CN109810642A - A kind of Hot melt adhesive tape and preparation method thereof - Google Patents
A kind of Hot melt adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN109810642A CN109810642A CN201910038068.1A CN201910038068A CN109810642A CN 109810642 A CN109810642 A CN 109810642A CN 201910038068 A CN201910038068 A CN 201910038068A CN 109810642 A CN109810642 A CN 109810642A
- Authority
- CN
- China
- Prior art keywords
- parts
- hot melt
- melt adhesive
- adhesive tape
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Hot melt adhesive tapes and preparation method thereof, by being improved to hot melt adhesive layer formula and processing step, compare common Hot melt adhesive tape performance in the prior art, Hot melt adhesive tape performance of the invention is more superior, pastes and is easy, retentivity is good, good toughness, tension effect is good, and tensile strength is high, does not have phenomenon of rupture.And Hot melt adhesive tape entire volume adhesive tape of the invention is longer, can greatly improve production efficiency and reduction is produced into.
Description
Technical field
The present invention relates to hot melt adhesive film technical field, specially a kind of Hot melt adhesive tape and preparation method thereof.
Background technique
Hot melt adhesive is a kind of solvent-free, free of contamination environmental-protection type adhesive, is increasingly had been favored by people, and is used extensively
In the industrial departments such as shoemaking, packaging, timber processing, automobile, light textile, electromechanics, space flight and aviation.Conventional hot melt glue only has bonding
Performance after position is fixed, reheats pressurization as long as being placed on adherend surface when use, adhesive property can be realized, but should
Type hot melt adhesive is only applicable to the bonding of conventional items, the demand now with the development of electronic product, to hot melt adhesive function
More and more, existing braiding Hot melt adhesive tape is not since the selection of pasty emulsion formula is scientific, so sticky poor, tensile strength
Weak, retentivity is poor, poor solvent resistance.It needs to its further research and development improvement.
Summary of the invention
The purpose of the present invention is to provide a kind of Hot melt adhesive tapes and preparation method thereof, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme:
A kind of Hot melt adhesive tape, the PET film layer being superimposed from top to bottom, melt pressure sensitive gel coating, hot melt adhesive layer composition, hot melt adhesive
Layer is formed according to following parts by weight: 20-50 parts of EVA resins, 30-40 parts of ethylene, 20-25 parts of vinyl acetates, 30-45 parts of titanium dioxides
Silicon hollow sphere, 15-18 part sodium cellulose glycolate, 10-12 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzo thiophene
Pheno;15-18 parts of polyester-type thermoplastic polyurethane;1-2.5 parts of plasticizer, 60-75 parts of solvent, 5-30 parts of natural terpene resins,
10-50 parts of naphthenic oil, 10-40 parts of calcium carbonate, 3-10 parts of PE wax, 2-10 parts of chain extension-crosslinking agent, 5-10 parts of fire retardants, 5-
8 parts of initiators;
Tackifier select 5-7 parts of C5 Petropols terpene resins, 3-5 parts of hydrogenated rosin resins, 8-12 parts of coumarone indene resins, 3-
At least one of 5 parts of paraffin, 2-4 parts of naphthenic oils;
Antioxidant be selected from 3-5 parts of phosphite ester antioxidants, 4-6 parts of sulfur-bearing esters any one.
Preferably, the PET film layer that is superimposed from top to bottom, melt pressure sensitive gel coating, hot melt adhesive layer composition, hot melt adhesive layer according to
Following parts by weight composition: 40 parts of EVA resins, 35 parts of ethylene, 23 parts of vinyl acetates, 40 parts of hollow silica balls, 17 parts of hydroxyl first
Base sodium cellulosate, 11 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzothiophene;16 parts of poly- ammonia of polyester-type thermoplastic
Ester;2 parts of plasticizer, 60 parts of solvent, 20 parts of natural terpene resins, 32 parts of naphthenic oil, 25 parts of calcium carbonate, 7 parts of PE wax,
6 parts of chain extension-crosslinking agent, 7 parts of fire retardants, 7 parts of initiators;Tackifier select 6 parts of C5 Petropols terpene resins, 4 parts of hydrogenated rosin trees
At least one of rouge, 10 parts of coumarone indene resins, 4 parts of paraffin, 3 parts of naphthenic oils;Antioxidant is selected from 4 parts of phosphite ester antioxidants, 5
Part sulfur-bearing esters any one.
Preferably, the hot melt adhesive layer account for PET film layer, melt pressure sensitive gel coating, hot melt adhesive layer summation quality 40%-
60%.
Preferably, the weight average molecular weight of the EVA resin is 4-5 ten thousand.
Preferably, the fire retardant selects phosphate and contains halophosphate, halogenated hydrocarbons, cooperates according to 1:2 mass ratio.
Preferably, the vinyl benzo-crown ether of 1-2.5 parts by weight is also blended in the EVA resin.
A kind of preparation method of Hot melt adhesive tape, comprising the following steps:
Step 1: preparation, first by EVA resin, ethylene, vinyl acetate, hollow silica ball, sodium cellulose glycolate,
2- vinyl -1- benzofuran or 2- vinyl -1- benzothiophene, polyester-type thermoplastic polyurethane;It is heat-treated after mixing,
Temperature controls under the conditions of 155-160 DEG C, and it is spare to obtain mixture A;
Step 2: and then mixture A obtained in the previous step is dissolved into solvent, it is stirred uniformly, until completely molten
Solution, obtains mixture B;
Step 3: initiator, which is first added, in mixture B makes it after evenly mixing, then sequentially adds plasticizer, day
Right terpene resin, naphthenic oil, calcium carbonate, PE wax, chain extension-crosslinking agent, fire retardant, when every kind of material is added all uniform stirring, set
The 5-10min between 100-120 DEG C, in a high speed mixer, high-speed stirred mix 35-60min;
Step 4: being filtered cooling for the material finally obtained in step 3, obtains the material of purity is high, then again
It returns to and carries out mixing 10-20min in high-speed mixer, in triplicate, finally obtain fine material C;
Step 5: material C is warming up to 95-105 DEG C, thickening is added in 25-30rpm in mixing speed control while stirring
Agent, antioxidant, are kneaded 50-60min together;
Step 6: the material after mixing well in step 5 squeezes out, and is pressed into and is evenly distributed with calender, with a thickness of 2-
2.5mm thin slice;
Step 7, then obtained 2-2.5mm thin slice upper berth melt pressure sensitive gel coating, the realization of PET film layer is hot-forming, cold
But, Hot melt adhesive tape can be obtained.
Compared with prior art, the beneficial effects of the present invention are: this Hot melt adhesive tape and preparation method thereof, by hot melt adhesive
Layer formula and processing step improve, and compare common Hot melt adhesive tape performance in the prior art, hot melt adhesive of the invention
Band performance is more superior, pastes and is easy, and retentivity is good, good toughness, and tension effect is good, and tensile strength is high, does not have phenomenon of rupture.
And Hot melt adhesive tape entire volume adhesive tape of the invention is longer, can greatly improve production efficiency and reduction is produced into.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
The present invention provides a kind of technical solution:
A kind of preparation method of Hot melt adhesive tape, comprising the following steps:
Step 1: preparation, first by EVA resin, ethylene, vinyl acetate, hollow silica ball, sodium cellulose glycolate,
2- vinyl -1- benzofuran or 2- vinyl -1- benzothiophene, polyester-type thermoplastic polyurethane;It is heat-treated after mixing,
Temperature controls under the conditions of 155-160 DEG C, and it is spare to obtain mixture A;
Step 2: and then mixture A obtained in the previous step is dissolved into solvent, it is stirred uniformly, until completely molten
Solution, obtains mixture B;
Step 3: initiator, which is first added, in mixture B makes it after evenly mixing, then sequentially adds plasticizer, day
Right terpene resin, naphthenic oil, calcium carbonate, PE wax, chain extension-crosslinking agent, fire retardant, when every kind of material is added all uniform stirring, set
The 5-10min between 100-120 DEG C, in a high speed mixer, high-speed stirred mix 35-60min;
Step 4: being filtered cooling for the material finally obtained in step 3, obtains the material of purity is high, then again
It returns to and carries out mixing 10-20min in high-speed mixer, in triplicate, finally obtain fine material C;
Step 5: material C is warming up to 95-105 DEG C, thickening is added in 25-30rpm in mixing speed control while stirring
Agent, antioxidant, are kneaded 50-60min together;
Step 6: the material after mixing well in step 5 squeezes out, and is pressed into and is evenly distributed with calender, with a thickness of 2-
2.5mm thin slice;
Step 7, then obtained 2-2.5mm thin slice upper berth melt pressure sensitive gel coating, the realization of PET film layer is hot-forming, cold
But, Hot melt adhesive tape can be obtained.
Embodiment 1
A kind of Hot melt adhesive tape, the PET film layer being superimposed from top to bottom, melt pressure sensitive gel coating, hot melt adhesive layer composition, hot melt adhesive
Layer is formed according to following parts by weight: 20 parts of EVA resins, 30 parts of ethylene, 20 parts of vinyl acetates, 30 parts of hollow silica balls, 15
Part sodium cellulose glycolate, 10 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzothiophene;15 parts of polyesters thermoplastics
Property polyurethane;1 part of plasticizer, 60 parts of solvent, 5 parts of natural terpene resins, 10 parts of naphthenic oil, 10 parts of calcium carbonate, 3 parts
PE wax, 2 parts of chain extension-crosslinking agent, 5 parts of fire retardants, 5 parts of initiators;Tackifier select 5 parts of C5 Petropols terpene resins;Antioxidant choosing
From 3 parts of phosphite ester antioxidants.
Embodiment 2
PET film layer, melt pressure sensitive gel coating, the hot melt adhesive layer composition being superimposed from top to bottom, hot melt adhesive layer is according to following heavy
Measure part composition: 40 parts of EVA resins, 35 parts of ethylene, 23 parts of vinyl acetates, 40 parts of hollow silica balls, 17 parts of hydroxylmethyl celluloses
Plain sodium, 11 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzothiophene;16 parts of polyester-type thermoplastic polyurethane;Plasticising
2 parts of agent, 60 parts of solvent, 20 parts of natural terpene resins, 32 parts of naphthenic oil, 25 parts of calcium carbonate, 7 parts of PE wax, 6 parts of chain extensions
Crosslinking agent, 7 parts of fire retardants, 7 parts of initiators;Tackifier select 4 parts of hydrogenated rosin resins, 10 parts of coumarone indene resins, 4 parts of paraffin, 3 parts
At least one of naphthenic oil;Antioxidant be selected from 4 parts of phosphite ester antioxidants, 5 parts of sulfur-bearing esters any one.
Embodiment 3
A kind of Hot melt adhesive tape, the PET film layer being superimposed from top to bottom, melt pressure sensitive gel coating, hot melt adhesive layer composition, hot melt adhesive
Layer is formed according to following parts by weight: 45 parts of EVA resins, 38 parts of ethylene, 24 parts of vinyl acetates, 42 parts of hollow silica balls, 17
Part sodium cellulose glycolate, 11 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzothiophene;17 parts of polyesters thermoplastics
Property polyurethane;2 parts of plasticizer, 68 parts of solvent, 27 parts of natural terpene resins, 40 parts of naphthenic oil, 35 parts of calcium carbonate, 8 parts
PE wax, 8 parts of chain extension-crosslinking agent, 7 parts of fire retardants, 7 parts of initiators;Tackifier select 6 parts of C5 Petropols terpene resins, 4 parts of hydrogen
Change at least one of rosin resin, 11 parts of coumarone indene resins, 4 parts of paraffin, 3 parts of naphthenic oils;Antioxidant is selected from 4.5 parts of phosphorous acid
Esters antioxidant, 5 parts of sulfur-bearing esters any one.
Embodiment 4
A kind of Hot melt adhesive tape, the PET film layer being superimposed from top to bottom, melt pressure sensitive gel coating, hot melt adhesive layer composition, hot melt adhesive
Layer is formed according to following parts by weight: 50 parts of EVA resins, 40 parts of ethylene, 25 parts of vinyl acetates, 45 parts of hollow silica balls, 18
Part sodium cellulose glycolate, 12 parts of 2- vinyl -1- benzofurans or 2- vinyl -1- benzothiophene;18 parts of polyesters thermoplastics
Property polyurethane;2.5 parts of plasticizer, 75 parts of solvent, 30 parts of natural terpene resins, 50 parts of naphthenic oil, 40 parts of calcium carbonate, 3-
10 parts of PE wax, 10 parts of chain extension-crosslinking agent, 10 parts of fire retardants, 8 parts of initiators;Tackifier select 7 parts of C5 Petropols terpene resins,
At least one of 5 parts of hydrogenated rosin resins, 12 parts of coumarone indene resins, 5 parts of paraffin, 4 parts of naphthenic oils;Antioxidant is selected from 5 parts of Asias
Phosphoric acid ester antioxidant, 6 parts of sulfur-bearing esters any one.
Hot melt adhesive layer is the main component for making hot melt adhesive, and according to required proportion when preparation, the ratio of hot melt adhesive layer is determined
The basic performance of hot melt adhesive, such as glue the selection of cohering ability, melting temperature and auxiliary agent and prepare, all with basic resin
Depending on ratio is different, therefore binds EVA hot-melt adhesive used and should need properly to select ethylene and acetic acid second according to object is sticked
The ratio of alkene selects to have certain flexibility, elasticity, adhesion, deforms small etc. kind to be deployed.
(some substances for capableing of congruent melting with basic resin are added, it is therefore intended that increase its bond performance, this is just needed in tackifier
Mix tackifier.Suitable tackifier is added in EVA hot-melt adhesive can also improve the mobility of colloid, to enhance colloid pair
It is sticked the wetting and penetrating power of object, improves bond strength, meet this needs to bond strength of books.
(tackifier are also one of main auxiliary agent of hot melt adhesive to tackifier, and effect is to reduce melting viscosity, increase flowing
Property, wetability, adjust setting rate, quickly cohere firm purpose to reach.There is no the addition of tackifier, colloid will viscosity
Too small, application difficulties are not easy to cohere securely.
(because of temperature drift oxygenolysis can occur antioxidant for colloid in melting, and suitable antioxidant, which is added, to be prevented
The premature aging of hot melt adhesive.And under the high temperature conditions, suitable antioxidant is added, the stickiness of adhesive will not become
Change, it is sufficient to which effect is cohered in guarantee.It is BHT (di-tert-butyl methyl phenol class) that antioxidant is also available, and effect is relatively good,
Dosage general control is advisable 0.5% or so.) antioxidant is also selected from phosphite ester antioxidant, containing sulphur ester antioxidant
At least one of.
It is listed following for above embodiments and Hot melt adhesive tape performance in the prior art by its performance of verification experimental verification
Table:
Contrast on effect through the foregoing embodiment, it is known that, the present invention by hot melt adhesive layer formula and processing step into
Row improves, and compares common Hot melt adhesive tape performance in the prior art, hence it is evident that it can be seen that Hot melt adhesive tape performance of the invention is more
Superior, performance is further improved, and is suitble to promote the use of.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of Hot melt adhesive tape, which is characterized in that PET film layer, the melt pressure sensitive gel coating, hot melt adhesive layer group being superimposed from top to bottom
At hot melt adhesive layer is formed according to following parts by weight: 20-50 parts of EVA resins, 30-40 parts of ethylene, 20-25 parts of vinyl acetates, 30-
45 parts of hollow silica balls, 15-18 parts of sodium cellulose glycolates, 10-12 parts of 2- vinyl -1- benzofurans or 2- ethylene
Base -1- benzothiophene;15-18 parts of polyester-type thermoplastic polyurethane;1-2.5 parts of plasticizer, 60-75 parts of solvent, 5-30 parts of day
Right terpene resin, 10-50 parts of naphthenic oil, 10-40 parts of calcium carbonate, 3-10 parts of PE wax, 2-10 parts of chain extension-crosslinking agent, 5-10
Part fire retardant, 5-8 parts of initiators;
Tackifier select 5-7 parts of C5 Petropols terpene resins, 3-5 parts of hydrogenated rosin resins, 8-12 parts of coumarone indene resins, 3-5 parts
At least one of paraffin, 2-4 part naphthenic oil;
Antioxidant be selected from 3-5 parts of phosphite ester antioxidants, 4-6 parts of sulfur-bearing esters any one.
2. a kind of Hot melt adhesive tape according to claim 1, it is characterised in that: PET film layer, the hot melt being superimposed from top to bottom are pressed
Quick gel coating, hot melt adhesive layer composition, hot melt adhesive layer are formed according to following parts by weight: 40 parts of EVA resins, 35 parts of ethylene, 23 portions of vinegar
Sour ethylene, 40 parts of hollow silica balls, 17 parts of sodium cellulose glycolates, 11 parts of 2- vinyl -1- benzofurans or 2- ethylene
Base -1- benzothiophene;16 parts of polyester-type thermoplastic polyurethane;2 parts of plasticizer, 60 parts of solvent, 20 parts of natural terpene resins, 32
Naphthenic oil, 25 parts of the calcium carbonate, 7 parts of PE wax, 6 parts of chain extension-crosslinking agent, 7 parts of fire retardants, 7 parts of initiators of part;Tackifier select 6
Part C5 Petropols terpene resin, 4 parts of hydrogenated rosin resins, 10 parts of coumarone indene resins, 4 parts of paraffin, 3 parts of naphthenic oils at least one
Kind;Antioxidant be selected from 4 parts of phosphite ester antioxidants, 5 parts of sulfur-bearing esters any one.
3. a kind of Hot melt adhesive tape according to claim 1, it is characterised in that: the hot melt adhesive layer accounts for PET film layer, hot melt pressure
The 40%-60% of quick gel coating, hot melt adhesive layer summation quality.
4. a kind of Hot melt adhesive tape according to claim 1, it is characterised in that: the weight average molecular weight of the EVA resin is 4-5
Ten thousand.
5. a kind of Hot melt adhesive tape according to claim 1, it is characterised in that: the fire retardant selects phosphate and halogen phosphorus
Acid esters, halogenated hydrocarbons cooperate according to 1:2 mass ratio.
6. a kind of Hot melt adhesive tape according to claim 1, it is characterised in that: be also blended with 1-2.5 weight in the EVA resin
Measure the vinyl benzo-crown ether of part.
7. a kind of preparation method for preparing a kind of Hot melt adhesive tape described in claim 1, which comprises the following steps:
Step 1: preparation, first by EVA resin, ethylene, vinyl acetate, hollow silica ball, sodium cellulose glycolate, 2- second
Alkenyl -1- benzofuran or 2- vinyl -1- benzothiophene, polyester-type thermoplastic polyurethane;It is heat-treated after mixing, temperature
It is spare to obtain mixture A under the conditions of 155-160 DEG C for control;
Step 2: and then mixture A obtained in the previous step is dissolved into solvent, it is stirred uniformly, until being completely dissolved, obtains
To mixture B;
Step 3: initiator, which is first added, in mixture B makes it after evenly mixing, then sequentially adds plasticizer, natural terpenes
Olefine resin, naphthenic oil, calcium carbonate, PE wax, chain extension-crosslinking agent, fire retardant, when every kind of material is added all uniform stirring, be placed in
5-10min between 100-120 DEG C, in a high speed mixer, high-speed stirred mix 35-60min;
Step 4: being filtered cooling for the material finally obtained in step 3, obtains the material of purity is high, then turns again to
Mixing 10-20min is carried out in high-speed mixer, in triplicate, finally obtains fine material C;
Step 5: being warming up to 95-105 DEG C for material C, and tackifier are added while stirring, resist in 25-30rpm for mixing speed control
Oxygen agent, is kneaded 50-60min together;
Step 6: the material after mixing well in step 5 squeezes out, and is pressed into and is evenly distributed with calender, with a thickness of 2-
2.5mm thin slice;
Step 7, then obtained 2-2.5mm thin slice upper berth melt pressure sensitive gel coating, PET film layer are realized into hot-forming, cooling,
Hot melt adhesive tape can be obtained.