CN109781576A - The detection method of battery car negative plate of lead storage battery lead paste formula reinforcing fiber - Google Patents
The detection method of battery car negative plate of lead storage battery lead paste formula reinforcing fiber Download PDFInfo
- Publication number
- CN109781576A CN109781576A CN201711118051.4A CN201711118051A CN109781576A CN 109781576 A CN109781576 A CN 109781576A CN 201711118051 A CN201711118051 A CN 201711118051A CN 109781576 A CN109781576 A CN 109781576A
- Authority
- CN
- China
- Prior art keywords
- lead
- lead plaster
- organic acid
- fiber
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the battery car detection methods of negative plate of lead storage battery lead paste formula reinforcing fiber, firstly, being dissolved by mixed solution of hydrogen peroxide alignment plate lead plaster, or are dissolved by organic acid soln to lead plaster, green plate, positive plate lead plaster;Then, sieving separating goes out staple fiber, dry, obtains staple fiber;Finally, calculating mass percent of the staple fiber in lead plaster by assay balance scale short fibre content;Wherein, mixed solution of hydrogen peroxide is made of the hydrogen peroxide that 20mL mass concentration 30% is added in 12% organic acid of 1000mL mass concentration;Organic acid soln is the organic acid of mass concentration 12%.On the one hand method of the invention analyzes the content of lead plaster middle short fiber to determine the uniformity of lead plaster middle short fiber, on the other hand the green plate after analysis curing and drying, the positive positive plate lead paste middle short fiber content after chemical conversion drying are lost to determine whether there is, short fibre content is set to meet technical requirements, the intensity for reaching lead plaster guarantees anti-vibration, the resistance to circulation, the performance that does not fall off of lead plaster of battery pole plates.
Description
Technical field
The present invention relates to silicon energy batteries, and in particular to a kind of battery car is fine with the enhancing of negative plate of lead storage battery lead paste formula
The detection method of dimension.
Background technique
Silicon energy battery pole plates on the make, are needed by processes such as mixing paste, coated plate, curing and drying, chemical conversion, dryings, in order to
Lead plaster has good bond strength, and suitable staple fiber is usually added in the auxiliary material of lead plaster mixing paste, and specific amount is 0.09%
~1% etc..How to ensure that lead plaster middle short fiber reaches uniformity in mixing paste, its intensity is being verified after curing and drying
Whether meet the requirements, whether has scaling loss failure after chemical conversion is dry, at present only by the uniformity for visually confirming staple fiber, apparently
How much fiber loses to determine whether there is, not scientific in this way, no data support.So needing a kind of method short in lead plaster to analyze
Fiber content makes reasonable judgement.
Summary of the invention
It is an object of the invention to: a kind of inspection of battery car negative plate of lead storage battery lead paste formula reinforcing fiber is provided
On the one hand survey method analyzes the content of lead plaster middle short fiber to determine the uniformity of lead plaster middle short fiber, separately by this method
On the one hand positive positive plate lead paste middle short fiber content after the green plate after analysis curing and drying, chemical conversion are dry determines whether there is
Loss, makes short fibre content meet technical requirements, reaches the intensity of lead plaster, guarantees the anti-vibration, resistance to of battery pole plates from source
The performance that circulation, lead plaster are not fallen off.
The technical solution of the invention is as follows: firstly, dissolved by mixed solution of hydrogen peroxide alignment plate lead plaster, or by
Organic acid soln dissolves lead plaster, green plate, positive plate lead plaster;Then, sieving separating goes out staple fiber, dry, obtains short fibre
Dimension;Finally, calculating mass percent of the staple fiber in lead plaster by assay balance scale short fibre content.
Wherein, mixed solution of hydrogen peroxide is by being added 20mL mass concentration 30% in 12% organic acid of 1000mL mass concentration
Hydrogen peroxide composition;Organic acid soln is the organic acid of mass concentration 12%.
Wherein, specific step is as follows for analysis method:
1, lead plaster, green plate, positive plate lead plaster: taking lead plaster in bulk, or takes green plate, positive plate lead plaster, not grind, should not mistake
Sieve directly takes block, weighs 40g and (accurately to 0.001g), is put into 500mL beaker, organic acid soln 300mL is added, boils
Boiling, stirring, so that organic lead plumbate is in dispersed, is slowly sieved in the center of 200 meshes to without obvious pimple, makes staple fiber
Be deposited in the center of sieve, be washed with water to the pure white free from admixture of staple fiber, 110 DEG C drying 30 minutes, obtain staple fiber;By analysis day
Flat scale short fibre content calculates mass percent of the staple fiber in lead plaster;
2, positive plate lead plaster: taking the lead plaster of positive plate, not grind, not be sieved, and directly takes block, and it is (accurate to weigh 40g
To 0.001g), it is put into 500mL beaker, mixed solution of hydrogen peroxide 200mL is added, to without obvious pimple, solution is in stirring and dissolving
Translucent muddiness shape, is slowly sieved in the center of 200 meshes, so that staple fiber is deposited in the center of sieve, be washed with water to short
The pure white free from admixture of fiber, 110 DEG C drying 30 minutes, obtain staple fiber;By assay balance scale short fibre content, short fibre is calculated
Tie up the mass percent in lead plaster.
The invention has the following advantages that it is 1. convenient and efficient, the analysis of multiple samples can be carried out simultaneously, determine a batch mixing paste mistake
The staple fiber uniformity of journey, while can also speculate the uniformity of other materials;2. the chemical reagent type needed is few, treatment process
Simply, free from admixture introduces, and tool is easy to use;3. analyzing, result is accurate and reliable, and staple fiber is obviously clear to.
Specific embodiment
Analysis method of the invention is further illustrated below with reference to specific embodiment, these embodiments are not to be construed as
Limitation to technical solution.
Embodiment 1: the lead plaster middle short fiber quality finished according to the analysis of step in detail below mixing paste:
The lead plaster for taking mixing paste to finish in three times is sealed by PE bags;Lead plaster is pinched into slabbing with hand, takes out blocky lead plaster,
40g is weighed (accurately to 0.001g), to be put into 500mL beaker, the organic acid soln 300mL of mass concentration 12% is added, boils, stirs
It mixes to without obvious pimple, so that organic lead plumbate is in dispersed, is slowly sieved in the center of 200 meshes, accumulates staple fiber
In the center of sieve, be washed with water to the pure white free from admixture of staple fiber, 110 DEG C drying 30 minutes, obtain staple fiber;By assay balance scale
Short fibre content calculates mass percent of the staple fiber in lead plaster.
For staple fiber by when auxiliary material is added, quality 900g, moisture at this time is 18.42%;One pot of (criticizing) lead
It is 610 kilograms that cream, which forms quality, then short fibre content dry at this time is 900 × (1-0.1842) ÷, 610 ÷ 1000 × 100%
=0.12%, and embodiment 1 measures 0.124%, 0.121%, 0.118% and meets technical requirements.
Embodiment 2: the dry lead plaster for finishing positive plate of chemical conversion is analyzed according to step in detail below:
The dry lead plaster for finishing positive plate of chemical conversion is taken in three times, is sealed by PE bags;Blocky lead plaster is taken out, it is (quasi- to weigh 40g
Really to 0.001g), it is put into 500mL beaker, mixed solution of hydrogen peroxide 200mL is added, stirring and dissolving is to without obvious pimple, solution
Be translucent muddy shape, is slowly sieved in the center of 200 meshes, so that staple fiber is deposited in the center of sieve, be washed with water to
The pure white free from admixture of staple fiber, 110 DEG C drying 30 minutes, obtain staple fiber;By assay balance scale short fibre content, calculate short
Mass percent of the fiber in lead plaster.
Positive plate lead plaster is after curing and drying, chemical conversion are dry, and the lead plaster before the non-coated plate of 100g obtains 92g at this time
Lead plaster will return and calculate staple fiber additive amount, then 0.92 × 0.128%=0.118%, differs only by 0.002% with technical requirements;
B, it is respectively 0.113%, 0.117% that the return of C, which calculates, and absolute error meets technical requirements less than 0.01%.
Claims (2)
1. the battery car detection method of negative plate of lead storage battery lead paste formula reinforcing fiber, it is characterised in that: firstly, by mistake
Hydrogen oxide mixed solution alignment plate lead plaster is dissolved, or molten to lead plaster, green plate, the progress of positive plate lead plaster by organic acid soln
Solution;Then, sieving separating goes out staple fiber, dry, obtains staple fiber;Finally, being calculated short by assay balance scale short fibre content
Mass percent of the fiber in lead plaster.
2. the battery car according to claim 1 detection method of negative plate of lead storage battery lead paste formula reinforcing fiber,
It is characterized by: wherein, mixed solution of hydrogen peroxide is by being added 20mL mass concentration in 12% organic acid of 1000mL mass concentration
30% hydrogen peroxide composition;Organic acid soln is the organic acid of mass concentration 12%.