CN109735252A - A kind of BOPP laser anti-counterfeiting glazing tacky film and preparation method thereof - Google Patents
A kind of BOPP laser anti-counterfeiting glazing tacky film and preparation method thereof Download PDFInfo
- Publication number
- CN109735252A CN109735252A CN201910097338.6A CN201910097338A CN109735252A CN 109735252 A CN109735252 A CN 109735252A CN 201910097338 A CN201910097338 A CN 201910097338A CN 109735252 A CN109735252 A CN 109735252A
- Authority
- CN
- China
- Prior art keywords
- bopp
- resin
- counterfeiting
- glazing
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of BOPP laser anti-counterfeiting glazing tacky films, are made of from top to bottom BOPP base membrane layer, resin medium layer, water-borne pressure sensitive adhesive adhesion coating, and BOPP base membrane layer lower surface is equipped with radium-shine embossing.BOPP laser anti-counterfeiting glazing tacky film of the invention can be used for label overlay film after direct uncoiling, alice is not wrinkle resistant, laser effect is clear, overlay film is high-efficient, easy to use, environmentally friendly for label after it has many advantages, such as overlay film, overcomes the defect that laser anti-counterfeiting film used in conventional labels is pre-coating film or adhesive-free film.The invention also discloses the preparation methods of the radium-shine glazing tacky film of the BOPP, its operating process controllability is strong, is conducive to large-scale industrial production, and the BOPP laser anti-counterfeiting glazing tacky film being prepared into has excellent overlay film performance, and viscous force is good, uncoiling power is light, can directly carry out overlay film use.
Description
Technical field
The present invention relates to anti-fake protective film field, in particular to a kind of laser anti-counterfeiting film.
Background technique
Laser anti-counterfeiting glazing tacky film is mainly used in label industry, can be used for the anti-fake protection of various product label, tool
There is the features such as good, beautiful, environmentally friendly, the resistance to ink of antifalsification corrodes, barrier steam and carbon dioxide ability is high.Domestic and international market is to radium
Penetrating anti-fake glazing tacky film has a certain amount of demand, however there are no the laser anti-counterfeiting glazing gluings of direct gluing on the market at present
Film product, laser anti-counterfeiting film used in label is pre-coating film or adhesive-free film in the market, there is the interim gluing overlay film of user or hot pressing patch
It closes, low efficiency and energy consumption height, for interim gluing coating technique, because environmental protection is strictly just gradually being eliminated increasingly.Therefore, urgently
A kind of laser anti-counterfeiting glazing tacky film that can be used directly need to be developed.
Summary of the invention
It is an object of the invention in view of the above shortcomings of the prior art, provide a kind of BOPP laser anti-counterfeiting glazing gluing
Film, while the preparation method of the BOPP laser anti-counterfeiting glazing tacky film being provided.
The technical solution used in the present invention is: a kind of BOPP laser anti-counterfeiting glazing tacky film, from top to bottom by BOPP
Base membrane layer, resin medium layer, water-borne pressure sensitive adhesive adhesion coating composition, BOPP base membrane layer lower surface is equipped with radium-shine embossing.
Specifically, the resin medium layer is the intermediate bridge for improving BOPP base membrane layer and water-borne pressure sensitive adhesive adhesion coating, can
The water-borne pressure sensitive adhesive adhesion coating when BOPP laser anti-counterfeiting glazing tacky film uncoiling is set not remove resin medium layer, to reach
It can directly wind, the purpose of uncoiling.
As a further improvement of the foregoing solution, the resin medium layer is coated by bottom coating resin, the primary coat tree
Rouge is mixed with by polyketone resin, neutral polyamide resin, maleficent acid resin, organic solvent and ethyl acetate.
As a further improvement of the foregoing solution, the preparation method of the bottom coating resin is first with condensing reflux equipment
Being added in closed container by raw material weight ratio is (5~8): the organic solvent and ethyl acetate of (2~5), is then added and presses raw material
Weight ratio is (32~35): (38~42): polyketone resin, neutral polyamide resin and the maleficent acid resin of (20~25),
It is stirred and is heated to being completely dissolved, cooling, control viscosity is 4500~6500CPS.Specifically, bottom coating resin of the present invention
Viscosity is moderate, and subsequent filming performance after drying is good, has moderate pliability and wetting index, not only can effectively protect radium
Penetrate embossing, and its binding force for sticking layer with water-borne pressure sensitive adhesive is good.
As a further improvement of the foregoing solution, the resin medium layer with a thickness of 3~5 μm, further make BOPP
There is moderate binding force between base membrane layer and water-borne pressure sensitive adhesive adhesion coating.
As a further improvement of the foregoing solution, the BOPP base membrane layer with a thickness of 21~25 μm.
As a further improvement of the foregoing solution, the depth of the radium-shine embossing is 2~3 μm, is not influencing BOPP base
Assign the BOPP laser anti-counterfeiting glazing tacky film excellent laser effect on the basis of film layer and resin medium layer.
As a further improvement of the foregoing solution, the BOPP base membrane layer is from top to bottom by surface layer, middle layer and bottom group
It is melt index >=3.8g/10min high transparent resin layer at, the surface layer, the middle layer is melt index 3.0~
Polypropylene resin layer within the scope of 3.8g/10min, the bottom are that melt index is poly- within the scope of 2.5~3.0g/10min
Allyl resin layer.
As a further improvement of the foregoing solution, the surface layer with a thickness of 1~2 μm, the middle layer with a thickness of 18
~20 μm, the bottom with a thickness of 2~3 μm.Wherein the restriction of skin depth advantageously reduces the attached of aqueous pressure sensitive adhesive layer
Put forth effort, so that the BOPP laser anti-counterfeiting glazing tacky film be made to reduce deflection when carrying out uncoiling.
As a further improvement of the foregoing solution, the surface layer by propylene-ethylene-vinyl acetate ter-polymer resin or
Propylene-ethylene block copolymer resin composition.
Another technical solution adopted by the present invention is: a kind of BOPP laser anti-counterfeiting glazing tacky film as described above
Preparation method comprising following processing step:
1) control die head temperature is 260~270 DEG C and carries out melting co-extrusion, through curtain coating, sharp cooling roll quenching treatment, 165~
3~5 times of longitudinal stretching, 5~8 times of cross directional stretch are carried out in 175 DEG C of insulating boxs, obtain BOPP base membrane layer;
2) BOPP base membrane layer lower surface coats bottom coating resin after radium-shine embossed, and drying obtains resin medium layer;
3) water-borne pressure sensitive adhesive stick is coated in resin medium layer lower surface, drying forms water-borne pressure sensitive adhesive adhesion coating, directly receives
Roll up to obtain finished product.
Specifically, the appropriateness crystallization of the longitudinal stretching multiple and transverse stretch ratio defined conducive to macromolecular chain,
To greatly improve the tensile strength of the BOPP base membrane layer, to be conducive to the stability and durability of radium-shine embossing, effectively mention
The high overlay film performance of the BOPP laser anti-counterfeiting glazing tacky film.
The beneficial effects of the present invention are:
BOPP laser anti-counterfeiting glazing tacky film of the invention can directly be used for label overlay film after uncoiling, with marking after overlay film
The advantages that alice is not wrinkle resistant, laser effect is clear, overlay film is high-efficient, easy to use, environmentally friendly is signed, is overcome used in conventional labels
Laser anti-counterfeiting film is the defect of pre-coating film or adhesive-free film.
Preparation method operating process controllability of the invention is strong, is conducive to large-scale industrial production, is prepared into
BOPP laser anti-counterfeiting glazing tacky film has excellent overlay film performance, and viscous force is good, uncoiling power is light, and can directly carry out overlay film makes
With.
Specific embodiment
The present invention is specifically described below with reference to embodiment, in order to technical field personnel to of the invention
Understand.It is necessary to it is emphasized that embodiment is only intended to, the present invention will be further described herein, should not be understood as to this
The limitation of invention protection scope, fields person skilled in the art, the non-intrinsically safe that the present invention is made according to foregoing invention content
The modifications and adaptations of property, should still fall within protection scope of the present invention.Mentioned raw materials following simultaneously are unspecified, are
Commercial product;The processing step or preparation method not referred in detail be processing step known to a person skilled in the art or
Preparation method.
Embodiment 1
A kind of BOPP laser anti-counterfeiting glazing tacky film, from top to bottom by with a thickness of 21 μm BOPP base membrane layer, with a thickness of 5
μm resin medium layer, with a thickness of 2 μm water-borne pressure sensitive adhesive adhesion coatings form, BOPP base membrane layer lower surface is equipped with depth
3 μm of radium-shine embossing, wherein the BOPP base membrane layer from top to bottom by with a thickness of 1 μm surface layer, with a thickness of 18 μm of middle layers
With the bottom composition with a thickness of 2 μm, the surface layer is melt index >=3.8g/10min high transparent resin layer, the middle layer
The polypropylene resin layer for being melt index within the scope of 3.0~3.8g/10min, the bottom is melt index 2.5~
3.0g/10min the polypropylene resin layer in range.
The resin medium layer is bottom coating resin layer, and the preparation method of the bottom coating resin is first to be condensed back equipment in band
Closed container in be added by raw material weight than the organic solvent and ethyl acetate for 5:2, be then added and be by raw material weight ratio
Polyketone resin, neutral polyamide resin and the maleficent acid resin of 32:42:20 is stirred and is heated to 80 DEG C to complete
Dissolution, cooling, control viscosity is 4500~6500CPS.
Preparation method:
1) by melt index >=3.8g/10min propylene-ethylene-vinyl acetate ter-polymer resin after drying
Or acrylic resin within the scope of 3.0~3.8g/10min of propylene-ethylene block copolymer resin, melt index, melting refer to
Acrylic resin of the number within the scope of 2.5~3.0g/10min is respectively placed in three-layer co-extruded each die head, controls die head temperature
Degree is 260 DEG C, and melting coextrusion material, material is extended down to the Quench that 35~45 DEG C of deionized waters are filled in surface polishing from gravity stream
Roller surface is quenched, and is then imported in 175 DEG C of constant temperature ovens through introduction and is carried out 3 times and 8 times of cross directional stretch of longitudinal stretching, obtains thick
The BOPP base membrane layer that degree is 21 μm;
2) BOPP base membrane layer lower surface coats bottom coating resin after radium-shine embossed, and drying obtains resin medium layer;
3) water-borne pressure sensitive adhesive stick is coated in resin medium layer lower surface, drying forms water-borne pressure sensitive adhesive adhesion coating, directly receives
Roll up to obtain 1 finished product of embodiment.
1 finished product of Example is tested for the property, and test result shows its 180 degree peel strength >=3N/24mm, initial bonding strength
≤ 20cm, holding power >=10min directly carry out label overlay film and laser anti-counterfeiting excellent effect after uncoiling.
Embodiment 2
A kind of BOPP laser anti-counterfeiting glazing tacky film, from top to bottom by with a thickness of 25 μm BOPP base membrane layer, with a thickness of 3
μm resin medium layer, with a thickness of 4 μm water-borne pressure sensitive adhesive adhesion coatings form, BOPP base membrane layer lower surface is equipped with depth
2 μm of radium-shine embossing, wherein the BOPP base membrane layer from top to bottom by with a thickness of 2 μm surface layer, with a thickness of 20 μm of middle layers
With the bottom composition with a thickness of 3 μm, the surface layer is melt index >=3.8g/10min high transparent resin layer, the middle layer
The polypropylene resin layer for being melt index within the scope of 3.0~3.8g/10min, the bottom is melt index 2.5~
3.0g/10min the polypropylene resin layer in range.
The resin medium layer is bottom coating resin layer, and the preparation method of the bottom coating resin is first to be condensed back equipment in band
Closed container in be added by raw material weight than the organic solvent and ethyl acetate for 8:5, be then added and be by raw material weight ratio
Polyketone resin, neutral polyamide resin and the maleficent acid resin of 35:38:25 is stirred and is heated to 80 DEG C to complete
Dissolution, cooling, control viscosity is 4500~6500CPS.
Preparation method:
1) by melt index >=3.8g/10min propylene-ethylene-vinyl acetate ter-polymer resin after drying
Or acrylic resin within the scope of 3.0~3.8g/10min of propylene-ethylene block copolymer resin, melt index, melting refer to
Acrylic resin of the number within the scope of 2.5~3.0g/10min is respectively placed in three-layer co-extruded each die head, controls die head temperature
Degree is 270 DEG C, and melting coextrusion material, material is extended down to the Quench that 35~45 DEG C of deionized waters are filled in surface polishing from gravity stream
Roller surface is quenched, and is then imported in 165 DEG C of constant temperature ovens through introduction and is carried out 5 times and 5 times of cross directional stretch of longitudinal stretching, obtains thick
The BOPP base membrane layer that degree is 25 μm;
2) BOPP base membrane layer lower surface coats bottom coating resin after radium-shine embossed, and drying obtains resin medium layer;
3) water-borne pressure sensitive adhesive stick is coated in resin medium layer lower surface, drying forms water-borne pressure sensitive adhesive adhesion coating, directly receives
Roll up to obtain 2 finished product of embodiment.
2 finished product of Example is tested for the property, and test result shows its 180 degree peel strength >=3N/24mm, initial bonding strength
≤ 20cm, holding power >=10min directly carry out label overlay film and laser anti-counterfeiting excellent effect after uncoiling.
Embodiment 3
A kind of BOPP laser anti-counterfeiting glazing tacky film, from top to bottom by with a thickness of 23 μm BOPP base membrane layer, with a thickness of 4
μm resin medium layer, with a thickness of 3 μm water-borne pressure sensitive adhesive adhesion coatings form, BOPP base membrane layer lower surface is equipped with depth
3 μm of radium-shine embossing, wherein the BOPP base membrane layer from top to bottom by with a thickness of 1 μm surface layer, with a thickness of 20 μm of middle layers
With the bottom composition with a thickness of 2 μm, the surface layer is melt index >=3.8g/10min high transparent resin layer, the middle layer
The polypropylene resin layer for being melt index within the scope of 3.0~3.8g/10min, the bottom is melt index 2.5~
3.0g/10min the polypropylene resin layer in range.
The resin medium layer is bottom coating resin layer, and the preparation method of the bottom coating resin is first to be condensed back equipment in band
Closed container in be added by raw material weight than the organic solvent and ethyl acetate for 7:3, be then added and be by raw material weight ratio
Polyketone resin, neutral polyamide resin and the maleficent acid resin of 35:40:25 is stirred and is heated to 80 DEG C to complete
Dissolution, cooling, control viscosity is 4500~6500CPS.
Preparation method:
1) by melt index >=3.8g/10min propylene-ethylene-vinyl acetate ter-polymer resin after drying
Or acrylic resin within the scope of 3.0~3.8g/10min of propylene-ethylene block copolymer resin, melt index, melting refer to
Acrylic resin of the number within the scope of 2.5~3.0g/10min is respectively placed in three-layer co-extruded each die head, controls die head temperature
Degree is 265 DEG C, and melting coextrusion material, material is extended down to the Quench that 35~45 DEG C of deionized waters are filled in surface polishing from gravity stream
Roller surface is quenched, and is then imported in 170 DEG C of constant temperature ovens through introduction and is carried out 4 times and 6 times of cross directional stretch of longitudinal stretching, obtains thick
The BOPP base membrane layer that degree is 23 μm;
2) BOPP base membrane layer lower surface coats bottom coating resin after radium-shine embossed, and drying obtains resin medium layer;
3) water-borne pressure sensitive adhesive stick is coated in resin medium layer lower surface, drying forms water-borne pressure sensitive adhesive adhesion coating, directly receives
Roll up to obtain 3 finished product of embodiment.
3 finished product of Example is tested for the property, and test result shows its 180 degree peel strength >=3N/24mm, initial bonding strength
≤ 20cm, holding power >=10min directly carry out label overlay film and laser anti-counterfeiting excellent effect after uncoiling.
Above-described embodiment is the preferred embodiment of the present invention, all with similar technique of the invention and made equivalence changes,
It should belong to protection category of the invention.
Claims (10)
1. a kind of BOPP laser anti-counterfeiting glazing tacky film, it is characterised in that: from top to bottom by BOPP base membrane layer, resin medium layer,
Water-borne pressure sensitive adhesive adhesion coating composition, BOPP base membrane layer lower surface are equipped with radium-shine embossing.
2. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 1, it is characterised in that: the resin medium layer
It is coated by bottom coating resin, the bottom coating resin is by polyketone resin, neutral polyamide resin, maleficent acid resin, organic
Solvent and ethyl acetate are mixed with.
3. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 2, it is characterised in that: the bottom coating resin
Preparation method be first band be condensed back equipment closed container in be added by raw material weight ratio be (5~8): (2~5) it is organic
Solvent and ethyl acetate, then be added by raw material weight ratio be (32~35): (38~42): the polyketone resin of (20~25), in
Property polyamide and maleficent acid resin, be stirred and be heated to being completely dissolved, it is cooling, control viscosity is 4500~
6500CPS。
4. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 1, it is characterised in that: the resin medium layer
With a thickness of 3~5 μm.
5. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 1, it is characterised in that: the BOPP base membrane layer
With a thickness of 21~25 μm.
6. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 1, it is characterised in that: the radium-shine embossing
Depth is 2~3 μm.
7. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 1 or 5, it is characterised in that: the BOPP base
Film layer is made of surface layer, middle layer and bottom from top to bottom, and the surface layer is melt index >=3.8g/10min high transparency tree
Rouge layer, the middle layer are polypropylene resin layer of the melt index within the scope of 3.0~3.8g/10min, and the bottom is melting
Polypropylene resin layer of the index within the scope of 2.5~3.0g/10min.
8. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 7, it is characterised in that: the thickness on the surface layer
Be 1~2 μm, the middle layer with a thickness of 18~20 μm, the bottom with a thickness of 2~3 μm.
9. a kind of BOPP laser anti-counterfeiting glazing tacky film according to claim 7, it is characterised in that: the surface layer is by third
Alkene-ethene-vinyl acetate ter-polymer resin or propylene-ethylene block copolymer resin composition.
10. a kind of preparation method of BOPP laser anti-counterfeiting glazing tacky film as described in any one of claims 1 to 9, feature
It is to comprise the technical steps that:
1) control die head temperature carries out melting co-extrusion for 260~270 DEG C, through curtain coating, sharp cooling roll quenching treatment, at 165~175 DEG C
3~5 times of longitudinal stretching, 5~8 times of cross directional stretch are carried out in insulating box, obtain BOPP base membrane layer;
2) BOPP base membrane layer lower surface coats bottom coating resin after radium-shine embossed, and drying obtains resin medium layer;
3) water-borne pressure sensitive adhesive stick is coated in resin medium layer lower surface, drying forms water-borne pressure sensitive adhesive adhesion coating, directly winds
Finished product.