CN109763607A - A kind of waterproof and breathable antibacterial, heat insulating film - Google Patents
A kind of waterproof and breathable antibacterial, heat insulating film Download PDFInfo
- Publication number
- CN109763607A CN109763607A CN201811599623.XA CN201811599623A CN109763607A CN 109763607 A CN109763607 A CN 109763607A CN 201811599623 A CN201811599623 A CN 201811599623A CN 109763607 A CN109763607 A CN 109763607A
- Authority
- CN
- China
- Prior art keywords
- layer
- waterproof
- aluminium film
- film
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of waterproof and breathable antibacterial, heat insulating films, including protective layer, reflecting layer, macromolecule layer, the enhancement layer being combined from top to bottom；The protective layer uses compound nonwoven cloth；The reflecting layer includes netted aluminium film, cladding medium, the longitudinal aluminium film twine width with transverse direction of netted aluminium film is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium film is with a thickness of 0.5-1 μm, and the cladding medium uses PET polyester；The macromolecule layer includes high molecular weight ptfe (PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, all contain nano silver antimicrobials in high molecular weight ptfe (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the Graphene antibiosis film content accounts for the 40% of macromolecule layer quality, and nanometer silver antimicrobial agent content accounts for the 2%-5% of macromolecule layer quality；The enhancement layer uses PE continuous yarn non-woven fabrics.The waterproof and breathable antibacterial, heat insulating film of the application has good waterproof and breathable heat-insulated and antibacterial functions, and energy-saving effect is suitble to promote remarkably.
Description
Technical field
The present invention relates to Archtectural Coatings technical field more particularly to a kind of waterproof and breathable antibacterial, heat insulating films.
Background technique
In the 1940s, the building scholar discovery of Germany, the tack of asphalt water-proof coiled material and coating film waterproof material with
Airtightness feature causes the residual moisture in concrete structure to be closed in structure, and the steam in concrete structure can not dissipate
It sends out and leads to roofing and wall mould growth, indoor air quality and people's health in residential environment are seriously threatened.Therefore, German construction circle
Begin to use the roof padding with permeability, to replace self-adhesive coiled material and coating waterproofing, this gas permeability bed course sky is laid on
It on roof-base, emits the steam of cast-in-place concrete roof plate rapidly, thus avoids the growth of mould.Waterproof is saturating
Air film scheme is widelyd popularize in European and American developed countries, is widely used in residential architecture and utilities building, waterproof ventilated membrane
Architectural construction is known as " house that can be breathed ".Waterproof ventilated membrane is layed on insulating layer, effective protection insulating layer, insulating layer
On do not need to pour pea gravel concreten again, the optimization of scheme reduces construction cost.The country such as Japan, Malaysia also draws in succession
Into the technology of Germany, the U.S., starts mass production and apply waterproof ventilated membrane.
Under historical background at that time, people to the understanding of building energy conservation not enough, in the 1970s, with world's energy
The outburst of source crisis, American-European countries increasingly pay attention to Building Energy-saving.Energy expert's discovery, this gas permeability bed course
Although the steam of cast-in-place concrete roof is enable to discharge, moisture-proof and mould problems are efficiently solved, however summer tile roofing temperature
After degree increases, a large amount of radiant heat, which enter the room, causes constant temperature to rise, and like a hen on a hot girdle with living environment, people are for a long time for work
It relies on room conditioning to cool down, however roofing constantly absorbs radiations heat energy and air-conditioning equipment must be in for a long time
High power operation increases energy consumption.
In order to solve the problems, such as roof insulation, thermal isolation film starts to be widely used on roofing.It is big that thermal isolation film generally can be divided into two
Class, one kind are metallic reflection thermal isolation films, and one kind is full dielectric reflective insulation film.In addition, there are also the gold that the two is combined
Belong to dielectric reflective insulation film.Common metal all has biggish extinction coefficient, when light beam by air incidence to metal surface when,
Decay rapidly into intrametallic light amplitude, so that the luminous energy into metal inside is accordingly reduced, and reflected light can increase.Delustring
Coefficient is bigger, and light amplitude decaying is rapider, and the luminous energy into metal inside is fewer, and reflectivity is higher.People always select spectrum
Those of number is larger, and optical property is more stable metal is as metal membrane material.In ultra-violet (UV) band, common metal thin material is aluminium,
Visible region often uses aluminium and silver, often uses gold, silver and copper in infrared region, in addition, chromium and platinum also often make the coating materials of some specialty films.
The round (thermal isolation film is not added) of thermal energy: the sun --- infrared magnetic wave --- thermal energy, which hits tile, makes temperature liter
It is high that --- tile becomes heat source and radiates thermal energy --- thermal energy hits cast-in-site roof and elevates the temperature --- cast-in-site roof becomes heat
Radiating thermal energy in source --- indoor environment temperature persistently increases；Thermal energy round (adds thermal isolation film): the sun --- infrared ray magnetic
--- thermal energy hits tile and elevates the temperature --- tile becomes heat source and radiates thermal energy ---, and thermal energy hits aluminium foil makes surface to wave
Temperature increases --- aluminium foil emissivity is extremely low, radiates a small amount of thermal energy --- the indoor comfortable environment temperature of holding, lower environment
Temperature reduces the burden of room conditioning to which the energy be greatly saved.
However roofing will not only have good heat insulation and moisture-proof ability because it is in special position, also guarantee to incite somebody to action
The steam of pouring concrete roof boarding emits rapidly, to avoid condensation vapor.
Summary of the invention
To overcome the problems, such as that roof insulation overlay film gas permeability existing in the prior art is bad, the present invention provides a kind of waterproofs
Air-permeable anti-bacterial thermal isolation film.
A kind of waterproof and breathable antibacterial, heat insulating film, including be combined from top to bottom protective layer, reflecting layer, macromolecule layer,
Enhancement layer；The protective layer uses compound nonwoven cloth；The reflecting layer includes netted aluminium film, cladding medium, the netted aluminium film
Longitudinal aluminium film twine width with transverse direction is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium film thickness
It is 0.5-1 μm, the cladding medium uses PET polyester；The macromolecule layer includes high molecular weight ptfe (PTFE) anti-
Water ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, the polyphosphazene polymer tetrafluoro
All contain nano silver antimicrobials in ethylene (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the Graphene antibiosis film content accounts for
The 40% of macromolecule layer quality, nanometer silver antimicrobial agent content account for the 2%-5% of macromolecule layer quality；The enhancement layer uses PE
Continuous yarn non-woven fabrics.
In a preferred embodiment, the compound nonwoven cloth that the protective layer 1 uses, including upper layer polypropylene fibre silk fiber
Non-woven fabrics, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
In a preferred embodiment, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 50-70 μm, polypropylene non-woven fabric
With a thickness of 20-40 μm.
In a preferred embodiment, for the polypropylene fiber silk fabric nonwoven cloth with a thickness of 60 μm, polypropylene non-woven fabric is thick
Degree is 30 μm；The polypropylene fiber silk fabric nonwoven cloth and polypropylene non-woven fabric aperture are 20-30 μm, are all made of transparent material manufacture.
In a preferred embodiment, the cladding medium is uniformly to be wrapped PET polyester material using spray process
It overlays in netted aluminium film, the PET polyester material will not block the hole in netted aluminium film.
In a preferred embodiment, the cladding medium average thickness is 0.3-0.6 μm.
In a preferred embodiment, the longitudinal aluminium film twine width with transverse direction of the netted aluminium film is 15mm, often
The spacing distance of the vertical/horizontal aluminium film twine of item is 4mm, aluminium film with a thickness of 1 μm.
In a preferred embodiment, the macromolecule layer is with a thickness of 30-50 μm.
In a preferred embodiment, the PE continuous yarn non-woven fabrics are 0.7mm average fiber length below and tool
There is the fiber of the hydrauture of 10mL/g or more to constitute.
In a preferred embodiment, protective layer 1, reflecting layer 2, macromolecule layer 3, enhancement layer 4 pass through point type hot pressing
It is combined.
Compared with prior art, the beneficial effects of the present invention are:
(1) a kind of waterproof and breathable antibacterial, heat insulating film of the invention, the compound nonwoven cloth that protective layer uses, including upper layer third
Synthetic fibre silk fiber non-woven fabrics, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.Wearability with higher and good
Tensile strength improves the service life of this product.
(2) a kind of waterproof and breathable antibacterial, heat insulating film of the invention, protective layer, reflecting layer, macromolecule layer, enhancement layer use point
Formula hot pressing combination process blocks air hole so as to avoid adhesives such as hot melt adhesive, substantially increases high molecular weight ptfe
(PTFE) air penetrability of waterproof ventilated membrane.
(3) a kind of waterproof and breathable antibacterial, heat insulating film of the invention, has roof insulation film by way of composite membrane
The function of waterproof and breathable, conventional construction method are to cover metallic reflection above after the construction of common waterproof ventilated membrane
Thermal isolation film, and it is spaced apart spacer block therebetween to generate gap conducive to steam diffusion, traditional construction process is many and diverse, low efficiency
Under；Waterproof and breathable antibacterial, heat insulating film of the invention has both the performance of waterproof and breathable and roof insulation simultaneously, only needs once-paving i.e.
Can, substantially increase construction efficiency.
(4) macromolecule layer of the invention uses high molecular weight ptfe (PTFE) waterproof ventilated membrane and Graphene antibiosis film
Double-layer structure adds nano silver antimicrobials, improves the sterilizing ability of the organic thermal isolation film of waterproof and breathable, keep waterproof and breathable heat-insulated
Film has better disinfection effect.
Specific embodiment
With reference to embodiments, the present invention will be described in further detail.It should be appreciated that specific reality described herein
Example is applied only to explain the present invention, is not intended to limit the present invention.
Embodiment one:
A kind of waterproof and breathable antibacterial, heat insulating film: including be combined from top to bottom protective layer 1, reflecting layer 2, macromolecule layer
3, enhancement layer 4；The protective layer 1 uses compound nonwoven cloth；The reflecting layer 2 includes netted aluminium film, coats medium, described netted
The longitudinal aluminium film twine width with transverse direction of aluminium film is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium
Film thickness is 0.5-1 μm, and the cladding medium uses PET polyester layer；The macromolecule layer 3 includes high molecular weight ptfe
(PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, the high score
All contain nano silver antimicrobials in sub- polytetrafluoroethylene (PTFE) (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the graphene is anti-
Mycoderm content accounts for the 40% of 3 mass of macromolecule layer, and nanometer silver antimicrobial agent content accounts for the 2%-5% of 3 mass of macromolecule layer；The increasing
Strong layer 4 uses PE continuous yarn non-woven fabrics.
In some embodiments, the netted aluminium film in the reflecting layer can be replaced using punching aluminium film, punch aluminum dipping form
With a thickness of 0.5-1 μm, aperture 0.1-0.5mm, perforated area ratio is 50%-55%.
In some embodiments, the compound nonwoven cloth that the protective layer 1 uses, including upper layer polypropylene fiber silk fiber non-woven
Cloth, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 50-70 μm, polypropylene non-woven fabric with a thickness of
20-40μm。
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μ
m；The polypropylene fiber silk fabric nonwoven cloth and polypropylene non-woven fabric aperture are 20-30 μm, are all made of transparent material manufacture.
In some embodiments, the cladding medium is that PET polyester material is uniformly coated on net using spray process
In shape aluminium film, the PET polyester material will not block the hole in netted aluminium film 5.
In some embodiments, the cladding medium average thickness is 0.3-0.6 μm.
In some embodiments, the netted aluminium film it is longitudinal be with lateral aluminium film twine width 15mm, every it is vertical/horizontal
The spacing distance of aluminium film twine is 4mm, aluminium film with a thickness of 1 μm.
In some embodiments, the macromolecule layer is with a thickness of 30-50 μm, the high molecular weight ptfe
(PTFE) waterproof ventilated membrane be as tetrafluoroethene it is aggregated made of high-molecular compound, there is excellent chemical stability, resistance to
Corrosivity, sealing property, high lubrication, non-stickiness, electrical insulation and good anti-aging endurance, heatproof are excellent, and corrosion resistance is to work as
Modern one of corrosion resistance optimal material in the world is resistant to all other chemicals, in king in addition to molten metal sodium and liquid fluorine
It boils in water and does not also change, be widely used in the antiacid alkali of various needs and organic solvent.Described waterproof ventilated membrane itself is to people
One of the raw material for not having toxicity, but using in process of production perfluorooctanoic acid is deemed likely to carcinogenesis.Graphite
Alkene film and nano silver can effectively inhibit the growth of bacterium.
In some embodiments, the PE continuous yarn non-woven fabrics are 0.7mm average fiber lengths below and have 10mL/
The fiber of the hydrauture of g or more is constituted.
Embodiment two:
A kind of waterproof and breathable antibacterial, heat insulating film, including be combined from top to bottom protective layer 1, reflecting layer 2, macromolecule layer
3, enhancement layer 4；The protective layer 1 uses compound nonwoven cloth；The reflecting layer 2 includes netted aluminium film, coats medium, described netted
The longitudinal aluminium film twine width with transverse direction of aluminium film is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium
Film thickness is 0.5-1 μm, and the cladding medium uses PET polyester layer；The macromolecule layer 3 includes high molecular weight ptfe
(PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, the high score
All contain nano silver antimicrobials in sub- polytetrafluoroethylene (PTFE) (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the graphene is anti-
Mycoderm content accounts for the 40% of 3 mass of macromolecule layer, and nanometer silver antimicrobial agent content accounts for the 3% of 3 mass of macromolecule layer；The enhancement layer
4 use PE continuous yarn non-woven fabrics.
In some embodiments, the netted aluminium film in the reflecting layer can be replaced using punching aluminium film, punch aluminum dipping form
With a thickness of 0.5 μm, aperture 0.1mm, perforated area ratio is 50%.
In some embodiments, the compound nonwoven cloth that the protective layer 1 uses, including upper layer polypropylene fiber silk fiber non-woven
Cloth, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 50 μm, and polypropylene non-woven fabric is with a thickness of 20 μ
m。
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μ
m；The polypropylene fiber silk fabric nonwoven cloth and polypropylene non-woven fabric aperture are 20 μm, are all made of transparent material manufacture.
In some embodiments, the cladding medium is that PET polyester material is uniformly coated on net using spray process
In shape aluminium film, the PET polyester material will not block the hole in netted aluminium film 5.
In some embodiments, the cladding medium average thickness is 0.3 μm.
In some embodiments, the netted aluminium film it is longitudinal be with lateral aluminium film twine width 15mm, every it is vertical/horizontal
The spacing distance of aluminium film twine is 4mm, aluminium film with a thickness of 1 μm.
In some embodiments, the macromolecule layer is with a thickness of 30 μm.
In some embodiments, the PE continuous yarn non-woven fabrics are 0.7mm average fiber lengths below and have 10mL/
The fiber of the hydrauture of g or more is constituted.
It is compared using product made from this product and other similar products and actually detected obtains lower example conclusion:
1, anticorrosive 1.1 times of effect promotion, 2,1.3 times of anti-oxidation efficacy promotion, 3,1.5 times of wear-resistant effect promotion, 4,
1.6 times of improved thermo stability, 5,2 times of thermal insulation promotion, 6,1.1 times of waterproofness promotion, 7,1.3 times of gas permeability promotion.
Embodiment three:
A kind of waterproof and breathable antibacterial, heat insulating film, including be combined from top to bottom protective layer 1, reflecting layer 2, macromolecule layer
3, enhancement layer 4；The protective layer 1 uses compound nonwoven cloth；The reflecting layer 2 includes netted aluminium film, coats medium, described netted
The longitudinal aluminium film twine width with transverse direction of aluminium film is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium film
With a thickness of 0.5-1 μm, the cladding medium uses PET polyester layer；The macromolecule layer 3 includes high molecular weight ptfe
(PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, the high score
All contain nano silver antimicrobials in sub- polytetrafluoroethylene (PTFE) (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the graphene is anti-
Mycoderm content accounts for the 40% of 3 mass of macromolecule layer, and nanometer silver antimicrobial agent content accounts for the 4% of 3 mass of macromolecule layer；The enhancement layer
4 use PE continuous yarn non-woven fabrics.
In some embodiments, the netted aluminium film in the reflecting layer can be replaced using punching aluminium film, punch aluminum dipping form
With a thickness of 0.75 μm, aperture 0.75mm, perforated area ratio is 52.5%.
In some embodiments, the compound nonwoven cloth that the protective layer 1 uses, including upper layer polypropylene fiber silk fiber non-woven
Cloth, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μ
m。
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μ
m；The polypropylene fiber silk fabric nonwoven cloth and polypropylene non-woven fabric aperture are 25 μm, are all made of transparent material manufacture.
In some embodiments, the cladding medium is that PET polyester material is uniformly coated on net using spray process
In shape aluminium film, the PET polyester material will not block the hole in netted aluminium film 5.
In some embodiments, the cladding medium average thickness is 0.45 μm.
In some embodiments, the netted aluminium film it is longitudinal be with lateral aluminium film twine width 15mm, every it is vertical/horizontal
The spacing distance of aluminium film twine is 4mm, aluminium film with a thickness of 1 μm.
In some embodiments, the macromolecule layer is with a thickness of 40 μm.
In some embodiments, the PE continuous yarn non-woven fabrics are 0.7mm average fiber lengths below and have 10mL/
The fiber of the hydrauture of g or more is constituted.
It is compared using product made from this product and other similar products and actually detected obtains lower example conclusion:
1, anticorrosive 1.2 times of effect promotion, 2,1.4 times of anti-oxidation efficacy promotion, 3,1.6 times of wear-resistant effect promotion, 4,
1.7 times of improved thermo stability, 5,2.1 times of thermal insulation promotion, 6,1.2 times of waterproofness promotion, 7,1.4 times of gas permeability promotion.
Example IV:
A kind of waterproof and breathable antibacterial, heat insulating film, including be combined from top to bottom protective layer 1, reflecting layer 2, macromolecule layer
3, enhancement layer 4；The protective layer 1 uses compound nonwoven cloth；The reflecting layer 2 includes netted aluminium film, coats medium, described netted
The longitudinal aluminium film twine width with transverse direction of aluminium film is 10-15mm, the spacing distance of every vertical/horizontal aluminium film twine is 3-5mm, aluminium
Film thickness is 0.5-1 μm, and the cladding medium uses PET polyester layer；The macromolecule layer 3 includes high molecular weight ptfe
(PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers of spaced staggered weave in, the high score
All contain nano silver antimicrobials in sub- polytetrafluoroethylene (PTFE) (PTFE) waterproof ventilated membrane and Graphene antibiosis film, the graphene is anti-
Mycoderm content accounts for the 40% of 3 mass of macromolecule layer, and nanometer silver antimicrobial agent content accounts for the 5% of 3 mass of macromolecule layer；The enhancement layer
4 use PE continuous yarn non-woven fabrics.
In some embodiments, the netted aluminium film in the reflecting layer can be replaced using punching aluminium film, punch aluminum dipping form
With a thickness of 1 μm, aperture 0.5mm, perforated area ratio is 55%.
In some embodiments, the compound nonwoven cloth that the protective layer 1 uses, including upper layer polypropylene fiber silk fiber non-woven
Cloth, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 70 μm, and polypropylene non-woven fabric is with a thickness of 40 μ
m。
In some embodiments, the polypropylene fiber silk fabric nonwoven cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μ
m；The polypropylene fiber silk fabric nonwoven cloth and polypropylene non-woven fabric aperture are 30 μm, are all made of transparent material manufacture.
In some embodiments, the cladding medium is that PET polyester material is uniformly coated on net using spray process
In shape aluminium film, the PET polyester material will not block the hole in netted aluminium film 5.
In some embodiments, the cladding medium average thickness is 0.6 μm.
In some embodiments, the netted aluminium film it is longitudinal be with lateral aluminium film twine width 15mm, every it is vertical/horizontal
The spacing distance of aluminium film twine is 4mm, aluminium film with a thickness of 1 μm.
In some embodiments, the macromolecule layer is with a thickness of 50 μm.
In some embodiments, the PE continuous yarn non-woven fabrics are 0.7mm average fiber lengths below and have 10mL/
The fiber of the hydrauture of g or more is constituted.
It is compared using product made from this product and other similar products and actually detected obtains lower example conclusion:
1, anticorrosive 1.3 times of effect promotion, 2,1.5 times of anti-oxidation efficacy promotion, 3,1.7 times of wear-resistant effect promotion, 4,
1.8 times of improved thermo stability, 5,2.2 times of thermal insulation promotion, 6,1.3 times of waterproofness promotion, 7,1.5 times of gas permeability promotion.
In some embodiments, protective layer 1, reflecting layer 2, macromolecule layer 3, enhancement layer 4 are compound by point type hot pressing
At at present there are mainly three types of the complex methods of composite membrane on the market: the compound technique of 1. curtain coatings, this technique is to use plastic pellet
It is compound by the viscosity of plastics itself after son hot melt.The disadvantage is that almost airtight.2. glue spraying or frictioning are compound (hot melt adhesive is compound)
Technique, it is most fatal because the micropore of intermediate ventilated membrane is actually all blocked by hot melt adhesive the disadvantage is that Air permenbility is relatively low
Disadvantage is exactly that resistance to temperature is very low, is only capable of bearing 60 degree of temperature.Because this glue is actually a kind of pressure sensitive adhesive.3. heat
Compound technique is pressed, real waterproof ventilated membrane should be that height is ventilative, and high temperature resistant is anti-aging, and hydrostatic pressing reaches 2 meters or more.
Production technology should be pure hot complex technique, be free of glue, so can reach 110 degree of heatproof or more, high-strength anti-aging, this is mesh
The preceding country can really reach the product of EU criteria, be latest domestic science and technology.It is exactly the compound work of hot pressing used in the present invention
Skill improves construction quality and construction efficiency.
It can be seen that the present invention has effects that good anticorrosive, anti-oxidation efficacy, wear-resistant effect, heat by above-mentioned data
Stability, thermal insulation, waterproofness, gas permeability.
The preferred embodiment of the present invention has shown and described in above description, as previously described, it should be understood that the present invention is not office
Be limited to form disclosed herein, should not be regarded as an exclusion of other examples, and can be used for various other combinations, modification and
Environment, and can be changed within that scope of the inventive concept describe herein by the above teachings or related fields of technology or knowledge
It is dynamic.And changes and modifications made by those skilled in the art do not depart from the spirit and scope of the present invention, then it all should be appended by the present invention
In scope of protection of the claims.
Claims (10)
1. a kind of waterproof and breathable antibacterial, heat insulating film, it is characterised in that: including be combined from top to bottom protective layer (1), reflection
Layer (2), macromolecule layer (3), enhancement layer (4)；The protective layer (1) uses compound nonwoven cloth；The reflecting layer (2) includes netted
Aluminium film, cladding medium, the longitudinal aluminium film twine width with transverse direction of the netted aluminium film is 10-15mm, every vertical/horizontal aluminium film twine
Spacing distance be 3-5mm, aluminium film with a thickness of 0.5-1 μm, the cladding medium is using PET polyester；The macromolecule layer (3)
Including high molecular weight ptfe (PTFE) waterproof ventilated membrane and Graphene antibiosis film double-layer structure, two layers spaced staggered
Weave in, it is all anti-containing nano silver in high molecular weight ptfe (PTFE) waterproof ventilated membrane and Graphene antibiosis film
Microbial inoculum, the Graphene antibiosis film content account for the 40% of macromolecule layer (3) quality, and nanometer silver antimicrobial agent content accounts for macromolecule layer
(3) 2%-5% of quality；The enhancement layer (4) uses PE continuous yarn non-woven fabrics.
2. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the protective layer (1) uses
Compound nonwoven cloth, including upper layer polypropylene fiber silk fabric nonwoven cloth, lower layer's polypropylene non-woven fabric are combined by hot pressure machine.
3. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the polypropylene fibre silk fiber
Nonwoven thickness is 50~70 μm, and polypropylene non-woven fabric is with a thickness of 20~40 μm.
4. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the polypropylene fiber silk fiber non-woven
Cloth is with a thickness of 60 μm, and polypropylene non-woven fabric is with a thickness of 30 μm；The polypropylene fiber silk fabric nonwoven cloth is with polypropylene non-woven fabric aperture
20~30 μm, it is all made of transparent material manufacture.
5. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the cladding medium is to use
PET polyester material is uniformly coated in netted aluminium film by spray process, and the PET polyester material will not block in netted aluminium film
Hole.
6. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the average thickness of the cladding medium
Degree is 0.3~0.6 μm.
7. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the netted aluminium film it is longitudinal with
Lateral aluminium film twine width is 15mm, the spacing distance of every vertical/horizontal aluminium film twine is 4mm, aluminium film is with a thickness of 1 μm.
8. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the macromolecule layer with a thickness of
30~50 μm.
9. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the PE continuous yarn non-woven fabrics are
The fiber of 0.7mm average fiber length below and the hydrauture with 10mL/g or more is constituted.
10. a kind of waterproof and breathable antibacterial, heat insulating film according to claim 1, it is characterised in that: the protective layer (1), anti-
Layer (2), macromolecule layer (3), enhancement layer (4) is penetrated to be combined by point type hot pressing.