CN109735383A - A kind of molybdenum disulfide-bismaleimide solid lubrication slide block and preparation method thereof - Google Patents
A kind of molybdenum disulfide-bismaleimide solid lubrication slide block and preparation method thereof Download PDFInfo
- Publication number
- CN109735383A CN109735383A CN201910015711.9A CN201910015711A CN109735383A CN 109735383 A CN109735383 A CN 109735383A CN 201910015711 A CN201910015711 A CN 201910015711A CN 109735383 A CN109735383 A CN 109735383A
- Authority
- CN
- China
- Prior art keywords
- molybdenum disulfide
- bismaleimide
- sliding block
- temperature
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of molybdenum disulfide-bismaleimide solid lubrication slide blocks and preparation method thereof.The present invention is formed on molybdenum disulfide surface using mineral base oil and is coated, then the molybdenum disulfide being wrapped by is passed through stirring and ultrasonic disperse among the liquid of diallyl bisphenol, forms slurry.The density of slurries is adjusted by adjusting the ratio of the two, so that the density and the density of bismaleimide melt are close.By the way that solidification process is decomposed into pre-polymerization and polymerization process, insufficient bring air bubble problem because mold shape complexity bring is deflated is reduced.Molybdenum disulfide/bismaleimide solid sliding block the intensity with higher and toughness, good wearability of this method preparation can use in higher temperature range.
Description
Technical field
The invention belongs to a kind of solid lubrication slide block in solid lubricant field and preparation method thereof, more particularly, to
A kind of molybdenum disulfide-bismaleimide solid lubrication slide block and preparation method thereof.
Background technique
The fretting wear of material is to cause the major reason of material failure, and friction can make the material surface temperature liter of material
High, energy consumption increases;Abrasion can destroy material surface shape and size, so that the stability of material reduces, eventually lead to workpiece
It destroys.China every year due to fretting wear caused by economic loss be up to hundred billion yuan.Extend part and mechanical service life, drop
The fretting wear of low material is an extremely urgent problem.
The ability for reducing fretting wear, the rub resistance abrasion for improving material is a weight for becoming engineering material in recent years
Want research field.Wherein, grease lubrication is the most common mode for reducing fretting wear, and grease lubrication is honest and clean in most cases
The settling mode that valence is easy to get, however in more demanding production environment, grease is since its lubrication contamination is big, top load under high temperature
Lower greasy property decline, it is difficult to meet requirement.Solid self-lubricating composite material is wide using temperature, bearing capacity is strong, physics
Stable chemical performance breaches the operating limit of conventional lubrication material, is widely used in heavy industry, electronics and aerospace etc.
Field is an important directions of lubrication technical field development.
Solid self-lubricating composite material can be divided into metallic based solid self-lubricating composite, inorganic non-solid self-lubricating is answered
Condensation material and polymer matrix solid self-lubricating composite material.Metallic based solid self-lubricating composite has good mechanics strong
Degree, but corrosion-vulnerable in use process;The hardness of inorganic non-solid self-lubricating composite is big, wearability is strong, but prepares
It is at high cost, post-production difficulty is big.The density low-friction coefficient of polymer matrix solid self-lubricating composite material is low and corrosion-resistant energy
Power is strong, however its heat resistance urgently improves.
Bismaleimide is with its excellent heat resistance, radiation hardness, anti-flammability, dimensionally stable, and good mechanical performance is wide
It is general to be applied in the industrial circles such as Aeronautics and Astronautics, machinery, electronics, as the resin matrix of advanced composite material, however its toughness
Difference, high intensity operate easy embrittlement;After general toughener is added, it is easy high temperature wear.
Molybdenum disulfide has unique sandwich structure, compares table as a kind of important two-dimensional layer nano material
Area is big, and thermal stability and chemical stability are good;Due to being combined between layers mainly by Van der Waals force for its layer structure, key
Can be low, it easily slides, reduces the fretting wear of itself and other materials;In addition, the multilayer chip structure easily slided is in shearing masterpiece
With the lower mobility that can effectively increase polymeric fluid, the processable type of reinforced polymeric material.However, molybdenum disulfide and its
His Material cladding, especially with polymeric matrix compound tense, interface compatibility is bad, and material fragility is caused to enhance and material
At elevated pressures fretting wear aggravation.Therefore, molybdenum disulfide is mainly used as composite lubricating film at present, and selects and do solid sliding block
Material is less.
Summary of the invention
In order to solve the problems, such as background technique, the invention proposes a kind of molybdenum disulfide-bismaleimide is solid
Body lubricates sliding block and preparation method thereof, by solid sliding block prepared by this method, has good intensity and toughness, has good
Furthermore good rub resistance and corrosion resistance has good wear resistance.
The present invention is prepared for molybdenum disulfide/bismaleimide solid sliding block, bright its technical problem of solution by three-step approach
Used technical solution be comprising the following steps:
Step 1: molybdenum disulfide-allyl bisphenol-A slurry preparation;
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation;
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation.
The step 1 specifically: carry out molybdenum disulfide (1-5um) and mineral base oil with the mass ratio of 1:1~1:2
Mixing and ultrasonic disperse obtain dispersion liquid, by dispersion liquid and diallyl bisphenol with the mass ratio of 1:1~2:1 at 70~85 DEG C
Lower carry out ultrasonic mixing, incorporation time are 15~20min, form molybdenum disulfide-allyl bisphenol-A slurry.
The molybdenum disulfide-allyl bisphenol-A slurry slurry density and bismaleimide fusant density are close.
The step 2 specifically: by the bismaleimide powder melts of yellow, molybdenum disulfide-allyl bis-phenol is added
A slurry and heating stirring are put into setting phase to reacting 0.5~1 hour after 130~140 DEG C, ultrasonic disperse 10~15 minutes
It is vacuumized in the baking oven of same reaction temperature (130~140 DEG C) until there is no bubble releasing, obtains molybdenum disulfide-span and come
Acid imide performed polymer.
The step 3 specifically:
(1) pre-heated solids slider mould sprays one layer of silicon systems release agent, with molybdenum disulfide-bismaleimide performed polymer
In a mold as sample casting, so that the liquid surface after casting is slightly above mould upper surface;
(2) it is then heated at 160 DEG C and keeps the temperature 2 hours;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, it finally takes out again
It carries out high-temperature process and obtains solid sliding block product, as molybdenum disulfide-bismaleimide solid so that resin sufficiently solidifies
Sliding block.
The silicon systems release agent is the mixture of Organosilicon wax, silicone oil and a small amount of fluorocarbon copolymer.
High-temperature process in (2) of the step 3 is specifically to keep the temperature 12 hours at 220 DEG C to be post-processed.
It is made of any the method for claim 1-7.
The present invention is formed on molybdenum disulfide surface using mineral base oil and is coated, then by the molybdenum disulfide being wrapped by by stirring
Ultrasonic disperse is mixed and stirred among the liquid of diallyl bisphenol, forms slurry.Slurries are adjusted by adjusting the ratio of the two
Density, so that the density and the density of bismaleimide melt are close.By the way that solidification process is decomposed into pre-polymerization and was polymerize
Journey reduces insufficient bring air bubble problem because mold shape complexity bring is deflated.
The present invention increases the wearability of composite material using molybdenum disulfide as the filler of bismaleimide, has
Quickly and efficiently feature, but the material fragility of molybdenum disulfide and bismaleimide direct combination is big, does not have engineer application valence
Value.Thus the present invention is formed on molybdenum disulfide surface using mineral base oil and is coated, then by the molybdenum disulfide being wrapped by by stirring
Ultrasonic disperse is mixed and stirred among the liquid of diallyl bisphenol, forms slurry.Slurries are adjusted by adjusting the ratio of the two
Density, so that the density and the density of bismaleimide melt are close.By the way that solidification process is decomposed into pre-polymerization and was polymerize
Journey reduces insufficient bring air bubble problem because mold shape complexity bring is deflated.It is added with sizing liquor, span is come
Acid imide has apparent toughening effect, and furthermore its coefficient of friction and wear rate have biggish reduction, is coated on molybdenum disulfide table
The mineral oil in face can also release during frictional experiment, form lubricating oil film, reduce the surface temperature in friction process
Rise, and reduce attrition value in a certain range, meets the requirement of solid lubrication slide block.
The beneficial effects of the present invention are:
(1) molybdenum disulfide-bismaleimide solid lubrication slide block prepared by the present invention, can be in higher temperature range
Interior use, the temperature range used are room temperature~200 DEG C.
(2) present invention prepared by molybdenum disulfide-bismaleimide solid lubrication slide block coefficient of friction and wear rate all
It is very low;
(3) molybdenum disulfide-bismaleimide solid lubrication slide block prepared by the present invention is ground during friction testing
The temperature raising for damaging surface is lower.
(4) molybdenum disulfide-bismaleimide solid lubrication slide block intensity with higher and tough prepared by the present invention
Property.
For synthesis, molybdenum disulfide/bismaleimide solid sliding block intensity with higher of the method for the present invention preparation
And toughness, good wearability can use in higher temperature range.
Specific embodiment
In the following, the present invention will be further described in detail by way of specific embodiments, but this should not be interpreted as this hair
Bright range is only limitted to example.Without departing from the idea of the above method of the present invention, according to ordinary skill
The various replacements or change that knowledge and customary means are made, should be included in the scope of the present invention.
The embodiment of the present invention is as follows:
Embodiment 1:
Step 1: the preparation of molybdenum disulfide slurry
Molybdenum disulfide (1-5um) is quickly mixed with mineral base oil with the mass ratio of 1:1 and ultrasonic disperse, will point
Dispersion liquid and diallyl bisphenol carry out ultrasonic mixing with the mass ratio of 1:1 at 70 DEG C, and incorporation time 15min forms two sulphur
Change molybdenum-allyl bisphenol-A slurry, slurry density and bismaleimide fusant density are close.
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation
By the bismaleimide powder melts of yellow, above-mentioned molybdenum disulfide-allyl bisphenol-A room temperature stirring is added
To 130 DEG C, ultrasonic disperse reacts 0.5 hour after ten minutes, and is put into the baking oven of setting same reaction temperature (130 DEG C) and takes out
Vacuum is not until having bubble releasing.
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation
(1) pre-heated solids slider mould, sprays one layer of silicon systems release agent, and silicon systems release agent is specially Organosilicon wax, silicone oil
And the mixture of a small amount of fluorocarbon copolymer, gained performed polymer is that sample is cast in a mold, so that the liquid surface of casting omits
Higher than mould upper surface.
(2) it is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, sample is taken out.It is most laggard
Row high-temperature post-treatment keeps the temperature 12 hours at 220 DEG C and is post-processed, so that resin sufficiently solidifies, obtains the production of solid sliding block
Product.
The surface-element content that the sliding block after frictional experiment carries out is analyzed with energy disperse spectroscopy, obtains surface-element composition
Are as follows: C62.4wt%;O:32.5wt%;S:1.1wt%;P:0.4wt%;Thus Mo1.8wt% illustrates that there are a small amount of two on surface
Molybdenum sulfide migrates, and the micro P element that this outer surface measures, there is also micro mineral oil for major surfaces wear surface.
With the temperature on non-contact infrared radiation thermometer test wear surface, the fretting wear region distance apart from sample is 10cm
When record temperature.
Bismaleimide sliding block in above table is prepared using following technical process as a control group: will be double
Maleimide powder melts at 140 DEG C, is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;It is cooled to 80
DEG C, ws takes out sample.Finally carrying out high-temperature post-treatment is to keep the temperature 12 hours at 220 DEG C to be post-processed, so that resin is abundant
Solidification, obtains solid sliding block product.
The visible molybdenum disulfide epoxy composite material of above-mentioned contrast and experiment has good intensity and tough simultaneously as a result,
Property, wearability be improved and surface temperature increase it is slower.
Embodiment 2:
Step 1: the preparation of molybdenum disulfide slurry
Molybdenum disulfide (1-5um) is quickly mixed with mineral base oil with the mass ratio of 1:2 and ultrasonic disperse, will point
Dispersion liquid and diallyl bisphenol carry out ultrasonic mixing with the mass ratio of 2:1 at 85 DEG C, and incorporation time 20min forms two sulphur
Change molybdenum-allyl bisphenol-A slurry, slurry density and bismaleimide fusant density are close.
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation
By the bismaleimide powder melts of yellow, above-mentioned molybdenum disulfide-allyl bisphenol-A room temperature stirring is added
It is reacted 1 hour after to 140 DEG C, ultrasonic disperse 15 minutes, and is put into the baking oven of setting same reaction temperature (140 DEG C) and takes out very
Sky is not until having bubble releasing.
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation
(1) pre-heated solids slider mould, sprays one layer of silicon systems release agent, and silicon systems release agent is specially Organosilicon wax, silicone oil
And the mixture of a small amount of fluorocarbon copolymer, gained performed polymer is that sample is cast in a mold, so that the liquid surface of casting omits
Higher than mould upper surface.
(2) it is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, sample is taken out.It is most laggard
Row high-temperature post-treatment keeps the temperature 12 hours at 220 DEG C and is post-processed, so that resin sufficiently solidifies, obtains the production of solid sliding block
Product.
The surface-element content that the sliding block after frictional experiment carries out is analyzed with energy disperse spectroscopy, obtains surface-element composition
Are as follows: C62wt%;O:34.1wt%;S:1.3wt%;P:0.5wt%;Mo2.1wt%.Illustrate that there is a small amount of molybdenum disulfide on surface
It migrates, the micro P element that this outer surface measures, there is also micro mineral oil for major surfaces wear surface.
With the temperature on non-contact infrared radiation thermometer test wear surface, the fretting wear region distance apart from sample is 10cm
When record temperature.
Bismaleimide sliding block in above table is prepared using following technical process as a control group: will be double
Maleimide powder melts at 140 DEG C, is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;It is cooled to 80
DEG C, take out sample.Finally carrying out high-temperature post-treatment is to keep the temperature 12 hours at 220 DEG C to be post-processed, so that resin is sufficiently solid
Change, obtains solid sliding block product.
The visible molybdenum disulfide epoxy composite material of above-mentioned contrast and experiment has good intensity and tough simultaneously as a result,
Property, wearability be improved and surface temperature increase it is slower.
Embodiment 3:
Step 1: the preparation of molybdenum disulfide slurry
Molybdenum disulfide (1-5um) is quickly mixed with mineral base oil with the mass ratio of 1:1.5 and ultrasonic disperse, it will
Dispersion liquid and diallyl bisphenol carry out ultrasonic mixing with the mass ratio of 1.5:1 at 80 DEG C, and incorporation time 18min is formed
Molybdenum disulfide-allyl bisphenol-A slurry, slurry density and bismaleimide fusant density are close.
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation
By the bismaleimide powder melts of yellow, above-mentioned molybdenum disulfide-allyl bisphenol-A room temperature stirring is added
It is reacted 0.8 hour after to 135 DEG C, ultrasonic disperse 12 minutes, and is put into the baking oven of setting same reaction temperature (135 DEG C) and takes out
Vacuum is not until having bubble releasing.
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation
(1) pre-heated solids slider mould, sprays one layer of silicon systems release agent, and silicon systems release agent is specially Organosilicon wax, silicone oil
And the mixture of a small amount of fluorocarbon copolymer, gained performed polymer is that sample is cast in a mold, so that the liquid surface of casting omits
Higher than mould upper surface.
(2) it is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, sample is taken out.It is most laggard
Row high-temperature post-treatment keeps the temperature 12 hours at 220 DEG C and is post-processed, so that resin sufficiently solidifies, obtains the production of solid sliding block
Product.
The surface-element content that the sliding block after frictional experiment carries out is analyzed with energy disperse spectroscopy, obtains surface-element composition
Are as follows: C61.8wt%;O:35.7wt%;S:0.9wt%;P:0.2wt%;Mo1.4wt%.Illustrate that there is a small amount of curing on surface
Molybdenum migrates, and the micro P element that this outer surface measures, there is also micro mineral oil for major surfaces wear surface.
With the temperature on non-contact infrared radiation thermometer test wear surface, the fretting wear region distance apart from sample is 10cm
When record temperature.
Bismaleimide sliding block in above table is prepared using following technical process as a control group: will be double
Maleimide powder melts at 140 DEG C, is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;It is cooled to 80
DEG C, take out sample.Finally carrying out high-temperature post-treatment is to keep the temperature 12 hours at 220 DEG C to be post-processed, so that resin is sufficiently solid
Change, obtains solid sliding block product.
The visible molybdenum disulfide epoxy composite material of above-mentioned contrast and experiment has good intensity and tough simultaneously as a result,
Property, wearability be improved and surface temperature increase it is slower.
Embodiment 4:
Step 1: the preparation of molybdenum disulfide slurry
Molybdenum disulfide (1-5um) is quickly mixed with mineral base oil with the mass ratio of 1:1.8 and ultrasonic disperse, it will
Dispersion liquid and diallyl bisphenol carry out ultrasonic mixing with the mass ratio of 1.5:1 at 78 DEG C, and incorporation time 20min is formed
Molybdenum disulfide-allyl bisphenol-A slurry, slurry density and bismaleimide fusant density are close.
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation
By the bismaleimide powder melts of yellow, above-mentioned molybdenum disulfide-allyl bisphenol-A room temperature stirring is added
To 140 DEG C, ultrasonic disperse reacts 0.5 hour after ten minutes, and is put into the baking oven of setting same reaction temperature (130 DEG C) and takes out
Vacuum is not until having bubble releasing.
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation
(1) pre-heated solids slider mould, sprays one layer of silicon systems release agent, and silicon systems release agent is specially Organosilicon wax, silicone oil
And the mixture of a small amount of fluorocarbon copolymer, gained performed polymer is that sample is cast in a mold, so that the liquid surface of casting omits
Higher than mould upper surface.
(2) it is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, sample is taken out.It is most laggard
Row high-temperature post-treatment keeps the temperature 12 hours at 220 DEG C and is post-processed, so that resin sufficiently solidifies, obtains the production of solid sliding block
Product.
The surface-element content that the sliding block after frictional experiment carries out is analyzed with energy disperse spectroscopy, obtains surface-element composition
Are as follows: C:58wt%;O:37.9wt%;S:1.6wt%;P:0.6wt%;Mo1.9wt%.Illustrate that there is a small amount of molybdenum disulfide on surface
It migrates, the micro P element that this outer surface measures, there is also micro mineral oil for major surfaces wear surface.
With the temperature on non-contact infrared radiation thermometer test wear surface, the fretting wear region distance apart from sample is 10cm
When record temperature.
Bismaleimide sliding block in above table is prepared using following technical process as a control group: will be double
Maleimide powder melts at 140 DEG C, is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;It is cooled to 80
DEG C, take out sample.Finally carrying out high-temperature post-treatment is to keep the temperature 12 hours at 220 DEG C to be post-processed, so that resin is sufficiently solid
Change, obtains solid sliding block product.
The visible molybdenum disulfide epoxy composite material of above-mentioned contrast and experiment has good intensity and tough simultaneously as a result,
Property, wearability be improved and surface temperature increase it is slower.
Embodiment 5:
Step 1: the preparation of molybdenum disulfide slurry
Molybdenum disulfide (1-5um) is quickly mixed with mineral base oil with the mass ratio of 1:2 and ultrasonic disperse, will point
Dispersion liquid and diallyl bisphenol carry out ultrasonic mixing with the mass ratio of 1.5:1 at 82 DEG C, and incorporation time 20min forms two
Molybdenum sulfide-allyl bisphenol-A slurry, slurry density and bismaleimide fusant density are close.
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation
By the bismaleimide powder melts of yellow, above-mentioned molybdenum disulfide-allyl bisphenol-A room temperature stirring is added
It is reacted 1 hour after to 140 DEG C, ultrasonic disperse 15 minutes, and is put into the baking oven of setting same reaction temperature (140 DEG C) and takes out very
Sky is not until having bubble releasing.
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation
(1) pre-heated solids slider mould, sprays one layer of silicon systems release agent, and silicon systems release agent is specially Organosilicon wax, silicone oil
And the mixture of a small amount of fluorocarbon copolymer, gained performed polymer is that sample is cast in a mold, so that the liquid surface of casting omits
Higher than mould upper surface.
(2) it is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, sample is taken out.It is most laggard
Row high-temperature post-treatment keeps the temperature 12 hours at 220 DEG C and is post-processed, so that resin sufficiently solidifies, obtains the production of solid sliding block
Product.
The surface-element content that the sliding block after frictional experiment carries out is analyzed with energy disperse spectroscopy, obtains surface-element composition
Are as follows: C:56.2wt%;O:39.4wt%;S:1.8wt%;P:0.4wt%;Mo:2.2wt%.Illustrate that surface there are two a small amount of sulphur
Change molybdenum to migrate, the micro P element that this outer surface measures, there is also micro mineral oil for major surfaces wear surface.
With the temperature on non-contact infrared radiation thermometer test wear surface, the fretting wear region distance apart from sample is 10cm
When record temperature.
Bismaleimide sliding block in above table is prepared using following technical process as a control group: will be double
Maleimide powder melts at 140 DEG C, is heated to keeping the temperature 2 hours at 160 DEG C;2 hours are kept the temperature at 180 DEG C;It is cooled to 80
DEG C, take out sample.Finally carrying out high-temperature post-treatment is to keep the temperature 12 hours at 220 DEG C to be post-processed, so that resin is sufficiently solid
Change, obtains solid sliding block product.
The visible molybdenum disulfide epoxy composite material of above-mentioned contrast and experiment has good intensity and tough simultaneously as a result,
Property, wearability be improved and surface temperature increase it is slower.
Claims (8)
1. a kind of molybdenum disulfide-bismaleimide solid sliding block preparation method, it is characterised in that comprise the steps of:
Step 1: molybdenum disulfide-allyl bisphenol-A slurry preparation;
Step 2: molybdenum disulfide-bismaleimide performed polymer preparation;
Step 3: molybdenum disulfide-bismaleimide solid sliding block preparation.
2. a kind of molybdenum disulfide according to claim 1-bismaleimide solid sliding block preparation method, feature exist
In the step 1 specifically: molybdenum disulfide (1-5um) and mineral base oil mix with the mass ratio of 1:1~1:2 and
Ultrasonic disperse obtains dispersion liquid, and dispersion liquid and diallyl bisphenol are carried out at 70~85 DEG C with the mass ratio of 1:1~2:1
Ultrasonic mixing, incorporation time are 15~20min, form molybdenum disulfide-allyl bisphenol-A slurry.
3. a kind of molybdenum disulfide according to claim 2-bismaleimide solid sliding block preparation method, feature exist
In: the molybdenum disulfide-allyl bisphenol-A slurry slurry density and bismaleimide fusant density are close.
4. a kind of molybdenum disulfide according to claim 1-bismaleimide solid sliding block preparation method, feature exist
In: the step 2 specifically: by bismaleimide powder melts, molybdenum disulfide-allyl bisphenol-A slurry is added and heats
Stirring is put into setting same reaction temperature to reacting 0.5~1 hour after 130~140 DEG C, ultrasonic disperse 10~15 minutes
Baking oven in vacuumize until do not have bubble releasing until, obtain molybdenum disulfide-bismaleimide performed polymer.
5. a kind of molybdenum disulfide according to claim 1-bismaleimide solid sliding block preparation method, feature exist
In: the step 3 specifically:
(1) pre-heated solids slider mould sprays one layer of silicon systems release agent, using molybdenum disulfide-bismaleimide performed polymer as
Sample is cast in a mold, so that the liquid surface after casting is higher than mould upper surface;
(2) it is then heated at 160 DEG C and keeps the temperature 2 hours;2 hours are kept the temperature at 180 DEG C;80 DEG C are cooled to, it finally takes out and carries out again
High-temperature process obtains solid sliding block product, as molybdenum disulfide-bismaleimide solid sliding block.
6. a kind of molybdenum disulfide according to claim 5-bismaleimide solid sliding block preparation method, feature exist
In: the silicon systems release agent is the mixture of Organosilicon wax, silicone oil and a small amount of fluorocarbon copolymer.
7. a kind of molybdenum disulfide according to claim 5-bismaleimide solid sliding block preparation method, feature exist
In: the high-temperature process in (2) of the step 3 is specifically to keep the temperature 12 hours at 220 DEG C to be post-processed.
8. a kind of molybdenum disulfide-bismaleimide solid sliding block, it is characterised in that: use any side of claim 1-7
Method is made.