compound feedway 60 and this open communication.Charging system 58 for example is following device, and it produces the high pressure about 30,000 volts, makes conduit need the position of voltage to produce arc voltage, makes by the powder of conduit charged.
In addition, powder feeding device is to make the powder parting compound keep floating state at internal tank, has fan, parting compound is delivered to the device of powder feeding mouth 54 sides from conduit 56.
The powder parting compound is that the powder etc. of main material is the parting compound base material, has sneaked into and make the parting compound base material have the mixture of organic compound that the metallic soap of tack and macromolecular compound etc. form and so on for being suitable for the inorganic compound by metal oxide etc. for example.
Fig. 3 is 18 the one being seen key diagrams of side of live metal mould from movable disk 14.Be penetrated with 4 pull bars 24 that also pass fixed disk side main part 20 in four angle parts that become foursquare movable disk side body of roughly being of background side.This movable disk 14 places on the guide rail 62, can be along this guide rail 62, and relative fixed dish 12 directions are made advance and retreat and are moved.
In Fig. 3, live metal mould 18 is contained in the central portion that private side roughly is the face shape.As mentioned above, in order to cast out goods surrounding edge shape, the metal pattern that embodiment relates to is provided with moving core 64a, 64b, the 64c of 3 amalgamations.
With the fitting projection 26 corresponding positions of above-mentioned half live metal mould 16 on be provided with chimeric recess 66, and make it leave the gap, relatively respectively establish 2 respectively, establish 3 pairs altogether.In addition, be central authorities with live metal mould 18, on the desired location of 120 ° of directions of roughly being separated by, dispose core driving cylinder 68 respectively, and the bar of this core driving cylinder 68 is configured in each gap to chimeric recess 66.Then, slide core 64a-64c is fixed on the end of this bar, and each cylinder 68 is advanced and retreat synchronously, does to keep out of the way mobile to the position location of core 64.
In Fig. 7-Fig. 9, show in detail the structure of well-known sliding-type core box, the guide part structure to the metal pattern direction in this structure has part difference, and slide core 64a-64c has substantive identical structure.For example slide core 64a is by the model cavity mould 70 of a part that constitutes die cavity 10, and the sliding shoe 74 that is maintained fixed this horizontal swaging die 70 and slip displacement on mold base 72 constitutes.
In addition, also as shown in Figure 1, the decompressor 76 with required electromagnetic valve mechanism etc. is installed above live metal mould 18, and it is communicated with the metal pattern die cavity 10 that is also formed by live metal mould 18.
78 is knock pins among the figure, and after casting, at the fully open position of movable disk 14, it ejects fixed disk 12 sides to goods, makes it to break away from the live metal mould.The 80th, be contained in the liftout plate on knock pin 78 base portions.
Below, the continuous casing of illustrative examples as carrying out with this die casting machine.
At first, with showing that the adjusted aluminum alloy materials holding furnace of illustrated composition remains on motlten metal in the temperature range of regulation.
Use slide block by the matched moulds driving, movable disk 14 is moved to fixed disk 12 directions carry out the action of die casting machine mold closing.
Fig. 1 illustrates this mold closing and moves completed state.The all closely contacts of movable disk 14, middle moving part 22 and body 20.Be oppositely arranged in order to form metal pattern die cavity 10, two metal patterns 16,18.Then, by cast gate 42 and runner gate portion 50, metal pattern die cavity 10 and down gate sleeve pipe 44 internal communication.
Behind the matched moulds, stop at after plunger rod 46 advances and inlet 52 is closed but powder feeding mouth 54 is on the position with down gate sleeve pipe 44 internal communication states.
Then, the not shown cut-off valve in the decompressor 76 (シ ャ ッ パ Le Block) descends, and makes decompression in metal pattern die cavity 10 and the down gate sleeve pipe 44.
Then, one reaches the decompression state of setting, and the powder parting compound that swims is just sent by powder parting compound feedway 60.At this moment, before arriving powder parting compound feeder 54, when by the Charging system 58 that is provided with, make the powder parting compound charged.Then, charged powder parting compound arrives in the metal pattern die cavity 10 by down gate sleeve pipe 44 inside, and electro-deposition is in the surface of half live metal mould 16 and live metal mould 18.Like this, owing to be deposited on the metal pattern surface, so the coating operation of parting compound can carry out by hypervelocity with making the electric property of charged powder, and can make coating evenly not have coating with being uneven, the reliability that final maintenance is moved.
After this powder parting compound spued ormal weight, the cut-off valve of decompressor 76 retreated.Plunger rod 46 also retreats to the position that makes inlet 52 openings.So not shown cast ladle is poured into a mould in inlet 52.After this, Yi Bian plunger rod 46 divides 3 grades to change issuing velocity, Yi Bian for example with 500kg/cm
2About pressure motlten metal M is pressed in the metal pattern die cavity 10.At this moment, when plunger rod 46 in move, in motlten metal arrives die cavity before, by decompressor 76, the scope that makes the pressure in the die cavity reduce pressure to and set.Then, motlten metal is filled in the die cavity, adds high pressure by plunger rod simultaneously, for example keep the pressure of 2-3 about second.After this be used in the water quench of metal pattern inner loop, the two-wheel light metal alloy has been taken turns with regard to moulding.At this moment, as mentioned above, cast gate 42 and runner gate portion 50 also are in the state of the motlten metal institute filling of being solidified rapidly by the surface.
According to die casting machine continuous casing of the present invention, after this, under the state of Fig. 1, movable disk 14 from filling the state of motlten metal be moved to the left, therewith synchronously, through drive rod 30, moving part 22 is moved to the left in the middle of making, and stops on the centre position before mould fully open position shown in Figure 4 by drive division 32.
Then, under this halted state, the cutoff tool 40 of the cutting mechanism 34 on moving part 22 tops falls in the middle of being installed in, and cuts off runner gate portion 50.
The product defect that such delicate deviation of action owing to the shearing of runner gate portion causes in die sinking is moved of so just can not producing over causes, and because the breakage of the moulded products that gate portions fracture causes or job run such as stop at state, and can successfully keep under the high-precision state, carry out die-cast at high speed continuously.
Owing to cut off this runner gate portion 50, just can the moulded products that filling takes shape in the metal pattern die cavity 10 have been taken out from metal pattern.
After this, the movable disk 14 that stops in the centre remakes the die sinking action, and meanwhile, middle moving part 22 resets to body 20 side shiftings.Then, as shown in Figure 5, move to the mould full-gear.At this moment,, slide core 64 is kept out of the way, removed mould hold mode the surrounding edge portion of moulded products by core driving cylinder 68.After this, moulded products is ejected, send by not shown conveying arrangement again by knock pin 78.
Below understand the casting manipulations cycle of the casting die that the present invention relates in detail.Its main points comprise following operation, after promptly being pressed into motlten metal in the metal pattern die cavity, when movable disk is done the die sinking action, make half live metal mould to of die sinking action synchronous move of die sinking direction do with required driving force with movable disk, centre position before the mould fully open position that arrives movable disk stops movable disk and half live metal mould, cut off the runner gate portion that is connected with goods at this state, this later half live metal mould resets to the body side shifting, its main points also comprise, before motlten metal being pressed in the metal pattern die cavity, in this metal pattern die cavity, supply with the charged powder parting compound, and make the inner pressure relief of metal pattern die cavity, make this powder parting compound electro-deposition on the metal pattern inwall, after this carry out the operation that is pressed into of motlten metal.These two parts are exactly the main points of die wheel continuous casing of the present invention.
Finish this operation one-period and need 60-80 second, and traditional when making similar wheel, finish the one-period operation and need about 3 minutes approximately with die-cast.By contrast, just can understand it is how to have shortened the activity duration significantly.This is also proved by experimental result.
The continuous casing of the die wheel that the present invention relates to and die casting machine have more than and are confined to the foregoing description structure, in the scope that does not break away from the invention spirit that is recorded in the claim scope, also are fine even do any change.
Just as described above, continuous casing according to the described die wheel of the present invention's the 1st scheme, owing to comprised following operation: after being pressed into motlten metal in the metal pattern die cavity, when movable disk is done the die sinking action, with required driving force, make half live metal mould to of synchronous the moving of die sinking action of die sinking direction do with movable disk; Centre position before movable disk arrives the mould fully open position stops movable disk and half live metal mould, in this state, cuts off the runner gate portion that is connected with goods; After this, half live metal mould resets to the body side shifting, therefore, can shorten the entire job cycle significantly, can not produce the action timing offset simultaneously, can high accuracy make die wheel moulding product continuously.And owing to also can not produce peeling off of gate portions, can also guarantee the reliability of moving and the actual effect of production in enormous quantities.
In addition, continuous casing according to the described die wheel of the present invention's the 2nd scheme, because before motlten metal being pressed in the metal pattern die cavity, in the charged powder parting compound of feeding molten metal portion internal feed, make the inner pressure relief of metal pattern die cavity, and make this powder parting compound electro-deposition in the metal pattern inwall, after this pass through the operation that is pressed into of motlten metal again, therefore, can carry out the coating operation of parting compound at a high speed equably to the metal pattern internal face, can improve operating efficiency, shorten the entire job cycle significantly.
In addition, use die casting machine of the present invention, just can guarantee the supply of powder parting compound, increase substantially operating efficiency.
Claims (3)
1, a kind of continuous casing of die wheel, it is characterized in that, its device therefor comprises the fixed disk with the half live metal mould that can separate with the body side contacts, and have the live metal mould relative, an and movable disk that can move to above-mentioned fixed disk direction advance and retreat with half live metal mould of this fixed disk, its operation comprises: when the back movable disk is made the mould breakdown action in motlten metal is pressed into the metal pattern die cavity, with required driving force the mould breakdown action of half live metal mould and movable disk is synchronously moved to the mould opening direction; During centre position before movable disk reaches the mould fully open position movable disk and half live metal mould are stopped, under this state, cutting off the runner gate portion that is connected with goods; After this, half live metal mould moves and resets to the body side.
2, a kind of continuous casing of die wheel, it is characterized in that, its device therefor comprises the fixed disk with the half live metal mould that can separate with the body side contacts, and have a live metal mould relative with half live metal mould of this fixed disk, and can be to the mobile movable disk of above-mentioned fixed disk direction advance and retreat, its operation comprises: before in motlten metal is pressed into the metal pattern die cavity, when in this metal pattern die cavity, supplying with the charged powder parting compound, make the inner pressure relief of metal pattern die cavity, make this powder parting compound electro-deposition on the metal pattern inwall, after this carry out the operation that is pressed into of motlten metal again.
3, a kind of die casting machine, it is characterized in that, comprise fixed disk with the half live metal mould that can separate with the body side contacts, and have a live metal mould relative with half live metal mould of this fixed disk, and can be to the mobile movable disk of above-mentioned fixed disk direction advance and retreat, also have with the metal pattern die cavity of above-mentioned two metal patterns under the matched moulds state and be communicated with, and be provided with the down gate sleeve pipe of inlet, on this down gate sleeve pipe, centre position in inlet and metal pattern side, be provided with in above-mentioned metal pattern chamber and supply with the powder feeding mouth that parting compound is used, and the Charging system and supply with the powder parting compound feedway that the powder parting compound is used of interlinking on this powder feeding mouth then.