CN109929373A - A kind of electronic component novel coating composition - Google Patents
A kind of electronic component novel coating composition Download PDFInfo
- Publication number
- CN109929373A CN109929373A CN201711352890.2A CN201711352890A CN109929373A CN 109929373 A CN109929373 A CN 109929373A CN 201711352890 A CN201711352890 A CN 201711352890A CN 109929373 A CN109929373 A CN 109929373A
- Authority
- CN
- China
- Prior art keywords
- electronic component
- coating composition
- novel coating
- agent
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of electronic component novel coating composition, it is characterised in that it includes the component of following parts by weight: the component including following parts by weight: Hydroxylated acrylic resin 19-32, polyvinyl chloride resin 8-17, aluminium oxide ceramics powder 7-18, azodiisobutyronitrile 5-11, polyvinyl alcohol 13-29, dispersing agent 7-12, thickener 5-9, fungicide 31-38, defoaming agent 4-7, pH adjusting agent 1-3, silicon carbide tiny balloon 42-59, nano SAPO-31 molecular sieve 31-47, distilled water 17-26.The present invention has drawn the advantages of prior art, by mechanical means is applied to product surface after the firing of electronic component external electrode, and through high temperature firing, being firmly combined for coating and product be will not cracking, and energy perfection covers in product exposed electrode；Electronic component novel coating composition also has functionality simultaneously, further increases the service life of product.
Description
Technical field
The present invention relates to electronic component protection technology fields, and in particular to a kind of electronics member applied to electronic component
Device novel coating composition.
Background technique
Electronic component is the component part of electronic component and electric small-sized machine, instrument, itself is often by several parts
It constitutes, it can be general in similar product;Often refer to electric appliance, radio, the industry such as instrument certain parts, as capacitor, transistor,
The general name of the sub- device such as balance spring, clockwork spring.It common are diode etc..
Because of the requirement of product characteristic, the back edge amount of existing low melting point cofired stack chip electronic component, i.e., interior electrode spacing
The distance of product edge is smaller and smaller.Due to the limitation of production equipment machining accuracy, it is exposed that most product will appear interior electrode
Phenomenon, need to be in product surface coating protective layer, to cover exposed interior electrode.The protection coating of surface coating at present substantially has
Two kinds, one is based on organic material, product surface is applied to by mechanical means after the firing of product external electrode, through adding
It is formed after heat drying, solidification, is not required to through high temperature firing, high temperature can not be resistant to, the combination of coating and product is insecure；It is another
Coating need to be burnt into through (700-900 DEG C) of high temperature, and coating and porcelain body form fine and close overall structure after firing, but in sintering process
In, because the sintering for the 15%-20% that wellability of the coating material to product porcelain body and electrode material is inconsistent and coating is intrinsic is received
Gap between volume change caused by the thermal expansion of shrinkage and porcelain body, coating easily crack.Electricity in the prior art simultaneously
The coating of sub- component does not have the performances such as antibacterial, high temperature resistant, salt spray resistance.
Summary of the invention
In view of this, the present invention provides a kind of electronic component novel coating composition, to solve asking for the prior art
Topic.
The technical solution of the present invention is as follows: a kind of electronic component novel coating composition, which is characterized in that including following
The component of parts by weight: the component including following parts by weight: Hydroxylated acrylic resin 19-32, polyvinyl chloride resin 8-17,
Aluminium oxide ceramics powder 7-18, azodiisobutyronitrile 5-11, polyvinyl alcohol 13-29, dispersing agent 7-12, thickener 5-9, sterilization
Agent 31-38, defoaming agent 4-7, pH adjusting agent 1-3, silicon carbide tiny balloon 42-59, nano SAPO-31 molecular sieve 31-47,
Distilled water 17-26.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 31-45, polyethylene
Pyrrolidones 13-27, to section Chinese ash leaf extract 39-48.
In the present invention, the alfalfa extract of the use of use, alfalfa (Medicago sativa) is for many years
Raw herbaceous plant, main root is longer, multi-branched, and stem Chang Zhili, almost hairless, 100 cm of plant height 30- is mainly distributed in China
In Qinghai, Xinjiang, Ningxia, Gansu and the Inner Mongol and other places.Nutritive value is abundant, and crude protein content usually 22% or so, contains 20
Kind or more amino acid.Clover flavone compound is quite abundant, it was reported that flavone compound contained by clover has
More than 80 kinds, and it is various structures, many kinds of.Flavone compound can remove free radical, effectively inhibit adrenergic oxygen
Change, reduce the concentration of low-density lipoprotein (LDL) concentration and peroxide;Myocardial infarction can also be reduced and hinder dead and artery
The disease incidence and the death rate of atherosis.
In the present invention, described pair of section Chinese ash leaf extract the preparation method comprises the following steps: at room temperature, will dry in the shade to section Chinese wax
Leaf (1000.0g) extracts 2.5d with 1500mL anhydrous methanol cold soaking, will sufficiently extract to the extract in section Chinese ash leaf
Come, extracting solution be concentrated under reduced pressure into it is solvent-free steam, obtain methanol extract.Methanol extract is first dissolved with distilled water, is then used
" liquid-liquid extraction method " is first used petroleum ether extraction 3 times, then is extracted 3 times with chloroform, is finally extracted 3 times with acetic acid ethyl ester, is used respectively
Rotary Evaporators be concentrated under reduced pressure into it is solvent-free steam, be subsequently placed in draught cupboard be dried with nitrogen it is spare.After water layer concentration, use is anhydrous
Ethyl alcohol dissolution concentration band water 3 times, be subsequently placed in draught cupboard be dried with nitrogen it is spare.Particularly, pilot scale or this preparation side when volume production
The amplification of method equal proportion.Of the invention has excellent bacteriostatic activity to section Chinese ash leaf extract, has for common bacterium
70% or more bacteriostasis rate.
In the present invention, polyvinylpyrrolidone is industrially used as expanded polystyrene (EPS) auxiliary agent, the gelling of suspension polymerisation
Agent, stabilizer, fibre finish, paper conversion auxiliary agent, adhesive, thickener.Polyvinylpyrrolidone PVP and its copolymer CAP
It is the important source material of cosmetics, is mainly used for hair style retention agent, the film high resilience and gloss that it is formed on hair, combing
Function admirable is not covered with dust, and using the resin of different size, can meet various relative humidity weather conditions, therefore it is sizing
Hair-cream, hair jelly, the indispensable raw material of mousse institute.It can be used for skin care moisturizing agent and the hair dyeing dispersion of fat base-material of cosmetics
Agent, foam stabiliser can improve the consistency of shampoo.It simultaneously can be with medical, aquaculture, herding disinfectant.For skin,
The disinfection of mucous membrane.
Fungicide of the invention, by alfalfa extract, to section Chinese ash leaf extract in polyvinylpyrrolidone
In synergistic effect, excellent fungistatic effect can be reached.Particularly, mixed to enter silicon carbide hollow micro- for fungicide of the invention
In ball, nano-beta molecular sieve, long-acting antibacterial layer is formed in coating surface.
Further, the dispersing agent is lauryl sodium sulfate, methyl anyl alcohol, polyacrylamide, guar gum, fatty acid
One of macrogol ester.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
Preferably, coating of the present invention the preparation method comprises the following steps:
S1. by Hydroxylated acrylic resin, polyvinyl chloride resin, aluminium oxide ceramics powder, azodiisobutyronitrile, polyvinyl alcohol, dispersion
It is shaken up after agent, thickener, defoaming agent, pH adjusting agent, distilled water dissolution, wherein acrylic monomers uses after newly steaming；It will shake up
Solution is heated to 40-50 DEG C afterwards, and stirs 60-90min with 60r/min, obtains mixed solution；S2. by silicon carbide tiny balloon,
Nano-beta molecular sieve is mixed with fungicide；S3. remaining component of component and coating in S1 and S2 is mixed according to mass fraction
It closes, 20-40min is dispersed with the rate of dispersion of 4000-5500r/min.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
The coating method technical problem of electronic component of the present invention novel coating composition is given by the following technical programs
To solve.
Preferably, the coating method of electronic component surface protection coating, including using XY horizontal reciprocating coating machine and
Small-bore spray gun coating, and high temperature sintering is carried out to coating.
The characteristics of coating method of this laminated sheet type electronic component surface protection coating is: the coating is using extremely
The multiple coating of few 2 coatings, is correspondingly formed at least 2 layers of laminated coating, by repeatedly smearing production coating, thickness
Uniformity is generally preferable, and the coating coating material different from the weight ratio of ceramic powder using filler material molecular sieve every time, to increase
Add the covering to product of the binding force and coating of coating and product magnet, protecting effect.
Preferably, the firing temperature of the high temperature sintering is 700 DEG C -900 DEG C.
Preferably, the firing temperature of the high temperature sintering is 800 DEG C.
The beneficial effects of the present invention are: the present invention has drawn the advantages of prior art, burns in electronic component external electrode
Product surface is applied to by mechanical means at rear, through high temperature firing, being firmly combined for coating and product be will not cracking, and energy
Perfection covers in product exposed electrode；Electronic component novel coating composition also has functionality simultaneously, further increases
The service life of product.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with embodiment, it is clear that described reality
Applying example is only a part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 19, polyvinyl chloride resin 8, aluminium oxide ceramics powder 7, azodiisobutyronitrile 5,
Polyvinyl alcohol 13, dispersing agent 7, thickener 5, fungicide 31, defoaming agent 4, pH adjusting agent 1, silicon carbide tiny balloon 42,
Nano SAPO-31 molecular sieve 31, distilled water 17.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 31, polyethylene pyrrole
Pyrrolidone 13, to section Chinese ash leaf extract 39.
In the present invention, the alfalfa extract of the use of use, alfalfa (Medicago sativa) is for many years
Raw herbaceous plant, main root is longer, multi-branched, and stem Chang Zhili, almost hairless, 100 cm of plant height 30- is mainly distributed in China
In Qinghai, Xinjiang, Ningxia, Gansu and the Inner Mongol and other places.Nutritive value is abundant, and crude protein content usually 22% or so, contains 20
Kind or more amino acid.Clover flavone compound is quite abundant, it was reported that flavone compound contained by clover has
More than 80 kinds, and it is various structures, many kinds of.Flavone compound can remove free radical, effectively inhibit adrenergic oxygen
Change, reduce the concentration of low-density lipoprotein (LDL) concentration and peroxide;Myocardial infarction can also be reduced and hinder dead and artery
The disease incidence and the death rate of atherosis.
In the present invention, described pair of section Chinese ash leaf extract the preparation method comprises the following steps: at room temperature, will dry in the shade to section Chinese wax
Leaf (1000.0g) extracts 2.5d with 1500mL anhydrous methanol cold soaking, will sufficiently extract to the extract in section Chinese ash leaf
Come, extracting solution be concentrated under reduced pressure into it is solvent-free steam, obtain methanol extract.Methanol extract is first dissolved with distilled water, is then used
" liquid-liquid extraction method " is first used petroleum ether extraction 3 times, then is extracted 3 times with chloroform, is finally extracted 3 times with acetic acid ethyl ester, is used respectively
Rotary Evaporators be concentrated under reduced pressure into it is solvent-free steam, be subsequently placed in draught cupboard be dried with nitrogen it is spare.After water layer concentration, use is anhydrous
Ethyl alcohol dissolution concentration band water 3 times, be subsequently placed in draught cupboard be dried with nitrogen it is spare.Particularly, pilot scale or this preparation side when volume production
The amplification of method equal proportion.Of the invention has excellent bacteriostatic activity to section Chinese ash leaf extract, has for common bacterium
70% or more bacteriostasis rate.
In the present invention, polyvinylpyrrolidone is industrially used as expanded polystyrene (EPS) auxiliary agent, the gelling of suspension polymerisation
Agent, stabilizer, fibre finish, paper conversion auxiliary agent, adhesive, thickener.Polyvinylpyrrolidone PVP and its copolymer CAP
It is the important source material of cosmetics, is mainly used for hair style retention agent, the film high resilience and gloss that it is formed on hair, combing
Function admirable is not covered with dust, and using the resin of different size, can meet various relative humidity weather conditions, therefore it is sizing
Hair-cream, hair jelly, the indispensable raw material of mousse institute.It can be used for skin care moisturizing agent and the hair dyeing dispersion of fat base-material of cosmetics
Agent, foam stabiliser can improve the consistency of shampoo.It simultaneously can be with medical, aquaculture, herding disinfectant.For skin,
The disinfection of mucous membrane.
Fungicide of the invention, by alfalfa extract, to section Chinese ash leaf extract in polyvinylpyrrolidone
In synergistic effect, excellent fungistatic effect can be reached.Particularly, mixed to enter silicon carbide hollow micro- for fungicide of the invention
In ball, nano-beta molecular sieve, long-acting antibacterial layer is formed in coating surface.
Further, the dispersing agent is lauryl sodium sulfate.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
Preferably, coating of the present invention the preparation method comprises the following steps:
S1. by Hydroxylated acrylic resin, polyvinyl chloride resin, aluminium oxide ceramics powder, azodiisobutyronitrile, polyvinyl alcohol, dispersion
It is shaken up after agent, thickener, defoaming agent, pH adjusting agent, distilled water dissolution, wherein acrylic monomers uses after newly steaming；It will shake up
Solution is heated to 40-50 DEG C afterwards, and stirs 60-90min with 60r/min, obtains mixed solution；S2. by silicon carbide tiny balloon,
Nano-beta molecular sieve is mixed with fungicide；S3. remaining component of component and coating in S1 and S2 is mixed according to mass fraction
It closes, 20-40min is dispersed with the rate of dispersion of 4000-5500r/min.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
The coating method technical problem of electronic component of the present invention novel coating composition is given by the following technical programs
To solve.
Preferably, the coating method of electronic component surface protection coating, including using XY horizontal reciprocating coating machine and
Small-bore spray gun coating, and high temperature sintering is carried out to coating.
The characteristics of coating method of this laminated sheet type electronic component surface protection coating is: the coating is using extremely
The multiple coating of few 2 coatings, is correspondingly formed at least 2 layers of laminated coating, by repeatedly smearing production coating, thickness
Uniformity is generally preferable, and the coating coating material different from the weight ratio of ceramic powder using filler material molecular sieve every time, to increase
Add the covering to product of the binding force and coating of coating and product magnet, protecting effect.
Preferably, the firing temperature of the high temperature sintering is 700 DEG C -900 DEG C.
Preferably, the firing temperature of the high temperature sintering is 800 DEG C.
The beneficial effects of the present invention are: the present invention has drawn the advantages of prior art, burns in electronic component external electrode
Product surface is applied to by mechanical means at rear, through high temperature firing, being firmly combined for coating and product be will not cracking, and energy
Perfection covers in product exposed electrode；Electronic component novel coating composition also has functionality simultaneously, further increases
The service life of product.
Embodiment 2
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 32, polyvinyl chloride resin 17, aluminium oxide ceramics powder 18, azodiisobutyronitrile
11, polyvinyl alcohol 29, dispersing agent 12, thickener 9, fungicide 38, defoaming agent 7, pH adjusting agent 3, silicon carbide are hollow micro-
Ball 59, nano SAPO-31 molecular sieve 47, distilled water 26.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 45, polyethylene pyrrole
Pyrrolidone 27, to section Chinese ash leaf extract 48.
Further, the dispersing agent is methyl anyl alcohol.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Embodiment 3
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 23, polyvinyl chloride resin 11, aluminium oxide ceramics powder 12, azodiisobutyronitrile
7, polyvinyl alcohol 16, dispersing agent 9, thickener 6, fungicide 33, defoaming agent 5, pH adjusting agent 1.5, silicon carbide are hollow micro-
Ball 45, nano SAPO-31 molecular sieve 34, distilled water 19.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 34, polyethylene pyrrole
Pyrrolidone 17, to section Chinese ash leaf extract 41.
Further, the dispersing agent is guar gum.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Embodiment 4
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 25, polyvinyl chloride resin 13, aluminium oxide ceramics powder 15, azodiisobutyronitrile
8, polyvinyl alcohol 23, dispersing agent 10, thickener 7, fungicide 36, defoaming agent 6, pH adjusting agent 2, silicon carbide tiny balloon
52, nano SAPO-31 molecular sieve 38, distilled water 23.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 41, polyethylene pyrrole
Pyrrolidone 24, to section Chinese ash leaf extract 43.
Further, the dispersing agent is polyacrylamide.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Embodiment 5
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 30, polyvinyl chloride resin 15, aluminium oxide ceramics powder 16, azodiisobutyronitrile
10, polyvinyl alcohol 27, dispersing agent 10, thickener 8, fungicide 37, defoaming agent 6, pH adjusting agent 2.7, silicon carbide are hollow
Microballoon 57, nano SAPO-31 molecular sieve 45, distilled water 24.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 42, polyethylene pyrrole
Pyrrolidone 25, to section Chinese ash leaf extract 46.
Further, the dispersing agent is fatty acid polyethylene glycol ester.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Comparative example 1
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 25, polyvinyl chloride resin 13, azodiisobutyronitrile 8, polyvinyl alcohol 23,
Dispersing agent 10, thickener 7, fungicide 36, defoaming agent 6, pH adjusting agent 2, silicon carbide tiny balloon 52, nanometer SAPO-31
Molecular sieve 38, distilled water 23.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 41, polyethylene pyrrole
Pyrrolidone 24, to section Chinese ash leaf extract 43.
Further, the dispersing agent is polyacrylamide.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Comparative example 2
A kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including following
The component of parts by weight: Hydroxylated acrylic resin 25, polyvinyl chloride resin 13, aluminium oxide ceramics powder 15, azodiisobutyronitrile
8, polyvinyl alcohol 23, dispersing agent 10, thickener 7, fungicide 36, defoaming agent 6, pH adjusting agent 2, nanometer SAPO-31 point
Son sieve 38, distilled water 23.
Further, the fungicide includes the component of following parts by weight: alfalfa extract 41, polyethylene pyrrole
Pyrrolidone 24, to section Chinese ash leaf extract 43.
Further, the dispersing agent is polyacrylamide.
Further, the thickener is hydroxyethyl ether cellulose.
Further, the defoaming agent is tributyl phosphate.
Further, the pH adjusting agent is diethanol amine.
The synergistic compounding of middle each component, the present invention are able to solve coating surface tension and generate change of gradient through the invention,
Phenomena such as system viscosity increases, and filler dispersion is uneven, Yi Fasheng orange peel, shrinkage cavity, mist shadow, has excellent levelling effect；
The present invention has excellent antibiotic property and flame retardant property, while salt spray resistance ability is good, is suitable for large-scale promotion and uses.
Coating property test
Salt spray resistance
Embodiment 1-5 and comparative example 1-2 are prepared into coating respectively, are coated in wooden test piece and aluminium alloy test piece respectively,
Aluminium alloy test piece selects 6063.After paint spraying, stands 48 hours and tested after film forming is fully cured in coating.To above-mentioned painting
Layer carries out adhesive force test, neutral salt spray test, and test method is carried out according to concerned countries standard, test result is as follows table.
Anti-microbial property and flame retardant property
According to concerned countries standard coating is prepared to embodiment 1-5 and comparative example 1-2 respectively and be tested for the property, as a result
As shown in the table.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.It is noted that the technical characteristic being not described in detail in the present invention, can pass through this
Field any prior art is realized.
Claims (6)
1. a kind of electronic component novel coating composition, which is characterized in that the component including following parts by weight: including with
The component of lower parts by weight: Hydroxylated acrylic resin 19-32, polyvinyl chloride resin 8-17, aluminium oxide ceramics powder 7-18, azo
Bis-isobutyronitrile 5-11, polyvinyl alcohol 13-29, dispersing agent 7-12, thickener 5-9, fungicide 31-38, defoaming agent 4-7,
PH adjusting agent 1-3, silicon carbide tiny balloon 42-59, nano SAPO-31 molecular sieve 31-47, distilled water 17-26.
2. electronic component novel coating composition according to claim 1, which is characterized in that the fungicide includes
The component of following parts by weight: alfalfa extract 31-45, polyvinylpyrrolidone 13-27, section Chinese ash leaf is extracted
Object 39-48.
3. electronic component novel coating composition according to claim 1, which is characterized in that the dispersing agent is ten
One of sodium dialkyl sulfate, methyl anyl alcohol, polyacrylamide, guar gum, fatty acid polyethylene glycol ester.
4. electronic component novel coating composition according to claim 1, which is characterized in that the thickener is hydroxyl
Cellulose ether.
5. electronic component novel coating composition according to claim 1, which is characterized in that the defoaming agent is phosphorus
Sour tributyl.
6. electronic component novel coating composition according to claim 1, which is characterized in that the pH adjusting agent is
Diethanol amine.