CN109853293A - A kind of release paper resistant to high temperature - Google Patents
A kind of release paper resistant to high temperature Download PDFInfo
- Publication number
- CN109853293A CN109853293A CN201811611480.XA CN201811611480A CN109853293A CN 109853293 A CN109853293 A CN 109853293A CN 201811611480 A CN201811611480 A CN 201811611480A CN 109853293 A CN109853293 A CN 109853293A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- high temperature
- release paper
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of release paper resistant to high temperature, including body paper, coating one, coating two are successively arranged on the body paper;The coating one is by including that the raw material of following parts by weight is made: the trade mark is 5~15 parts of 85~95 parts of polypropylene, the glycidyl methacrylate graft polypropylene of H2800;The coating two is by including that the raw material of following parts by weight is made: the trade mark is 2~10 parts of 90~98 parts of polypropylene, the acrylamide graft polypropylene of H2800;By die head Extrusion Coating on body paper after the coating one and coating two are compound in die head.The high comprehensive performances such as the paper membrane bond strength of release paper resistant to high temperature of the invention, peel strength, high temperature resistance, shrinking percentage, and release paper surface refractory, be unlikely to deform, coating and body paper are not easily stripped, long service life.
Description
Technical field
The present invention relates to release paper fields, and in particular to a kind of release paper resistant to high temperature.
Background technique
Release paper needs to be widely used in industrial processes, is the transfer coated indispensable carrier of processing, from
Type paper surface needs high temperature resistant, is unlikely to deform;Polypropylene (PP) material making coatings can make release paper surface refractory, be not easy
Deformation, peeling effect is good, but PP material is not easy to combine with body paper, and polyethylene (PE) material making coatings can make between coating and body paper
There is higher bond strength, but do not have high temperature resistant and on-deformable characteristic, uses the mixing material of one layer of PE and PP at present
As the coating of release paper, so that the former base stock of release paper and release paper surface are easily-deformable, remove, service life is shorter, and table
Face does not have preferable high temperature resistant, on-deformable characteristic, and peeling effect is also bad.
Based on the above situation, the invention proposes a kind of release paper resistant to high temperature, problem above can effectively be solved.
Summary of the invention
The purpose of the present invention is to provide a kind of release papers resistant to high temperature.The paper membrane knot of release paper resistant to high temperature of the invention
It closes intensity, peel strength, high temperature resistance, the high comprehensive performances such as shrinking percentage, and release paper surface refractory, is unlikely to deform,
Coating and body paper are not easily stripped, long service life.
The present invention is achieved through the following technical solutions:
A kind of release paper resistant to high temperature, including body paper are successively arranged coating one, coating two on the body paper;The coating
One by including that the raw material of following parts by weight is made: the trade mark is 85~95 parts of the polypropylene of H2800, glycidyl methacrylate
5~15 parts of graft polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is the polypropylene 90 of H2800
~98 parts, 2~10 parts of acrylamide graft polypropylene;It is squeezed out and is applied by die head after the coating one and coating two are compound in die head
It is overlying on body paper.
The paper membrane bond strength of release paper resistant to high temperature of the invention, peel strength, high temperature resistance, shrinking percentage etc. are comprehensive
Function admirable, and release paper surface refractory, be unlikely to deform, coating and body paper are not easily stripped, long service life.
Preferably, the coating one by include following parts by weight raw material be made: the trade mark be H2800 88 parts of polypropylene,
12 parts of glycidyl methacrylate graft polypropylene.
Preferably, the coating two is by including that the raw material of following parts by weight is made: the trade mark is the polypropylene 96.5 of H2800
Part, 3.5 parts of acrylamide graft polypropylene.
Preferably, the overall thickness of the coating one and coating two is 0.1~1mm.
Preferably, the ratio between thickness of the coating one and the coating two is 1:2~5.
Preferably, the polyacrylic grafting rate of the glycidyl methacrylate graft is 0.15~0.25%.
Preferably, the polyacrylic grafting rate of the acrylamide graft is 0.12~0.22%.
Preferably, it is equipped with the back side of leaching membrane layer in the body paper, is additionally provided with the coating of the polyvinyl chloride of 1~2g/m2.
Compared with prior art, the present invention have the following advantages that and the utility model has the advantages that
The paper membrane bond strength of release paper resistant to high temperature of the invention, peel strength, high temperature resistance, shrinking percentage etc. are comprehensive
Function admirable, and release paper surface refractory, be unlikely to deform, coating and body paper are not easily stripped, long service life.
The present invention abandons selecting the polypropylene and methacrylic acid contracting that the trade mark of proper proportion is H2800 using polyethylene
Water glyceride graft polypropylene, which is blended, is used as coating one, using glycidyl methacrylate graft polypropylene in molten condition
Lower good fluidity, penetrating power be strong and the feature strong with the adhesive force on body paper, increases middle layer, so that release paper surface covering
Two due to PP material makes release paper surface have high temperature resistant, be unlikely to deform and production process in need transfer coated peeling effect good
The characteristics of, coating one makes coating one and body paper have higher knot due to the polyacrylic addition of glycidyl methacrylate graft
Intensity is closed, and coating one and coating two also have preferable bond strength, so that there have release paper surface covering and body paper to be higher
Bond strength so that the release paper produced have long service life, the good feature of peeling effect, the prior art produce from
Type paper service life is about 30 times, and the release paper service life that the present invention produces is about 70 times;It is carried on the back in conjunction in body paper
Face covers PVA coating, so that release paper is not easy to crimp in process of production and during producing artificial leather using release paper.
Specific embodiment
The present invention is described in further detail below with reference to embodiment, embodiments of the present invention are not limited thereto.
Test method described in following embodiments or test method are unless otherwise specified conventional method;The reagent
And material is obtained from routine business approach, or prepare in conventional manner unless otherwise specified.
Embodiment 1:
A kind of release paper resistant to high temperature, including body paper are successively arranged coating one, coating two on the body paper;The coating
One by including that the raw material of following parts by weight is made: the trade mark is 85~95 parts of the polypropylene of H2800, glycidyl methacrylate
5~15 parts of graft polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is the polypropylene 90 of H2800
~98 parts, 2~10 parts of acrylamide graft polypropylene;It is squeezed out and is applied by die head after the coating one and coating two are compound in die head
It is overlying on body paper.
Embodiment 2:
A kind of release paper resistant to high temperature, including body paper are successively arranged coating one, coating two on the body paper;The coating
One by including that the raw material of following parts by weight is made: the trade mark is 95 parts of polypropylene, the glycidyl methacrylate graft of H2800
5 parts of polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is 98 parts of polypropylene, the acryloyl of H2800
2 parts of amine graft polypropylene;By die head Extrusion Coating on body paper after the coating one and coating two are compound in die head.
In the present embodiment, the overall thickness of the coating one and coating two is 0.8mm.
In the present embodiment, the ratio between thickness of the coating one and the coating two is 1:2.
In the present embodiment, the polyacrylic grafting rate of the glycidyl methacrylate graft is 0.15%.
In the present embodiment, the polyacrylic grafting rate of the acrylamide graft is 0.12%.
In the present embodiment, it is equipped with the back side of leaching membrane layer in the body paper, is additionally provided with the coating of the polyvinyl chloride of 1g/m2.
Embodiment 3:
A kind of release paper resistant to high temperature, including body paper are successively arranged coating one, coating two on the body paper;The coating
One by including that the raw material of following parts by weight is made: the trade mark is 85 parts of polypropylene, the glycidyl methacrylate graft of H2800
15 parts of polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is 90 parts of polypropylene, the propylene of H2800
10 parts of acid amide-grafted polypropylene;By die head Extrusion Coating on body paper after the coating one and coating two are compound in die head.
In the present embodiment, the overall thickness of the coating one and coating two is 0.8mm.
In the present embodiment, the ratio between thickness of the coating one and the coating two is 1:5.
In the present embodiment, the polyacrylic grafting rate of the glycidyl methacrylate graft is 0.25%.
In the present embodiment, the polyacrylic grafting rate of the acrylamide graft is 0.22%.
In the present embodiment, it is equipped with the back side of leaching membrane layer in the body paper, is additionally provided with the coating of the polyvinyl chloride of 2g/m2.
Embodiment 4:
A kind of release paper resistant to high temperature, including body paper are successively arranged coating one, coating two on the body paper;The coating
One by including that the raw material of following parts by weight is made: the trade mark is 88 parts of polypropylene, the glycidyl methacrylate graft of H2800
12 parts of polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is 96.5 parts of the polypropylene of H2800, third
3.5 parts of acrylamide graft polypropylene;By die head Extrusion Coating on body paper after the coating one and coating two are compound in die head.
In the present embodiment, the overall thickness of the coating one and coating two is 0.8mm.
In the present embodiment, the ratio between thickness of the coating one and the coating two is 1:4.
In the present embodiment, the polyacrylic grafting rate of the glycidyl methacrylate graft is 0.18%.
In the present embodiment, the polyacrylic grafting rate of the acrylamide graft is 0.16%.
In the present embodiment, it is equipped with the back side of leaching membrane layer in the body paper, is additionally provided with the painting of the polyvinyl chloride of 1.5g/m2
Layer.
In the present invention, coating one and coating two it is compound in die head after by die head Extrusion Coating on body paper: first according to painting
Melting mixing is uniform respectively in a reservoir for the group raw material proportioning of layer one and coating two, and two kinds of coatings enter mould by double-layer coextrusion
Head, two kinds of coatings respectively enter die internal, and die internal has vertical clapboard that die head is divided into the channel one and channel two controlled,
Channel one is connected in die internal close to the exit of die head straight down with channel two, and two kinds of coatings converge in die head, then
It is squeezed out on the surface for covering body paper straight down from die head mouth.
Comparative example: according to the standby release paper of the patent system application No. is 201710057755.9.
The embodiment of the present invention 2 to embodiment 4, comparative example and common release paper are tested for the property below, test knot
Fruit is as shown in table 1:
Table 1
As can be seen from the above table, the release paper heat-resisting quantity resistant to high temperature of the embodiment of the present invention 2, embodiment 3 and embodiment 4
It can be excellent.
In addition, the paper membrane bond strength of release paper of the invention is up to 1.13N/15mm after tested;Peel strength is reachable
0.214N/cm;Shrinking percentage is up to 1.6%;Number is reused to reach 70 times;Tensile strength (vertical) is up to 9.75kN/m;Anti-tensile
Intensity (cross) is up to 1583mN;Solvent resistance is preferable.
The above is only presently preferred embodiments of the present invention, not does limitation in any form to the present invention, it is all according to
According to technical spirit any simple modification to the above embodiments of the invention, equivalent variations, protection of the invention is each fallen within
Within the scope of.
Claims (8)
1. a kind of release paper resistant to high temperature, including body paper, it is characterised in that: be successively arranged coating one, coating two on the body paper;
The coating one is by including that the raw material of following parts by weight is made: the trade mark is 85~95 parts of the polypropylene of H2800, methacrylic acid contracting
5~15 parts of water glyceride graft polypropylene;The coating two is by including that the raw material of following parts by weight is made: the trade mark is H2800's
90~98 parts of polypropylene, 2~10 parts of acrylamide graft polypropylene;By mould after the coating one and coating two are compound in die head
Head Extrusion Coating is on body paper.
2. release paper resistant to high temperature according to claim 1, it is characterised in that: the coating one is by including following parts by weight
Raw material be made: the trade mark be H2800 12 parts of 88 parts of polypropylene, glycidyl methacrylate graft polypropylene.
3. release paper resistant to high temperature according to claim 1, it is characterised in that: the coating two is by including following parts by weight
Raw material be made: the trade mark be H2800 3.5 parts of 96.5 parts of polypropylene, acrylamide graft polypropylene.
4. release paper resistant to high temperature according to any one of claims 1 to 3, it is characterised in that: according to claim 1
Release paper resistant to high temperature, it is characterised in that: the overall thickness of the coating one and coating two be 0.1~1mm.
5. release paper resistant to high temperature according to any one of claims 1 to 3, it is characterised in that: the coating one and described
The ratio between thickness of coating two is 1:2~5.
6. release paper resistant to high temperature according to any one of claims 1 to 3, it is characterised in that: according to claim 1
Release paper resistant to high temperature, it is characterised in that: the polyacrylic grafting rate of glycidyl methacrylate graft be 0.15
~0.25%.
7. release paper resistant to high temperature according to any one of claims 1 to 3, it is characterised in that: the acrylamide graft
Polyacrylic grafting rate is 0.12~0.22%.
8. release paper resistant to high temperature according to any one of claims 1 to 3, it is characterised in that: be equipped with leaching in the body paper
The back side of film layer is additionally provided with the coating of the polyvinyl chloride of 1~2g/m2.