CN109912226A - A kind of ambetti disk production technology and the ambetti disk made using the technique - Google Patents
A kind of ambetti disk production technology and the ambetti disk made using the technique Download PDFInfo
- Publication number
- CN109912226A CN109912226A CN201910134087.4A CN201910134087A CN109912226A CN 109912226 A CN109912226 A CN 109912226A CN 201910134087 A CN201910134087 A CN 201910134087A CN 109912226 A CN109912226 A CN 109912226A
- Authority
- CN
- China
- Prior art keywords
- glass
- temperature
- ambetti
- production technology
- promoted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to ambetti disk field, a kind of ambetti disk production technology is disclosed, including air brushing is carried out to glass；Tempering processing is carried out to glass；Glass temperature is promoted to 780 DEG C -810 DEG C；The compacting of shape is carried out to glass；Reduce glass temperature；Glass temperature is promoted to 500 DEG C -550 DEG C；Glass temperature is promoted to 700 DEG C；Glass temperature is reduced to room temperature state.The present invention has the effect of reducing fraction defective.
Description
Technical field
The present invention relates to the technical fields of ambetti disk, more particularly, to a kind of ambetti disk production technology and use
The ambetti disk of technique production.
Background technique
Can all have certain pattern on glass plate at present, so that glass plate is more beautiful, be easy by consumer
Like.
What the mode that silk-screen is usually used in the pattern on existing glass plate was printed.
Prior art among the above have the following deficiencies: due to silk-screen can only a kind of color of one-step print, work as glass
When the color of disk is more various, it is easy to appear the inaccurate situation of chromatography in process of production and occurs, leads to the glass produced
The fraction defective of disk is promoted.
Summary of the invention
In view of the deficienciess of the prior art, the invention reside in provide a kind of ambetti disk production technology and use the work
The ambetti disk of skill production has the effect of reducing fraction defective.
To achieve the above object, the present invention provides the following technical scheme that a kind of ambetti disk production technology, including,
Air brushing is carried out to glass；
Tempering processing is carried out to glass；
Glass temperature is promoted to 780 DEG C -810 DEG C；
The compacting of shape is carried out to glass；
Reduce glass temperature；
Glass temperature is promoted to 500 DEG C -550 DEG C；
Glass temperature is promoted to 700 DEG C；
Glass temperature is reduced to room temperature state.
By using above-mentioned technical proposal, by air brushing by pattern it is relatively firm stay in glass surface, then to glass
Tempering processing is carried out, internal stress is eliminated, so that glass is relatively stable, it is not easily broken；Then the temperature of glass is promoted to 780
DEG C -810 DEG C, so that glass melting, can suppress glass by mold at this time, so that decorated disk shape is formed, it is then right
Glass cools down, so that the shape of glass plate is fixed；The temperature of glass is then lifted out to 500 DEG C -550 DEG C, is then promoted again
To 700 DEG C, so that the stress to inside glass is eliminated, keeps the intensity of glass higher, be finally reduced to the temperature of glass
Room temperature reduces fraction defective to complete the production of ambetti disk.
The present invention is further arranged to: it is described to include to glass progress tempering,
Glass temperature is promoted to 700 DEG C；
Maintain glass temperature at 700 DEG C ± 50 DEG C；
Keep 6min-8min.
By using above-mentioned technical proposal, by promoting the temperature of glass, so that the stress of inside glass is eliminated, so that glass
The intensity of glass itself gets a promotion, so that glass be made to be not easily broken.
The present invention is further arranged to: the reduction glass temperature includes,
It is reduced by temperature of the air cooling way to glass；
The temperature reducing rate for controlling glass is 50 DEG C/min；
When the temperature of glass is reduced to same room temperature equal, stop air-cooled operation.
By using above-mentioned technical proposal, by air-cooled mode the temperature of glass is more quickly declined, every point
Zhong Wushi degrees Celsius of decrease speed, so that the rate of descent of temperature is more uniform, so that glass itself is not susceptible to rupture,
Reduce fraction defective.
The present invention is further arranged to: the wind direction of the air cooling way is towards glass interior recess after molding.
By using above-mentioned technical proposal, wind direction towards glass interior recess after molding so that air and glass it
Between contact increase, so that the temperature of glass be enable more quickly to decline.
The present invention is further arranged to: the promotion glass temperature includes to 500 DEG C -550 DEG C,
Stand glass 5-10min；
Glass temperature is promoted to 450 DEG C -460 DEG C；
It maintains glass temperature at 450 DEG C -460 DEG C, and continues 3min-4min；
Glass temperature is promoted to 500 DEG C -550 DEG C, and continues 10min.
By using above-mentioned technical proposal, segmentation promotes the temperature of glass, while eliminating glass internal stress, so that glass
Glass itself is not easy to be damaged since temperature more quickly changes.
The present invention is further arranged to: the reduction glass temperature to room temperature state includes,
Glass temperature is reduced to 600 DEG C, and continues 5min；
Glass temperature is reduced to 500 DEG C, and continues 5min；
Make the temperature cooled to room temperature of glass.
By using above-mentioned technical proposal, the temperature of glass is stablized in two times while reducing glass temperature,
So that the temperature drop rate of glass is slower, can the stress to inside glass preferably removed.
The present invention is further arranged to: it is described to glass carry out shape compacting include,
Glass is suppressed to the shape of requirement；
Modification is adjusted to glass shape.
By using above-mentioned technical proposal, after the completion of the compacting of the shape of glass, since glass at this time is in molten
State, the edge of pressed glass plate are easy to appear protuberance, to need to modify the shape of glass, to make glass plate
It is more beautiful, reduce fraction defective.
The present invention is further arranged to: it is described to include to glass progress air brushing,
By high temp glass emitting ink in glass surface；
High temp glass ink is preheated, pre-setting is carried out.
By using above-mentioned technical proposal, high temp glass ink first constitutes figure in glass surface, then in heat gun
Heating is lower to realize pre-setting, and stable is located at glass surface, in heating process later, realizes sizing completely, reduces not
Yield.
To achieve the above object, the present invention provides the following technical scheme that a kind of ambetti disk, using claim 1-
Ambetti disk production technology described in 8 any one is made.
By using above-mentioned technical proposal, by above-mentioned technique, so that the glass plate intensity and color produced are all more
It meets the requirements, to reduce fraction defective.
In conclusion the invention has the following advantages:
It is handled by air brushing and tempering, so that the color of glass and intensity are improved, while by the promotion of two sides temperature,
And the Temperature fall after temperature promotion, so that the stress of inside glass is reduced, so that glass not cracky, reduces fraction defective.
Detailed description of the invention
Fig. 1 is step figure of the invention.
Specific embodiment
Below in conjunction with attached drawing, invention is further described in detail.
It referring to Fig.1, is a kind of ambetti disk production technology disclosed by the invention, including,
S1: air brushing is carried out to glass；High temp glass ink is uniformly sprayed in glass surface, and is added by heat gun
Heat, to complete the pre-setting of high temp glass ink.
S2: tempering processing is carried out to glass；Glass is heated, the temperature of glass is made to be promoted to 700 DEG C, then to adding
Hot temperature, which carries out control, to be made, and glass own temperature maintains 730 DEG C, and keeps 6min-8min, and high temp glass ink is in height at this time
It is formed completely under the action of temperature.
S3: glass temperature is promoted to 780 DEG C -810 DEG C；The temperature of glass is promoted to 800 DEG C, glass is in complete at this time
Molten condition.
S4: the compacting of shape is carried out to glass；After glass melts completely, glass is suppressed by mold, thus shape
At the pattern of required ambetti disk, the shape of glass is further modified after the completion of compacting, meets shape
Design requirement.
S5: glass temperature is reduced；Cooled down by air-cooled mode, wind direction is controlled towards glass inner concave after molding
The cooling rate of glass processed, making glass own temperature per minute reduces by 50 DEG C, when the difference between the temperature and room temperature of glass is small
When 3 DEG C, stop air-cooled operation.
S6: glass temperature is promoted to 500 DEG C -550 DEG C；By glass after cooling static 10 minutes, make glass temperature and room
Temperature is identical, then heats to glass, so that the temperature of glass is reached 450 DEG C, then control heating temperature, makes the temperature of glass
Stablize at 450 DEG C and continue 4 minutes, then glass is continued to heat, so that the temperature of glass is risen to 550 DEG C, then control
Heating temperature processed makes the temperature of glass stablize at 550 DEG C and continue 10 minutes.
S7: glass temperature is promoted to 700 DEG C；The temperature of glass is promoted to 700 DEG C from 550 DEG C, then control heating temperature
Degree, makes the temperature of glass maintain 700 degrees Celsius and continues 5 minutes.
S8: glass temperature is reduced to room temperature state；The temperature of glass is reduced to 600 DEG C, then the temperature of glass is carried out
Control, makes the temperature of glass maintain 600 DEG C and continues 5 minutes, then cool down to glass, so that the temperature of glass reduces
To 500 DEG C, then the temperature of glass is controlled, the temperature of glass is made to maintain 500 DEG C and continues 5 minutes, finally makes glass
Glass warms to room temperature state in the decline of natural cooling state.
The implementation principle of the present embodiment are as follows: by air brushing by pattern it is relatively firm stay in glass surface, then to glass
Tempering processing is carried out, internal stress is eliminated, so that glass is relatively stable, it is not easily broken；Then the temperature of glass is promoted to 800
DEG C, so that glass is completely melt, glass can be suppressed by mold at this time, to form decorated disk shape, complete to make
The modification for carrying out shape to glass plate after type then cools down to glass so that glass plate meets design requirement, so that glass
The shape of disk is fixed；The temperature of glass is then lifted out to 500 DEG C DEG C, first time heating is carried out, is then promoted to 700 DEG C again, into
Second of heating of row keeps the intensity of glass higher, finally drops the temperature of glass to eliminate to the stress of inside glass
Down to room temperature, temperature realizes 600 DEG C and 500 DEG C of staged cooling during reducing, and makes glass not cracky.
The embodiment of present embodiment is presently preferred embodiments of the present invention, not limits protection of the invention according to this
Range, therefore: the equivalence changes that all structures under this invention, shape, principle are done, should all be covered by protection scope of the present invention it
It is interior.
Claims (9)
1. a kind of ambetti disk production technology, it is characterized in that: include,
Air brushing is carried out to glass；
Tempering processing is carried out to glass；
Promoted glass temperature to 780 DEG C -810 DEG C,；
The compacting of shape is carried out to glass；
Reduce glass temperature；
Glass temperature is promoted to 500 DEG C -550 DEG C；
Glass temperature is promoted to 700 DEG C；
Glass temperature is reduced to room temperature state.
2. a kind of ambetti disk production technology according to claim 1, it is characterized in that: described carry out tempering packet to glass
It includes,
Glass temperature is promoted to 700 DEG C；
Maintain glass temperature at 700 DEG C ± 50 DEG C；
Keep 6min-8min.
3. a kind of ambetti disk production technology according to claim 1, it is characterized in that: the reduction glass temperature packet
It includes,
It is reduced by temperature of the air cooling way to glass；
The temperature reducing rate for controlling glass is 50 DEG C/min；
When the temperature of glass is reduced to same room temperature equal, stop air-cooled operation.
4. a kind of ambetti disk production technology according to claim 3, it is characterized in that: the wind direction court of the air cooling way
To glass interior recess after molding.
5. a kind of ambetti disk production technology according to claim 1, it is characterized in that: the promotion glass temperature is extremely
500 DEG C -550 DEG C include,
Stand glass 5-10min；
Glass temperature is promoted to 450 DEG C -460 DEG C；
It maintains glass temperature at 450 DEG C -460 DEG C, and continues 3min-4min；
Glass temperature is promoted to 500 DEG C -550 DEG C, and continues 10min.
6. a kind of ambetti disk production technology according to claim 1, it is characterized in that: the reduction glass temperature is to room
Temperature state includes,
Glass temperature is reduced to 600 DEG C, and continues 5min；
Glass temperature is reduced to 500 DEG C, and continues 5min；
Make the temperature cooled to room temperature of glass.
7. a kind of ambetti disk production technology according to claim 1, it is characterized in that: described carry out shape to glass
Compacting includes,
Glass is suppressed to the shape of requirement；
Modification is adjusted to glass shape.
8. a kind of ambetti disk production technology according to claim 1, it is characterized in that: described carry out air brushing packet to glass
It includes,
By high temp glass emitting ink in glass surface；
High temp glass ink is preheated, pre-setting is carried out.
9. a kind of ambetti disk, it is characterized in that: using ambetti disk production technology described in claim 1-8 any one
It is made.