CN109943401A - A kind of lubricating grease for air compressor machine - Google Patents
A kind of lubricating grease for air compressor machine Download PDFInfo
- Publication number
- CN109943401A CN109943401A CN201910299753.XA CN201910299753A CN109943401A CN 109943401 A CN109943401 A CN 109943401A CN 201910299753 A CN201910299753 A CN 201910299753A CN 109943401 A CN109943401 A CN 109943401A
- Authority
- CN
- China
- Prior art keywords
- parts
- additive
- lubricating grease
- air compressor
- lithium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
It include: alpha olefine synthetic oil, alkylbenzene, pentaerythritol ester, lithium hydroxide, naphthenic mineral oil, thiadiazoles derivative, department this 80, chlorobromoalkyl phosphate combustion inhibitor, phosphatization species additive, polytetrafluoroethylene (PTFE) lubricated granules additive, high-temperature oxidation resistant additive the invention discloses a kind of lubricating grease for air compressor machine.Advantage is: the additive that various performances are added is used to improve the high temperature resistant of product, Adhesion Resistance, film strength, inoxidizability and reduces the performances such as noise, excellent product formula ensure that the compatibility of every additive in grease structure, it utmostly ensure that the quality of product, so that the present invention is highly competititve.
Description
Technical field
The present invention relates to chemical technology field more particularly to a kind of lubricating grease for air compressor machine.
Background technique
Air compressor is a kind of equipment to compressed gas.Air compressor is similar with water pump structure.Most of skies
Air compressor is reciprocating-piston, rotating vane or rotary screw.Lubrication can not only reduce the friction and wear of machine, simultaneously also
It can play the role of sealing, cooling and reduce running noise, good lubricating condition is that air compressor works reliably and with long-term
Important guarantee.Lubricating grease is to be dispersed in obtained in one or more fluid lubricants as one or more thickening agents between semi-fluid
Body is to the series lubricant agent with non-newtonian flow body characteristics between solid.Grease base eigen is that have certain type
State is easy to adhere to, and mobility is lower than corresponding base oil.Lubricating grease can be used for the reduction mechanical friction in air compressor machine, prevent
The effect of mechanical wear, meanwhile, it is also simultaneous to act the protective effect for preventing metal erosion and sealing and dustproof effect.
Thus applicant carried out beneficial exploration and trial, result of the above problems is had found, will be detailed below being situated between
The scheme to continue is generated under this background.
Summary of the invention
Technical problem to be solved by the present invention lies in view of the deficiencies of the prior art with defect and provide a kind of for sky
The lubricating grease of press.
Technical problem solved by the invention can be realized using following technical scheme:
A kind of lubricating grease for air compressor machine, which is characterized in that prepared by the raw material of following parts by weight: 30-35 parts of α-alkene
Hydrocarbon synthetic oil, 45-50 part alkylbenzene, 60-75 parts of pentaerythritol esters, 5-10 parts of lithium hydroxides, 30-35 parts of naphthenic mineral oils,
3-6 parts of thiadiazoles derivatives, 2-4 parts of this 80,1-3 parts of chlorobromoalkyl phosphate combustion inhibitor of department, 2-7 parts of phosphatization species additions
Agent, 5-10 parts of polytetrafluoroethylene (PTFE) lubricated granules additives, 4-6 parts of high-temperature oxidation resistant additives.
In a preferred embodiment of the invention, the high-temperature oxidation resistant additive is in alkyl diphenylamine or thiamines
It is one or two kinds of.
A kind of manufacture craft of the lubricating grease for air compressor machine is as follows:
A, 70% alpha olefine synthetic oil, 50% alkylbenzene, 50% naphthenic mineral oil is taken to be put into heating in reaction kettle
To thawing；
B, lithium hydroxide solution is made in the ratio of 1:8 in lithium hydroxide and water, adds when being heated to 80-85 DEG C in step a
Enter the lithium hydroxide solution；
C, pentaerythritol ester, polytetrafluoroethylene (PTFE) profit are added after the lithium hydroxide solution is completely dissolved in the reaction kettle
Constant temperature 20 minutes after sliding particulate additive and being warming up to 230 DEG C, then it is cooled to 110 DEG C and sequentially adds thiadiazoles derivative, department originally
80；
D, remaining 30% alpha olefine synthetic oil, 50% alkylbenzene, 50% naphthenic mineral oil are put into after step c
The reaction kettle in and be heated to melting, then add chlorobromoalkyl phosphate combustion inhibitor, phosphatization species additive, high temperature
Antioxidant, constant temperature 15 minutes after being kept for 180 DEG C, it is then cooling and by grinder grinding, filtering, refining at lubrication
Rouge.
Due to using technical solution as above, the beneficial effects of the present invention are: various performances are added in the present invention
Additive is used to improve the performances such as high temperature resistant, Adhesion Resistance, film strength, inoxidizability and the reduction noise of product, excellent
Product formula ensure that the compatibility of every additive in grease structure, utmostly ensure that the quality of product, so that this
It invents highly competititve.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below into
One step illustrates the present invention.
Embodiment 1
Take 30 parts of alpha olefine synthetic oils, 45 parts of alkylbenzenes, 60 parts of pentaerythritol esters, 5 parts of lithium hydroxides, 30 parts of naphthenic base mines
Object oil, 3 parts of thiadiazoles derivatives, 2 parts of departments this 80,1 parts of chlorobromoalkyl phosphate combustion inhibitors, 2 parts of phosphatization species additives, 5
Part polytetrafluoroethylene (PTFE) lubricated granules additive, 4 parts of high-temperature oxidation resistant additives.
Wherein, high-temperature oxidation resistant additive is one or both of alkyl diphenylamine or thiamines.
Manufacture craft is as follows:
A, 21 parts of alpha olefine synthetic oils, 22.5 parts of alkylbenzene, 15 naphthenic mineral oils is taken to be put into reaction kettle and be heated to
Melt；
B, lithium hydroxide solution is made in the ratio of 1:8 in 5 parts of lithium hydroxides and water, when being heated to 80-85 DEG C in step a
Lithium hydroxide solution is added；
C, 60 parts of pentaerythritol esters, 5 parts of polytetrafluoroethylene (PTFE) profits are added after lithium hydroxide solution is completely dissolved in reaction kettle
Constant temperature 20 minutes after sliding particulate additive and being warming up to 230 DEG C, then it is cooled to 110 DEG C and sequentially adds 3 parts of thiadiazoles derivatives, 2
Part department sheet 80；
D, remaining 9 parts of alpha olefine synthetic oils, 22.5 parts of alkylbenzenes, 15 naphthenic mineral oils are put into after step c
Reaction kettle in and be heated to melting, then add 1 part of chlorobromoalkyl phosphate combustion inhibitor, 2 parts of phosphatization species additives, 4
Part high-temperature oxidation resistant additive, constant temperature 15 minutes after being kept for 180 DEG C, it is then cooling and by grinder grinding, filtering, refine
At lubricating grease.
Embodiment 2
Take 35 parts of alpha olefine synthetic oils, 50 parts of alkylbenzenes, 75 parts of pentaerythritol esters, 10 parts of lithium hydroxides, 35 parts of naphthenic base
Mineral oil, 6 parts of thiadiazoles derivatives, this 80,3 parts of chlorobromoalkyl phosphate combustion inhibitors of 4 parts of departments, 7 parts of phosphatization species additives,
10 parts of polytetrafluoroethylene (PTFE) lubricated granules additives, 6 parts of high-temperature oxidation resistant additives.
Wherein, high-temperature oxidation resistant additive is one or both of alkyl diphenylamine or thiamines.
Manufacture craft is as follows:
A, it takes 24.5 parts of alpha olefine synthetic oils, 25 parts of alkylbenzene, 17.5 parts of naphthenic mineral oils to be put into reaction kettle to add
Heat is extremely melted；
B, lithium hydroxide solution is made in the ratio of 1:8 in 10 parts of lithium hydroxides and water, is heated to 80-85 DEG C in step a
When lithium hydroxide solution is added；
C, 75 pentaerythritol esters, 10 polytetrafluoroethylene (PTFE) lubrication are added after lithium hydroxide solution is completely dissolved in reaction kettle
Grain additive and constant temperature 20 minutes after being warming up to 230 DEG C, then be cooled to 110 DEG C and sequentially add 6 parts of thiadiazoles derivatives, 4 parts of departments
This 80；
D, remaining 10.5 parts of alpha olefine synthetic oils, 25 parts of alkylbenzenes, 17.5 parts of naphthenic mineral oils are put by step
It in reaction kettle after rapid c and is heated to melting, then adds 3 parts of chlorobromoalkyl phosphate combustion inhibitors, 7 parts of phosphatization species additions
Agent, 6 parts of high-temperature oxidation resistant additives, constant temperature 15 minutes after being kept for 180 DEG C, then cool down and ground by grinder, filtered,
Refine into lubricating grease.
Embodiment 3
Take 33 parts of alpha olefine synthetic oils, 48 parts of alkylbenzenes, 68 parts of pentaerythritol esters, 8 parts of lithium hydroxides, 33 parts of naphthenic base mines
Object oil, 4 parts of thiadiazoles derivatives, 3 parts of departments this 80,2 parts of chlorobromoalkyl phosphate combustion inhibitors, 5 parts of phosphatization species additives, 8
Part polytetrafluoroethylene (PTFE) lubricated granules additive, 5 parts of high-temperature oxidation resistant additives.
Wherein, high-temperature oxidation resistant additive is one or both of alkyl diphenylamine or thiamines.
Manufacture craft is as follows:
A, it takes 23 parts of alpha olefine synthetic oil, 24 parts of alkylbenzene, 16.5 parts of naphthenic mineral oils to be put into reaction kettle to add
Heat is extremely melted；
B, lithium hydroxide solution is made in the ratio of 1:8 in 8 parts of lithium hydroxides and water, when being heated to 80-85 DEG C in step a
Lithium hydroxide solution is added；
C, 68 parts of pentaerythritol esters, 8 parts of polytetrafluoroethylene (PTFE) profits are added after lithium hydroxide solution is completely dissolved in reaction kettle
Constant temperature 20 minutes after sliding particulate additive and being warming up to 230 DEG C, then it is cooled to 110 DEG C and sequentially adds 4 parts of thiadiazoles derivatives, 3
Part department sheet 80；
D, remaining 10 parts of alpha olefine synthetic oils, 24 parts of alkylbenzenes, 16.5 naphthenic mineral oils are put into after step c
Reaction kettle in and be heated to melting, then add 2 parts of chlorobromoalkyl phosphate combustion inhibitors, 5 parts of phosphatization species additives, 5
Part high-temperature oxidation resistant additive, constant temperature 15 minutes after being kept for 180 DEG C, it is then cooling and by grinder grinding, filtering, refine
At lubricating grease.
Product Validation:
The physical and chemical index of this product reaches company standard through detection, and user's use shows complete qualification.Its technical indicator number
According to as follows.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of lubricating grease for air compressor machine, which is characterized in that prepared by the raw material of following parts by weight: 30-35 parts of alpha-olefins
Synthetic oil, 45-50 part alkylbenzene, 60-75 parts of pentaerythritol esters, 5-10 parts of lithium hydroxides, 30-35 parts of naphthenic mineral oils, 3-6
Part thiadiazoles derivative, 2-4 parts of departments this 80,1-3 parts of chlorobromoalkyl phosphate combustion inhibitors, 2-7 parts of phosphatization species additives, 5-
10 parts of polytetrafluoroethylene (PTFE) lubricated granules additives, 4-6 parts of high-temperature oxidation resistant additives.
2. a kind of lubricating grease for air compressor machine as described in claim 1, which is characterized in that the high-temperature oxidation resistant additive
For one or both of alkyl diphenylamine or thiamines.
3. a kind of manufacture craft of the lubricating grease for air compressor machine is as follows:
A, it takes 70% alpha olefine synthetic oil, 50% alkylbenzene, 50% naphthenic mineral oil to be put into be heated to melting in reaction kettle
Change；
B, lithium hydroxide solution is made in the ratio of 1:8 in lithium hydroxide and water, and institute is added when being heated to 80-85 DEG C in step a
State lithium hydroxide solution；
C, pentaerythritol ester, polytetrafluoroethylene (PTFE) lubrication are added after the lithium hydroxide solution is completely dissolved in the reaction kettle
Grain additive and constant temperature 20 minutes after being warming up to 230 DEG C, then be cooled to 110 DEG C sequentially add thiadiazoles derivative, department this 80；
D, remaining 30% alpha olefine synthetic oil, 50% alkylbenzene, 50% naphthenic mineral oil are put into the institute after step c
It states in reaction kettle and is heated to melting, then add chlorobromoalkyl phosphate combustion inhibitor, phosphatization species additive, high temperature antioxygen
Change additive, constant temperature 15 minutes after being kept for 180 DEG C, it is then cooling and by grinder grinding, filtering, refining at lubricating grease.