CN109749555A - Antistatic paint and safety cap - Google Patents
Antistatic paint and safety cap Download PDFInfo
- Publication number
- CN109749555A CN109749555A CN201910055274.3A CN201910055274A CN109749555A CN 109749555 A CN109749555 A CN 109749555A CN 201910055274 A CN201910055274 A CN 201910055274A CN 109749555 A CN109749555 A CN 109749555A
- Authority
- CN
- China
- Prior art keywords
- paint
- antistatic
- safety cap
- parts
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses a kind of antistatic paint and safety cap, security protection articles fields.A kind of antistatic paint, proportion includes that component is as follows: 10 parts of paint in parts by weight, and 2-3 parts of powder for antistatic, appropriate amount of water.A kind of safety cap includes cap shell, sprays the antistatic paint in the surfaces externally and internally of cap shell and forms anti-static coating.The paint of the application is film forming matter, can adhere to the surface of safety cap and forms coating；Powder for antistatic is conductive material, is entrained in paint, and coating may make to have antistatic performance.The proportion 0.2-0.3:1 of powder for antistatic and paint, can be realized long-time antistatic.The inner surface of the cap shell of the safety cap of the application and outer surface spray the antistatic paint, so that safety cap has prolonged antistatic performance.Since the coating is the coating being additionally formed on the basis of cap shell, the original material property of cap shell will not influence, so that safety cap keeps original resistance performance.
Description
Technical field
This application involves security protection articles fields, more particularly to a kind of antistatic paint and safety cap.
Background technique
Safety cap is the protective articles for preventing alluvium injury operating personnel head.By cap shell, hat lining, lower cheekstrap and back ferrule
Composition.When impact of the operation person head by falling object, first impact force is decomposed in moment using safety helmet shell, hat lining
Onto the entire area of cranium, the flexible deformation of each position buffer structure of safety cap, plastic deformation and permission are then utilized
Structure destruction absorbs most of impact force, reduces the impact to operating personnel head, to play protection operating personnel head
Effect.It plays an important role as it can be seen that the cap shell material of safety cap integrally resists safety cap performance.
In addition, safety cap should also have anti-static function.Have at present and is added in the production and processing material of safety helmet shell
The mode of antistatic agent makes safety cap have anti-static function.Its disadvantages are that: safety cap overall flexibility is deteriorated, frangible
It splits.Due to consideration that the resistance performance of safety cap, the metering that can add antistatic agent is seldom, so that anti-static effect is bad, and
It cannot achieve long-time antistatic.
Therefore, needing to develop a kind of can either keep the resistance performance of safety cap to have both long-time antistatic performance again
Antistatic paint and safety cap.
Summary of the invention
Aiming to overcome that the above problem or at least being partially solved or extenuate for the application solves the above problems.
According to the one aspect of the application, a kind of antistatic paint is provided, is matched in parts by weight including component such as
Under:
10 parts of paint, 2-3 parts of powder for antistatic, appropriate amount of water.
Optionally, the paint is acrylic paint or amino paint.
Optionally, the powder for antistatic is one of copper powder, titanium dioxide or mica.
Optionally, the antistatic paint further includes 0.1-0.5 parts of auxiliary agent.
Optionally, the auxiliary agent include one of defoaming agent, levelling agent, optical brightener, coupling agent, wetting and dispersing auxiliary agent or
It is a variety of.
According to further aspect of the application, a kind of safety cap, including cap shell are provided, in the surfaces externally and internally of the cap shell
Spraying antistatic paint simultaneously forms anti-static coating, wherein
The antistatic paint match in parts by weight include: paint 10 parts, 2-3 parts of powder for antistatic, appropriate amount of water.
Optionally, the paint is acrylic paint or amino paint.
Optionally, the powder for antistatic is one of copper powder, titanium dioxide or mica.
Optionally, the antistatic paint further includes 0.1-0.5 parts of auxiliary agent.
Optionally, the auxiliary agent include one of defoaming agent, levelling agent, optical brightener, coupling agent, wetting and dispersing auxiliary agent or
It is a variety of.
The antistatic paint and safety cap of the application paints as film forming matter, can adhere to the surface of safety cap and formation
Coating；Powder for antistatic is conductive material, is entrained in paint, and coating may make to have anti-static function.Powder for antistatic and paint
Proportion 0.2-0.3:1, can be realized long-time antistatic.The inner surface of the cap shell of the safety cap of the application and outer surface spraying
The antistatic paint, so that safety cap has prolonged antistatic performance.Due to the coating be on the basis of cap shell it is another
The coating of outer formation, therefore will not influence the original material property of cap shell, so that safety cap keeps original resistance performance.
Further, in the application, by the way that coupling agent is added, wetting and dispersing auxiliary agent improves the compactness of coating and to base
The adhesive force of material.The workability that coating is improved by the way that defoaming agent aid is added, reduces the hair of the surface defects such as pin hole, pit
It is raw.
According to the accompanying drawings to the detailed description of the specific embodiment of the application, those skilled in the art will be more
Above-mentioned and other purposes, the advantages and features of the application are illustrated.
Detailed description of the invention
Some specific embodiments of the application are described in detail by way of example and not limitation with reference to the accompanying drawings hereinafter.
Identical appended drawing reference denotes same or similar part or part in attached drawing.It should be appreciated by those skilled in the art that these
What attached drawing was not necessarily drawn to scale.In attached drawing:
Fig. 1 is the schematic diagram according to the safety cap of the application one embodiment.
Each symbol indicates that meaning is as follows in figure:
10 safety caps,
11 cap shells, 12 anti-static coatings.
Specific embodiment
Embodiment 1
A kind of antistatic paint, proportion includes that component is as follows in parts by weight: 10 parts of acrylic paint lotion, titanium dioxide 2
Part, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, 0.1 part of optical brightener, coupling agent 0.05,0.0 part of Ricinate, water is suitable
Amount.
A kind of antistatic paint preparation method:
Step 100,2 parts of titanium dioxide are weighed, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, are coupled by 0.1 part of optical brightener
Agent 0.05, is added 5 parts of deionized waters and is configured to mixed liquor by 0.05 part of Ricinate.Titanium is sequentially added under magnetic agitation state
2 parts of white powder, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, 0.1 part of optical brightener, coupling agent 0.05, Ricinate 0.05
Part.1000r/min high-speed stirred is dispersed 1 hour, is ground 10-20 minutes, ultrasonic wave dispersion stirring 20-30 minutes, obtains filler
Slurry.
Step 200, above-mentioned filler slurry is added 10 parts of acrylic paint lotion, 300-500r/min stirs at low speed 20min
Finished product is made.
The antistatic paint of the application paints as film forming matter, can adhere to the surface of safety cap and form coating；Prevent quiet
Electric powder is conductive material, is entrained in paint, and coating may make to have anti-static function.The proportion 0.2- of powder for antistatic and paint
0.3:1 can be realized long-time antistatic.The compactness of coating and right is improved by the way that coupling agent, wetting and dispersing auxiliary agent is added
The adhesive force of substrate.The workability that coating is improved by the way that defoaming agent aid is added, reduces the hair of the surface defects such as pin hole, pit
It is raw.
Embodiment 2
A kind of antistatic paint, proportion includes that component is as follows in parts by weight: 10 parts of amino paint lotion, 3 parts of copper powder,
0.2 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, coupling agent 0.1,0.1 part of Ricinate, appropriate amount of water.
A kind of antistatic paint preparation method:
Step 100,3 parts of copper powder are weighed, 0.2 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, coupling agent 0.1 moistens dispersion
0.1 part of agent, 6 parts of deionized waters are added and are configured to mixed liquor.3 parts of copper powder are sequentially added under magnetic agitation state, NXZ defoaming agent
0.2 part, 2,020 0.1 part of levelling agents, coupling agent 0.1,0.1 part of Ricinate.1000r/min high-speed stirred is dispersed 1 hour, is ground
Mill 15-25 minutes ultrasonic wave dispersion stirring 20-30 minutes, obtains filler slurry.
Step 200, above-mentioned filler slurry is added 10 parts of amino paint lotion, 300-500r/min stirs at low speed 20min system
At finished product.
The antistatic paint of the application paints as film forming matter, can adhere to the surface of safety cap and form coating；Prevent quiet
Electric powder is conductive material, is entrained in paint, and coating may make to have anti-static function.The proportion 0.2- of powder for antistatic and paint
0.3:1 can be realized long-time antistatic.The compactness of coating and right is improved by the way that coupling agent, wetting and dispersing auxiliary agent is added
The adhesive force of substrate.The workability that coating is improved by the way that defoaming agent aid is added, reduces the hair of the surface defects such as pin hole, pit
It is raw.
Embodiment 3
A kind of antistatic paint, proportion includes that component is as follows in parts by weight: 10 parts of acrylic paint lotion, mica 2.5
Part, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, coupling agent 0.1,0.1 part of Ricinate, appropriate amount of water.
A kind of antistatic paint preparation method:
Step 100,2.5 parts of mica are weighed, 2.5 parts of mica, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, coupling agent
0.1,0.1 part of Ricinate, 5 parts of deionized waters are added and are configured to mixed liquor.Mica 2.5 is sequentially added under magnetic agitation state
Part, 0.1 part of NXZ defoaming agent, 2,020 0.1 part of levelling agents, coupling agent 0.1,0.1 part of Ricinate.1000r/min high-speed stirred
Dispersion 1 hour is ground 10-20 minutes, ultrasonic wave dispersion stirring 20-30 minutes, obtains filler slurry.
Step 200, above-mentioned filler slurry is added 10 parts of acrylic paint lotion, 300-500r/min stirs at low speed 20min
Finished product is made.
The antistatic paint of the application paints as film forming matter, can adhere to the surface of safety cap and form coating；Prevent quiet
Electric powder is conductive material, is entrained in paint, and coating may make to have anti-static function.The proportion 0.2- of powder for antistatic and paint
0.3:1 can be realized long-time antistatic.The compactness of coating and right is improved by the way that coupling agent, wetting and dispersing auxiliary agent is added
The adhesive force of substrate.The workability that coating is improved by the way that defoaming agent aid is added, reduces the hair of the surface defects such as pin hole, pit
It is raw.
Embodiment 4
Fig. 1 is the schematic diagram according to the safety cap of the application one embodiment.A kind of safety cap 10, generally can be with
Including cap shell 11, hat lining, lower cheekstrap and back ferrule.It is sprayed in above-described embodiment 1-3 in the inner surface of the cap shell 11 and outer surface
Any antistatic paint simultaneously forms anti-static coating 12.Wherein, cap shell, hat lining, lower cheekstrap and rear cuff structure and the prior art
It is identical, it is repeated no more in the present embodiment for this part.
The inner surface of the cap shell of the safety cap of the application and outer surface spray the antistatic paint, therefore safety cap has
Prolonged antistatic performance.Since the coating is the coating being additionally formed on the basis of cap shell, cap shell will not influence
Original material property, so that safety cap keeps original resistance performance.
According to the antistatic testing standard requirement in GB/T 2812-2006 " safety cap test method ", by above-mentioned implementation
The corresponding surfaces externally and internally for being sprayed on safety cap of antistatic paint in example 1-3,100-200 microns of coating layer thickness.Each safety cap
Antistatic test is carried out respectively, and the specific test method is as follows:
1. measure safety cap antistatic performance, constant indoor temperature constant humidity is kept.
2. testing preceding safety cap otherwise being less than pretreatment for 24 hours.
Preprocess method: conditioning, the above pre-processing requirements can cooperate A705 safety cap comprehensive pretreatment case.
3. sticking two strip electrodes in parallel at the flatter position of tested safety cap:
Electrode length: 100mm ± 1mm, electrode width: 1mm ± 0.1mm, spacing are 10mm ± 0.5mm, and electrode should be parallel
It places.Electrode material is metal foil.
4. using resistance value < 1K Ω conductive adhesive between electrode and safety cap.
5. the measurement of megger is connected to electrode, the resistance value that megger is shown is read.
6. it is primary to exchange electrode duplicate measurements.
7. record display numerical value；The average value of survey measurements is actually measured surface resistivity twice.
Wherein, the megger error of indication: ± 1%, voltage: 100V DC.
Test result is shown in Table 1.
| Serial number | Spray antistatic paint | Coating layer thickness (micron) | Surface conductivity (ohm) |
| 1 | Embodiment 1 | 100 | 8×1010 |
| 2 | Embodiment 2 | 110 | 2×1010 |
| 3 | Embodiment 3 | 100 | 6×1010 |
Each safety cap surface resistivity is below 1 × 10 after tested9Ω。
It should be noted that unless otherwise indicated, technical term or scientific term used in this application should be this Shen
It please the ordinary meaning that is understood of one of ordinary skill in the art.
In the description of the present application, it is to be understood that term " center ", " longitudinal direction ", " transverse direction ", " length ", " width ",
" thickness ", "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top", "bottom" "inner", "outside", " up time
The orientation or positional relationship of the instructions such as needle ", " counterclockwise ", " axial direction ", " radial direction ", " circumferential direction " be orientation based on the figure or
Positional relationship is merely for convenience of description the application and simplifies description, rather than the device or element of indication or suggestion meaning must
There must be specific orientation, be constructed and operated in a specific orientation, therefore should not be understood as the limitation to the application.
In addition, term " first ", " second " etc. are used for description purposes only, it is not understood to indicate or imply relatively important
Property or implicitly indicate the quantity of indicated technical characteristic.In the description of the present application, the meaning of " plurality " is two or more,
Unless otherwise specifically defined.
In this application unless specifically defined or limited otherwise, term " installation ", " connected ", " connection ", " fixation " etc.
Term shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or integral；It can be mechanical connect
It connects, is also possible to be electrically connected；It can be directly connected, can also can be in two elements indirectly connected through an intermediary
The interaction relationship of the connection in portion or two elements.It for the ordinary skill in the art, can be according to specific feelings
Condition understands the concrete meaning of above-mentioned term in this application.
In this application unless specifically defined or limited otherwise, fisrt feature in the second feature " on " or " down " can be with
It is that the first and second features directly contact or the first and second features pass through intermediary mediate contact.Moreover, fisrt feature exists
Second feature " on ", " top " and " above " but fisrt feature be directly above or diagonally above the second feature, or be merely representative of
First feature horizontal height is higher than second feature.Fisrt feature can be under the second feature " below ", " below " and " below "
One feature is directly under or diagonally below the second feature, or is merely representative of first feature horizontal height less than second feature.
The preferable specific embodiment of the above, only the application, but the protection scope of the application is not limited thereto,
Within the technical scope of the present application, any changes or substitutions that can be easily thought of by anyone skilled in the art,
Should all it cover within the scope of protection of this application.Therefore, the protection scope of the application should be with scope of protection of the claims
Subject to.
Claims (10)
1. a kind of antistatic paint, which is characterized in that proportion includes that component is as follows in parts by weight:
10 parts of paint, 2-3 parts of powder for antistatic, appropriate amount of water.
2. antistatic paint according to claim 1, which is characterized in that the paint is acrylic paint or amino paint.
3. antistatic paint according to claim 1, which is characterized in that the powder for antistatic is copper powder, titanium dioxide or cloud
One of mother.
4. antistatic paint according to any one of claim 1-3, which is characterized in that further include 0.1-0.5 parts of auxiliary agent.
5. antistatic paint according to claim 4, which is characterized in that the auxiliary agent includes defoaming agent, levelling agent, adds lustre to
One of agent, coupling agent, wetting and dispersing auxiliary agent are a variety of.
6. a kind of safety cap, including cap shell, which is characterized in that in the inner and outer surfaces spraying antistatic paint and shape of the cap shell
At anti-static coating, wherein
The antistatic paint match in parts by weight include: paint 10 parts, 2-3 parts of powder for antistatic, appropriate amount of water.
7. safety cap according to claim 6, which is characterized in that the paint is acrylic paint or amino paint.
8. safety cap according to claim 6, which is characterized in that the powder for antistatic is in copper powder, titanium dioxide or mica
One kind.
9. safety cap a method according to any one of claims 6-8, which is characterized in that the antistatic paint further includes auxiliary agent
0.1-0.5 parts.
10. safety cap according to claim 9, which is characterized in that the auxiliary agent include defoaming agent, levelling agent, optical brightener,
One of coupling agent, wetting and dispersing auxiliary agent are a variety of.