CN109749422A - A kind of albronze particle Heat Conduction Material - Google Patents
A kind of albronze particle Heat Conduction Material Download PDFInfo
- Publication number
- CN109749422A CN109749422A CN201711073468.3A CN201711073468A CN109749422A CN 109749422 A CN109749422 A CN 109749422A CN 201711073468 A CN201711073468 A CN 201711073468A CN 109749422 A CN109749422 A CN 109749422A
- Authority
- CN
- China
- Prior art keywords
- parts
- albronze
- particle
- heat conduction
- conduction material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of albronze particle Heat Conduction Material, it is characterized in that, in parts by weight, comprising: 10-15 parts of albronze particle, 8-15 parts of polyamide, 1-5 parts of phenol, 3-6 parts of methylimidazole, 5-8 parts of tackifier, 10-15 parts of diamond dust, 3-6 parts of copper, 3-6 parts of aluminium, 3-6 parts of polyvinyl chloride, 4-6 parts of silver powder, 1-3 parts of vulcanizing agent, 2-4 parts of graphite, 3-6 parts of silicon rubber, 1-3 parts of ABS resin.
Description
Technical field
The present invention relates to a kind of albronze particle Heat Conduction Materials.
Background technique
Electronics, electric equipment products production process in, it is often necessary to operation is potted with Heat Conduction Material, to reach close
Envelope, heat extraction effect.Existing Heat Conduction Material plasticity is poor, the scope of application is small and at high cost.
In view of the above shortcomings, the designer, is actively subject to research and innovation, to found a kind of new bio-fertilizer,
Make it with more the utility value in industry.
Summary of the invention
In order to solve the above technical problems, the object of the present invention is to provide a kind of albronze particle Heat Conduction Materials.
Technical scheme is as follows:
A kind of albronze particle Heat Conduction Material, which is characterized in that in parts by weight, comprising:
10-15 parts of albronze particle, 8-15 parts of polyamide, 1-5 parts of phenol, 3-6 parts of methylimidazole, 5-8 parts of tackifier,
10-15 parts of diamond dust, 3-6 parts of copper, 3-6 parts of aluminium, 3-6 parts of polyvinyl chloride, 4-6 parts of silver powder, 1-3 parts of vulcanizing agent, graphite 2-4
Part, 3-6 parts of silicon rubber, 1-3 parts of ABS resin.
Further, in parts by weight, comprising:
12 parts of albronze particle, 10 parts of polyamide, 3 parts of phenol, 4 parts of methylimidazole, 6 parts of tackifier, diamond dust
12 parts, 4 parts of copper, 4 parts of aluminium, 4 parts of polyvinyl chloride, 4 parts of silver powder, 2 parts of vulcanizing agent, 3 parts of graphite, 4 parts of silicon rubber, 2 parts of ABS resin.
Further, the method are as follows: by albronze particle, polyamide, phenol, methylimidazole, tackifier, diamond
Powder, copper, aluminium, polyvinyl chloride, silver powder, vulcanizing agent, graphite, silicon rubber, ABS resin mix 30-60 points in high speed disperser
Clock.
According to the above aspect of the present invention, the present invention has at least the following advantages:
Heat Conduction Material made from this method, has excellent performance, good heat conductivity.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
A kind of preparation method of albronze particle Heat Conduction Material, the method are as follows: by albronze particle, polyamide,
Phenol, methylimidazole, tackifier, diamond dust, copper, aluminium, polyvinyl chloride, silver powder, vulcanizing agent, graphite, silicon rubber, ABS tree
Rouge mixes 30-60 minutes in high speed disperser.
Embodiment 1
10 parts of albronze particle, 8 parts of polyamide, 1 part of phenol, 3 parts of methylimidazole, 5 parts of tackifier, diamond dust 10
Part, 3 parts of copper, 3 parts of aluminium, 3 parts of polyvinyl chloride, 4 parts of silver powder, 1 part of vulcanizing agent, 2 parts of graphite, 3 parts of silicon rubber, 1 part of ABS resin.
Embodiment 2
10 parts of albronze particle, 8 parts of polyamide, 1 part of phenol, 3 parts of methylimidazole, 5 parts of tackifier, diamond dust 10
Part, 3 parts of copper, 3 parts of aluminium, 3 parts of polyvinyl chloride, 4 parts of silver powder, 1 part of vulcanizing agent, 2 parts of graphite, 3 parts of silicon rubber, 1 part of ABS resin.
Embodiment 3
15 parts of albronze particle, 15 parts of polyamide, 5 parts of phenol, 6 parts of methylimidazole, 8 parts of tackifier, diamond dust
15 parts, 6 parts of copper, 6 parts of aluminium, 6 parts of polyvinyl chloride, 6 parts of silver powder, 3 parts of vulcanizing agent, 4 parts of graphite, 6 parts of silicon rubber, 3 parts of ABS resin.
Heat Conduction Material made from this method made from this method, has excellent performance, good heat conductivity.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of albronze particle Heat Conduction Material, which is characterized in that in parts by weight, comprising:
10-15 parts of albronze particle, 8-15 parts of polyamide, 1-5 parts of phenol, 3-6 parts of methylimidazole, 5-8 parts of tackifier, Buddha's warrior attendant
10-15 parts of stone powder, 3-6 parts of copper, 3-6 parts of aluminium, 3-6 parts of polyvinyl chloride, 4-6 parts of silver powder, 1-3 parts of vulcanizing agent, 2-4 parts of graphite,
3-6 parts of silicon rubber, 1-3 parts of ABS resin.
2. a kind of albronze particle Heat Conduction Material according to claim 1, which is characterized in that in parts by weight,
Include:
12 parts of albronze particle, 10 parts of polyamide, 3 parts of phenol, 4 parts of methylimidazole, 6 parts of tackifier, 12 parts of diamond dust,
4 parts of copper, 4 parts of aluminium, 4 parts of polyvinyl chloride, 4 parts of silver powder, 2 parts of vulcanizing agent, 3 parts of graphite, 4 parts of silicon rubber, 2 parts of ABS resin.
3. a kind of preparation method of albronze particle Heat Conduction Material according to claim 1, which is characterized in that the side
Method are as follows: by albronze particle, polyamide, phenol, methylimidazole, tackifier, diamond dust, copper, aluminium, polyvinyl chloride, silver
Powder, vulcanizing agent, graphite, silicon rubber, ABS resin mix 30-60 minutes in high speed disperser.