CN109943250B - Glue residue prevention silica gel protective film for manufacturing process - Google Patents
Glue residue prevention silica gel protective film for manufacturing process Download PDFInfo
- Publication number
- CN109943250B CN109943250B CN201910246301.5A CN201910246301A CN109943250B CN 109943250 B CN109943250 B CN 109943250B CN 201910246301 A CN201910246301 A CN 201910246301A CN 109943250 B CN109943250 B CN 109943250B
- Authority
- CN
- China
- Prior art keywords
- parts
- protective film
- silica gel
- film
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an anti-adhesive residue silica gel protective film for a manufacturing process, which comprises a substrate layer and an organic silica gel layer coated on the surface of the substrate layer, wherein the organic silica gel layer consists of the following components: 200-350 parts of methyl vinyl silicone rubber, 10-40 parts of polyisoprene rubber, 10-25 parts of silicone resin, 2-6 parts of vinyl silicone oil, 0.5-5 parts of hydrogen-containing silicone oil, 0.3-4 parts of 3-thiocyanatopropyltriethoxysilane, 0.3-2 parts of 2-aminobenzimidazole, 0.5-3 parts of methylbutinol, 0.5-2 parts of platinum catalyst, 0.3-1 part of cyclohexanone peroxide, 0.2-3.8 parts of nano graphite powder, 1-3 parts of potassium monododecyl phosphate, 400-600 parts of toluene and 250-400 parts of ethyl acetate; the protective film is moderate in viscosity, the problem that the edge is warped and even falls off is not easy to occur in the using process, the residual glue is easy to remove, and the process requirement of temporary fixation in the manufacturing process of the mobile phone can be met.
Description
Technical Field
The invention relates to a protective film, in particular to an anti-adhesive residue silica gel protective film for a manufacturing process.
Background
Before the smart phone is assembled, the periphery of the frame of the smart phone needs to be pasted and temporarily fixed by a medium-viscosity protective film, and after the smart phone is assembled, the protective film pasted on the periphery of the frame is torn off. At present, the protective film comes from foreign suppliers, and the products made in China have the following technical problems and can not replace imported products, and the main problems are that: 1. the viscosity is too low or too high, so that edge lifting and even falling off occur in the using process, or residual glue is generated in the removing process; 2. the base material is too hard or too soft, so that the edge is easy to warp or the base material is easy to break; 3. the antistatic effect is not good, and the automatic continuous production is influenced.
Therefore, the development and development of the protective film which has moderate viscosity, easy removal and excellent antistatic effect to replace imported products have important economic and social benefits.
Disclosure of Invention
The invention aims to provide an adhesive residue prevention silica gel protective film for a manufacturing process, which is moderate in viscosity, easy to remove and excellent in antistatic effect, does not have adhesive residue, and can meet the process requirement of temporary fixation in the manufacturing process of a smart phone.
In order to achieve the purpose, the invention adopts the technical scheme that: the anti-adhesive-residue silica gel protective film for the manufacturing process comprises a base material layer and an organic silicon adhesive layer coated on the surface of the base material layer, wherein the base material layer further comprises a PET film and a PE film, and the PET film and the PE film are compounded together through an adhesive layer;
the organic silica gel layer comprises the following components in parts by weight:
200 to 350 parts of methyl vinyl silicone rubber,
10-40 parts of polyisoprene rubber,
10-25 parts of silicone resin,
2-6 parts of vinyl silicone oil,
0.5 to 5 parts of hydrogen-containing silicone oil,
0.3 to 4 parts of 3-thiocyanatopropyltriethoxysilane,
0.3 to 2 parts of 2-aminobenzimidazole,
0.5 to 3 parts of methylbutinol,
0.5 to 2 parts of a platinum catalyst,
0.3 to 1 part of cyclohexanone peroxide,
0.2 to 3.8 portions of nano graphite powder,
1-3 parts of potassium monododecyl phosphate,
400-600 parts of toluene,
250-400 parts of ethyl acetate.
The technical scheme of further improvement in the technical scheme is as follows:
1. in the scheme, the thickness of the PET film is 15-25 mu m.
2. In the scheme, the thickness of the PE film is 15-25 mu m.
3. In the scheme, the thickness of the adhesive layer is 5-15 mu m.
4. In the above scheme, the adhesive layer is a polyester adhesive layer.
5. In the scheme, the thickness of the organic silica gel layer is 10-30 mu m.
6. In the scheme, the hydrogen content of the hydrogen-containing silicone oil is 0.1-1.2%.
7. In the above scheme, the platinum catalyst is selected from one or more of chloroplatinic acid, chloroplatinic acid/alkenylsiloxane complexes, and chloroplatinic acid/olefin complexes.
Due to the application of the technical scheme, compared with the prior art, the invention has the following advantages:
1. the anti-adhesive-residue silica gel protective film for the manufacturing process adopts the PET/PE composite film as the base material, the composite film has the good mechanical property of the PET film and the flexibility of the PE film, the edge is not easy to warp when the composite film is used as the base material of the protective film, and the composite film is not easy to break when being stretched and peeled; in addition, the organic silicon adhesive with a special formula is adopted, the stripping force is moderate, the cohesion is strong, the problem that the protective film is not prone to edge warping or even falling off in the using process is solved, the protective film is easy to remove, and no residual adhesive is left when the protective film is taken down.
2. According to the anti-adhesive-residue silica gel protective film for the manufacturing process, the organic silicon adhesive formula is additionally added with 0.3-2 parts of 2-aminobenzimidazole and 1-3 parts of potassium monododecyl phosphate on the basis of 0.2-3.8 parts of nano graphite powder, so that the antistatic effect is remarkably improved, and the surface resistivity is remarkably improvedUp to 107And the adhesive is used for a protective film for manufacturing process, can solve the problem that automatic continuous production is influenced due to the fact that static electricity cannot be discharged, and reduces labor and time cost in the production process.
Drawings
FIG. 1 is a schematic view of a structure of a protective film for preventing residual glue on a silicon substrate.
In the above drawings: 1. a substrate layer; 101. a PET film; 102. an adhesive layer; 103. a PE film; 2. and (4) an organic silica gel layer.
Detailed Description
The invention is further described below with reference to the following examples:
examples 1 to 4: the anti-adhesive-residue silica gel protective film for the manufacturing process comprises a substrate layer 1 and an organic silica gel layer 2 coated on the surface of the substrate layer 1, wherein the substrate layer 1 further comprises a PET film 101 and a PE film 103, and the PET film 101 and the PE film 103 are compounded together through an adhesive layer 102;
the thickness of the PET film 101 is 20 micrometers, the thickness of the PE film 103 is 20 micrometers, the thickness of the adhesive layer 102 is 10 micrometers, and the thickness of the organic silica gel layer 2 is 15 micrometers;
the adhesive layer 102 is a polyester adhesive layer.
The organic silica gel layer 2 is composed of the following components in parts by weight:
TABLE 1
Components | Example 1 | Example 2 | Example 3 | Example 4 |
Methyl vinyl silicone rubber | 270 | 200 | 300 | 350 |
Polyisoprene rubberGlue | 40 | 15 | 30 | 20 |
Silicone resin | 10 | 20 | 25 | 15 |
Vinyl silicone oil | 6 | 5 | 4 | 2 |
Hydrogen-containing silicone oil | 5 | 4 | 0.5 | 2 |
3-thiocyanatopropyltriethoxysilane | 1.8 | 0.3 | 2.5 | 4 |
2-aminobenzimidazole | 0.8 | 2 | 0.3 | 1.5 |
| 1 | 0.5 | 2 | 3 |
| 2 | 1.5 | 1 | 0.5 |
Cyclohexanone | 1 | 0.5 | 0.7 | 0.3 |
Nano graphite powder | 1.5 | 0.2 | 3.8 | 2.5 |
Potassium monododecyl phosphate | 2.5 | 1 | 2 | 3 |
Toluene | 500 | 600 | 400 | 450 |
Ethyl acetate | 400 | 250 | 330 | 270 |
The preparation method of the glue residue prevention silica gel protective film for the manufacturing process comprises the following steps:
s1, coating an adhesive on the surface of a PET film 101, drying to form an adhesive layer 102, and then compounding the PET film 101 and a PE film 103 in a hot pressing manner to obtain a substrate layer 1;
s2, uniformly mixing 200-350 parts of methyl vinyl silicone rubber, 10-40 parts of polyisoprene rubber, 10-25 parts of silicone resin, 2-6 parts of vinyl silicone oil, 0.5-5 parts of hydrogen-containing silicone oil, 0.3-4 parts of 3-thiocyanatopropyltriethoxysilane, 0.3-2 parts of 2-aminobenzimidazole, 0.2-3.8 parts of nano graphite powder, 1-3 parts of potassium monododecyl phosphate, 400-600 parts of toluene and 250-400 parts of ethyl acetate, stirring for 30-60 min, then adding 0.5-3 parts of methylbutynol, 0.5-2 parts of platinum catalyst and 0.3-1 part of cyclohexanone peroxide, and stirring for 10-20 min to prepare the organic silicon adhesive;
s3, uniformly coating the organic silicon adhesive on the surface of the substrate layer 1, and curing at 140-150 ℃ to form an organic silicon adhesive layer 2 to obtain a semi-finished product of the protective film;
and S4, cutting the semi-finished product of the protective film into strips according to the requirement to obtain the residual glue preventing silica gel protective film for the manufacturing process.
Comparative examples 1 to 3: a protective film comprises a substrate layer 1 and an organic silica gel layer 2 coated on the surface of the substrate layer 1, wherein the substrate layer 1 further comprises a PET film 101 and a PE film 103, and the PET film 101 and the PE film 103 are compounded together through an adhesive layer 102;
the thickness of the PET film 101 is 20 micrometers, the thickness of the PE film 103 is 20 micrometers, the thickness of the adhesive layer 102 is 10 micrometers, and the thickness of the organic silica gel layer 2 is 15 micrometers;
the adhesive layer 102 is a polyester adhesive layer.
The organic silica gel layer 2 is composed of the following components in parts by weight:
TABLE 2
Components | Comparative example 1 | Comparative example 2 | Comparative example 3 |
Methyl vinyl silicone rubber | 200 | 300 | 350 |
Polyisoprene rubber | 40 | - | 25 |
Silicone resin | 10 | 15 | 25 |
Vinyl silicone oil | 5 | 4 | 2 |
Hydrogen-containing | 2 | 5 | 0.5 |
3-thiocyanatopropyltriethoxysilane | - | 0.3 | 2.5 |
2-aminobenzimidazole | 0.8 | - | 0.3 |
Methyl butynol | 3 | 0.5 | 1 |
| 2 | 1.5 | 1 |
| 1 | 0.3 | - |
Nano graphite powder | - | 2.5 | 3.5 |
Potassium monododecyl phosphate | 3 | 1 | - |
Toluene | 500 | 600 | 400 |
Ethyl acetate | 350 | 250 | 400 |
The preparation process is the same as the embodiment.
The product performance of the protective films prepared in the above examples 1 to 4 and comparative examples 1 to 3 is shown in table 3:
TABLE 3
As shown in the evaluation results of table 3, the peeling force of the anti-adhesive residue silica gel protective film for the manufacturing process in the embodiments of the present invention is moderate, the problem of edge lifting and even falling off is not easy to occur during the use process, and the protective film is easy to remove without leaving adhesive residue when being taken down; the surface resistivity of the protective film is obviously lower than that of the protective film prepared in each proportion, and the problem that the automatic continuous production is influenced because static electricity cannot be discharged can be solved.
The above embodiments are merely illustrative of the technical ideas and features of the present invention, and the purpose thereof is to enable those skilled in the art to understand the contents of the present invention and implement the present invention, and not to limit the protection scope of the present invention. All equivalent changes and modifications made according to the spirit of the present invention should be covered within the protection scope of the present invention.
Claims (8)
1. The utility model provides a processing procedure is with preventing incomplete glue silica gel protection film which characterized in that: the adhesive comprises a substrate layer (1) and an organic silica gel layer (2) coated on the surface of the substrate layer (1), wherein the substrate layer (1) further comprises a PET film (101) and a PE film (103), and the PET film (101) and the PE film (103) are compounded together through an adhesive layer (102);
the organic silica gel layer (2) is composed of the following components in parts by weight:
200 to 350 parts of methyl vinyl silicone rubber,
10-40 parts of polyisoprene rubber,
10-25 parts of silicone resin,
2-6 parts of vinyl silicone oil,
0.5 to 5 parts of hydrogen-containing silicone oil,
0.3 to 4 parts of 3-thiocyanatopropyltriethoxysilane,
0.3 to 2 parts of 2-aminobenzimidazole,
0.5 to 3 parts of methylbutinol,
0.5 to 2 parts of a platinum catalyst,
0.3 to 1 part of cyclohexanone peroxide,
0.2 to 3.8 portions of nano graphite powder,
1-3 parts of potassium monododecyl phosphate,
400-600 parts of toluene,
250-400 parts of ethyl acetate.
2. The protective film of claim 1, wherein: the thickness of the PET film (101) is 15-25 mu m.
3. The protective film of claim 1, wherein: the thickness of the PE film (103) is 15-25 mu m.
4. The protective film of claim 1, wherein: the thickness of the adhesive layer (102) is 5-15 μm.
5. The protective film of claim 1, wherein: the adhesive layer (102) is a polyester adhesive layer.
6. The protective film of claim 1, wherein: the thickness of the organic silica gel layer (2) is 10-30 mu m.
7. The protective film of claim 1, wherein: the hydrogen content of the hydrogen-containing silicone oil is 0.1-1.2%.
8. The protective film of claim 1, wherein: the platinum catalyst is selected from one or more of chloroplatinic acid, chloroplatinic acid/alkenylsiloxane complexes, and chloroplatinic acid/olefin complexes.