CN109796760A - A kind of table tennis of environmental protection - Google Patents
A kind of table tennis of environmental protection Download PDFInfo
- Publication number
- CN109796760A CN109796760A CN201811509954.XA CN201811509954A CN109796760A CN 109796760 A CN109796760 A CN 109796760A CN 201811509954 A CN201811509954 A CN 201811509954A CN 109796760 A CN109796760 A CN 109796760A
- Authority
- CN
- China
- Prior art keywords
- parts
- shell
- environmental protection
- table tennis
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of tablees tennis of environmental protection, including shell, the shell synthetic material includes the raw material of following parts by weight: 20 ~ 27 parts of cellulose diacetate, 30 ~ 37 parts of polysulfones, 30 ~ 37 parts of polyetherimide, 10 ~ 17 parts of acetoglyceride, 10 ~ 17 parts of camphor powder, 1 ~ 8 part of isopropanol, 1 ~ 8 part of acetone, 1 ~ 8 part of corrdination type phosphite ester, 0.1 ~ 0.8 part of acetyl tri-n-butyl citrate, 1 ~ 8 part of aluminium powder, 1 ~ 8 part of pigment, 10 ~ 17 parts of titanium dioxide, 5 ~ 12 parts of calcium carbonate crystal whisker, 5 ~ 12 parts of liquid nylon, 20 ~ 27 parts of acrylonitrile-butadiene-styrene copolymer, 1 ~ 8 part of strawberry essence.Intensity of the present invention is high, and good toughness, stable gravity center, elastic force is good, and there is strawberry flavor to replace plastics taste, more environmentally friendly.
Description
Technical field
The present invention relates to a kind of tablees tennis of environmental protection.
Background technique
Existing table tennis haves the shortcomings that low intensity, poor toughness, gravity center instability, poor flexibility, plastics taste are big.
Summary of the invention
In view of the deficienciess of the prior art, the object of the invention is that providing a kind of table tennis of environmental protection, intensity
Height, good toughness, stable gravity center, elastic force is good, and there is strawberry flavor to replace plastics taste, more environmentally friendly.
To achieve the goals above, the technical solution adopted by the present invention is that such: a kind of table tennis of environmental protection, including shell
Body, the shell synthetic material include the raw material of following parts by weight: 20 ~ 27 parts of cellulose diacetate, gathers 30 ~ 37 parts of polysulfones
30 ~ 37 parts of etherimide, 10 ~ 17 parts of acetoglyceride, 10 ~ 17 parts of camphor powder, 1 ~ 8 part of isopropanol, 1 ~ 8 part of acetone, corrdination type
1 ~ 8 part of phosphite ester, 0.1 ~ 0.8 part of acetyl tri-n-butyl citrate, 1 ~ 8 part of aluminium powder, 1 ~ 8 part of pigment, 10 ~ 17 parts of titanium dioxide,
5 ~ 12 parts of calcium carbonate crystal whisker, 5 ~ 12 parts of liquid nylon, 20 ~ 27 parts of acrylonitrile-butadiene-styrene copolymer, strawberry essence 1 ~ 8
Part.
As a preferred embodiment, the weight of the shell is 3 ~ 4g.
As a preferred embodiment, the thickness of the shell is in 0.5 ~ 1mm.
As a preferred embodiment, the diameter of the shell is 40 ~ 45mm.
As a preferred embodiment, the shell is formed by two hollow semi-cylindrical structures to form.
As a preferred embodiment, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization,
Material grain is molded into two hollow semi-cylindrical structures through injection molding machine again, two hollow semi-cylindrical construction bonds form shell ball together
Then shell ball base is carried out swollen ball processing by base in a mold, finished product housing of finally polishing to obtain.
Compared with prior art, beneficial effects of the present invention: intensity of the present invention is high, and good toughness, stable gravity center, elastic force is good, and
Plastics taste is replaced with strawberry flavor, it is more environmentally friendly.
Specific embodiment
The invention will be further described combined with specific embodiments below.Following embodiment is only used for clearly illustrating
Technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 20 parts, 30 parts of polysulfones, 30 parts of polyetherimide, 10 parts of acetoglyceride, 10 parts of camphor powder, 1 part of isopropanol, 1 part of acetone,
1 part of corrdination type phosphite ester, 0.1 part of acetyl tri-n-butyl citrate, 1 part of aluminium powder, 1 part of pigment, 10 parts of titanium dioxide, calcium carbonate are brilliant
It must 5 parts, 5 parts of liquid nylon, 20 parts of acrylonitrile-butadiene-styrene copolymer, 1 part of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 2:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 21 parts, 31 parts of polysulfones, 31 parts of polyetherimide, 11 parts of acetoglyceride, 11 parts of camphor powder, 2 parts of isopropanol, 2 parts of acetone,
2 parts of corrdination type phosphite ester, 0.2 part of acetyl tri-n-butyl citrate, 2 parts of aluminium powder, 2 parts of pigment, 11 parts of titanium dioxide, calcium carbonate are brilliant
It must 6 parts, 6 parts of liquid nylon, 21 parts of acrylonitrile-butadiene-styrene copolymer, 2 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 3:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 22 parts, 32 parts of polysulfones, 32 parts of polyetherimide, 12 parts of acetoglyceride, 12 parts of camphor powder, 3 parts of isopropanol, 3 parts of acetone,
3 parts of corrdination type phosphite ester, 0.3 part of acetyl tri-n-butyl citrate, 3 parts of aluminium powder, 3 parts of pigment, 12 parts of titanium dioxide, calcium carbonate are brilliant
It must 7 parts, 7 parts of liquid nylon, 22 parts of acrylonitrile-butadiene-styrene copolymer, 3 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 4:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 23 parts, 33 parts of polysulfones, 33 parts of polyetherimide, 13 parts of acetoglyceride, 4 parts of camphor powder, 4 parts of isopropanol, 4 parts of acetone,
4 parts of corrdination type phosphite ester, 0.4 part of acetyl tri-n-butyl citrate, 4 parts of aluminium powder, 4 parts of pigment, 13 parts of titanium dioxide, calcium carbonate are brilliant
It must 8 parts, 8 parts of liquid nylon, 23 parts of acrylonitrile-butadiene-styrene copolymer, 4 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 5:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 24 parts, 34 parts of polysulfones, 34 parts of polyetherimide, 14 parts of acetoglyceride, 14 parts of camphor powder, 5 parts of isopropanol, 5 parts of acetone,
5 parts of corrdination type phosphite ester, 0.5 part of acetyl tri-n-butyl citrate, 5 parts of aluminium powder, 5 parts of pigment, 14 parts of titanium dioxide, calcium carbonate are brilliant
It must 9 parts, 9 parts of liquid nylon, 24 parts of acrylonitrile-butadiene-styrene copolymer, 5 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 6:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 25 parts, 35 parts of polysulfones, 35 parts of polyetherimide, 15 parts of acetoglyceride, 15 parts of camphor powder, 6 parts of isopropanol, 6 parts of acetone,
6 parts of corrdination type phosphite ester, 0.6 part of acetyl tri-n-butyl citrate, 6 parts of aluminium powder, 6 parts of pigment, 15 parts of titanium dioxide, calcium carbonate are brilliant
It must 10 parts, 10 parts of liquid nylon, 25 parts of acrylonitrile-butadiene-styrene copolymer, 6 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 7:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 26 parts, 36 parts of polysulfones, 36 parts of polyetherimide, 16 parts of acetoglyceride, 16 parts of camphor powder, 7 parts of isopropanol, 7 parts of acetone,
7 parts of corrdination type phosphite ester, 0.7 part of acetyl tri-n-butyl citrate, 7 parts of aluminium powder, 7 parts of pigment, 16 parts of titanium dioxide, calcium carbonate are brilliant
It must 11 parts, 11 parts of liquid nylon, 26 parts of acrylonitrile-butadiene-styrene copolymer, 7 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
Embodiment 8:
A kind of table tennis of environmental protection, including shell, the shell synthetic material include the raw material of following parts by weight: two acetic acid are fine
Dimension element 27 parts, 37 parts of polysulfones, 37 parts of polyetherimide, 17 parts of acetoglyceride, 17 parts of camphor powder, 8 parts of isopropanol, 8 parts of acetone,
8 parts of corrdination type phosphite ester, 0.8 part of acetyl tri-n-butyl citrate, 8 parts of aluminium powder, 8 parts of pigment, 17 parts of titanium dioxide, calcium carbonate are brilliant
It must 12 parts, 12 parts of liquid nylon, 27 parts of acrylonitrile-butadiene-styrene copolymer, 8 parts of strawberry essence.
Preferably, the weight of the shell is 3 ~ 4g.
Preferably, the thickness of the shell is in 0.5 ~ 1mm.
Preferably, the diameter of the shell is 40 ~ 45mm.
Preferably, the shell is formed by two hollow semi-cylindrical structures to form.
Preferably, it is put into after mixed at high speed by the raw material mixing of mass parts through dual-screw-stem machine extruding pelletization, then will material grain warp
Injection molding machine is molded into two hollow semi-cylindrical structures, and two hollow semi-cylindrical construction bonds form shell ball base together, then by shell
Body ball base carries out swollen ball processing in a mold, finished product housing of finally polishing to obtain.
In conclusion the shell made of embodiment 1 ~ 8, performance test data are as follows:
The above is only a preferred embodiment of the present invention, it is noted that those skilled in the art are come
It says, without departing from the technical principles of the invention, several improvement and deformations can also be made, these improvement and deformations are also answered
It is considered as protection scope of the present invention.
Claims (6)
1. a kind of table tennis of environmental protection, including shell, which is characterized in that the shell synthetic material includes following parts by weight
Raw material: 20 ~ 27 parts of cellulose diacetate, 30 ~ 37 parts of polysulfones, 30 ~ 37 parts of polyetherimide, 10 ~ 17 parts of acetoglyceride, camphor
10 ~ 17 parts of powder, 1 ~ 8 part of isopropanol, 1 ~ 8 part of acetone, 1 ~ 8 part of corrdination type phosphite ester, acetyl tri-n-butyl citrate 0.1 ~ 0.8
Part, 1 ~ 8 part of aluminium powder, 1 ~ 8 part of pigment, 10 ~ 17 parts of titanium dioxide, 5 ~ 12 parts of calcium carbonate crystal whisker, 5 ~ 12 parts of liquid nylon, acrylonitrile-
20 ~ 27 parts of butadiene-styrene copolymer, 1 ~ 8 part of strawberry essence.
2. a kind of table tennis of environmental protection according to claim 1, it is characterised in that: the weight of the shell is 3 ~ 4g.
3. a kind of table tennis of environmental protection according to claim 1, it is characterised in that: the thickness of the shell is in 0.5 ~ 1mm.
4. a kind of table tennis of environmental protection according to claim 1, it is characterised in that: the diameter of the shell is 40 ~ 45mm.
5. a kind of table tennis of environmental protection according to claim 1, it is characterised in that: the shell is by two hollow semi-cylindrical knots
Structure is spliced.
6. a kind of table tennis of environmental protection according to claim 5, it is characterised in that: be put into height by the raw material mixing of mass parts
Through dual-screw-stem machine extruding pelletization after speed mixing, then material grain through injection molding machine is molded into two hollow semi-cylindrical structures, two hollow half
Circle construction bonds form shell ball base together, shell ball base is then subjected to swollen ball processing in a mold, finally polish at
Product shell.