CN109776992A - A kind of calcium-zinc composite stabilizing agent and its preparation method and application - Google Patents
A kind of calcium-zinc composite stabilizing agent and its preparation method and application Download PDFInfo
- Publication number
- CN109776992A CN109776992A CN201811446526.7A CN201811446526A CN109776992A CN 109776992 A CN109776992 A CN 109776992A CN 201811446526 A CN201811446526 A CN 201811446526A CN 109776992 A CN109776992 A CN 109776992A
- Authority
- CN
- China
- Prior art keywords
- calcium
- zinc
- stabilizing agent
- composite stabilizing
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to chemical stabilizer technical field, a kind of calcium-zinc composite stabilizing agent and its preparation method and application is disclosed.The calcium-zinc composite stabilizing agent is made of the raw material of following mass percent: isooctyl acid: 10 ~ 30%, benzoic acid: 2 ~ 10%, zinc oxide: 0.5 ~ 4.2%, calcium oxide: 1.2 ~ 6.5%, nontoxic phosphite ester: 8 ~ 15%, DINCH:20 ~ 35%, ATBC:1 ~ 5%, TXIB:0.1 ~ 3%, chloro methyl esters: 18 ~ 32%.Novel calcium-zinc composite stabilizing agent of the invention uses novel non-toxic environmental protection composite elasticizer under specific calcium zinc salt proportion in a creative way, obtains colourless transparent liquid calcium zinc stabilizer;And the method for the invention simple production process, it is easy to implement.
Description
Technical field
The invention belongs to chemical stabilizer technical fields, more particularly, to a kind of calcium-zinc composite stabilizing agent and its preparation
Methods and applications.
Background technique
Well known heat stabilizer mainly has lead salts, metal soap, organic tin, terres rares and Ca/Zn class in PVC industry
Equal stabilizers, but the most heat stabilizer of application is lead salts and metal soap.Lead salt stabilizer is cheap, thermostabilization effect
Fruit is good, but its toxicity is big, seriously endangers human health and simultaneously pollutes environment, and lead salt stabilizer have the shortcomings that it is opaque.Have
Machine the tin stabilizer not only transparency and good thermal stability, but also small toxicity, it is widely used in high grade of transparency polyvinyl chloride
Plate, sheet material, food, in medical packaging, but it is expensive, and some products will control in toxicity entirely without poison ring
It protects, thus it is using also restrained.
Raising with society to environmental consciousness, and the raising to the requirement of heat stabilizer comprehensive performance, heat stabilizer
Production and consumption develops to nontoxic, the pollution-free, high grade of transparency, the good and efficient direction of heat resistance.And nontoxic calcium zinc compound thermal
Stabilizer is universally acknowledged nontoxic, environment-benign heat stabilizer, and has many advantages, such as that cheap, lubricity is good, has pole
Wide development space.
However, the plasticizer that existing calcium-zinc composite stabilizing agent uses, for a long time based on mainly adjacent benzene-type products, but
As the adjacent benzene class plasticizer such as DOP, DINP is using more and more extensive, its toxicity is also increasingly subject to insider and consumer
Concern.Neighbour's benzene class plasticizer such as DOP, DINP is the organic matter containing benzene, to the toxic effect of human reproductive system, while having research
Show that such compound has the harm such as carcinogenic, teratogenesis, 6 kinds of DOP, DEHP, BBP etc. are classified as excellent by American National Environmental Protection Agency (EPA)
The toxic pollutant first controlled is forbidden applying in the materials such as medical treatment, food, the numerous and confused response green environmental protection concept of overseas enterprise,
Corresponding laws and regulations are constantly put into effect, the technical barrier to home products is increased.
Summary of the invention
For deficiency existing for calcium zinc stabilizer in the prior art, it is multiple that the purpose of the present invention is to provide a kind of new calcium zinc
Close stabilizer.The novel calcium-zinc composite stabilizing agent is compound using novel non-toxic environmental protection in a creative way under specific calcium zinc salt proportion
Plasticizer obtains colourless transparent liquid calcium zinc stabilizer.
Another object of the present invention is to provide a kind of preparation methods of above-mentioned calcium-zinc composite stabilizing agent.Side of the present invention
Method simple production process, is easy to implement.
Another object of the present invention is to provide a kind of calcium-zinc composite stabilizing agent PVC paste shape resin ward off glue, leaching modeling plus
Application in work or medical apparatus.
The purpose of the present invention is achieved through the following technical solutions:
A kind of calcium-zinc composite stabilizing agent is made of the raw material of following mass percent:
Isooctyl acid: 10~30%,
Benzoic acid: 2~10%,
Zinc oxide: 0.5~4.2%,
Calcium oxide: 1.2~6.5%,
Nontoxic phosphite ester: 8~15%,
DINCH:20~35%,
ATBC:1~5%,
TXIB:0.1~3%,
Chloro methyl esters: 18~32%.
The performance of calcium-zinc composite stabilizing agent can by adjusting each component proportion and obtain different effects.Work as calcium content
When increase, so that the long-term thermal stability performance of stabilizer is excellent, the product transparency is good, but the initial stage thermal stability of product is owed
Good, i.e., first discolouration increases;And when the increase of zinc soap content, although being able to suppress initial coloration performance, the zinc chloride of generation
It is a kind of lewis acid, HCl is taken off with catalytic action to PVC, dosage excessively readily facilitates PVC decomposition, is allowed to generate stain " zinc
Burn " phenomenon.Zinc soap is regenerated since displacement reaction occurs for the zinc chloride that calcium soap can be generated with zinc soap, it is of the invention
Calcium-zinc composite stabilizing agent uses calcium soap and zinc soap simultaneously, and mixes in specific proportion, is reduced by the synergistic effect of the two
" zinc burning " phenomenon.
Plasticizer of the invention is that DINCH, ATBC and TXIB are compounded under certain proportion, and obtained plasticizer is colourless
Asepsis environment-protecting effectively solves the toxicity defect of adjacent benzene class plasticizer.Wherein, DINCH is the hexamethylene 1 of German BASF production,
2- dioctyl phthalate diisononyl esters, molecular formula C26H48O4, it is a kind of non-phthalic ester plasticizer, the plasticizer is in Europe
Continent is tested by rigorous toxicity;In addition, DINCH has fine compatibility to PVC, there is excellent processing performance, low volatility,
Excellent cryogenic property, resistance to low temperature is especially prominent, no mould/fungi growth, low migration, brilliant toxicological profile,
It can be used for toy, high-grade electric appliance, food etc..
ATBC, the tributyl 2-acetylcitrate produced using Jiangsu Lei Meng company, molecular formula C12H17O8, there is dissolution
Property it is strong, oil resistivity, light resistance are good, and have good fungus resistance, it and most of celluloses, polyvinyl chloride, polyvinyl acetate
And chlorinated rubber etc. has good intermiscibility.Meanwhile it is also widely used for food packaging, medical apparatus, toy for children, individual
Amenities, PVC are granulated, and ward off glue rubber patch product, cigarette filter etc..
TXIB, for the double isobutyrates of 2,2,4- trimethyl -1,3- pentanediols of Eastman company, U.S. production, molecular formula is
C16H30O4, it is a kind of primary plasticizer, is non-neighboring benzene class environment-friendly plasticizer, with all general primary and secondary plasticizer phases
Hold, is widely used in PVC plastic colloidal sol and organosol, and its chemical property is stablized, and is not easy to be mixed into bubble, energy in the solution
Keep product it is smooth with it is beautiful, be a kind of with plasticization and lower volatile thinner, it is good product can be assigned
Cold resistance and water resistance.
Therefore, the present invention is using DINCH, TXIB and ATBC as plasticizer, and wherein TXIB, DINCH viscosity are lower,
The viscosity that batching system can be reduced reduces the use of thinner;ATBC oil resistivity, light resistance, fungus resistance are splendid, with TXIB,
DINCH be used in compounding can be improved PVC product have many advantages, such as low temperature flex performance and sealing when thermal stability it is good, non-discolouring.
Further, the zinc oxide is super fine zinc oxide, and the average grain diameter of the super fine zinc oxide is 30~80nm.
Further, the calcium oxide is ultra-fine calcium oxide, and the average grain diameter of the ultra-fine calcium oxide is 40~80nm.
Further, the nontoxic phosphite ester is phosphorous acid 4, different fork bis-phenol (12~14) the carbon Arrcostab of 4- bis-.
Further, the calcium-zinc composite stabilizing agent is made of the raw material of following mass percent:
Isooctyl acid: 10~25%,
Benzoic acid: 4~8%,
Super fine zinc oxide: 0.5~3.5%,
Ultra-fine calcium oxide: 1.5~5%,
Nontoxic phosphite ester: 10~15%,
DINCH:24~30%,
ATBC:3~5%,
TXIB:0.5~2.5%,
Chloro methyl esters: 20~28%.
Further, the calcium-zinc composite stabilizing agent is made of the raw material of following mass percent:
Isooctyl acid: 20~25%,
Benzoic acid: 5~6%,
Super fine zinc oxide: 1~2%,
Ultra-fine calcium oxide: 4~5%,
Nontoxic phosphite ester: 12~15%,
DINCH:25~28%,
ATBC:4~5%,
TXIB:1~1.5%,
Chloro methyl esters: 24~26%.
A kind of preparation method that above-mentioned Ca Zn composite is stable, comprising the following steps:
S1. isooctyl acid, benzoic acid, zinc oxide and calcium oxide are carried out being dehydrated into salt treatment by said ratio, is produced respectively
Obtain calcium salt and zinc salt;
S2. certain nontoxic phosphite ester, plasticizer and chloro methyl esters are added into the obtained calcium salt of step S1 and zinc salt, fills
Divide stirring to get the calcium-zinc composite stabilizing agent.
Further, in step S1, the technological parameter for being dehydrated into salt treatment are as follows: reaction temperature is 100~120 DEG C,
Reaction time is 15~25min.
Calcium-zinc composite stabilizing agent of the invention uses mixed acid and compound calcium, zinc oxide by being dehydrated at salt first
Reason, after the auxiliary reagents such as the plasticizer of nontoxic phosphite ester and above-mentioned asepsis environment-protecting are then added, obtains nontoxic transparent, hot
The liquid calcium zinc complex stabilizer of stability, photostability and the transparency and good weatherability.
A kind of application warded off in glue, leaching modeling processing or medical apparatus of above-mentioned calcium-zinc composite stabilizing agent in PVC paste shape resin.
Compared with prior art, the beneficial effects of the present invention are:
For the present invention using DINCH, TXIB and ATBC as plasticizer, DINCH, TXIB viscosity are lower, can reduce
The viscosity of batching system reduces the use of thinner;ATBC oil resistivity, light resistance, fungus resistance are splendid, compound with TXIB, DINCH
Have many advantages, such as that low temperature flex performance and thermal stability when sealing are good, non-discolouring using can be improved PVC product;In addition, addition
There is synergistic effect between chloro methyl esters and DINCH, the physical property of product can be significantly improved.
The environment-friendly type plasticizer that the present invention uses be free of benzene, produce without benzene calcium-zinc composite stabilizing agent, no benzene
It is nontoxic, it can be used in food, medical appliance field.
The preparation method process flow of calcium-zinc composite stabilizing agent of the invention is simple and environmentally-friendly, raw material is easy to get, energy less energy consumption,
Greatly reduce production cost, and waterless operation in entire production process, safe ready, without three waste discharge, to environment dirt
Dye is few.
Specific embodiment
To facilitate the understanding of the present invention, present invention work more comprehensively, is meticulously described below in conjunction with embodiment, but this hair
Bright protection scope is not limited to embodiment in detail below.
Unless otherwise defined, all technical terms used hereinafter and the normally understood meaning of those skilled in the art
It is identical.Technical term used herein is intended merely to the purpose of description specific embodiment, it is no intended to limit of the invention
Protection scope.
Unless otherwise specified, various raw material, reagent, the instrument and equipment etc. used in the present invention can pass through city
Field is commercially available or can be prepared by existing method.
Embodiment 1
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are made of the raw material of following mass percent: isooctyl acid:
10%, benzoic acid: 10%, super fine zinc oxide: 4.2%, ultra-fine calcium oxide: 6.5%, nontoxic phosphite ester: 8%, DINCH:
35%, ATBC:1%, TXIB:0.3%, chloro methyl esters: 25%;The average grain diameter of super fine zinc oxide is 30nm;Ultra-fine calcium oxide
Average grain diameter be 40nm, nontoxic phosphite ester be phosphorous acid 4, different fork bis-phenol (12~14) the carbon Arrcostab of 4- bis-;
The preparation method of above-mentioned calcium-zinc composite stabilizing agent, specifically includes the following steps:
S1. it carries out isooctyl acid, benzoic acid, zinc oxide and calcium oxide said ratio to be dehydrated into salt treatment, produce respectively
To calcium salt and zinc salt;Wherein, it is dehydrated into the technological parameter of salt treatment are as follows: reaction temperature is 100 DEG C, reaction time 25min;
S2. nontoxic phosphite ester, DINCH, ATBC, TXIB and nontoxic Asia is added to the obtained calcium salt of step S1 and in zinc salt
Phosphate is sufficiently stirred to get calcium-zinc composite stabilizing agent.
Embodiment 2
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are with the main distinction of embodiment 1, by following quality percentage
The raw material of ratio forms: isooctyl acid: 30%, benzoic acid: and 2%, super fine zinc oxide: 0.5%, ultra-fine calcium oxide: 1.2%, nontoxic Asia
Phosphate: 15%, DINCH:20%, ATBC:5%, TXIB:3%, chloro methyl esters: 23.3%;The average grain diameter of super fine zinc oxide
For 80nm;The average grain diameter of ultra-fine calcium oxide is 80nm;
Referring to the operating procedure of embodiment 1, the main distinction is for the preparation method of above-mentioned calcium-zinc composite stabilizing agent, step S1
In, the technological parameter for being dehydrated into salt treatment is as follows: reaction temperature is 120 DEG C, reaction time 15min.
Embodiment 3
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are with the main distinction of embodiment 1, by following quality percentage
The raw material of ratio forms: isooctyl acid: 22%, benzoic acid: and 4%, super fine zinc oxide: 3%, ultra-fine calcium oxide: 1.9%, nontoxic phosphorous
Acid esters: 10%, DINCH:25%, ATBC:2%, TXIB:0.1%, chloro methyl esters: 32%;The average grain diameter of super fine zinc oxide is
50nm;The average grain diameter of ultra-fine calcium oxide is 50nm;
Referring to the operating procedure of embodiment 1, the main distinction is for the preparation method of above-mentioned calcium-zinc composite stabilizing agent, step S1
In, the technological parameter for being dehydrated into salt treatment is as follows: reaction temperature is 110 DEG C, reaction time 20min.
Embodiment 4
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are with the main distinction of embodiment 1, by following quality percentage
The raw material of ratio forms: isooctyl acid: 12%, benzoic acid: and 8%, super fine zinc oxide: 2%, ultra-fine calcium oxide: 5%, nontoxic phosphorous acid
Ester: 12%, DINCH:30%, ATBC:3%, TXIB:2%, chloro methyl esters: 26%;The average grain diameter of super fine zinc oxide is
60nm;The average grain diameter of ultra-fine calcium oxide is 60nm;
Referring to the operating procedure of embodiment 1, the main distinction is for the preparation method of above-mentioned calcium-zinc composite stabilizing agent, step S1
In, the technological parameter for being dehydrated into salt treatment is as follows: reaction temperature is 105 DEG C, reaction time 18min.
Embodiment 5
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are with the main distinction of embodiment 1, by following quality percentage
The raw material of ratio forms: isooctyl acid: 25%, benzoic acid: and 3.5%, super fine zinc oxide: 1%, ultra-fine calcium oxide: 6%, nontoxic phosphorous
Acid esters: 9%, DINCH:32%, ATBC:4%, TXIB:1.5%, chloro methyl esters: 18%;The average grain diameter of super fine zinc oxide is
70nm;The average grain diameter of ultra-fine calcium oxide is 70nm;Operation of the preparation method of above-mentioned calcium-zinc composite stabilizing agent referring to embodiment 4
Step.
Embodiment 6
The present embodiment provides a kind of calcium-zinc composite stabilizing agents, are with the main distinction of embodiment 1, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.5%, ultra-fine calcium oxide: 4.5%, nontoxic Asia
Phosphate: 12.5%, DINCH:26%, ATBC:4.2%, TXIB:1.3%, chloro methyl esters: 25%;Super fine zinc oxide is averaged
Partial size is 40nm;The average grain diameter of ultra-fine calcium oxide is 60nm;The preparation method of above-mentioned calcium-zinc composite stabilizing agent is referring to embodiment 4
Operating procedure.
Comparative example 1
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.7%, ultra-fine calcium oxide: 4.8%, nontoxic Asia
Phosphate: 12.5%, DINCH:31%, chloro methyl esters: 25%;The preparation method of above-mentioned calcium-zinc composite stabilizing agent is referring to embodiment
6 operating procedure.
Comparative example 2
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.7%, ultra-fine calcium oxide: 4.8%, nontoxic Asia
Phosphate: 12.5%, ATBC:31%, chloro methyl esters: 25%;The preparation method of above-mentioned calcium-zinc composite stabilizing agent is referring to embodiment 6
Operating procedure.
Comparative example 3
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.7%, ultra-fine calcium oxide: 4.8%, nontoxic Asia
Phosphate: 12.5%, TXIB:31%, chloro methyl esters: 25%;The preparation method of above-mentioned calcium-zinc composite stabilizing agent is referring to embodiment 6
Operating procedure.
Comparative example 4
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.7%, ultra-fine calcium oxide: 4.8%, nontoxic Asia
Phosphate: 12.5%, DINCH:13%, ATBC:6%, TXIB:4%, chloro methyl esters: 33%;Above-mentioned calcium-zinc composite stabilizing agent
Operating procedure of the preparation method referring to embodiment 6.
Comparative example 5
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 20%, benzoic acid: and 5%, super fine zinc oxide: 1.7%, ultra-fine calcium oxide: 4.8%, nontoxic Asia
Phosphate: 12.5%, DINCH:40%, ATBC:0.5%, TXIB:0.05%, chloro methyl esters: 15.45%;Above-mentioned Ca Zn composite
Operating procedure of the preparation method of stabilizer referring to embodiment 6.
Comparative example 6
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 35%, benzoic acid: and 1%, super fine zinc oxide: 0.1%, ultra-fine calcium oxide: 8%, nontoxic phosphorous
Acid esters: 18%, DINCH:18%, ATBC:0.9%, TXIB:5%, chloro methyl esters: 14%;The system of above-mentioned calcium-zinc composite stabilizing agent
Operating procedure of the Preparation Method referring to embodiment 6.
Comparative example 7
This comparative example provides a kind of calcium-zinc composite stabilizing agent, is with the main distinction of embodiment 6, by following quality percentage
The raw material of ratio forms: isooctyl acid: 5%, benzoic acid: and 10.5%, super fine zinc oxide: 4.45%, ultra-fine calcium oxide: 0.5%, it is nontoxic
Phosphite ester: 6%, DINCH:35.5%, ATBC:5.5%, TXIB:0.05%, chloro methyl esters: 32.5%;Above-mentioned Ca Zn composite
Operating procedure of the preparation method of stabilizer referring to embodiment 6.
Performance detection is carried out to the calcium-zinc composite stabilizing agent that Examples 1 to 6 and comparative example 1~7 are prepared, including saturating
The performances such as light rate, degree of atomization and Congo red time, wherein Congo red test carries out at 200 DEG C, and testing result is shown in Table 1.
Table 1
Heat stabilization test
Heat stabilization test, including dynamic are carried out to calcium-zinc composite stabilizing agent prepared by Examples 1 to 6 and comparative example 1~7
And static heat stability, specific test result are shown in Table 2.
Wherein, the specific operation method is as follows for heat stabilization test:
Dynamic thermal stability test: after temperature on double roller plastic-making device is constant, 180 DEG C ± 1 DEG C is controlled, is weighed up in handle cup
Material stirring is uniform, mixes up stopwatch, then pours between two rollers material and carries out film-making, after material all forms on roller,
Sampling in every 5 minutes is a piece of, until roll banding.
Static heat stability test: by polyvinyl chloride resin, the mixing such as plasticizer and heat stabilizer, the film-making on double roller plastic-making device
(180 DEG C), control is with a thickness of 40mm, and full sheet pulls out after five minutes, lays flat cooling, is cut into 5 × 8cm piece, is divided into 6~8 groups, so
It is placed in ageing oven, takes one group within every 10 minutes, test its blackening time i.e. thermal aging time.
Table 2
Note: 1 represents white;2 represent it is pale yellow;3 represent sallow;4 represent it is black.
Obviously, above-described embodiment is only intended to clearly illustrate technical solution of the present invention example, and is not
Restriction to embodiments of the present invention.For those of ordinary skill in the art, on the basis of the above description also
It can make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.It is all
Made any modifications, equivalent replacements, and improvements etc. within the spirit and principles in the present invention should be included in right of the present invention and want
Within the protection scope asked.
Claims (9)
1. a kind of calcium-zinc composite stabilizing agent, which is characterized in that be made of the raw material of following mass percent:
Isooctyl acid: 10 ~ 30%,
Benzoic acid: 2 ~ 10%,
Zinc oxide: 0.5 ~ 4.2%,
Calcium oxide: 1.2 ~ 6.5%,
Nontoxic phosphite ester: 8 ~ 15%,
DINCH:20 ~ 35%,
ATBC:1 ~ 5%,
TXIB:0.1 ~ 3%,
Chloro methyl esters: 18 ~ 32%.
2. calcium-zinc composite stabilizing agent according to claim 1, which is characterized in that the zinc oxide is super fine zinc oxide, described
The average grain diameter of super fine zinc oxide is 30 ~ 80 nm.
3. calcium-zinc composite stabilizing agent according to claim 1, which is characterized in that the calcium oxide is ultra-fine calcium oxide, described
The average grain diameter of ultra-fine calcium oxide is 40 ~ 80 nm.
4. calcium-zinc composite stabilizing agent according to claim 1, which is characterized in that the nontoxic phosphite ester is phosphorous acid 4,4-
Two different fork bis-phenol (12~14) carbon Arrcostabs.
5. any one calcium-zinc composite stabilizing agent according to claim 1 ~ 4, which is characterized in that by the original of following mass percent
Material composition:
Isooctyl acid: 10 ~ 25%,
Benzoic acid: 4 ~ 8%,
Super fine zinc oxide: 0.5 ~ 3.5%,
Ultra-fine calcium oxide: 1.5 ~ 5%,
Nontoxic phosphite ester: 10 ~ 15%,
DINCH:24 ~ 30%,
ATBC:3 ~ 5%,
TXIB:0.5 ~ 2.5%,
Chloro methyl esters: 20 ~ 28%.
6. calcium-zinc composite stabilizing agent according to claim 5, which is characterized in that be made of the raw material of following mass percent:
Isooctyl acid: 20 ~ 25%,
Benzoic acid: 5 ~ 6%,
Super fine zinc oxide: 1 ~ 2%,
Ultra-fine calcium oxide: 4 ~ 5%,
Nontoxic phosphite ester: 12 ~ 15%,
DINCH:25 ~ 28%,
ATBC:4 ~ 5%,
TXIB:1 ~ 1.5%,
Chloro methyl esters: 24 ~ 26%.
7. the preparation method of any one calcium-zinc composite stabilizing agent according to claim 1 ~ 6, which is characterized in that including following step
It is rapid:
S1. isooctyl acid, benzoic acid, zinc oxide and calcium oxide are carried out being dehydrated into salt treatment by said ratio, produces to obtain respectively
Calcium salt and zinc salt;
S2. certain nontoxic phosphite ester, plasticizer and chloro methyl esters are added into the obtained calcium salt of step S1 and zinc salt, sufficiently stirs
It mixes to get the calcium-zinc composite stabilizing agent.
8. calcium-zinc composite stabilizing agent according to claim 7, which is characterized in that in step S1, the salt treatment that is dehydrated into
Technological parameter are as follows: reaction temperature is 100 ~ 120 DEG C, and the reaction time is 15 ~ 25 min.
9. according to claim 1 ~ 8 described in any item calcium-zinc composite stabilizing agents PVC paste shape resin ward off glue, leaching modeling processing or
Application in medical apparatus.