CN109821502A - Air cleaning is with removing formaldehyde porous elastomers - Google Patents
Air cleaning is with removing formaldehyde porous elastomers Download PDFInfo
- Publication number
- CN109821502A CN109821502A CN201910220272.5A CN201910220272A CN109821502A CN 109821502 A CN109821502 A CN 109821502A CN 201910220272 A CN201910220272 A CN 201910220272A CN 109821502 A CN109821502 A CN 109821502A
- Authority
- CN
- China
- Prior art keywords
- carbon
- air cleaning
- tube bundle
- porous elastomers
- removing formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of air cleanings with removing formaldehyde porous elastomers, the compound porous elastomer of carbon nanotube includes carbon nano tube bundle and the titania powder that is scattered in the carbon nano tube bundle, the carbon nano tube bundle includes multiple carbon nanotubes, and is attracted each other between carbon nanotube by Van der Waals force；The end of the carbon nanotube includes multiple defects, and the carbon atom in the multiple defect is oxidized to form the hydroxyl and carboxyl of multiple crosslinkings, and part titania powder is filled in the defect.
Description
Technical field
The present invention relates to a kind of air cleanings with removing formaldehyde porous elastomers.
Background technique
Formaldehyde is the No.1 polluted gas in room air, is the major pollutants for influencing human health, is greater than
0.08m3Concentration of formaldehyde can cause to be envious, many symptom such as eye is itched, throat discomfort.
Currently, absorption method and edman degradation Edman are the important methods of two kinds of removal formaldehyde.In numerous adsorbent materials, carbon materials
Material, especially carbon nanotube are a kind of most widely used adsorbent materials.And in edman degradation Edman, titanium dioxide is the most commonly used material
Material.Although having in the prior art by titanium dichloride load in the composite material of carbon nanotube, the composite material preparation process
Complexity, and the binding force between two kinds of materials is lower, it is difficult to play the coordinative role between both materials.
Summary of the invention
The present invention provides a kind of air cleanings with formaldehyde porous elastomers are removed, and can effectively solve the above problems.
The present invention is implemented as follows:
With formaldehyde porous elastomers are removed, the compound porous elastomer of carbon nanotube includes carbon nanotube for a kind of air cleaning
Cluster and the titania powder being scattered in the carbon nano tube bundle, the carbon nano tube bundle include multiple carbon nanotubes, and carbon
It is attracted each other between nanotube by Van der Waals force；The end of the carbon nanotube includes multiple defects, in the multiple defect
Carbon atom be oxidized to form the hydroxyl and carboxyl of multiple crosslinkings, part titania powder is filled in the defect.
As further improved, the carbonyl and hydroxy functional group account for the 8~12% of gross mass.
As further improved, the titania powder accounts for the 2~5% of gross mass.
As further improved, the carbon nano tube bundle is directly to scrape to obtain from a carbon nano pipe array.
As further improved, by the carbon nano tube bundle is immersed in be dispersed with titania powder nitric acid it is molten
It is taken out immediately after liquid and forms precast body；Then the precast body is irradiated by substantial radiation source, and stood；It will finally stand
Precast body afterwards is cleaned to neutrality, and freeze-drying obtains under vacuum conditions after sizing.
As further improved, 2~10kGy/s of radiation dose rate, total radiation dose is 100~150kGy.
As further improved, the air cleaning is returned in two minutes with after removing formaldehyde porous elastomers compression half
It is bound to 80vt% or more.
The beneficial effects of the present invention are: the present invention irradiates the precast body by substantial radiation source, so as to so that
Multiple defects are formed in the both ends of carbon nanotube, on the one hand multiple defect can be used for accommodating titania powder, thus dioxy
Change and forms good combination between titanium powder and the carbon nanotube；On the other hand multiple defect is easy to aoxidize shape by nitric acid
At multiple functional groups, to reduce the reaction time, and make to react to each other to form complicated cross-linked structure between functional group, most
After make the compound porous elastomer of the carbon nanotube have good resilience performance.
Detailed description of the invention
It, below will be to use required in embodiment in order to illustrate more clearly of the technical solution of embodiment of the present invention
Attached drawing be briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not to be seen as
It is the restriction to range, it for those of ordinary skill in the art, without creative efforts, can be with root
Other relevant attached drawings are obtained according to these attached drawings.
Fig. 1 is the air cleaning provided in an embodiment of the present invention preparation method flow chart for removing formaldehyde porous elastomers.
Fig. 2 is the air cleaning provided in an embodiment of the present invention photo for removing formaldehyde porous elastomers.
Fig. 3 is the structural schematic diagram of air purifier provided in an embodiment of the present invention.
Specific embodiment
To keep the purposes, technical schemes and advantages of embodiment of the present invention clearer, implement below in conjunction with the present invention
The technical solution in embodiment of the present invention is clearly and completely described in attached drawing in mode, it is clear that described reality
The mode of applying is some embodiments of the invention, rather than whole embodiments.Based on the embodiment in the present invention, ability
Domain those of ordinary skill every other embodiment obtained without creative efforts, belongs to the present invention
The range of protection.Therefore, the detailed description of the embodiments of the present invention provided in the accompanying drawings is not intended to limit below and is wanted
The scope of the present invention of protection is sought, but is merely representative of selected embodiment of the invention.Based on the embodiment in the present invention,
Every other embodiment obtained by those of ordinary skill in the art without making creative efforts belongs to this
Invent the range of protection.
Shown in referring to Fig.1, a kind of air cleaning preparation method for removing formaldehyde porous elastomers, comprising the following steps:
S1 provides a carbon nano tube bundle, which includes multiple carbon nanotubes, and passes through model between carbon nanotube
De Huali attracts each other to form the carbon nano tube bundle；
The carbon nano tube bundle is immersed in after the nitric acid solution for being dispersed with titania powder and takes out formation immediately in advance by S2
Body processed；
S3 irradiates the precast body by substantial radiation source, and stands；
Precast body after standing is cleaned to neutrality, is freeze-dried under vacuum conditions after sizing by S4.
In step sl, the carbon nano tube bundle is directly to scrape to obtain from a carbon nano pipe array.Carbon nanotube it is straight
Diameter is 20 nanometers~30 nanometers.The length of the carbon nanotube is 5 millimeters~10 millimeters.Carbon nanotube is preferably that surface is more pure
It is net and free from foreign meter, to make that there is better active force between carbon nanotube.The preparation method of the carbon nano tube bundle
Are as follows: one carbon nano-pipe array of preparation is listed in a substrate；The carbon nano pipe array is scraped from the substrate using blade or other tools
It falls, obtains the carbon nano tube bundle.
In step s 2, concentration of the titania powder in nitric acid solution is 0.01g~0.05g/ml.Described two
The partial size of titanium dioxide powder can be nanoscale, it is preferred that the partial size of the titania powder be 20 nanometers~30 nanometers it
Between.The concentration of the nitric acid is 50wt%~70wt%.
In step s3, it will be understood that by the control of radiation dose rate and accumulated dose, so as to so that carbon nanotube
Both ends form multiple defects, and on the one hand multiple defect can be used for accommodating titania powder, thus titania powder and institute
It states and forms good combination between carbon nanotube；On the other hand multiple defect is easy to be aoxidized to form multiple functions by nitric acid
Group to reduce the reaction time, and makes to react to each other to form complicated cross-linked structure between functional group, finally makes the carbon
The compound porous elastomer of nanotube has good resilience performance.In general, the carbon nanotube both ends in carbon nano pipe array
It is all more complete, so that carbon nanotube be made to be difficult to quickly be aoxidized, therefore multiple defects can be formed by radiation, to be conducive to
Subsequent reaction.In addition, if radiation is excessive to generate excessive levels of impurities, to reduce the active force between carbon nanotube.Therefore it is excellent
Choosing, 2~10kGy/s of radiation dose rate, total radiation dose is 100~150kGy.It is furthermore preferred that the radiation dose rate 5~
8kGy/s, the total radiation dose are 120~150kGy.
In step s3, the time of the standing is 2h~8h.During standing, nitric acid can with carbon atom in defect after
Supervention gives birth to oxidation reaction, to form multiple hydroxyls and carboxyl functional group.
In step s 4, the precast body by after standing, which is cleaned to neutral step, includes:
S42, it is the precast body after standing is submerged in water and cleaned by ultrasonication to neutrality.
As further improved, the corresponding frequency of the ultrasonic wave is 68KHz~34KHz.Due to the wavelength of ultrasonic wave
It is suitable with the wavelength of carbon nanotube, therefore, the carbon nanotube be easy to happen resonance and mutually wind, and various functional groups it
Between can also react to each other, form the structure of crosslinking.
In step s 4, include: the step of freeze-drying under the vacuum condition
The precast body is put into freeze drier by S41, is chilled to -20 DEG C~-30 DEG C, and keep the temperature 2~4 hours.
Fig. 2 is referred to, the present invention also provides a kind of air cleanings obtained by the above method with removing formaldehyde poroelasticity
Body.The compound porous elastomer of carbon nanotube includes carbon nano tube bundle and the titanium dioxide that is scattered in the carbon nano tube bundle
Titanium powder, which includes multiple carbon nanotubes, and is attracted each other between carbon nanotube by Van der Waals force；The carbon
The end of nanotube includes multiple defects, and the carbon atom in the multiple defect is oxidized to form the hydroxyl and carboxylic of multiple crosslinkings
Base, part titania powder are filled in the defect.Preferably, the carbonyl and hydroxy functional group account for gross mass 8~
12%, and the titania powder accounts for the 2~5% of gross mass.The air cleaning compresses one with formaldehyde porous elastomers are removed
After half, 80vt% or more is sprung back in two minutes.
Embodiment 1:
The carbon nano tube bundle of 1g or so is immersed in after 100ml is dispersed with the nitric acid solution of titania powder and is taken out immediately
Form precast body, wherein the content of titania powder is 0.02g/ml, and the concentration of nitric acid is 70wt%；Substantial radiation source pair
The precast body is irradiated, wherein radiation dose rate 8kGy/s, total radiation dose 150kGy, and stands 2 hours；Finally,
It is precast body after standing is submerged in water and cleaned by ultrasonication to neutrality, and -30 DEG C are chilled to, and it is small to keep the temperature 2
When, wherein ultrasonic frequency 40KHz.The sample A for being finally cut to 1cm*1cm*1cm continues to employ test.
Comparative example 2:
It is substantially the same manner as Example 1, the difference is that: precast body described in ultrasonication is not used, obtains sample B.
Comparative example 1:
It is substantially the same manner as Example 1, the difference is that: substantial radiation source is not used and irradiates the precast body, obtains sample
C。
Comparative example 2:
It is substantially the same manner as Example 1, the difference is that: radiation dose rate 15kGy/s, total radiation dose 200kGy,
Obtain sample D.
Pressing rebound test: the sample in embodiment 1-2 and comparative example 1-2 is subjected to pressing rebound test, wherein by sample
Product A is compressed to 0.5cm, and 0.9cm is sprung back to after one minute, springs back prototype substantially in two minutes.Sample B is compressed to 0.5cm, one
0.8cm is sprung back to after minute, is rebound to essentially 0.9cm in two minutes.Sample C is compressed to 0.5cm, it is basic in two minutes only to return
It is bound to 0.6cm.Sample D is compressed to 0.5cm, only springs back to 0.7cm substantially in two minutes.
In addition, after testing, the functional groups such as carbonyl and hydroxyl account for 12% of gross mass or so in embodiment 1-2.And it compares
The functional groups such as carbonyl and hydroxyl account for the 3% of gross mass hereinafter, the functional groups such as carbonyl and hydroxyl account for gross mass in comparative example 2 in example 1
It can reach 15% or more.It can be seen that the carbon nanotube in comparative example 2 is excessively oxidated, it is made to lose the function of support, therefore
Its resilience performance is lower.And in comparative example 1, the amount that carbon nanotube is oxidized is lower, so that cross-linked structure can not be formed.
Referring to figure 3., the present invention also provides a kind of air cleaning units, comprising: lower header 10 and with the lower header
The filter cavity 20 of 10 connection；For once being filtered to gas, the filter cavity 20 is used for institute the lower header 10
It states gas and carries out secondary filter.The filter cavity 20 includes air-supply assembly, air filtering core 21 and the purple being set in air duct
Outer fluorescent tube 18/19.The air-supply assembly is set to the air inlet in the air duct, and the ultraviolet lamp tube is for irradiating the air filter
Core 21；The air filtering core 21 is to be prepared by air cleaning with formaldehyde porous elastomers are removed；The carbon nanotube is compound
Porous elastomers include carbon nano tube bundle and the titania powder that is scattered in the carbon nano tube bundle, the carbon nano tube bundle
It is attracted each other including multiple carbon nanotubes, and between carbon nanotube by Van der Waals force；The end of the carbon nanotube includes more
A defect, the carbon atom in the multiple defect are oxidized to form the hydroxyl and carboxyl of multiple crosslinkings, part titania powder
It is filled in the defect.Due to air cleaning with remove carbon nanotube in formaldehyde porous elastomers have good specific surface and
And absorption property, it can be used for capturing the organic pollutants such as formaldehyde, and ultraviolet lamp tube 18/19 cooperates titania powder to form light
Catalyst is decomposed so as to organic pollutants such as PARA FORMALDEHYDE PRILLS(91,95)s, therefore, the air cleaning unit of this case can be said with fertile absorber
Solve the organic pollutants such as formaldehyde.
The lower header 10 includes admission line 11, the sponge interlayer 12 for being set to 10 bottom of lower header；It is described into
The air inlet of feed channel 11 and extraneous connection；The lower header 10 is divided into two parts, the air inlet by the sponge interlayer 12
The venthole 112 of pipeline 11 is set to the lower part of the sponge interlayer 12, to make logical from the venthole 112 discharge air pocket
It crosses the sponge interlayer 12 and is divided into minute bubbles, so that pollutant and dust in gas be allow to completely dissolve in water.
It is further preferred that the venthole 112 is arranged along the length direction interval of the admission line 11, and from described
Direction in the middle part of 10 both sides of lower header to the lower header 10, the diameter of the venthole 112 are incremented by successively.
It is further preferred that the ultraviolet lamp tube 18/19 is respectively arranged at the two sides of the air filtering core 21.
It is further preferred that the short transverse of the air filtering core 21 and the filter cavity 20 forms 35 °~45 ° folders
Angle.Angle by controlling the air filtering core 21 can improve the contact area of air filtering core 21 Yu air to greatest extent, separately
Outside, can also play the role of reducing vibration.
It is further preferred that the air-supply assembly includes driving motor 14, the first blade 16 and the second blade 15；It is described
First blade 16 and second blade 15 are connect by shaft with the driving motor 14 respectively；First blade 16 is stretched
Enter in the lower header 10, for mixing the water in water tank uniformly；Second blade 15 is placed in the air inlet in the air duct.
It is further preferred that the arragement direction of first blade 16 and second blade 15 is identical.It is described to be lauched
The bottom of case 10 further comprises sewage draining exit 13.The driving motor 14 is for controlling first blade 16 and described second
Blade 15 is rotated forward to carry out air cleaning.Specifically, the driving motor 14 rotates forward, the lower header 10 is made to form negative pressure,
Air enters from the admission line 11 under the action of negative pressure, and is divided into minute bubbles progress air filtration net by sponge interlayer 12
Change.The driving motor 14 is for controlling first blade 16 and second blade 15 reversion with from the sewage draining exit 13
Carry out blowdown.Specifically, the driving motor 14 inverts, the lower header 10 is made to form positive pressure, at this point, closing admission line 11
And sewage draining exit 13 is opened, the water in the sponge interlayer 12 can be flowed out since pressure is acted on from the sewage draining exit 13, in addition, due to
Sponge interlayer 12 is accumulated close to the side of 10 bottom of lower header compared with multi-pollutant, at this point it is possible in the shock effect of water flow
Under fall, and from the sewage draining exit 13 be discharged.
The foregoing is merely the preferred embodiment of the present invention, are not intended to restrict the invention, for this field
For technical staff, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any
Modification, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of air cleaning is with removing formaldehyde porous elastomers, which is characterized in that the compound porous elastomer packet of carbon nanotube
The titania powder for including carbon nano tube bundle and being scattered in the carbon nano tube bundle, the carbon nano tube bundle include that multiple carbon are received
Mitron, and attracted each other between carbon nanotube by Van der Waals force；The end of the carbon nanotube includes multiple defects, described more
Carbon atom in a defect is oxidized to form the hydroxyl and carboxyl of multiple crosslinkings, and part titania powder is filled in the defect
In.
2. air cleaning as described in claim 1 is with removing formaldehyde porous elastomers, which is characterized in that the carbonyl and hydroxyl official
It can roll into a ball and account for the 8~12% of gross mass.
3. air cleaning as described in claim 1 is with removing formaldehyde porous elastomers, which is characterized in that the titania powder
Account for the 2~5% of gross mass.
4. air cleaning as described in claim 1 is with removing formaldehyde porous elastomers, which is characterized in that the carbon nano tube bundle is
It directly scrapes and obtains from a carbon nano pipe array.
5. air cleaning as described in claim 1 is with removing formaldehyde porous elastomers, which is characterized in that by by the carbon nanometer
Tube bundle, which is immersed in after the nitric acid solution for being dispersed with titania powder to take out immediately, forms precast body；Then pass through substantial radiation source pair
The precast body is irradiated, and is stood；Finally the precast body after standing is cleaned to neutrality, it is cold under vacuum conditions after sizing
Dry acquisition is lyophilized.
6. air cleaning as claimed in claim 5 is with removing formaldehyde porous elastomers, which is characterized in that radiation dose rate 2~
10kGy/s, total radiation dose are 100~150kGy.
7. air cleaning as described in claim 1 is with removing formaldehyde porous elastomers, which is characterized in that the air cleaning is with removing
After formaldehyde porous elastomers compress half, 80vt% or more is sprung back in two minutes.