CN109847296A - A kind of manufacturing method of easy weld counterweight block - Google Patents
A kind of manufacturing method of easy weld counterweight block Download PDFInfo
- Publication number
- CN109847296A CN109847296A CN201811432714.4A CN201811432714A CN109847296A CN 109847296 A CN109847296 A CN 109847296A CN 201811432714 A CN201811432714 A CN 201811432714A CN 109847296 A CN109847296 A CN 109847296A
- Authority
- CN
- China
- Prior art keywords
- outer layer
- tungsten
- alloy
- layer shell
- counterweight block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacturing methods of easy weld counterweight block, comprising steps of perhaps alloy material uses the metal material or the outer layer shell of alloy material casting clump weight to metal material similar in A1, selection and golf club head material melting point;Tungsten-bast alloy is filled in A2, the outer layer shell;A3, the outer layer shell is sintered in a vacuum furnace with the tungsten-bast alloy.The present invention improves the manufacturing method of prior art weld clump weight, first select the outer layer shell with metal or alloy cast clump weight similar in golf club head material melting point, tungsten-bast alloy is filled using spray regime in metal thin shell, the fastness and precision of welding were both ensure that in this way, it in turn avoids that mold is used for multiple times when sintering compared with the prior art, the cost for saving mould development and consumption, reduces production cost on the whole, improves the application range of weld counterweight block.
Description
Technical field
The present invention relates to golf clubs, and in particular to a kind of manufacturing method of easy weld counterweight block.
Background technique
Totally 18 hole in golf sports throws match play into fewer number that swings and then wins, wherein each hole then corresponds to different fields
Then there is varying environment obstacle in ground, each place, as shown in Figure 1, from service area to greens on the way Equestrian-Jumping have sand pit, pond,
Lake, the woods and rough, when strike, must hit in two times and control ball in short grass section, and hypertelorism is possible to fall sand
Hole, distance, which deviates, to be possible to fall into art forest zone, lake and sand pit, must be controlled striking distance when into greens, is not strayed into rough.
To be tested in response to varying environment, golf club often totally 14, wherein including rod (Wood) 3~5, iron (Iron) 7~8
Branch, pitching wedge head (PW) 1~2, sand wedge (SW) 1, push rod (putter) 1, are broadly divided into: club wooden head, iron club,
Push rod, three classes.
Golf club head can be divided into three categories:
1. club wooden head: also known as kick off rod (Driver) and Fairway Woods (Fairway), and rod of kicking off is as its name suggests
The first ball kicked off requires distance with direction the most, and the fault of the first ball will affect ball match progress, need to beat directly, is quasi-, is remote
Rate is hit with lower mistake, therefore bulb development trend direction is enlarged, reduction material density increase bulb sweet spot area, and titanium
Tone sense is good when the mechanical property of alloy possesses higher specific strength, corrosion stability and strike, for common bulb material.Common material
Material has titanium alloy, stainless steel and composite material.The made club wooden head of composite material is with new material, new construction, new design cooperation
It most preferably beats sense, best tone sense, best accuracy out and creates optimal counterbalancing effect.
2. iron club: iron club hits purpose, and distance and direction are earnestly hoped in control mainly after kicking off, and stablizes and promotes fruit
Ridge, to direction with apart from error more require, material based on stainless steel, have expand hitting area reduce lose hit rate and reduce
The designer trends of hitting distance error, with the product development of new construction and composite material and tool shock attenuation result.
3. push rod: when push rod is used in into greens, ball is accurately driven into hole, direction and the distance of ball must be can control,
Still none standard in moulding, when how the design of functionally attention center of gravity maintains ball head of pushing rod and the cooperation of middle tube rod, the scope of attack
It will not rotate.To maintain the position of center of gravity and keep the uniformity of bulb, have in processing towards directly processing bulb using CNC, but
On conventionally manufactured based on hot investment casting, on material, stainless steel is still mainstream.
Club wooden head and iron head have been formed " trend for being not required to basket purchase " at present, thus the following titanium alloy club wooden head with it is compound
The sale ratio of the club wooden head of material will have trend higher and higher.The designs trend of bulb, mainly with reduce lose hit rate,
Based on increasing that strike is handling and being accustomed to customized corresponding different hitter's stature bulbs and different strikes.
For the design for adding clump weight on bulb, make bulb low center of gravity, to reach stable hitting property and preferably
Hitting point position, and increase twisting inertia, improve hitting distance, and the position of centre of gravity of adjustable hitter's height and habit.
The Materials of golf, since the development trend of the bulb weight specifications of USGA, rod material of kicking off is mostly big
Type, therefore the titanium alloy of high specific strength becomes one of rod Materials mainstream of kicking off, the Materials of iron club are more more
Sample, for the against corrosion and intensity for seeking bulb, iron club is mostly stainless steel using material.The structure composition of golf club is largely divided into
Bulb bottom, hitting area and neck, wherein neck is the tie point for connecting club, and the torsion generated when hitting in strike holds
It easily reverses, in order to increase the smooth and good hitting point of strike, the adjustment of center of gravity is even more important, lower center of gravity and suitable
When counterweight and position be adjustment hit important key.
The position of center of gravity will will affect flight path, direction and the distance of ball in the strike of golf, by taking iron club as an example,
The design maximum differential point of hollow back formula and knife spine formula in, density design direction on the contrary, difference is very big in exterior design, hollow back
Though formula design can effectively reduce and lose rate of hitting and but improve the range error after batting, the design of knife spine formula mainly contracts bulb volume
It is small, it can effectively improve the flying distance error after batting to change its batter's box but.Golf club head as shown in Figure 2 and Figure 3 is not
With angle striking distance difference.
To make bulb low center of gravity and freely adjusting center of gravity, the cooperation of clump weight design mainly has following three:
1. screw lockable clump weight
Lockable clump weight mainly cooperates principle to be that golf club head bottom cover has the solid lock screw hole of fixation, screw solid lock
There are two types of modes for formula clump weight, first is that another kind is that screw itself has both counterweight with screw by clump weight solid lock in bulb bottom cover
With the function of solid lock.Such clump weight mainly has both solid lock and advantage easy to loading and unloading.
2. embedded clump weight
Embedded clump weight mainly cooperates principle and lockable, and some are difference, embedded the same embedding with what is fixed in bottom cover
Based on entering slot, fasten clump weight using clump weight external form and dimensional tolerance, such clump weight cooperation, possess quick despatch it
Advantage.
3. welded type clump weight
The main counterweight in a conventional manner of welded type clump weight, with welding manner by fixed weight block welding in bulb bottom,
The case where forming different club difference counterweights, but welded type clump weight is if the material for selecting to have larger difference with bulb
Will cause welding surface and bulb body has the defect of color difference, if selection will limit clump weight with material similar in bulb again
Density adjustment, this contradiction greatly limit effective application of welded type clump weight.
Summary of the invention
The technical problem to be solved in the present invention is that providing a kind of manufacturing method of easy weld counterweight block, existing skill is overcome
The defect that art welded type clump weight welding surface and bulb body have the density adjustment of color difference, clump weight limited.
The present invention to solve above-mentioned technical problem used by technical solution are as follows:
A kind of manufacturing method of easy weld counterweight block, comprising steps of
Metal material or alloy material similar in A1, selection and golf club head material melting point, use the metal material
Or the outer layer shell of alloy material casting clump weight;
Tungsten-bast alloy is filled in A2, the outer layer shell;
A3, the outer layer shell is sintered in a vacuum furnace with the tungsten-bast alloy.
According to an embodiment of the invention, the step A1 is comprising steps of select 17-4PH stainless steel, 1650 DEG C of furnace temperature with
Outer layer shell described in hot investment casting at 1250 DEG C of shell temperature.
According to an embodiment of the invention, the step A1 is comprising steps of select 304 stainless steels, in 1650 DEG C of furnace temperature and shell
Outer layer shell described in hot investment casting at 1250 DEG C of temperature.
According to an embodiment of the invention, the step A1 is comprising steps of select 8620 carbon steels, in 1650 DEG C of furnace temperature and shell temperature
Outer layer shell described in hot investment casting at 1250 DEG C.
According to an embodiment of the invention, the tungsten-bast alloy include tungsten 79.2%, nickel 11.5%, iron 6.9%, chromium 0.9%,
Copper 1.5%.
According to an embodiment of the invention, filling tungsten-bast alloy in the outer layer shell using spraying technique
Advantageous effect of the invention: the present invention improves the manufacturing method of prior art weld clump weight, first select with
The outer layer shell of metal or alloy cast clump weight, uses in metal thin shell similar in golf club head material melting point
Spray regime fills tungsten-bast alloy, both ensure that the fastness and precision of welding in this way, and had in turn avoided compared with the prior art
Mold is used for multiple times when sintering, saves the cost of mould development and consumption, reduces production cost on the whole, improves welding
The application range of clump weight.
Detailed description of the invention
It is specifically described the present invention below with reference to attached drawing and in conjunction with example, advantages of the present invention and implementation will
It is more obvious, wherein content only for the purpose of explanation of the present invention shown in attached drawing, without constitute to it is of the invention in all senses
On limitation, in the accompanying drawings:
Fig. 1 is golf course environment and corresponding golf club schematic diagram;
Fig. 2 is that golf club head hits center of gravity and flight angle relation schematic diagram;
Fig. 3 is that golf club head hits center of gravity and flying distance relation schematic diagram;
Fig. 4 is golf club head schematic diagram of the present invention;
Fig. 5 is iron of the present invention-tungsten binary phase diagraml;
Fig. 6 is the outer layer shell microstructure schematic diagram of clump weight of the present invention;
Fig. 7 is the tungsten-bast alloy microstructure schematic diagram of clump weight of the present invention;
Fig. 8 is the present invention easily weld counterweight block microstructure schematic diagram;
Fig. 9 is the present invention easily weld counterweight block concentration of element trend schematic diagram.
Specific embodiment
As shown in Fig. 4, Fig. 5, Fig. 6, Fig. 7, Fig. 8 and Fig. 9, the manufacturing method of the easy weld counterweight block of the present invention, comprising steps of
Metal material or alloy material similar in A1, selection and golf club head material melting point, use the metal material
Or the outer layer shell of alloy material casting clump weight;
Tungsten-bast alloy is filled in A2, the outer layer shell;
A3, the outer layer shell is sintered in a vacuum furnace with the tungsten-bast alloy.
According to an embodiment of the invention, the step A1 is comprising steps of select 17-4PH stainless steel, 1650 DEG C of furnace temperature with
Outer layer shell described in hot investment casting at 1250 DEG C of shell temperature.
The step A1 is comprising steps of select 304 stainless steels in another embodiment of the invention, 1650 DEG C of furnace temperature with
Outer layer shell described in hot investment casting at 1250 DEG C of shell temperature.
The step A1 is comprising steps of select 8620 carbon steels in another embodiment of the invention, 1650 DEG C of furnace temperature with
Outer layer shell described in hot investment casting at 1250 DEG C of shell temperature.
According to an embodiment of the invention, the tungsten-bast alloy include tungsten 79.2%, nickel 11.5%, iron 6.9%, chromium 0.9%,
Copper 1.5%.It is and thin with PM powder metallurgy or MIM metal injection molding in shell partial interior with reference to Fig. 5 iron-tungsten binary phase diagraml
Shell parts combine, and finally carry out high temperature sintering.
Outer layer shell material of the present invention is close with commercial golf club head material melting point, can be conventional cast, PM powder smelting
Gold is manufactured with MIM metal powder injection molding, is tungsten nickel iron alloy inside shell, and ingredient is iron -75~80% tungsten -10~15%
- 1.5~2.5% bronze medal counterweight block of material of nickel -1~2% chromium, by PM powder metallurgy or MIM metal powder injection molding in shell
Portion, after sintering in conjunction with shell part.
The manufacturing method step of golf clump weight of the present invention is to prepare shell some materials, and shell some materials can be
Commercial bulb alloy, such as 17-4PH stainless steel, 8620 carbon steels, 304 stainless steels, precasting shapes in a manner of hot investment casting, or is PM
Powder metallurgy and MIM metal powder injection molding manufacture;Shell internal material powder be tungsten sill powder, wherein iron -75~
- 1.5~2.5% bronze medal of -1~2% chromium of -10~15% nickel of 80% tungsten.
Clump weight of the present invention is a kind of weldable clump weight, is broadly divided into A, B two parts, and part A 11 is the ring of precasting
Shape welding section can be seen that A 11 microstructures of part referring to Fig. 6, and materials'use commercialization bulb alloy 17-4PH precipitation hardening type is not
Become rusty steel, and density is about 7.7g/cm3, and fusing point is about 1400 DEG C close with bulb body material melting point, increases the welding of clump weight
Property, part B 12 is the counterweight block body of high density, can be seen that B 12 microstructures of part referring to Fig. 7, and material selection tungsten ferronickel closes
Gold, actual constituent are iron -75~-1.5~2.5% bronze medal counterweight block of material of -1~2% chromium of -10~15% nickel of 80% tungsten, and density is about
It is the microstructure of this embodiment of the present invention referring to Fig. 8 for 14.2g/cm3, top is the tungsten ferronickel counterweight block of material of high density,
Lower section is the 17-4PH precipitation hardening type stainless steel of casting and forming, and middle section is then two material phase melting zones.Referring to Fig. 9, can see
The concentration of element trend of the present invention out, wolfram element are increased to center by B part 75.6% gradually and mix area boundary 84.6% finally
Drop to A part;Nickel element rises to center from B part 14% and mixes area up to 28.5% finally to dropping to A part 17-4PH
Stainless steel normal value;Chromium is cumulative to A part 17% by B part content 1%, meets 17-4PH stainless steel normal value;Copper coin
Plain whole control is 1~3%.
Those skilled in the art do not depart from essence and spirit of the invention, can there are many deformation scheme realize the present invention,
The foregoing is merely preferably feasible embodiments of the invention, and not thereby limiting the scope of the invention, all with this
The variation of equivalent structure made by description of the invention and accompanying drawing content, is intended to be included within the scope of the present invention.
Claims (6)
1. a kind of manufacturing method of easy weld counterweight block, which is characterized in that comprising steps of
Metal material similar in A1, selection and golf club head material melting point perhaps alloy material using the metal material or
The outer layer shell of alloy material casting clump weight;
Tungsten-bast alloy is filled in A2, the outer layer shell;
A3, the outer layer shell is sintered in a vacuum furnace with the tungsten-bast alloy.
2. the manufacturing method of easy weld counterweight block according to claim 1, which is characterized in that the step A1 includes step
It is rapid: to select 17-4PH stainless steel, the outer layer shell described in hot investment casting at 1650 DEG C and 1250 DEG C of shell temperature of furnace temperature.
3. the manufacturing method of easy weld counterweight block according to claim 1, which is characterized in that the step A1 includes step
It is rapid: to select 304 stainless steels, the outer layer shell described in hot investment casting at 1650 DEG C and 1250 DEG C of shell temperature of furnace temperature.
4. the manufacturing method of easy weld counterweight block according to claim 1, which is characterized in that the step A1 includes step
It is rapid: to select 8620 carbon steels, the outer layer shell described in hot investment casting at 1650 DEG C and 1250 DEG C of shell temperature of furnace temperature.
5. according to the manufacturing method of any easy weld counterweight block of claim 2 to 4, it is characterised in that: the tungsten base closes
Gold includes tungsten 79.2%, nickel 11.5%, 6.9 % of iron, chromium 0.9%, copper 1.5%.
6. the manufacturing method of easy weld counterweight block according to claim 5, which is characterized in that using spraying technique described
Tungsten-bast alloy is filled in outer layer shell.