CN109762456A - A kind of polyurethane coating and preparation method thereof for shoes coating - Google Patents
A kind of polyurethane coating and preparation method thereof for shoes coating Download PDFInfo
- Publication number
- CN109762456A CN109762456A CN201910085077.6A CN201910085077A CN109762456A CN 109762456 A CN109762456 A CN 109762456A CN 201910085077 A CN201910085077 A CN 201910085077A CN 109762456 A CN109762456 A CN 109762456A
- Authority
- CN
- China
- Prior art keywords
- coating
- preparation
- shoes
- polyurethane coating
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of polyurethane coating and preparation method thereof for shoes coating, wherein, the preparation method comprises the following steps: step (1): isocyanates, polyester polyol, deicer and diluent being proportionally added into reaction kettle, it stirs evenly, it is reacted 6-8 hours under the conditions of 80-120 DEG C, vacuum removal bubble, cooling obtain component A;Step (2): the glycerite of polyester polyol, chain extender, catalyst and dehydration Potassium aluminum sulfate dodecahydrate is proportionally added into reaction kettle, is stirred evenly, is vacuumized 2 ~ 3 hours removing bubbles, obtain component B;Step (3): component A and component B are proportionally uniformly mixed, and vacuum removal bubble 30s obtains polyurethane coating.Polyurethane coating obtained is used to be coated in shoes surface, can be with one-pass molding, and solving the problems, such as that known spray polyurethane elastomer is reacted with moisture causes coat inside to generate bubble.
Description
Technical field
The present invention relates to a kind of polyurethane coatings and preparation method thereof, and in particular to a kind of polyurethane for shoes coating
Coating and preparation method thereof.
Background technique
Conventional article of footwear generally includes two main elements: vamp and footwear sole construction, it is generally the case that sole and shoes
What face was fabricated separately, sole is closely knit wear-resisting material, has waterproof performance;Vamp is made using leather or fabric, is guaranteed
Gas permeability.But in traditional shoes, if the height of sole is too low, water can be entered in shoes by seam and vamp, and galosh are
Using the shoes in the rainy day, the sole and vamp of galosh are integrated forms, and waterproof effect is fine, but vamp it is too closely knit and
Gas permeability is lost, outdoor sports are unfavorable for.Therefore a kind of vamp coating is needed, can be very good cladding sole and part vamp,
In the case where guaranteeing that sole is wear-resisting, moreover it is possible to it is waterproof, there is good gas permeability, while the material is there are also good appearance,
Convenient for Fashion Design.
Polyurethane paint is more typical a kind of coating at present, but paint due to containing a large amount of solvent (organic solvent or
Water), it is easy to it penetrates into inside the vamp of dry goods, vamp is caused to pollute losing functionality, in order to prevent to the infiltration of vamp,
It needs to do surface-closed processing, affects production efficiency.In addition, paint single track molding thickness is usually needed in 20-50 microns
The road 10-20 spraying process is wanted to can be only achieved the thickness of 0.2-2.0mm, per pass spraying process must wait preceding working procedures dry, solvent
Evaporating just can be carried out.Cause production efficiency extremely low in this way.Although paint can achieve required transparency simultaneously
And gloss, but wear-resisting property is very poor, is unable to reach required wear-resisting property.
For sole polyurethane elastomer have excellent abrasion resistant effect, but due to polyurethane material itself be easy with
The characteristics of moisture reacts, it is easy to generate a large amount of bubbles.To solve the problems, such as that polyurethane is easy to react with moisture, earliest by
The Dudley J.Primeaux II of Huntsman company takes the lead in researching and developing successfully spray Polyurea Elastomer Technology, sends out for the first time within 1989
Table research paper.The technology is commercially available in north America region within 1991, shows its excellent comprehensive performance immediately, by
User welcomes.The technology is applied to high-speed railway, aquatic products pond, swimming place and hall.Since polyureas has adhesive force strong, rub resistance, firmly
The features such as strong is spent, the high-end fields such as space flight, ordnance, ship, automobile are commonly applied to;But spray polyurea materials'use high-pressure spraying machine
Spraying, reaction speed is too fast, although itself is not reacted with the moisture in air, the air bubble trapped in spraying process due to
Reaction speed is too fast, can not escape out resin body, forms many small bubbles in the coating, cannot achieve desired
Obvious results fruit.In addition the aerosol caused by spraying can descend slowly and lightly in coating surface, form many short grained defects, it is also necessary to be beaten
Grinding and polishing light can be only achieved desired effect.
In addition, conventional polyurethane elastomer is difficult to realize the effect of high transparency, high brightness.The poly- ammonia made using polyethers
Ester elastomer is easy to get transparent effect, but its performance is difficult to abrasion resistant effect needed for meeting sole.Polyester production gathers
Urethane abrasion resistant effect is enough, but elastomer transparency is inadequate, it is difficult to meet desired demand.
Therefore, the prior art has much room for improvement.
Summary of the invention
The polyurethane coating and preparation method thereof that the purpose of the present invention is to provide a kind of for shoes coating, it is intended to overcome
Bubble is more in existing polyurethane coating and is difficult to realize the defect of the high grade of transparency.
Technical scheme is as follows:
A kind of preparation method of the polyurethane coating for shoes coating, wherein the following steps are included:
Step (1): isocyanates, polyester polyol, deicer and diluent are proportionally added into reaction kettle, and stirring is equal
It is even, it is reacted 6-8 hours under the conditions of 80-120 DEG C, vacuum removal bubble, cooling obtains component A;
Step (2): the glycerite of polyester polyol, chain extender, catalyst and dehydration Potassium aluminum sulfate dodecahydrate is added in proportion
Enter into reaction kettle, stir evenly, vacuumizes (- 0.095MPa) 2 ~ 3 hours removing bubbles, obtain component B;
Step (3): component A and component B are proportionally uniformly mixed, and vacuum removal bubble 30s obtains polyurethane coating.
The preparation method of the polyurethane coating for shoes coating, wherein by weight percentage,
In the step (1), isocyanates, polyester polyol, the proportion of deicer and diluent are as follows: isocyanates 60-70%,
Polyester polyol 15-25%, deicer 1-5%, diluent 5-20%;
In the step (2), polyester polyol, chain extender, catalyst and the glycerite for being dehydrated Potassium aluminum sulfate dodecahydrate are as follows:
Polyester polyol 70-85%, chain extender 5-20%, catalyst 1-3%, the glycerite 8-12% for being dehydrated Potassium aluminum sulfate dodecahydrate.
The preparation method of the polyurethane coating for shoes coating, wherein isocyanates described in step (1) is
The mixture of 2,4-MDI isomers and 4,4-MDI isomers.
The preparation method of the polyurethane coating for shoes coating, wherein deicer described in step (1) is carbon
Change diimine class deicer.
The preparation method of the polyurethane coating for shoes coating, wherein diluent described in step (1) is carbon
Acid propylene ester.
The preparation method of the polyurethane coating for shoes coating, wherein chain extender described in step (2) is 1,
4 '-butanediols.
The preparation method of the polyurethane coating for shoes coating, wherein catalyst described in step (2) is two
Dibutyl tin laurate.
The preparation method of the polyurethane coating for shoes coating, wherein in step (3), the component A and group
The ratio for dividing B is 1:2-1:1.
The preparation method of the polyurethane coating for shoes coating, wherein the dehydration Potassium aluminum sulfate dodecahydrate
Glycerite in be dehydrated Potassium aluminum sulfate dodecahydrate content be 5-20%.
Polyurethane coating made from above-mentioned preparation method is utilized it is a further object of the present invention to provide a kind of.
Dehydration Potassium aluminum sulfate dodecahydrate and glycerine is added in the present invention during preparing component B, due to dehydration 12
Water aluminum aluminum sulfate and glycerine all have stronger water imbibition, can effectively prevent to change caused by moisture excess in polyol
Learn the generation of bubble;Being dehydrated Potassium aluminum sulfate dodecahydrate has stronger convergence, and test proves, is applied to the solvent-free painting of polyurethane
It is a kind of natural deaeration agent in Material system;Glycerine (glycerol) is natural lubricant, in operation high-speed stirred
When, it can significantly reduce the coefficient of friction of substance interface, play the role of effective foam inhibition;In addition, glycerine (glycerol) is trifunctional
The low mass molecule alcohol of degree, the thermal response later period in system play the role of optimal thermosensitive response balance, are promoting internal gel
While speed, coating surface curing is also accelerated, working efficiency can be effectively improved.
In addition, catalyst dibutyltin dilaurylate selected by the present invention can also reduce bubble to a certain extent
It generates.
Polyurethane coating produced by the present invention is used to be coated in shoes surface and (can be directly immersed in sole and part vamp
In polyurethane coating), it can not need to carry out coating construction again again after preceding one of material solidification, repeatedly with one-pass molding
Curing molding reduces and repeatedly sprays cured cumbersome process using what coating needed, and solves known spray polyurethane
Elastomer is reacted with moisture causes coat inside to lead to the problem of bubble.Coating is normal temperature cure, save the cost, without any molten
Agent, low-carbon environment-friendly, own transparent are bright.
In addition, polyurethane coating produced by the present invention can be also used for luggage surface, it is comprehensive to carry out topical application raising
Can, reach scratch resistance, tear the particular/special requirements such as strong, peel strength height, waterproof, antifouling, antibacterial, anti-skidding, beautiful.
The surface effect of novel transparent light is realized using the product of the polyurethane coating, and realizes integral seamless
Effect, while having saved construction cost, production efficiency be greatly improved.
Detailed description of the invention
Fig. 1 is the photo of polyurethane coating made from the embodiment of the present invention 1.
Fig. 2 is the photo of polyurethane coating made from comparative example 1.
Fig. 3 is the photo of polyurethane coating made from comparative example 2.
Specific embodiment
Embodiments of the present invention are described below in detail, the example of the embodiment is shown in the accompanying drawings, wherein from beginning
Same or similar element or element with the same or similar functions are indicated to same or similar label eventually.Below by ginseng
The embodiment for examining attached drawing description is exemplary, and for explaining only the invention, and is not considered as limiting the invention.
Embodiment 1
The present embodiment is related to a kind of preparation method of polyurethane coating for shoes coating, wherein the following steps are included:
Step (1): isocyanates 6kg is weighed, the polyester polyol 2.5kg that molecular weight is 2000, carbodiimides (deicer)
0.1kg and propene carbonate (diluent) 1.4kg, is added in reaction kettle, stirs evenly, and it is small that 7 are reacted under the conditions of 100 DEG C
When, vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 10.4%;
Step (2): polyester polyol 7.0kg, 1,4 '-butanediols (chain extender) 2.0kg, dibutyl tin dilaurate are weighed and (is urged
Agent) the 0.2kg and glycerite 0.8kg for being dehydrated Potassium aluminum sulfate dodecahydrate, it is added in reaction kettle, stirs evenly, vacuumize
(- 0.095MPa) 3 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint (as shown in Figure 1).
Wherein, in above-mentioned steps (1), isocyanates is 40% 2,4-MDI isomers and 60% 4,4-MDI isomers
The mixture of composition;In above-mentioned steps (2), ten sulfate dihydrate aluminium are dehydrated in the glycerite of the dehydration Potassium aluminum sulfate dodecahydrate
The content of potassium is 15%.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains the product of transparent bubble-free.
Embodiment 2
The present embodiment is related to a kind of preparation method of polyurethane coating for shoes coating, wherein the following steps are included:
Step (1): isocyanates 7kg is weighed, the polyester polyol 2.0kg that molecular weight is 2000, carbodiimides (deicer)
0.5kg and propene carbonate (diluent) 0.5kg, is added in reaction kettle, stirs evenly, and reacts 7 hours under the conditions of 90 DEG C,
Vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 21.3%;
Step (2): polyester polyol 7.5kg, 1,4 '-butanediols (chain extender) 1.0kg, dibutyl tin dilaurate are weighed and (is urged
Agent) the 0.3kg and glycerite 1.2kg for being dehydrated Potassium aluminum sulfate dodecahydrate, it is added in reaction kettle, stirs evenly, vacuumize
(- 0.095MPa) 2 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint.
Wherein, in above-mentioned steps (1), isocyanates is 50% 2,4-MDI isomers and 50% 4,4-MDI isomers
The mixture of composition;In above-mentioned steps (2), ten sulfate dihydrate aluminium are dehydrated in the glycerite of the dehydration Potassium aluminum sulfate dodecahydrate
The content of potassium is 10%.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains the product of transparent bubble-free.
Embodiment 3
The present embodiment is related to a kind of preparation method of polyurethane coating for shoes coating, wherein the following steps are included:
Step (1): isocyanates 6.5kg is weighed, the polyester polyol 2.2kg that molecular weight is 2000, carbodiimides (water removal
Agent) 0.3kg and propene carbonate (diluent) 1.0kg, it is added in reaction kettle, stirs evenly, it is small that 8 are reacted under the conditions of 80 DEG C
When, vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 16.2%;
Step (2): polyester polyol 8.0kg, 1,4 '-butanediols (chain extender) 0.9kg, dibutyl tin dilaurate are weighed and (is urged
Agent) the 0.1kg and glycerite 1.0kg for being dehydrated Potassium aluminum sulfate dodecahydrate, it is added in reaction kettle, stirs evenly, vacuumize
(- 0.095MPa) 3 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint.
Wherein, in above-mentioned steps (1), isocyanates is 60% 2,4-MDI isomers and 40% 4,4-MDI isomers
The mixture of composition;In above-mentioned steps (2), ten sulfate dihydrate aluminium are dehydrated in the glycerite of the dehydration Potassium aluminum sulfate dodecahydrate
The content of potassium is 20%.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains the product of transparent bubble-free.
Embodiment 4
The present embodiment is related to a kind of preparation method of polyurethane coating for shoes coating, wherein the following steps are included:
Step (1): isocyanates 6.0kg is weighed, the polyester polyol 1.5kg that molecular weight is 2000, carbodiimides (water removal
Agent) 0.5kg and propene carbonate (diluent) 2.0kg, it is added in reaction kettle, stirs evenly, react 6 under the conditions of 120 DEG C
Hour, vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 12.4%;
Step (2): polyester polyol 8.5kg, 1,4 '-butanediols (chain extender) 0.5kg, dibutyl tin dilaurate are weighed and (is urged
Agent) the 0.1kg and glycerite 0.9kg for being dehydrated Potassium aluminum sulfate dodecahydrate, it is added in reaction kettle, stirs evenly, vacuumize
(- 0.095MPa) 2.5 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint.
Wherein, in above-mentioned steps (1), isocyanates is 45% 2,4-MDI isomers and 55% 4,4-MDI isomers
The mixture of composition;In above-mentioned steps (2), ten sulfate dihydrate aluminium are dehydrated in the glycerite of the dehydration Potassium aluminum sulfate dodecahydrate
The content of potassium is 5%.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains the product of transparent bubble-free.
Comparative example 1
This comparative example prepares polyurethane coating using following methods:
Step (1): isocyanates 6kg is weighed, the polyester polyol 2.5kg that molecular weight is 2000, carbodiimides (deicer)
0.1kg and propene carbonate (diluent) 1.4kg, is added in reaction kettle, stirs evenly, and it is small that 7 are reacted under the conditions of 100 DEG C
When, vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 10.4%;
Step (2): polyester polyol 7.5kg, 1,4 '-butanediols (chain extender) 2.3kg, dibutyl tin dilaurate are weighed and (is urged
Agent) 0.2kg, it is added in reaction kettle, stirs evenly, vacuumize (- 0.095MPa) 3 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint (as shown in Figure 2).
Wherein, in above-mentioned steps (1), isocyanates is 40% 2,4-MDI isomers and 60% 4,4-MDI isomers
The mixture of composition.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains transparent having and containing a large amount of gas
The product of bubble.
Comparative example 2
This comparative example prepares polyurethane coating using following methods:
Step (1): isocyanates 6kg is weighed, the polyester polyol 2.5kg that molecular weight is 2000, carbodiimides (deicer)
0.1kg and propene carbonate (diluent) 1.4kg, is added in reaction kettle, stirs evenly, and it is small that 7 are reacted under the conditions of 100 DEG C
When, vacuum removal bubble (- 0.095MPa), the cooling component A for obtaining NCO content and being 10.4%;
Step (2): polyester polyol 7kg, 1,4 '-butanediols (chain extender) 2kg, dibutyl tin dilaurate (catalyst) are weighed
The glycerite 0.8kg of 0.2kg and dehydration Potassium aluminum sulfate dodecahydrate is proportionally added into reaction kettle, is stirred evenly, is vacuumized
(- 0.095MPa) 3 hours removing bubbles, obtain component B;
Step (3): the component A of 8kg is added in the component B of 10kg, is uniformly mixed, vacuum removal bubble 30s obtains poly- ammonia
Ester paint (as shown in Figure 3).
Wherein, in above-mentioned steps (1), isocyanates 4,4-MDI isomers;In above-mentioned steps (2), the dehydration 12
The content that Potassium aluminum sulfate dodecahydrate is dehydrated in the glycerite of water aluminum aluminum sulfate is 15%.
Polyurethane coating made from the present embodiment is poured on plate, room temperature curing, obtains color and whiten opaque system
Product.
By comparative example 1 it is found that suitable dehydration Potassium aluminum sulfate dodecahydrate is added in the present invention during preparing component B
Glycerite can eliminate the bubble in polyurethane coating, this is because dehydration Potassium aluminum sulfate dodecahydrate and glycerine all have compared with
Strong water imbibition can effectively prevent the generation of chemical bubbles caused by moisture excess in polyol;It is dehydrated 12 water sulphur
Sour aluminium potassium has stronger convergence, and test proves, is applied in polyurethane solventless coatings system, is a kind of natural deaeration
Agent;Glycerine (glycerol) is natural lubricant, in operation when high-speed stirred, can significantly reduce the friction of substance interface
Coefficient plays the role of effective foam inhibition;In addition, glycerine (glycerol) is the low mass molecule alcohol of three-functionality-degree, the heat in system is anti-
It answers the later period to play the role of optimal thermosensitive response balance and also accelerates coating surface while promoting internal gelation rate
Curing, can effectively improve working efficiency.
By comparison 2 it is found that when the isocyanates selects 4,4-MDI isomers, become cloudy solution because reacting too fast,
And 2,4-MDI isomers and 4 are used, the mixture of 4-MDI isomers can obtain transparent gather with active balance reaction speed
Urethane coating.
The polyurethane coating that the present invention is obtained can be by conventional construction means coated on footwear sole and part shoes
On the surface in face, formed one layer of whole clearing, surface-brightening, wear-resisting waterproof coating, not only waterproof antiwear, and it is beautiful when
Still, while on the gas permeability of vamp other parts it does not influence.Conventional construction means such as spray, showering, dip-coating, brushing,
Blade coating etc., preferred technology mode is showering and dip-coating.
The present invention is described in detail above, it for those of ordinary skills, can be according to above stating
It is bright to be improved or converted, and all these modifications and variations should all belong to the protection domain of appended claims of the present invention.
Claims (10)
1. a kind of preparation method of the polyurethane coating for shoes coating, which comprises the following steps:
Step (1): isocyanates, polyester polyol, deicer and diluent are proportionally added into reaction kettle, and stirring is equal
It is even, it is reacted 6~8 hours under the conditions of 80-120 DEG C, vacuum removal bubble, cooling obtains component A;
Step (2): the glycerite of polyester polyol, chain extender, catalyst and dehydration Potassium aluminum sulfate dodecahydrate is added in proportion
Enter into reaction kettle, stir evenly, vacuumizes 2 ~ 3 hours removing bubbles, obtain component B;
Step (3): component A and component B are proportionally uniformly mixed, and vacuum removal bubble 30s obtains polyurethane coating.
2. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that with weight
Percentages,
In the step (1), isocyanates, polyester polyol, the proportion of deicer and diluent are as follows: isocyanates 60-70%,
Polyester polyol 15-25%, deicer 1-5%, diluent 5-20%;
In the step (2), polyester polyol, chain extender, catalyst and the glycerite for being dehydrated Potassium aluminum sulfate dodecahydrate are as follows:
Polyester polyol 70-85%, chain extender 5-20%, catalyst 1-3%, the glycerite 8-12% for being dehydrated Potassium aluminum sulfate dodecahydrate.
3. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(1) isocyanates described in is the mixture of 2,4-MDI isomers and 4,4-MDI isomers.
4. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(1) deicer described in is Carbodiimides deicer.
5. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(1) diluent described in is propene carbonate.
6. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(2) chain extender described in is 1,4 '-butanediols.
7. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(2) catalyst described in is dibutyl tin dilaurate.
8. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that step
(3) in, the ratio of the component A and component B are 1:2-1:1.
9. the preparation method of the polyurethane coating according to claim 1 for shoes coating, which is characterized in that described de-
The content that Potassium aluminum sulfate dodecahydrate is dehydrated in the glycerite of water Potassium aluminum sulfate dodecahydrate is 5-20%.
10. polyurethane coating made from preparation method according to claim 1 to 8.