CN109957863A - It is a kind of to use polyester filament spinning process - Google Patents
It is a kind of to use polyester filament spinning process Download PDFInfo
- Publication number
- CN109957863A CN109957863A CN201910123155.7A CN201910123155A CN109957863A CN 109957863 A CN109957863 A CN 109957863A CN 201910123155 A CN201910123155 A CN 201910123155A CN 109957863 A CN109957863 A CN 109957863A
- Authority
- CN
- China
- Prior art keywords
- polyester filament
- spinning process
- spun yarn
- filament spinning
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Polyester filament spinning process is used the invention discloses a kind of, comprising: step 1: polyester filament is machined to spun yarn by spun yarn；Step 2: spun yarn is formed by automatic winder；Step 3: it is put into steam box high-temperature shaping, obtains finished product.The beneficial effects of the present invention are: process of the present invention is few, can save labour, reduce energy consumption while improve yield, it is often more important that it is uneven and other issues to can solve cotton knot, slubbing, details and the lines generated in former traditional spinning process.
Description
Technical field
The present invention relates to textile technology fields, and in particular to a kind of to use polyester filament spinning process.
Background technique
Former spinning products kicked the beam flower, bar, cotton carding, rove, again spun yarn form, process is tedious；Since spinning process is joined
Several differences, the quality for often resulting in spinning products is irregular, more, blowing work that there are raw cotton impurity in existing spinning process
Sequence equipment is larger to fibre damage, carding process noil is more, twist factor is small and strength is worth low defective workmanship, to spinning products
Quality influences also bigger.
Summary of the invention
For above-mentioned technical deficiency, polyester filament spinning process is used the object of the present invention is to provide a kind of, it can be with
It saves process portion (light flower, bar, cotton carding, rove), while decreasing labour, save labour cost, reduce energy consumption
While improve yield；It more importantly can solve cotton knot, slubbing, details and the lines generated in former traditional spinning process not
Uniformly and other issues.
In order to solve the above technical problems, the present invention adopts the following technical scheme:
It is a kind of to use polyester filament spinning process, comprising:
Step 1: polyester filament is machined to spun yarn by spun yarn；
Step 2: spun yarn is formed by automatic winder；
Step 3: it is put into steam box high-temperature shaping, obtains finished product.
Preferably, further include that polyester filament adds the blended sizing of dacron short silk, obtain finished product.
Preferably, the polyester filament includes: DTY, FDY and POY.
The beneficial effects of the present invention are: process of the present invention is few, can save labour, reduce energy consumption while improve and produce
Amount, it is often more important that can solve the quality such as cotton knot, slubbing, details and the lines generated in former traditional spinning process are uneven and ask
Topic.
Specific embodiment
It is a kind of to use polyester filament spinning process, comprising:
Step 1: polyester filament is machined to spun yarn by spun yarn；
Step 2: spun yarn is formed by automatic winder；
Step 3: it is put into steam box high-temperature shaping, obtains finished product.
Further, further include that polyester filament adds the blended sizing of dacron short silk, obtain finished product.
Further, the polyester filament includes: DTY, FDY and POY.
Process of the present invention is few, can save labour, improves yield while reduce energy consumption, it is often more important that can solve
Cotton knot, slubbing, details and the lines generated in former tradition spinning process are uneven and other issues.
Obviously, various changes and modifications can be made to the invention without departing from essence of the invention by those skilled in the art
Mind and range.In this way, if these modifications and changes of the present invention belongs to the range of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to include these modifications and variations.
Claims (3)
1. a kind of use polyester filament spinning process characterized by comprising
Step 1: polyester filament is machined to spun yarn by spun yarn；
Step 2: spun yarn is formed by automatic winder；
Step 3: it is put into steam box high-temperature shaping, obtains finished product.
2. a kind of polyester filament spinning process as described in claim 1, which is characterized in that further include that polyester filament adds terylene
Short silk blend sizing, obtains finished product.
3. a kind of polyester filament spinning process is used as claimed in claim 1 or 2, which is characterized in that the polyester filament includes:
DTY, FDY and POY.