CN1097446A - Single-component pollution-free coating - Google Patents
Single-component pollution-free coating Download PDFInfo
- Publication number
- CN1097446A CN1097446A CN 93108559 CN93108559A CN1097446A CN 1097446 A CN1097446 A CN 1097446A CN 93108559 CN93108559 CN 93108559 CN 93108559 A CN93108559 A CN 93108559A CN 1097446 A CN1097446 A CN 1097446A
- Authority
- CN
- China
- Prior art keywords
- antifouling paint
- weight
- tetrafluoroethylene
- pigment extender
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of monocomponent room-temperature cured non-toxic anti-pollution paint for sea is made up of base-material, functional stuffing, pigment extender, auxiliary agent and organic solvent.Base-material is selected modified organic silicon for use, and functional stuffing is that tetrafluoroethylene, paraffin oil, pigment extender are made up of metal oxide.The present invention can prevent the stained of marine sessile organism effectively, and to no toxic biological effect.
Description
The present invention has narrated a kind of single-component antifouling paint, is coated on the bottom of ship, can prevent the stained of marine sessile organism.
Throughout the year the bottom of ship of navigation in the ocean be except that the corrosion that is subjected to seawater, also is subjected to the infringement of marine sessile organisms such as barnacle, oyster, lime worm, Ascidian and algae and stained.According to estimates, the marine biofouling rate is the twice that 5% o'clock running resistance just is equivalent to clean surface, and fuel consumption increases by 10%.Traditional antifouling paint then utilizes wherein contained toxic agent to ooze out with certain speed and fouling organism is caused death, no matter but in the manufacturing of coating or apply in the use, a large amount of toxic agent (as organotin) enters in ocean and other environment and has promptly poisoned marine organisms, jeopardize marine food chain, also influence mankind itself's safety simultaneously.
From the viewpoint of preserving the ecological environment, the exploitation nontoxic antifouling paint has become the important topic of being badly in need of solution in the world.With the low surface energy anti-fouling paint that the additive of room temperature vulcanized silicone rubber and other low surface tension is formed, the surface that its coating in use can keep very low is powerful, makes marine life be difficult to adhere to and reaches anti-fouling effect (Mar.Eng.Rev., 1984,8,18).
The objective of the invention is to overcome organosilicon and be nontoxic antifouling paint self cure difficulty that base-material forms and with shortcomings such as the ground adhesion is not firm.And a kind of single-component antifouling paint is provided, have self-vulcanizing, bond and prevent the excellent properties of marine biofouling with ground.
Purpose of the present invention realizes by following measure:
The present invention is formed by modulation such as base-material, functional stuffing, pigment extender, auxiliary agent and solvents.Base-material is selected modified organic silicone resin for use, and functional stuffing tetrafluoroethylene and paraffin oil are formed.The present invention's prescription comprises (weight percentage), modified organic silicon 18.0-45.6, tetrafluoroethylene 3.0-19.3, paraffin oil 0-10.1, pigment extender 2.0-11.8, auxiliary agent 0.1-1.3, organic solvent surplus.
Pigment extender of the present invention is made up of titanium oxide and magnesium oxide.
Auxiliary agent of the present invention is made up of fluorocarbon surfactant, organo-silicon coupling agent, silicone oil, wilkinite, N-BUTYL ACETATE Mierocrystalline cellulose etc.
Organic solvent of the present invention is the mixing solutions of ketone, ester, aromatic hydrocarbon.
The preparation method of modified organic silicon of the present invention comprises:
(a) with 69.3-95%(weight) with hydroxy-end capped polydimethylsiloxane, blow to put at 100-150 ℃ of nitrogen and stirred 1-5 hour;
(b) add 0.3-4.9%(weight) polyfunctional oximino silane and 1.3-28.7%(weight) the base polyurethane prepolymer for use as (isocyanic acid content 5-8nt%) of Viscotrol C alcoholysis make after backflow 0.5-8 hour.
Tetrafluoroethylene process of the present invention
60Co γ penetrates shallow 2 * 10
3-3.5 * 10
5The Gy radiation treatment can make its cohesive force reduce like this, more helps disperseing.
The pigment extender granularity that the present invention selects for use is advisable with 0.5-2.5 μ m.
The concrete preparation process of coating of the present invention is: will carry out ground and mixed through tetrafluoroethylene, paraffin oil, the oxide compound of radiation treatment, add the auxiliary agent ball milling, then the base-material modified organic silicone resin is dissolved in the organic solvent with ball milling good material and stirs ball milling.
Single-component self-vulcanizing non-toxic anti-pollution paint for sea of the present invention is coated in the A of rust-inhibiting paint
3On the steel plate (300 * 150 * 1.5), the rust-inhibiting paint build is about 200 μ m.
Characteristics of the present invention are:
1, single-component
2, self-vulcanizing
3, nontoxic
Coating method of the present invention is achieved in that
1, spraying: under 0.15-0.25MPa pressure, make spray gun and object maintain a horizontal throw (＞coating is sprayed on the rust-inhibiting paint surface on 250mm).
2, brush: coating of the present invention can be coated on the rust-inhibiting paint surface by the first direction about the back up and down of brushing direction with painting brush.
Coat-thickness of the present invention is controlled at 100 μ m-150 μ m can obtain promising result.
The performance of paint spay-coating of the present invention back coating on tinplate is as follows:
(1) drying varniss time: GB1728-79, room temperature 18-25 ℃, 24 hours surface dryings, 3 days actual drying time.
(2) sticking power: GB1720-79, draws the circle method by 2 grades.
(3) snappiness: GB1731-79, the 1mm deflection
(4) shock-resistance: GB1732-79,50 kilograms centimetres
(5) wettability: drying varniss is after ten days, and the contact angle that records coating and distilled water with CA-A type contact angle instrument is 110-126 °.
Antifouling paint and antifouling property test thereof that the present invention makes according to the prescription (weight) of table 1 are as follows.Anti-fouling effect such as table 2.
1, after the antifouling coating preparation, the entry phase is no more than 20 days.
2, the shallow sea soak test is in the Small Qingdao Miniature gulf, sample apart from about the water surface 0.4-1.5 rice, water speed＜0.5 meter per second (waters is pollution-free).
3, soak time: year November in April, 1992-1992.
Claims (6)
1, a kind of marine biofouling single-component antifouling paint that prevents, prescription comprises (weight percentage):
Modified organic silicon 18.0-45.6%
Tetrafluoroethylene 3.0-19.3%
Paraffin oil 0-10.1%
Pigment extender 2.0-11.8%
Auxiliary agent 0.1-1.3%
The organic solvent surplus.
2,, it is characterized in that pigment extender is made up of titanium oxide and magnesium oxide as the said antifouling paint of claim 1.
3,, it is characterized in that auxiliary agent is made up of fluorocarbon surfactant, organo-silicon coupling agent, silicone oil, wilkinite, N-BUTYL ACETATE Mierocrystalline cellulose as the said antifouling paint of claim 1.
4,, it is characterized in that organic solvent is the mixing solutions of ketone, ester, aromatic hydrocarbon as the said antifouling paint of claim 1.
5,, it is characterized in that the preparation method of modified organic silicon comprises as the said antifouling paint of claim 1:
(a) with 69.3-95%(weight), blow to put at 100-150 ℃ of nitrogen with hydroxy-end capped polydimethylsiloxane and stirred 1-5 hour;
(b) add 0.3-4.9%(weight) polyfunctional oximino silane and 1.3-28.7%(weight) base polyurethane prepolymer for use as (isocyanic acid content 5-8nt%) of Viscotrol C alcoholysis makes after backflow 0.5-8 hour.
6,, it is characterized in that the tetrafluoroethylene process as the said antifouling paint of claim 1
60Co gamma-rays 2 * 10
3-3.5 * 10
5The Cy radiation treatment.