CN109755575A - A kind of composition and preparation method thereof - Google Patents
A kind of composition and preparation method thereof Download PDFInfo
- Publication number
- CN109755575A CN109755575A CN201711071861.9A CN201711071861A CN109755575A CN 109755575 A CN109755575 A CN 109755575A CN 201711071861 A CN201711071861 A CN 201711071861A CN 109755575 A CN109755575 A CN 109755575A
- Authority
- CN
- China
- Prior art keywords
- resin
- composition
- acid
- methyl pyrrolidone
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of compositions, by forming following weight percentage components: sour 1%~13%, polypropylene 10%~40%, resin 7%~15%, N-Methyl pyrrolidone 20%~80%.Binder in the present invention has higher adhesion strength, and safe and non-toxic, sufficiently is combined organic solvent and inorganic solvent to form novel binder.
Description
Technical field
The present invention relates to a kind of composition and preparation method thereof more particularly to a kind of sizing materials and preparation method thereof.
Background technique
Binder is very important component part in lithium ion battery and the electrode material of supercapacitor, binder
Main function be bonding and keep active material, enhancing electrode active material and conductive agent and active material and collector
Between electronic contact, the structure of preferably stable pole piece.Moreover, for lithium ion cell electrode in charge and discharge process
Volume expansion/contraction, binder can play definitely buffer function.
Summary of the invention
The present invention is bad in order to solve binder caking property in the prior art, and the not high problem of degree of safety provides one kind
Adhesive composition.
The technical solution used in the present invention are as follows: a kind of composition, by forming following weight percentage components:
Acid 1%~13%,
Polypropylene 10%~40%,
Resin 7%~15%,
N-Methyl pyrrolidone 20% ~ 50%.
Further, the acid is hydrochloric acid.
Further, the resin is propionic aldehyde resin.
Further, the N-Methyl pyrrolidone content is 50% ~ 60%.
The invention further relates to a kind of preparation methods of composition, include the following steps
1) acid is mixed with polypropylene;
2) resin and N-Methyl pyrrolidone are mixed and heated to 50 ~ 80 degrees Celsius;
3) it is sufficiently mixed after mixture in step 2 is cooling with mixture in step 1.
Further, heating time is 20 ~ 30 minutes in the step 2.
The utility model has the advantages that the binder in the present invention has higher adhesion strength caused by of the invention, and it is safe and non-toxic,
Sufficiently organic solvent and inorganic solvent are combined to form novel binder.
Specific embodiment
Further details of explanation is done to the present invention With reference to embodiment, it should be appreciated that of the invention
Protection scope be not limited by the specific implementation.
Embodiment 1
A kind of composition, by forming following weight percentage components:
Acid 1%
Polypropylene 30%
Resin 7%
N-Methyl pyrrolidone .62%.
The acid is hydrochloric acid.The resin is propionic aldehyde resin.
A kind of preparation method of above-mentioned composition, includes the following steps
1) acid is mixed with polypropylene;
2) resin and N-Methyl pyrrolidone are mixed and heated to 50 ~ 80 degrees Celsius;
3) it is sufficiently mixed after mixture in step 2 is cooling with mixture in step 1.
Heating time is 20 ~ 30 minutes in the step 2.
Embodiment 2
A kind of composition, by forming following weight percentage components:
Acid 13%,
Polypropylene 40%,
Resin 15%,
N-Methyl pyrrolidone 32%.
The acid is hydrochloric acid.The resin is propionic aldehyde resin.
A kind of preparation method of above-mentioned composition, includes the following steps
1) acid is mixed with polypropylene;
2) resin and N-Methyl pyrrolidone are mixed and heated to 50 ~ 80 degrees Celsius;
3) it is sufficiently mixed after mixture in step 2 is cooling with mixture in step 1.
Heating time is 20 ~ 30 minutes in the step 2.
Embodiment 3
A kind of composition, by forming following weight percentage components:
Acid 8%,
Polypropylene 20%,
Resin 10%,
N-Methyl pyrrolidone 62%.
The acid is hydrochloric acid.The resin is propionic aldehyde resin.The N-Methyl pyrrolidone content is 50% ~ 60%.
A kind of preparation method of above-mentioned composition, includes the following steps
1) acid is mixed with polypropylene;
2) resin and N-Methyl pyrrolidone are mixed and heated to 50 ~ 80 degrees Celsius;
3) it is sufficiently mixed after mixture in step 2 is cooling with mixture in step 1.
Heating time is 20 ~ 30 minutes in the step 2.
Claims (6)
1. a kind of composition, which is characterized in that by forming following weight percentage components:
Acid 1%~13%,
Polypropylene 10%~40%,
Resin 7%~15%,
N-Methyl pyrrolidone 20%~80%.
2. composition according to claim 1, it is characterised in that: the acid is hydrochloric acid.
3. according to right to go 1 described in composition, it is characterised in that: the resin be propionic aldehyde resin.
4. composition according to claim 1, it is characterised in that: the N-Methyl pyrrolidone content is 50% ~ 60%.
5. a kind of preparation method of composition described in claim 1, it is characterised in that: include the following steps
1) acid is mixed with polypropylene;
2) resin and N-Methyl pyrrolidone are mixed and heated to 50 ~ 80 degrees Celsius;
3) it is sufficiently mixed after mixture in step 2 is cooling with mixture in step 1.
6. preparation method according to claim 1, it is characterised in that: heating time is 20 ~ 30 minutes in the step 2.