CN109735206A - A kind of slim outdoor fireproof coating of weatherability and its preparation process - Google Patents
A kind of slim outdoor fireproof coating of weatherability and its preparation process Download PDFInfo
- Publication number
- CN109735206A CN109735206A CN201910034931.6A CN201910034931A CN109735206A CN 109735206 A CN109735206 A CN 109735206A CN 201910034931 A CN201910034931 A CN 201910034931A CN 109735206 A CN109735206 A CN 109735206A
- Authority
- CN
- China
- Prior art keywords
- agent
- weatherability
- slim
- fireproof coating
- melamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, more particularly to a kind of slim outdoor fireproof coating of weatherability and its preparation process, a kind of slim outdoor fireproof coating of weatherability, it includes following component by weight percentage, epoxy resin 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine 5-8%, defoaming agent 2-5%, dispersing agent 3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-2% and water 46-69%；A kind of slim outdoor fireproof coating preparation process of weatherability, it includes the following steps: the first step, weighing, weighs in the ratio of epoxy resin 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine 5-8%, defoaming agent 2-5%, dispersing agent 3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-2% and water 46-69%；Second step prepares finished product；Component alleged by the first step is added in container, and is sufficiently stirred 30-40 minutes.Coating storage stability and physicochemical property provided by the invention are stronger, and have very strong photosensitivity and weatherability.
Description
Technical field
The present invention relates to the slim outdoor fireproof coating of technical field of coatings more particularly to a kind of weatherability and its preparation works
Skill.
Background technique
Slim fireproof coating refers to that fire temperature occurs for the fireproof coating that thickness is no more than between 3-7mm, this kind of fireproof coating
Degree can be expanded foamed rapidly after increasing, and forms fine and close fire proof heat-insulation layer, be outdoor steel structure especially airport, in exhibitions
The common fireproof coatings such as the outdoor buildings light weight steel roof truss such as the heart, recreational and sports activities place, ball-joint Elements of Space Grid Truss, but at present thin
The storage stability of fireproof coating and physicochemical property are bad outside type room, and weatherability is poor.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of slim outdoor fireproof coating of weatherability and its preparation processes.
The present invention is to be achieved by the following technical programs:
The slim outdoor fireproof coating of a kind of weatherability comprising following component by weight percentage, epoxy resin 5-
9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine 5-8%, defoaming agent 2-5%, dispersing agent 3-
5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-2% and water 46-69%.
Specific embodiment one, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 5%, aliphatic isocyanates 4%, ammonium polyphosphate 6%, melamine 5%, defoaming agent 2%, dispersing agent
3%, silicone oil 1%, expanded graphite 2%, coalescing agent 2%, antifreezing agent 1% and water 69%.
Specific embodiment two, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 9%, aliphatic isocyanates 8%, ammonium polyphosphate 8%, melamine 8%, defoaming agent 5%, dispersing agent
5%, silicone oil 3%, expanded graphite 3%, coalescing agent 3%, antifreezing agent 2% and water 46%.
Specific embodiment three, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 7%, aliphatic isocyanates 6%, ammonium polyphosphate 7%, melamine 6.5%, defoaming agent 3.5%, dispersion
Agent 4%, silicone oil 2%, expanded graphite 2.5%, coalescing agent 2.5%, antifreezing agent 1.5% and water 57.5%.
Further, antifreezing agent is propylene glycol.
A kind of slim outdoor fireproof coating preparation process of weatherability comprising following steps:
The first step, weighing, by epoxy resin 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, trimerization
It is cyanamide 5-8%, defoaming agent 2-5%, dispersing agent 3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreeze
The ratio of agent 1-2% and water 46-69% are weighed；
Second step prepares finished product；Component alleged by the first step is added in container, and is sufficiently stirred 30-40 minutes.
Beneficial effects of the present invention
A kind of slim outdoor fireproof coating of weatherability provided by the invention, ammonium polyphosphate is foaming agent, and fire is occurring
Temperature expands rapidly after increasing, and releases non-flammable gases, makes coating expansion, and form reticulated foams in coating, prevents
The sprawling of fire；The storage stability and physicochemical property of epoxy resin are stronger, and have very strong photosensitivity and weather-proof
Property, it is particularly suitable for outdoor light weight steel roof truss, ball-joint Elements of Space Grid Truss fireproof coating；Melamine and propylene glycol is added, makes
The stability of coating is stronger, have it is very strong it is water-fast, heat-resisting, resistance to freeze, be ageing-resistant, is resistance to electric arc, resistant to chemical etching, and have good
Insulation performance, glossiness and mechanical strength.
Specific embodiment
The slim outdoor fireproof coating of a kind of weatherability comprising following component by weight percentage, epoxy resin 5-
9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine 5-8%, defoaming agent 2-5%, dispersing agent 3-
5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-2% and water 46-69%.
Specific embodiment one, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 5%, aliphatic isocyanates 4%, ammonium polyphosphate 6%, melamine 5%, defoaming agent 2%, dispersing agent
3%, silicone oil 1%, expanded graphite 2%, coalescing agent 2%, antifreezing agent 1% and water 69%.
Specific embodiment two, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 9%, aliphatic isocyanates 8%, ammonium polyphosphate 8%, melamine 8%, defoaming agent 5%, dispersing agent
5%, silicone oil 3%, expanded graphite 3%, coalescing agent 3%, antifreezing agent 2% and water 46%.
Specific embodiment three, a kind of slim outdoor fireproof coating of weatherability comprising by weight percentage such as the following group
Point, epoxy resin 7%, aliphatic isocyanates 6%, ammonium polyphosphate 7%, melamine 6.5%, defoaming agent 3.5%, dispersion
Agent 4%, silicone oil 2%, expanded graphite 2.5%, coalescing agent 2.5%, antifreezing agent 1.5% and water 57.5%.
Further, antifreezing agent is propylene glycol.
A kind of slim outdoor fireproof coating preparation process of weatherability comprising following steps:
The first step, weighing, by epoxy resin 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, trimerization
It is cyanamide 5-8%, defoaming agent 2-5%, dispersing agent 3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreeze
The ratio of agent 1-2% and water 46-69% are weighed；
Second step prepares finished product；Component alleged by the first step is added in container, and is sufficiently stirred 30-40 minutes.
Due to a kind of slim outdoor fireproof coating of weatherability provided by the invention, ammonium polyphosphate is foaming agent, is being occurred
Fire temperature expands rapidly after increasing, and releases non-flammable gases, makes coating expansion, and form reticulated foams in coating,
Prevent the sprawling of fire；The storage stability and physicochemical property of epoxy resin are stronger, and have very strong photosensitivity and
Weatherability is particularly suitable for outdoor light weight steel roof truss, ball-joint Elements of Space Grid Truss fireproof coating；Melamine and the third two are added
Alcohol keeps the stability of coating stronger, have it is very strong it is water-fast, heat-resisting, resistance to freeze, be ageing-resistant, is resistance to electric arc, resistant to chemical etching, and have
There are good insulation performance, glossiness and mechanical strength.
Specific test result is shown in Table one
Table one
| Test item | Specific embodiment one | Specific embodiment two | Specific embodiment three |
| Drying time h | 12 | 13 | 15 |
| Initial dry crack resistance | Flawless | Flawless | Flawless |
| Adhesive strength MPa | 0.42 | 0.45 | 0.44 |
| Water resistance h | 460 | 520 | 560 |
| Heat-resisting cyclicity number | 45 | 45 | 42 |
| Acid resistance/h | 408 | 410 | 416 |
| Alkali resistance/h | 432 | 428 | 432 |
| Fire endurance h | 2.2 | 2.4 | 2.5 |
| Rub resistance number | 1509 | 1538 | 1536 |
According to GB/14907-2002 standard testing, specifically: 1, surface drying time answer≤for 24 hours；2, crack resistance: allow to occur
1-3 Crack, width answer≤0.5mm；3, adhesion strength >=0.1Mpa；4, water resistance: after for 24 hours, coating is not cracked, is risen
Layer, obscission；5, cold-hot cyclicity/number: after 15 times, coating do not crack, aliquation, obscission；6, fire endurance:
Fire endurance is not less than 2h, can be seen that a kind of slim outdoor fire prevention of weatherability provided by the invention applies by experimental data in table
Material, performance indexes is considerably beyond requirements of the national standard.
In conclusion a kind of slim outdoor fireproof coating of weatherability provided by the invention, storage stability and physicochemical property
It is relatively strong, and there is very strong photosensitivity and weatherability.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of slim outdoor fireproof coating of weatherability, which is characterized in that including following component by weight percentage, asphalt mixtures modified by epoxy resin
Rouge 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine 5-8%, defoaming agent 2-5%, dispersing agent
3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-2% and water 46-69%.
2. a kind of slim outdoor fireproof coating of weatherability, which is characterized in that including following component by weight percentage, asphalt mixtures modified by epoxy resin
Rouge 5%, aliphatic isocyanates 4%, ammonium polyphosphate 6%, melamine 5%, defoaming agent 2%, dispersing agent 3%, silicone oil
1%, expanded graphite 2%, coalescing agent 2%, antifreezing agent 1% and water 69%.
3. a kind of slim outdoor fireproof coating of weatherability, which is characterized in that including following component by weight percentage, asphalt mixtures modified by epoxy resin
Rouge 9%, aliphatic isocyanates 8%, ammonium polyphosphate 8%, melamine 8%, defoaming agent 5%, dispersing agent 5%, silicone oil
3%, expanded graphite 3%, coalescing agent 3%, antifreezing agent 2% and water 46%.
4. a kind of slim outdoor fireproof coating of weatherability, which is characterized in that including following component by weight percentage, asphalt mixtures modified by epoxy resin
Rouge 7%, aliphatic isocyanates 6%, ammonium polyphosphate 7%, melamine 6.5%, defoaming agent 3.5%, dispersing agent 4%, silicon
Oil 2%, expanded graphite 2.5%, coalescing agent 2.5%, antifreezing agent 1.5% and water 57.5%.
5. the slim outdoor fireproof coating of a kind of weatherability described in -4 according to claim 1, which is characterized in that the antifreezing agent is
Propylene glycol.
6. a kind of slim outdoor fireproof coating preparation process of weatherability, which comprises the steps of:
The first step, weighing, by epoxy resin 5-9%, aliphatic isocyanates 4-8%, ammonium polyphosphate 6-8%, melamine
5-8%, defoaming agent 2-5%, dispersing agent 3-5%, silicone oil 1-3%, expanded graphite 2-3%, coalescing agent 2-3%, antifreezing agent 1-
The ratio of 2% and water 46-69% is weighed；
Second step prepares finished product；Component alleged by the first step is added in container, and is sufficiently stirred 30-40 minutes.