CN109776046A - A kind of low preparation process for playing enhanced type foam concrete - Google Patents
A kind of low preparation process for playing enhanced type foam concrete Download PDFInfo
- Publication number
- CN109776046A CN109776046A CN201910097608.3A CN201910097608A CN109776046A CN 109776046 A CN109776046 A CN 109776046A CN 201910097608 A CN201910097608 A CN 201910097608A CN 109776046 A CN109776046 A CN 109776046A
- Authority
- CN
- China
- Prior art keywords
- foam concrete
- cement
- preparation process
- polyurethane body
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of low preparation processes for playing enhanced type foam concrete, belong to foam concrete preparation technical field, a kind of low preparation process for playing enhanced type foam concrete, its preparation process is the following steps are included: active addition pre-processes, cement slurry preparation, frostproof froth n, foamed slurry mixing, scattered slurry is helped to mix, in foam and cement slurry mixed process, arc is added from scattered particle, and start ultrasonic High-frequency machine, make arc from scattered seed the dispersion mixing in cement slurry, the foaming effect of the foaming agent of enhancing foam concrete may be implemented, the foam generated is better dispersed with cement slurry to mix, it is formed after the content outflow in flexible polyurethane body set simultaneously and is coupled elastomer pipe, it is filled among foam concrete, as the connection object in foam concrete, by being coupled elastomer pipe Involve with ligament act on, enhance the toughness and integrality of foam concrete.
Description
Technical field
The present invention relates to foam concrete preparation technical fields, mixed more specifically to a kind of low bullet enhanced type foam
Coagulate the preparation process of soil.
Background technique
Foam concrete also known as lightweight concrete are by the foamed system of foaming machine that foaming agent is mechanically abundant
Foaming, and foam is uniformly mixed with cement slurry, cast-in-place construction or mold molding then are carried out by the pumping system of foaming machine,
A kind of novel light insulation material containing a large amount of sealed porositys is formed by through natural curing.It belongs to air bubble-shaped heat insulating material
Material, outstanding feature is to form closed foam hole in inside concrete, makes concrete light and thermal insulation separation thermalization;It is also simultaneously
A special kinds in air entrained concrete, its pore structure and material property all close to air entrained concrete, both theys'
Difference, the only difference between stomata shape and aerating means, air entrained concrete stomata is usually ellipse, and foam is mixed
Solidifying soil is influenced by pore effect, is deformed, and forming polyhedron air entrained concrete is to pass through chemistry using chemical gas generation
Reaction generates gas by inside and forms stomata, and lightweight concrete is then that first foaming agent is made up of the method for mechanical system bubble
Foam, then again by foam be added cement, magnesite, in calcium plaster, form foam slurry, then through natural curing steam curing and
At.
Existing foam concrete during the preparation process, needs repeatedly to be added foaming agent and generates foam, wait combination reaction
It is middle to generate a large amount of gas, so that slurry is generated a large amount of bubble, becomes foam concrete, this production method is to production equipment
It is more demanding, need staff rule of thumb to select the repeatedly time of addition foaming agent and dosage with response situation, to increase
The foaming effect of strong foaming agent, therefore be easy to cause shadow to foaming effect due to the difference of foaming agent additive amount and addition time
It rings, defect occurs so as to cause the foam concrete quality of final molding, simultaneously because foaming agent is added after slurry mixing
, after being added into slurry, easily coated by slurry, become dry powder block, can not with slurry dispersion mixing, thus can not be well
Foaming effect is played, therefore had both caused the waste of applied foam agent, also the quality of foam concrete after molding is caused not
Benefit influences.
Summary of the invention
1. technical problems to be solved
Aiming at the problems existing in the prior art, the purpose of the present invention is to provide a kind of low bullet enhanced type foam concrete
Preparation process, it may be implemented enhancing foam concrete foaming agent foaming effect, make generate foam and cement slurry
Mixing is better dispersed, while being formed after the content outflow in flexible polyurethane body set and being coupled elastomer pipe, filling
Among foam concrete, as the connection object in foam concrete, acted on by being coupled involving for elastomer pipe with ligament,
Enhance the toughness and integrality of foam concrete.
2. technical solution
To solve the above problems, the present invention adopts the following technical scheme that.
A kind of low preparation process for playing enhanced type foam concrete, its components include: foaming agent, portland cement,
Active addition, river sand, glass fibre, naphthalene sulfonate water-reducing agent, active silica, thickener, high-strength light coarse aggregate, height
Imitate water-reducing agent, water, mortar, normal sands and additive, preparation process the following steps are included:
Step 1: active addition pre-processes, river sand, glass fibre are sequentially added in blender, start blender,
Mix it uniformly, segmentation plus water in whipping process;
Step 2: prepared by cement slurry, in blender whipping process, silicate is added by preset blending ratio into blender
Cement, active addition, thickener;
Step 3: frostproof froth n, the foaming agent of preparation is added in cement foam maker using charging basket, control cement foamed
By plunger pump and air compressor machine foam is made in foaming agent by machine;
Step 4: foamed slurry mixes, cement slurry prepared by step 2 is added in cement foam maker, starts cement
It is stirred frame on foaming machine, foam is mixed by stirring into frame with cement slurry and is stirred;
Step 5: scattered slurry is helped to mix, in foam and cement slurry mixed process, addition arc is from particle is dissipated, again
Starting is stirred frame, and starts ultrasonic High-frequency machine, and making arc from scattered seed, the dispersion mixing in cement slurry, obtained mixing are steeped
Foam cement slurry may be implemented the foaming effect of the foaming agent of enhancing foam concrete, make the foam generated and cement slurry more
Dispersion mixing well, while being formed after the content outflow in flexible polyurethane body set and being coupled elastomer pipe, it is filled in
Among foam concrete, as the connection object in foam concrete, is acted on, increased with ligament by being coupled involving for elastomer pipe
The toughness and integrality of strong foam concrete.
Further, the step 5 help scattered slurry mix in the arc mentioned from scattered seed include flexible polyurethane body
Set and porous masses particle, flexible polyurethane body set two is dug there are four leaking hole from dissipating endoplasm up and down, described more
Screen mesh particle is located in flexible polyurethane body set, described to heat packaging plastic, the hot melt from dissipating endoplasm and leak to be equipped in hole
It is filled with metal microplate in packaging plastic, the hot melt packaging plastic matches with from scattered endoplasm hole of leaking, and hot melt packaging plastic both ends
It is fixedly connected with from dissipating the endoplasm hole inner wall that leaks, and forms closed structure with flexible polyurethane body set, it is mixed convenient for enhancing foam
The foaming effect for coagulating the foaming agent of soil better disperses the foam generated with cement slurry and mixes.
Further, filled with mixed liquid solute is dispersed in the flexible polyurethane body set, the porous masses particle exists
Flexible polyurethane body is uniformly distributed in covering with the mixed liquid solute of dispersion, and porous masses particles coat mixes in liquid solute in dispersion,
Convenient for making the sizing distribution in flexible polyurethane body covers of porous masses particle, porous masses particle is reduced in flexible polyurethane bullet
The case where being gathered at one in body set generation.
Further, multiple dispersing agent concentrated granulars, the dispersing agent are also filled in the flexible polyurethane body set
Concentrated granular is uniformly distributed in flexible polyurethane body set, and the dispersing agent concentrated granular is same in flexible polyurethane body set
Sample is uniformly mixed with mixed liquid solute is dispersed, dispersing agent concentrated granular in foam and cement mortar mixed process, convenient for foam with
Cement mortar dispersion mixing.
Further, digging in the porous masses particle has fine and closely woven sieve pore, and the fine and closely woven sieve pore is in porous masses particle
Upper uniformly arrangement, convenient for making porous masses particle in flexible polyurethane body covers after outflow, using its porous structural super
It is shaken under the action of sound High-frequency machine, from fine foam is generated, increases the foam volume in foam concrete, promote foam concrete
Porous structure, to enhance the quality of foam concrete.
Further, be filled with multiple nano metal powders in the fine and closely woven sieve pore, multiple nano metal powders with
Porous masses particles stick increases the foam volume of generation convenient for shaking porous masses particle under the action of ultrasonic High-frequency machine.
Further, in the step 1 active addition preprocessing process, river sand, glass fibre is sequentially added and stirred
After mixing machine, then naphthalene sulfonate water-reducing agent and active silica are added into blender, convenient for enhancing the cement mortar prepared
Viscosity.
Further, the specification of the glass fibre is length between 12 to 20 millimeters.
Further, the active silica is diatomite of the partial size less than 25 microns, and the cement is compound
Portland cement.
Further, the ternary polymerization formed in the flexible polyurethane body set mixed with acrylonitrile, butadiene, styrene
Object convenient for the elasticity of enhancing flexible polyurethane body set, while restoring former after the content outflow for covering flexible polyurethane body
Shape.
3. beneficial effect
Compared with the prior art, the present invention has the advantages that
(1) foaming effect of the foaming agent of enhancing foam concrete may be implemented in this programme, makes the foam and cement generated
Slurry better disperses mixing, while being formed after the content outflow in flexible polyurethane body set and being coupled elastomer pipe,
Be filled among foam concrete, as the connection object in foam concrete, by be coupled elastomer pipe involve and ligament
Effect, enhances the toughness and integrality of foam concrete.
(2) flexible polyurethane body set makes the foam generated convenient for the foaming effect of the foaming agent of enhancing foam concrete
It better disperses and mixes with cement slurry.
(3) filled with mixed liquid solute is dispersed in flexible polyurethane body set, porous masses particle is in flexible polyurethane body
It is uniformly distributed in covering with the mixed liquid solute of dispersion, and porous masses particles coat mixes in liquid solute in dispersion, convenient for making porous masses
Particle sizing distribution in flexible polyurethane body covers reduces porous masses particle and is gathered in one in flexible polyurethane body set
The case where place, occurs.
(4) multiple dispersing agent concentrated granulars are also filled in flexible polyurethane body set, dispersing agent concentrated granular is in toughness
It is uniformly distributed in polyurethane body set, dispersing agent concentrated granular is equally equal with the mixed liquid solute of dispersion in flexible polyurethane body set
Even mixing, dispersing agent concentrated granular is in foam and cement mortar mixed process, convenient for foam and cement mortar dispersion mixing.
(5) digging in porous masses particle has fine and closely woven sieve pore, and fine and closely woven sieve pore is uniformly arranged on porous masses particle, is convenient for
Make porous masses particle in flexible polyurethane body covers after outflow, using its porous structural under the action of ultrasonic High-frequency machine
Concussion increases the foam volume in foam concrete, the porous structure of foam concrete is promoted, to increase from fine foam is generated
The quality of strong foam concrete.
(6) multiple nano metal powders are filled in fine and closely woven sieve pore, multiple nano metal powders and porous masses particle are viscous
It connects, convenient for shaking porous masses particle under the action of ultrasonic High-frequency machine, increases the foam volume of generation.
(7) in step 1 active addition preprocessing process, after river sand, glass fibre are sequentially added blender, then
Naphthalene sulfonate water-reducing agent and active silica are added, into blender convenient for the viscosity of the cement mortar of enhancing preparation.
(8) terpolymer formed in flexible polyurethane body set mixed with acrylonitrile, butadiene, styrene, convenient for increasing
The elasticity of obdurability polyurethane body set, while resiling after the content outflow for covering flexible polyurethane body.
Detailed description of the invention
Fig. 1 is broad flow diagram of the invention;
Fig. 2 is sectional view of the arc of the present invention from scattered particle fraction;
Fig. 3 is the structural schematic diagram in Fig. 2 at A;
Fig. 4 is the structural schematic diagram of porous masses particle of the present invention part;
Fig. 5 is the structural schematic diagram that the present invention is coupled elastomer tube portion.
Figure label explanation:
1 arc from dissipate particle, 2 flexible polyurethane body sets, 3 from dissipate endoplasms leak hole, 4 hot melt packaging plastics, 5 disperse mixed liquid
Solute, 6 porous masses particles, 7 dispersing agent concentrated granulars, 8 nano metal powders, 9 are coupled elastomer pipe.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description;Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments, is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
In the description of the present invention, it should be noted that the instruction such as term " on ", "lower", "inner", "outside", " top/bottom end "
Orientation or positional relationship be based on the orientation or positional relationship shown in the drawings, be merely for convenience of description the present invention and simplification retouch
It states, rather than the device or element of indication or suggestion meaning must have a particular orientation, be constructed and operated in a specific orientation,
Therefore it is not considered as limiting the invention.In addition, term " first ", " second " are used for description purposes only, and cannot understand
For indication or suggestion relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " installation " " is set
Be equipped with ", " be arranged/connect ", " connection " etc., shall be understood in a broad sense, such as " connection ", may be a fixed connection, be also possible to removable
Connection is unloaded, or is integrally connected, can be mechanical connection, is also possible to be electrically connected, can be directly connected, it can also be in
Between medium be indirectly connected, can be the connection inside two elements, for the ordinary skill in the art, can be specific
Situation understands the concrete meaning of above-mentioned term in the present invention.
Embodiment 1:
Referring to Fig. 1, a kind of low preparation process for playing enhanced type foam concrete, its components include: foaming agent, silicon
It is acid salt cement, active addition, river sand, glass fibre, naphthalene sulfonate water-reducing agent, active silica, thickener, high-strength light
Coarse aggregate, high efficiency water reducing agent, water, mortar, normal sands and additive, preparation process the following steps are included:
Step 1: active addition pre-processes, river sand, glass fibre are sequentially added in blender, start blender,
It mixes it uniformly, then adds naphthalene sulfonate water-reducing agent and active silica into blender, convenient for the cement of enhancing preparation
The viscosity of mortar, active silica are diatomite of the partial size less than 25 microns, and cement is composite Portland cement, stirring
Segmentation plus water in the process, the specification of glass fibre are length between 12 to 20 millimeters;
Step 2: prepared by cement slurry, in blender whipping process, silicate is added by preset blending ratio into blender
Cement, active addition, thickener;
Step 3: frostproof froth n, the foaming agent of preparation is added in cement foam maker using charging basket, control cement foamed
By plunger pump and air compressor machine foam is made in foaming agent by machine;
Step 4: foamed slurry mixes, cement slurry prepared by step 2 is added in cement foam maker, starts cement
It is stirred frame on foaming machine, foam is mixed by stirring into frame with cement slurry and is stirred;
Step 5: scattered slurry is helped to mix, in foam and cement slurry mixed process, addition arc is from particle is dissipated, again
Starting is stirred frame, and starts ultrasonic High-frequency machine, and making arc from scattered seed, the dispersion mixing in cement slurry, obtained mixing are steeped
Foam cement slurry.
Referring to Fig. 2, step 5 helps the arc mentioned in scattered slurry mixing to include flexible polyurethane body set from scattered seed 1
2 and porous masses particle 6, flexible polyurethane body set about 2 two is dug there are four leaking hole 3 from scattered endoplasm, porous masses
Particle 6 is located in flexible polyurethane body set 2, and leaking from scattered endoplasm, hole 3 is interior to be equipped with hot melt packaging plastic 4, heats and fills out in packaging plastic 4
Filled with metal microplate, heat packaging plastic 4 and match from dissipating endoplasm hole 3 of leaking, and heat 4 both ends of packaging plastic with from outside scattered endoplasm
It lets out 3 inner wall of hole to be fixedly connected, and forms closed structure with flexible polyurethane body set 2, in ultrasonic High-frequency machine to arc from scattered
When grain 1 emits ultrasonic high-frequency signal, the nano metal powder 8 on porous masses particle 6 is under the effect of ultrasonic high-frequency signal, hot melt
Metal microplate fever in packaging plastic 4 makes to heat packaging plastic 4 and cover in flexible polyurethane body to melt on 2, the toughness of torsional deformation
Polyurethane body set 2 restores to the original state after hot melt packaging plastic 4 melts, and flexible polyurethane body is covered the porous masses in 2
Grain 6 and dispersing agent concentrated granular 7 from from dissipate endoplasm leak hole 3 pop-up, the moving process in cement mortar of porous masses particle 6
In, the nano metal powder 8 on porous masses particle 6 shakes under the effect of ultrasonic high-frequency signal, passes through porous masses particle 6
Porous structural generates foam during vibration, and the dispersing agent of dispersing agent concentrated granular 7 is scattered in cement mortar after pop-up
Between foam, enhance the mixing of foam and cement mortar, convenient for the foaming effect of the foaming agent of enhancing foam concrete, makes to give birth to
At foam better disperse and mix with cement slurry, after the content outflow in flexible polyurethane body set 2, formed and be coupled bullet
Property fibre pipe 9, be coupled elastomer pipe 9 be filled among foam concrete, as the connection object in foam concrete, pass through connection
Involving for knot elastomer pipe is acted on ligament, enhances the toughness and integrality of foam concrete.
Referring to Fig. 2, porous masses particle 6 is in toughness filled with mixed liquid solute 5 is dispersed in flexible polyurethane body set 2
It is uniformly distributed in polyurethane body set 2 with the mixed liquid solute 5 of dispersion, and porous masses particle 6 is coated in the mixed liquid solute 5 of dispersion,
It is distributed convenient for making porous masses particle 6 be formed in flexible polyurethane body set 2, reduces porous masses particle 6 in the poly- ammonia of toughness
The case where being gathered at one in ester body set 2 generation.
Referring to Fig. 2, multiple dispersing agent concentrated granulars 7 are also filled in flexible polyurethane body set 2, dispersing agent concentration
Grain 7 flexible polyurethane body set 2 in is uniformly distributed, dispersing agent concentrated granular 7 flexible polyurethane body set 2 in equally with point
The mixed uniformly mixing of liquid solute 5 is dissipated, dispersing agent concentrated granular 7 is convenient for foam and cement in foam and cement mortar mixed process
Mortar dispersion mixing, the interior terpolymer formed mixed with acrylonitrile, butadiene, styrene of flexible polyurethane body set 2, is convenient for
Enhance the elasticity of flexible polyurethane body set 2, while resiling after making the content outflow of flexible polyurethane body set 2.
Referring to Fig. 4, digging in porous masses particle 6 has fine and closely woven sieve pore, fine and closely woven sieve pore is uniform on porous masses particle 6
Arrangement, after making porous masses particle 6 outflow in flexible polyurethane body set 2, using its porous structural ultrasonic high
It is shaken under the action of frequency machine, from fine foam is generated, increases the foam volume in foam concrete, promote the porous of foam concrete
Structure is filled with multiple nano metal powders 8, multiple nano metals to enhance the quality of foam concrete in fine and closely woven sieve pore
Powder 8 is Nian Jie with porous masses particle 6, convenient for shaking porous masses particle 6 under the action of ultrasonic High-frequency machine, increases and generates
Foam volume.
The present invention enhances the foaming effect of the foaming agent of foam concrete, divides the foam generated preferably with cement slurry
Mixing is dissipated, after the content outflow in flexible polyurethane body set 2, is formed and is coupled elastomer pipe 9, be coupled elastomer pipe 9
Be filled among foam concrete, as the connection object in foam concrete, by be coupled elastomer pipe involve and ligament
Effect, enhances the toughness and integrality of foam concrete.
The foregoing is intended to be a preferred embodiment of the present invention;But scope of protection of the present invention is not limited thereto.
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
It improves design and is subject to equivalent substitution or change, should be covered by the scope of protection of the present invention.
Claims (10)
1. a kind of low preparation process for playing enhanced type foam concrete, it is characterised in that: its components include: foaming agent, silicon
Acid salt cement, river sand, glass fibre, naphthalene sulfonate water-reducing agent, active silica, thickener, efficiently subtracts active addition
Aqua, water, normal sands and additive, preparation process the following steps are included:
Step 1: active addition pre-processes, river sand, glass fibre are sequentially added in blender, starts blender, makes it
It uniformly mixes, segmentation plus water in whipping process;
Step 2: prepared by cement slurry, in blender whipping process, silicate cement is added by preset blending ratio into blender
Mud, active addition, propylene class organic thickening agent;
Step 3: frostproof froth n, the foaming agent of preparation is added in cement foam maker using charging basket, cement foam maker is controlled,
Foam is made in foaming agent by plunger pump and air compressor machine;
Step 4: foamed slurry mixes, cement slurry prepared by step 2 is added in cement foam maker, is started cement foamed
It is stirred frame on machine, foam is mixed by stirring into frame with cement slurry and is stirred;
Step 5: scattered slurry is helped to mix, in foam and cement slurry mixed process, addition arc is again started up from particle is dissipated
Be stirred frame, and start ultrasonic High-frequency machine, make arc from scattered seed the dispersion mixing in cement slurry, be made mix-froth water
Material-mud.
2. the low preparation process for playing enhanced type foam concrete of one kind according to claim 1, it is characterised in that: the step
Rapid five help scattered slurry mix in the arc mentioned from scattered seed (1) include flexible polyurethane body set (2) and porous masses particle
(6), the flexible polyurethane body set (2) up and down two dig there are four from dissipate endoplasm leak hole (3), the porous masses
Grain (6) is located in flexible polyurethane body set (2), described to heat packaging plastic (4) from dissipating endoplasm and leak to be equipped in hole (3), described
It heats and is filled with metal microplate in packaging plastic (4), the hot melt packaging plastic (4) matches with from scattered endoplasm hole (3) of leaking, and hot
Molten packaging plastic (4) both ends are fixedly connected with from dissipating endoplasm hole (3) inner wall that leaks, and close with flexible polyurethane body set (2) formation
Close structure.
3. the low preparation process for playing enhanced type foam concrete of one kind according to claim 2, it is characterised in that: described tough
Property polyurethane body set (2) in filled with mixed liquid solute (5) are dispersed, the porous masses particle (6) is in flexible polyurethane body
It is uniformly distributed in set (2) with dispersion mixed liquid solute (5), and porous masses particle (6) is coated in dispersion mixed liquid solute (5).
4. the low preparation process for playing enhanced type foam concrete of one kind according to claim 2, it is characterised in that: described tough
Property polyurethane body set (2) in be also filled with multiple dispersing agent concentrated granulars (7), the dispersing agent concentrated granular (7) is in toughness
Is uniformly distributed in polyurethane body set (2), the dispersing agent concentrated granular (7) in flexible polyurethane body set (2) equally with
Disperse mixed liquid solute (5) uniformly to mix.
5. the low preparation process for playing enhanced type foam concrete of one kind according to claim 2, it is characterised in that: described more
Digging in screen mesh particle (6) has fine and closely woven sieve pore, and the fine and closely woven sieve pore is uniformly arranged on porous masses particle (6).
6. the low preparation process for playing enhanced type foam concrete of one kind according to claim 5, it is characterised in that: described thin
Multiple nano metal powders (8) are filled in close sieve pore, multiple nano metal powders (8) and porous masses particle (6) are viscous
It connects.
7. the low preparation process for playing enhanced type foam concrete of one kind according to claim 1, it is characterised in that: the step
In rapid active addition preprocessing process, after river sand, glass fibre are sequentially added blender, then add into blender
Naphthalene sulfonate water-reducing agent and active silica.
8. the low preparation process for playing enhanced type foam concrete of one kind according to claim 1, it is characterised in that: the glass
The specification of glass fiber is length between 12 to 20 millimeters.
9. the low preparation process for playing enhanced type foam concrete of one kind according to claim 7, it is characterised in that: the work
Property silica be diatomite of the partial size less than 25 microns, the cement be composite Portland cement.
10. the low preparation process for playing enhanced type foam concrete of one kind according to claim 2, it is characterised in that: described
The terpolymer formed in flexible polyurethane body set (2) mixed with acrylonitrile, butadiene, styrene.