CN109749263A - A kind of wear-resisting high-strength degree felt pad - Google Patents
A kind of wear-resisting high-strength degree felt pad Download PDFInfo
- Publication number
- CN109749263A CN109749263A CN201711073494.6A CN201711073494A CN109749263A CN 109749263 A CN109749263 A CN 109749263A CN 201711073494 A CN201711073494 A CN 201711073494A CN 109749263 A CN109749263 A CN 109749263A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- felt pad
- strength degree
- resisting high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of wear-resisting high-strength degree felt pads, the component of the wear-resisting high-strength degree felt pad is as follows according to parts by weight: 25-40 parts of chlorinated polyethylene rubber, 15-20 parts of epoxy natural rubber, 20-25 parts of polycaprolactone, 5-10 parts of hydrogenated butadiene polymer, 3-7 parts of promotor, 2-5 parts of decabromodiphenyl oxide, 0.5-1.3 parts of toughener, 1-4 parts of aluminium nitride, 8-10 parts of packing agent.Cost of manufacture of the present invention is cheap, and abrasion resistant effect is good, and intensity is high, while insulation effect is good, has broad application prospects.
Description
Technical field
The present invention relates to insulating materials technical field more particularly to a kind of wear-resisting high-strength degree felt pads.
Background technique
In power production process, felt pad is a kind of essential security protection articles.Under normal conditions, in production work
It is to be laid on felt pad on ground or other horizontal planes to use in work, and it cannot be by felt pad side hanging or to be laid on other non-aqueous
Flat body surface, thus limit the use scope of felt pad.
Felt pad in the prior art due to applicable situation require it is different, therefore it is required that different, to some pairs of intensity requirements
Application place that is higher while having certain toughness again, traditional felt pad are unable to satisfy.
Summary of the invention
To solve the above problems, the present invention provides a kind of wear-resisting high-strength degree felt pads.
Technical scheme is as follows:
A kind of wear-resisting high-strength degree felt pad, it is characterised in that: the component of the wear-resisting high-strength degree felt pad is according to parts by weight
It is as follows: 25-40 parts of chlorinated polyethylene rubber, 15-20 parts of epoxy natural rubber, 20-25 parts of polycaprolactone, to hydrogenate poly- fourth
5-10 parts of diene, 3-7 parts of promotor, 2-5 parts of decabromodiphenyl oxide, 0.5-1.3 parts of toughener, 1-4 parts of aluminium nitride, packing agent 8-10
Part.
Further, the promotor is one of dithiocar-bamate, thiazole and thiuram.
Further, the toughener is one of polyvinyl alcohol, polyvinyl butyral.
Further, the filler is mica powder, titanium dioxide and bentonite mixture.
Further, mica powder, titanium dioxide and bentonite mass ratio are 3:4:1 in the filler.
According to the above aspect of the present invention, the present invention at least has the advantages that
Cost of manufacture of the present invention is cheap, and abrasion resistant effect is good, and intensity is high, while insulation effect is good, before wide application
Scape.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
A kind of wear-resisting high-strength degree felt pad, it is characterised in that: the component of the wear-resisting high-strength degree felt pad is according to parts by weight
It is as follows: 29 parts of chlorinated polyethylene rubber, 17 parts of epoxy natural rubber, 23 parts of polycaprolactone, 9 parts of hydrogenated butadiene polymer,
5 parts of dithiocar-bamate, 4 parts of decabromodiphenyl oxide, 0.5 part of polyvinyl alcohol, 4 parts of aluminium nitride, 10 parts of packing agent.Wherein, institute
Stating mica powder in filler, titanium dioxide and bentonite mass ratio is 3:4:1.
Embodiment 2
A kind of wear-resisting high-strength degree felt pad, it is characterised in that: the component of the wear-resisting high-strength degree felt pad is according to parts by weight
It is as follows: 35 parts of chlorinated polyethylene rubber, 18 parts of epoxy natural rubber, 25 parts of polycaprolactone, 7 parts of hydrogenated butadiene polymer,
4 parts of thiuram, 3 parts of decabromodiphenyl oxide, 1.3 parts of polyvinyl alcohol, 1 part of aluminium nitride, 9 parts of packing agent.Wherein, mica in the filler
Powder, titanium dioxide and bentonite mass ratio are 3:4:1.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of wear-resisting high-strength degree felt pad, it is characterised in that: the component of the wear-resisting high-strength degree felt pad according to parts by weight such as
Shown in lower: 25-40 parts of chlorinated polyethylene rubber, 15-20 parts of epoxy natural rubber, 20-25 parts of polycaprolactone, hydrogenating polybutadiene
5-10 parts of alkene, 3-7 parts of promotor, 2-5 parts of decabromodiphenyl oxide, 0.5-1.3 parts of toughener, 1-4 parts of aluminium nitride, packing agent 8-10
Part.
2. a kind of wear-resisting high-strength degree felt pad according to claim 1, it is characterised in that: the promotor is two thio ammonia
One of base formates, thiazole and thiuram.
3. a kind of wear-resisting high-strength degree felt pad according to claim 1, it is characterised in that: the toughener is polyethylene
One of alcohol, polyvinyl butyral.
4. a kind of wear-resisting high-strength degree felt pad according to claim 1, it is characterised in that: the filler is mica powder, titanium
White powder and bentonite mixture.
5. a kind of wear-resisting high-strength degree felt pad according to claim 1, it is characterised in that: mica powder, titanium in the filler
White powder and bentonite mass ratio are 3:4:1.