CN109940929A - A kind of summer double-wall corrugated pipe and preparation method thereof - Google Patents
A kind of summer double-wall corrugated pipe and preparation method thereof Download PDFInfo
- Publication number
- CN109940929A CN109940929A CN201910198051.2A CN201910198051A CN109940929A CN 109940929 A CN109940929 A CN 109940929A CN 201910198051 A CN201910198051 A CN 201910198051A CN 109940929 A CN109940929 A CN 109940929A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- outer layer
- wall corrugated
- corrugated pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of summer double-wall corrugated pipes and preparation method thereof, it includes the internal layer and outer layer set gradually from inside to outside, and the outer layer includes the raw material components of following parts by weight: PPH26 ~ 30 part;HDPE25 ~ 32 part;MPE3 ~ 8 part;30 ~ 40 parts of inorganic filler;2.5 ~ 3 parts of lubricant;1.5 ~ 2.5 parts of color masterbatch;2 ~ 2.5 parts of agent composition of coupling;0.2 ~ 0.5 part of antioxidant;0.2 ~ 0.25 part of auxiliary antioxidant;0.5 ~ 0.8 part of light stabilizer;0.2 ~ 0.25 part of ultraviolet absorbing agent;Material each in this way is uniformly mixed and interacts, and produces comprehensive synergy: obtaining the physicochemical properties such as excellent tensile strength, ring stiffness, Charpy Impact;Meet the construction requirement that summer ultraviolet light is strong and temperature is high simultaneously.
Description
Technical field
The invention belongs to pipeline fields, are related to a kind of feed pipe, and in particular to a kind of summer double-wall corrugated pipe and its system
Preparation Method.
Background technique
Double-wall corrugated pipe (main component is usually high density polyethylene (HDPE), i.e. HDPE) be it is a kind of have cyclic structure outer wall and
The novel tube of smooth internal walls, the beginning of the eighties succeed in developing first in Germany.By the development of more than ten years and perfect, via list
One Cultivar development is to complete product line.Double-wall corrugated pipe feed pipe, because light weight, inside and outside wall are smooth, corrosion-resistant, close
The advantages that envelope property is good, dominates the market rapidly;But its there are non-refractory, be exposed to the sun, pipeline longitudinal tensile strain rate is larger under high temperature, and
Summer ultraviolet light and high temperature are contained especially, and the above problem is more prominent.
Summary of the invention
A kind of summer double-wall corrugated pipe is provided the invention aims to overcome the deficiencies in the prior art.
In order to achieve the above objectives, the technical solution adopted by the present invention is that: a kind of summer double-wall corrugated pipe, it includes by interior
The internal layer and outer layer set gradually outward, the outer layer include the raw material components of following parts by weight:
The internal layer includes the raw material components of following parts by weight:
The inorganic filler is heavy calcium carbonate, wollastonite in powder and alkali-free glass fibre 10:2:3 in mass ratio composition
Mixture;The coupling agent composition is the mixture that titanate coupling agent and silane coupling agent 1:1 in mass ratio are formed;It is described
Lubricant is the mixture that stearic acid and PE wax 1:1 in mass ratio are formed.
Optimally, the outer layer includes the raw material components of following parts by weight:
Optimally, the internal layer includes the raw material components of following parts by weight:
Another object of the present invention is to provide a kind of preparation method of above-mentioned summer double-wall corrugated pipe, it includes following
Step:
(a) the internal layer raw material and outer layer raw material for weighing formula ratio respectively are then added separately to carry out in two batch mixers
Mixing;
(b) the internal layer raw material and outer layer raw material are heated respectively, is squeezed out through two-layer compound die head;
(c) bellows is pulled out through molding machine and is formed, cut after cooling and obtain finished product.
Optimally, in step (a), the mixing of the outer layer raw material specifically: using silane coupling agent to alkali-free glass fibre
Dimension is surface-treated, and then carries out melting extrusion granulation with PPH;Weigh the stearic acid of formula ratio, PE wax, wollastonite in powder and again
Matter Paris white is stirred activation in 70~90 DEG C in batch mixer;Remaining outer layer raw material is added, is carried out in 70~90 DEG C
Stirring, dehumidifying, blowing are stand-by.
Optimally, in step (a), the mixing of the internal layer raw material specifically: weigh the stearic acid of formula ratio, PE wax, again
Matter calcium carbonate is stirred activation in 70~90 DEG C in batch mixer;Remaining outer layer raw material is added, is stirred in 70~90 DEG C
It mixes, dehumidify, blowing is stand-by.
Due to the above technical solutions, the present invention has the following advantages over the prior art: summer use of the invention is double
Wall bellows is mixed respectively by using the raw material components of certain content, and to form ectonexine structure, material each in this way is mixed
It closes uniformly and interacts, produce comprehensive synergy: obtaining the reason such as excellent tensile strength, ring stiffness, Charpy Impact
Change performance;Meet the construction requirement that summer ultraviolet light is strong and temperature is high simultaneously.
Specific embodiment
Summer double-wall corrugated pipe of the invention, it includes the internal layer and outer layer set gradually from inside to outside, the outer layer packet
Include the raw material components of following parts by weight: PPH26~30 part;HDPE25~32 part;MPE3~8 part;30~40 parts of inorganic filler;
2.5~3 parts of lubricant;1.5~2.5 parts of color masterbatch;2~2.5 parts of agent composition of coupling;0.2~0.5 part of antioxidant;Auxiliary is anti-
0.2~0.25 part of oxidant;0.5~0.8 part of light stabilizer;0.2~0.25 part of ultraviolet absorbing agent;The internal layer includes following
The raw material components of parts by weight: HDPE30~40 part;PPR30~40 part;LLDPE3~8 part;15~25 parts of heavy calcium carbonate;
1.5~2.5 parts of color masterbatch;1~3 part of lubricant;0.5~1.5 part of titanate coupling agent;The inorganic filler is powdered whiting
The mixture of powder, wollastonite in powder and alkali-free glass fibre 10:2:3 in mass ratio composition;The coupling agent composition is titanate esters
The mixture of coupling agent and silane coupling agent 1:1 in mass ratio composition;The lubricant is stearic acid and PE wax 1:1 in mass ratio
The mixture of composition.It is mixed respectively by using the raw material components of certain content, to form ectonexine structure, object each in this way
Material is uniformly mixed and interacts, and produces comprehensive synergy: obtaining excellent tensile strength, ring stiffness, Charpy Impact
Equal physicochemical properties;Meet the construction requirement that summer ultraviolet light is strong and temperature is high simultaneously.
Outer layer preferably includes the raw material components of following parts by weight: PPH27 parts;HDPE30 parts;MPE5 parts;Inorganic filler 30
Part;2.8 parts of lubricant;2 parts of color masterbatch;2 parts of agent composition of coupling;0.3 part of antioxidant;0.2 part of auxiliary antioxidant;Light is stablized
0.5 part of agent;0.2 part of ultraviolet absorbing agent.The internal layer preferably includes the raw material components of following parts by weight: HDPE34 parts;
PPR34 parts;LLDPE5 parts;20 parts of heavy calcium carbonate;2 parts of color masterbatch;2 parts of lubricant;1 part of titanate coupling agent.
The preparation method of above-mentioned summer double-wall corrugated pipe, it is the following steps are included: (a) weighs the internal layer of formula ratio respectively
Raw material and outer layer raw material are then added separately to be mixed in two batch mixers;(b) by the internal layer raw material and outer layer raw material
It heats, is squeezed out through two-layer compound die head respectively;(c) bellows is pulled out through molding machine and is formed, cut after cooling and obtain finished product.Step
Suddenly in (a), the mixing of the outer layer raw material specifically: alkali-free glass fibre is surface-treated using silane coupling agent, with
Melting extrusion granulation is carried out with PPH afterwards;Stearic acid, PE wax, wollastonite in powder and the heavy calcium carbonate for weighing formula ratio, in mixing
Activation is stirred in 70~90 DEG C in machine;Remaining outer layer raw material is added, is stirred, dehumidifies in 70~90 DEG C, blowing waits for
With;In step (a), the mixing of the internal layer raw material specifically: stearic acid, the PE wax, powdered whiting for weighing formula ratio, mixed
Activation is stirred in 70~90 DEG C in material machine;Remaining outer layer raw material is added, is stirred, dehumidifies in 70~90 DEG C, blowing
For use;Above-mentioned processing step is conducive to each being sufficiently mixed for raw material and can promote the overall performance of product.
Below in conjunction with embodiment, invention is further explained.
Embodiment 1-3, comparative example 1-2
Embodiment 1-3, comparative example 1-2 provide a kind of summer double-wall corrugated pipe respectively, they are respectively included from inside to outside
The internal layer and outer layer (specific composition of raw materials is shown in Table 1) set gradually, specific preparation process can be using routines: by formula ratio
Internal layer raw material be sequentially placed into blender and mixed, mixture temperature is 80 DEG C, mixing time 25min;By formula ratio
Outer layer raw material, which is sequentially placed into blender, to be mixed, and mixture temperature is 80 DEG C, mixing time 25min;By internal layer raw material and
Outer layer raw material is added separately in two extruders, one section of machine barrel, two sections, three sections, four sections, five sections of temperature be respectively 50 DEG C, 180
DEG C, 200 DEG C, 210 DEG C and 220 DEG C, die temperature is divided into four sections, one section of die orifice, two sections, three sections, four sections of temperature be respectively 220
DEG C, 220 DEG C, 220 DEG C and 225 DEG C, after molding machine pulls out bellows, by cutting machine fixed length cutting (application No. is
Disclosed in 201610697945.2).
The formula table (unit: kg) of summer double-wall corrugated pipe in 1 embodiment 1-3 of table, comparative example 1-2
The outer layer formula of summer double-wall corrugated pipe in embodiment 1-3, comparative example 1-2 is total to by above-mentioned (a) step
After mixed processing, double screw extruder melting extrusion under the conditions of 190~210 DEG C, after cooling pelletizing are used.By manufactured particle
The standard examination for meeting GB/T1040.1-2006, GB/T1043.1-2008 is prepared under the conditions of 190~210 DEG C using injection molding machine
It is tested for the property after sample, the result is shown in tables 2.
Summer double-wall corrugated outer tube layer formula materials performance table in 2 embodiment 1-3 of table, comparative example 1-2
Summer obtained in embodiment 1-3, comparative example 1-2 is tested for the property with double-wall corrugated pipe, the result is shown in tables
3。
Summer double-wall corrugated outer tube layer formula materials performance table in 3 embodiment 1-3 of table, comparative example 1-2
Embodiment 4
The present embodiment provides a kind of summer double-wall corrugated pipe, composition of raw materials is consistent in embodiment 1, unlike
Preparation method is slightly different, specifically:
(a) alkali-free glass fibre is surface-treated using silane coupling agent, then carries out melting extrusion with PPH and makes
Grain;Above-mentioned pellet, stearic acid, PE wax, wollastonite in powder and the heavy calcium carbonate for weighing formula ratio, in 70~90 in batch mixer
DEG C it is stirred activation;Remaining outer layer raw material is added, is stirred, dehumidifies in 70~90 DEG C, blowing is stand-by;Weigh formula ratio
Stearic acid, PE wax, powdered whiting, be stirred activation in 70~90 DEG C in batch mixer;Remaining outer layer raw material is added,
It is stirred, dehumidifies in 70~90 DEG C, blowing is stand-by;After similarly carrying out blending processing, using double screw extruder 190~
Melting extrusion under the conditions of 210 DEG C, after cooling pelletizing;Manufactured particle is prepared under the conditions of 190~210 DEG C using injection molding machine
At being tested for the property after the standard sample for meeting GB/T1040.1-2006, GB/T1043.1-2008, result is better than implementation
In example 1;
(b) internal layer raw material and outer layer raw material are heated respectively, through two-layer compound die head extrusion, (heating, the parameter squeezed out are still
Using in embodiment 1);
(c) bellows is pulled out through molding machine and is formed, cut after cooling and obtain finished product.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention, it is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of summer double-wall corrugated pipe, it includes the internal layer and outer layer set gradually from inside to outside, it is characterised in that:
The outer layer includes the raw material components of following parts by weight:
26 ~ 30 parts of PPH;
25 ~ 32 parts of HDPE;
3 ~ 8 parts of mPE;
30 ~ 40 parts of inorganic filler;
2.5 ~ 3 parts of lubricant;
1.5 ~ 2.5 parts of color masterbatch;
2 ~ 2.5 parts of agent composition of coupling;
0.2 ~ 0.5 part of antioxidant;
0.2 ~ 0.25 part of auxiliary antioxidant;
0.5 ~ 0.8 part of light stabilizer;
0.2 ~ 0.25 part of ultraviolet absorbing agent;
The internal layer includes the raw material components of following parts by weight:
30 ~ 40 parts of HDPE;
30 ~ 40 parts of PPR;
3 ~ 8 parts of LLDPE;
15 ~ 25 parts of heavy calcium carbonate;
1.5 ~ 2.5 parts of color masterbatch;
1 ~ 3 part of lubricant;
0.5 ~ 1.5 part of titanate coupling agent;
The inorganic filler is the mixing of heavy calcium carbonate, wollastonite in powder and alkali-free glass fibre 10:2:3 in mass ratio composition
Object;The coupling agent composition is the mixture that titanate coupling agent and silane coupling agent 1:1 in mass ratio are formed;The lubrication
Agent is the mixture that stearic acid and PE wax 1:1 in mass ratio are formed.
2. summer double-wall corrugated pipe according to claim 1, which is characterized in that the outer layer includes following parts by weight
Raw material components:
27 parts of PPH;
30 parts of HDPE;
5 parts of mPE;
30 parts of inorganic filler;
2.8 parts of lubricant;
2 parts of color masterbatch;
2 parts of agent composition of coupling;
0.3 part of antioxidant;
0.2 part of auxiliary antioxidant;
0.5 part of light stabilizer;
0.2 part of ultraviolet absorbing agent.
3. summer double-wall corrugated pipe according to claim 1, which is characterized in that the internal layer includes following parts by weight
Raw material components:
34 parts of HDPE;
34 parts of PPR;
5 parts of LLDPE;
20 parts of heavy calcium carbonate;
2 parts of color masterbatch;
2 parts of lubricant;
1 part of titanate coupling agent.
4. the preparation method of summer double-wall corrugated pipe any one of claims 1 to 3, which is characterized in that it includes following
Step:
(a) the internal layer raw material and outer layer raw material for weighing formula ratio respectively are then added separately to be mixed in two batch mixers;
(b) the internal layer raw material and outer layer raw material are heated respectively, is squeezed out through two-layer compound die head;
(c) bellows is pulled out through molding machine and is formed, cut after cooling and obtain finished product.
5. the preparation method of summer double-wall corrugated pipe according to claim 4, which is characterized in that described outer in step (a)
The mixing of layer raw material specifically: alkali-free glass fibre is surface-treated using silane coupling agent, is then melted with PPH
Extruding pelletization;Weigh formula ratio stearic acid, PE wax, wollastonite in powder and heavy calcium carbonate, in batch mixer in 70 ~ 90 DEG C into
Row stir-activating;Remaining outer layer raw material is added, is stirred, dehumidifies in 70 ~ 90 DEG C, blowing is stand-by.
6. the preparation method of summer double-wall corrugated pipe according to claim 4, which is characterized in that described interior in step (a)
The mixing of layer raw material specifically: stearic acid, the PE wax, powdered whiting for weighing formula ratio carry out in batch mixer in 70 ~ 90 DEG C
Stir-activating;Remaining outer layer raw material is added, is stirred, dehumidifies in 70 ~ 90 DEG C, blowing is stand-by.