CN109721951A - A kind of freeway guardrail composite material - Google Patents
A kind of freeway guardrail composite material Download PDFInfo
- Publication number
- CN109721951A CN109721951A CN201711044840.8A CN201711044840A CN109721951A CN 109721951 A CN109721951 A CN 109721951A CN 201711044840 A CN201711044840 A CN 201711044840A CN 109721951 A CN109721951 A CN 109721951A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- freeway guardrail
- cloth
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to freeway guardrail field more particularly to a kind of freeway guardrail composite materials.A kind of freeway guardrail composite material, the component including following parts by weight: 60-100 parts of resin, 0.02-0.2 parts of infrared absorbent, 10-50 parts of filler, 0.2-5 parts of curing agent, 0.3-5 parts of ultraviolet absorbing agent, 50-100 parts of Multiaxial Fiberglass Fabrics, 2-20 parts of basalt fiber cloth.Resistance to ag(e)ing of the invention, weatherability is preferable, quality is light, good toughness, be unlikely to deform, impact resistance is stronger, once car body, which is hit, has buffer function, greatly reduces the injury to the person.In addition, the production cost of composite material of the present invention, is conducive to the sustainable development of enterprise.
Description
Technical field
The invention belongs to freeway guardrail field more particularly to a kind of freeway guardrail composite materials.
Background technique
Freeway guardrail generally refer in highway two sides or median strip with road is disposed in parallel blocks
Facility, main function are that improper fleet vehicles caused by preventing faulty driver or other reasons run off highway or pass through center
The traffic accident that dividing strip swarms into opposite lane occurs, occupant safety on protection trackside pedestrian, building, driver and Che,
It has induction pilot's line of vision concurrently simultaneously, increase traffic safety sense and beautifies the effect of highway environment.With China's highway
The steel using amount of fast development, freeway guardrail is growing day by day.The output of steel in China is always maintained at 100,000,000 tons or more in recent years, entirely
The iron and steel resource of state is nervous.Environmental pollution when in order to keep the long-term sustainable development of mineral resources and reduce steel-making, it is necessary to effectively
Control steel-making yield.Therefore it should practice every conceivable frugality in every profession and trade using steel, rationally utilize iron and steel resource, while selecting other materials
Material replaces steel.
Freeway guardrail generally uses metal material bending and molding at present, it is that one kind is mutually spliced with ripple steel guard rail
And the continuous structure supported by main pillar.It, can since waveform steel guard rail plate has good crash-worthiness to act on when vehicle collides it
To effectively prevent smashing, spark can be especially generated during collision and causes car crash, most of traffic accident be by
Caused by expressway barrier is smashed.Existing freeway guardrail is unlikely to deform, and bending strength effect is undesirable.Cause
This it is necessary to improve the mechanical property of freeway guardrail on the basis of not increasing cost.
Summary of the invention
The defect that it is an object of the invention to overcome prior art freeway guardrail bending strength effect undesirable, provides
A kind of freeway guardrail composite material.
A kind of freeway guardrail composite material, the component including following parts by weight: 60-100 parts of resin, infrared ray absorbing
0.02-0.2 parts of agent, 10-50 parts of filler, 0.2-5 parts of curing agent, 0.3-5 parts of ultraviolet absorbing agent, Multiaxial Fiberglass Fabrics
50-100 parts, 2-20 parts of basalt fiber cloth.
Specifically, the resin be vinylite, adjacent one of benzene unsaturated-resin or isophthalic unsaturated-resin or
Two or more mixtures.
Specifically, the infrared absorbent is one or more mixtures of ITO, ATO or GTO.
Specifically, the filler is one or both of calcium carbonate, talcum powder, kaolin, aluminium hydroxide or mica powder
The above mixture.
Specifically, the curing agent is methyl ethyl ketone peroxide, benzoyl peroxide, cyclohexanone peroxide, the tertiary fourth of peroxidating
One or more mixtures of ester, isopropyl benzene hydroperoxide or tert-butyl hydroperoxide.
Specifically, institute's ultraviolet absorbing agent is one of zinc oxide, iron oxide, titanium dioxide, UV-326 or UV-531
Or two or more mixtures.
Specifically, the Multiaxial Fiberglass Fabrics are the axial cloth of glass fibre two, the axial cloth of glass fibre three or glass
One or more mixtures of axial cloth of fiber four.
Specifically, the glass of the Multiaxial Fiberglass Fabrics are 2400tex the axial cloth of glass fibre three, 4800tex
One of axial cloth of glass fibre two of the axial cloth of fiber three, the axial cloth of glass fibre four of 4800tex or 9600tex or two
Kind or more mixture.
Specifically, the grammes per square metre of the basalt fiber cloth is 30g/m2、40g/m2Or 60g/m2One of grammes per square metre or two
Kind or more mixture.
In addition, including the following steps: the present invention also provides a kind of preparation method of freeway guardrail composite material
(1) prepare high-strength composite material: sequentially added into stirred tank resin, curing agent, infrared absorbent, filler,
Ultraviolet absorbing agent is transferred in glue groove after stirring;
(2) impregnation: being arranged in Multiaxial Fiberglass Fabrics and basalt fibre on warp thread plate, and warp thread plate is put into glue groove leaching
Glue;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 110 DEG C -180 DEG C draws depanning.
Beneficial effects of the present invention: (1) due in of the invention composite material containing Multiaxial Fiberglass Fabrics, so that this
The freeway guardrail composite material of invention has higher tensile strength, bending strength and impact flexibility, and when shock is unlikely to deform,
Bending strength effect is ideal, once car body, which is hit, has buffer function, greatly reduces the injury to the person, can satisfy open air makes
With safety;(2) composite material quality of the invention is relatively light, convenient in carrying;(3) weatherability of the invention is preferable.Due to the present invention
Composite material in contain infrared absorbent and ultraviolet absorbing agent, in the common of infrared absorbent and ultraviolet absorbing agent
Under effect, the temperature of composite material can be effectively reduced, shield infrared, ultraviolet light radiation.Specifically, infrared in summer
Light absorbers can shield most infrared rays in sunlight, and ultraviolet absorbing agent can shield exhausted most in sunlight
Number ultraviolet light, so that composite material has good barrier action to infrared ray, the ultraviolet light in strong sunlight.In addition, red
The performance of ultraviolet absorbers and ultraviolet absorbing agent makes composite material have excellent thermal insulation property.It in winter again can be effectively
The radiation for obstructing infrared ray, ultraviolet light, preventing composite material, outwardly air conducts heat, and prevents composite material from cracking, thus
Extend the service life of composite material;(4) present invention uses green material basalt fiber cloth, which is by single profound
Wire drawing obtains after military rock and ore melts at high temperature, and product and production process are nontoxic, is real green product,
Compared with steel type freeway guardrail, the usage amount of steel is greatly reduced, resource has been saved, is reduced environmental pollution, is met
Scientific development concepts;Abundant, the low in raw material price additionally, due to China's basalt ore, therefore it is compound to greatly reduce the present invention
The production cost of material has great Social benefit and economic benefit.
Detailed description of the invention
Fig. 1 is the flow chart of preparation method of the present invention.
Specific embodiment
The present invention is further illustrated combined with specific embodiments below.
Embodiment 1
A kind of freeway guardrail composite material, the component including following parts by weight: 60 parts of vinylite, ITO 0.02
Part, 10 parts of calcium carbonate, 0.2 part of methyl ethyl ketone peroxide, 0.3 part of zinc oxide, 2400tex three axial 50 parts of cloth, 30g/m2It is profound
2 parts of military rock fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps (as shown in Figure 1):
(1) it prepares high strength composite: sequentially adding 60 parts of vinylites, 0.2 part of peroxidating first into stirred tank
Ethyl ketone, 0.02 part of ITO, 10 parts of calcium carbonate, 0.3 part of zinc oxide, are transferred in glue groove after stirring;
(2) impregnation: the axial cloth of glass fibre three of 50 parts of 2400tex and 2 parts of 30g/m2Basalt fibre be arranged in
On warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 110 DEG C draws depanning.
Embodiment 2
A kind of freeway guardrail composite material, the component including following parts by weight: 70 parts of adjacent benzene unsaturated-resin, ATO
0.05 part, 20 parts of talcum powder, 1.5 parts of benzoyl peroxide, 1.5 parts of iron oxide, 4800tex three axial 60 parts of cloth, 40g/m2
8 parts of basalt fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 70 parts of adjacent benzene unsaturated-resins, 1.5 parts of peroxidating into stirred tank
Benzoyl, 0.05 part of ATO, 20 parts of talcum powder, 1.5 parts of iron oxide, are transferred in glue groove after stirring;
(2) impregnation: the axial cloth of glass fibre three of 60 parts of 4800tex and 8 parts of 40g/m2Basalt fibre be arranged in
On warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 120 DEG C draws depanning.
Embodiment 3
A kind of freeway guardrail composite material, the component including following parts by weight: 80 parts of isophthalic unsaturated-resin, GTO
0.1 part, 30 parts of kaolin, 3 parts of cyclohexanone peroxide, 3 parts of titanium dioxide, 4800tex four axial 75 parts of cloth, 60g/m2It is profound
16 parts of military rock fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 80 parts of isophthalic unsaturated-resins, 3 parts of peroxidating rings into stirred tank
Hexanone, 0.1 part of GTO, 30 parts of kaolin, 3 parts of titanium dioxide, are transferred in glue groove after stirring;
(2) impregnation: the axial cloth of glass fibre four of 75 parts of 4800tex and 16 parts of 60g/m2Basalt fibre be arranged in
On warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 130 DEG C draws depanning.
Embodiment 4
A kind of freeway guardrail composite material, the component including following parts by weight: 90 parts of adjacent benzene unsaturated-resin, GTO
0.15 part, 40 parts of aluminium hydroxide, 4 parts of t-butylperbenzoate, 4 parts of UV-326,9600tex 90 parts of biaxially cloth, 30g/m2's
18 parts of basalt fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 90 parts of adjacent benzene unsaturated-resins, 4 parts of peroxidating uncles into stirred tank
Butyl ester, 0.15 part of GTO, 30 parts of kaolin, 4 parts of UV-326, are transferred in glue groove after stirring;
(2) impregnation: the glass fibre of 90 parts of 9600tex biaxially cloth and 18 parts of 30g/m2Basalt fibre be arranged in
On warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 140 DEG C draws depanning.
Embodiment 5
A kind of freeway guardrail composite material, the component including following parts by weight: 100 parts of vinylite, ATO 0.2
Part, 50 parts of mica powder, 5 parts of isopropyl benzene hydroperoxide, 5 parts of UV-531,2400tex four axial 100 parts, 60g/m2The Black Warrior
20 parts of rock fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 100 parts of vinylites, 5 parts of isopropylbenzene peroxidating into stirred tank
Hydrogen, 0.2 part of ATO, 50 parts of mica powders, 5 parts of UV-531, are transferred in glue groove after stirring;
(2) impregnation: four axial direction of glass fibre of 100 parts of 2400tex and 20 parts of 60g/m2Basalt fibre be arranged in
On warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 160 DEG C draws depanning.
Embodiment 6
A kind of freeway guardrail composite material, the component including following parts by weight: 80 parts of isophthalic unsaturated-resin, ITO
0.1 part, 30 parts of kaolin, 3 parts of benzoyl peroxide, 3 parts of titanium dioxide, 9600tex three axial 80 parts, 40g/m2The Black Warrior
10 parts of rock fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 80 parts of isophthalic unsaturated-resins, 3 parts of benzoyl peroxides into stirred tank
Formyl, 0.1 part of ITO, 30 parts of kaolin, 3 parts of titanium dioxide, are transferred in glue groove after stirring;
(2) impregnation: three axial direction of glass fibre of 80 parts of 9600tex and 10 parts of 40g/m2Basalt fibre be arranged in through
On yarn plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 180 DEG C draws depanning.
Embodiment 7
A kind of freeway guardrail composite material, the component including following parts by weight: 30 parts of vinylite, adjacent benzene insatiable hunger
With 30 parts of resin, 0.01 part of ITO, 0.01 part of ATO, 5 parts of calcium carbonate, 5 parts of talcum powder, 0.1 part of methyl ethyl ketone peroxide, peroxidating
0.1 part of benzoyl, 0.2 part of zinc oxide, 0.1 part of UV-531, three axial 25 parts of the cloth of 2400tex, 9600tex glass fibre
Two axial 25 parts of cloth, 30g/m21 part of basalt fiber cloth, 40g/m21 part of basalt fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps (as shown in Figure 1):
(1) it prepares high strength composite: sequentially adding 30 parts of vinylite, adjacent benzene unsaturated-resin into stirred tank
30 parts, 0.1 part of methyl ethyl ketone peroxide, 0.1 part of benzoyl peroxide, 0.01 part of ITO, 0.01 part of ATO, 5 parts of calcium carbonate, talcum
5 parts of powder, 0.2 part of zinc oxide, 0.1 part of UV-531, are transferred in glue groove after stirring;
(2) impregnation: three axial 25 parts of the cloth of 2400tex, 25 parts of the axial cloth of glass fibre two of 9600tex and 30g/m2
1 part of basalt fiber cloth, 40g/m21 part of basalt fiber cloth be arranged on warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 110 DEG C draws depanning.
Embodiment 8
A kind of freeway guardrail composite material, the component including following parts by weight: 35 parts of vinylite, isophthalic insatiable hunger
With 35 parts of resin, 0.02 part of ITO, 0.03 part of GTO, 10 parts of talcum powder, 5 parts of aluminium hydroxide, 5 parts of aluminium hydroxide, benzoyl peroxide
0.5 part of formyl, 0.5 part of cyclohexanone peroxide, 0.5 part of t-butylperbenzoate, 0.5 part of iron oxide, 0.5 part of titanium dioxide, UV-
326 0.5 parts, three axial 30 parts of the cloth of 4800tex, 4800tex three axial 30 parts of cloth, 30g/m24 parts of basalt fibres
Cloth, 60g/m24 parts of basalt fiber cloths.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 35 parts of vinylite, isophthalic unsaturated-resin 35 into stirred tank
Part, 0.5 part of benzoyl peroxide, 0.5 part of cyclohexanone peroxide, 0.5 part of t-butylperbenzoate, 0.02 part of ITO, GTO 0.03
Part, 10 parts of talcum powder, 5 parts of aluminium hydroxide, 5 parts of aluminium hydroxide, 0.5 part of iron oxide, 0.5 part of titanium dioxide, 0.5 part of UV-326,
It is transferred in glue groove after stirring;
(2) impregnation: three axial 30 parts of the cloth of 4800tex, three 30 parts of the axial cloth of 4800tex and 30g/m24 parts it is profound
Military rock fiber cloth, 60g/m24 parts of basalt fibres be arranged on warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 150 DEG C draws depanning.
Embodiment 9
A kind of freeway guardrail composite material, the component including following parts by weight: 40 parts of adjacent benzene unsaturated-resin, isophthalic
40 parts of unsaturated-resin, 0.05 part of ATO, 0.05 part of GTO, 10 parts of talcum powder, 5 parts of kaolin, 5 parts of aluminium hydroxide, mica powder
10 parts, 0.6 part of benzoyl peroxide, 0.6 part of cyclohexanone peroxide, 0.6 part of t-butylperbenzoate, isopropyl benzene hydroperoxide 0.6
Part, 0.6 part of tert-butyl hydroperoxide, 0.5 part of iron oxide, 0.5 part of titanium dioxide, 1 part of UV-326,1 part of UV-531,
Axial 35 parts of the cloth of 9600tex glass fibre two, 4800tex glass fibre four axial 40 parts of cloth, 40g/m2Basalt fiber cloth 8
Part, 60g/m28 parts of basalt fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 40 parts of adjacent benzene unsaturated-resin, isophthalic unsaturation tree into stirred tank
40 parts of rouge, 0.6 part of benzoyl peroxide, 0.6 part of cyclohexanone peroxide, 0.6 part of t-butylperbenzoate, isopropyl benzene hydroperoxide
0.6 part, 0.6 part of tert-butyl hydroperoxide, 0.05 part of ATO, 0.05 part of GTO, 10 parts of talcum powder, 5 parts of kaolin, aluminium hydroxide
5 parts, 10 parts of mica powder, 0.5 part of iron oxide, 0.5 part of titanium dioxide, 1 part of UV-326,1 part of UV-531, are transferred to glue groove after stirring
In;
(2) impregnation: axial 35 parts of the cloth of 9600tex glass fibre two, 40 parts of the axial cloth of 4800tex glass fibre four with
40g/m28 parts of basalt fiber cloth, 60g/m28 parts of basalt fiber cloth be placed on warp thread plate, warp thread plate be put into glue groove leaching
Glue;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 120 DEG C draws depanning.
Embodiment 10
A kind of freeway guardrail composite material, the component including following parts by weight: 30 parts of vinylite, adjacent benzene insatiable hunger
With 30 parts of resin, 30 parts of isophthalic unsaturated-resin, 0.05 part of ITO, 0.05 part of ATO, 0.05 part of GTO, 8 parts of calcium carbonate, talcum
8 parts of powder, 8 parts of kaolin, 8 parts of aluminium hydroxide, 8 parts of mica powder, 0.5 part of methyl ethyl ketone peroxide, 0.5 part of benzoyl peroxide, mistake
1 part of peroxyester, 1 part of t-butylperbenzoate, 0.5 part of isopropyl benzene hydroperoxide, 0.5 part of tert-butyl hydroperoxide, zinc oxide
0.5 part, 0.5 part of iron oxide, 1 part of titanium dioxide, 1 part, 30 parts 1 part of UV-326, UV-531 9600tex two axis of glass fibre
Xiang Bu, the axial cloth of 30 parts of 4800tex glass fibres three, 4800tex glass fibre four axial 30 parts of cloth, 30g/m2Basalt it is fine
Tie up 6 parts of basalt fiber cloth, the 60g/m of 6 parts of cloth, 40g/m26 parts of basalt fiber cloth.
A kind of preparation method of freeway guardrail composite material, includes the following steps:
(1) it prepares high-strength composite material: sequentially adding 30 parts of vinylite, adjacent benzene unsaturated-resin 30 into stirred tank
Part, 30 parts of isophthalic unsaturated-resin, 0.5 part of methyl ethyl ketone peroxide, 0.5 part of benzoyl peroxide, 1 part of cyclohexanone peroxide, mistake
Aoxidize 1 part of the tert-butyl ester, 0.5 part of isopropyl benzene hydroperoxide, 0.5 part of tert-butyl hydroperoxide, 0.05 part of ITO, 0.05 part of ATO,
0.05 part of GTO, 8 parts of calcium carbonate, 8 parts of talcum powder, 8 parts of kaolin, 8 parts of aluminium hydroxide, 8 parts of mica powder, 0.5 part of zinc oxide, oxygen
Change 0.5 part of iron, 1 part of titanium dioxide, 1 part of UV-326,1 part of UV-531, is transferred in glue groove after stirring;
(2) impregnation: the axial cloth of glass fibre two of 30 parts of 9600tex, the axial cloth of 30 parts of 4800tex glass fibres three,
30 parts of the axial cloth of 4800tex glass fibre four and 30g/m26 parts of basalt fiber cloth, 40g/m 6 parts of basalt fiber cloth,
60g/m26 parts of basalt fiber cloth be placed on warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 130 DEG C draws depanning.
Bending strength test
The freeway guardrail composite material of the component preparation of 10 parts by weight of embodiment 1- embodiment according to the invention
Bending strength test, referring to GB/T9341-2000, obtained result is as follows for bending strength test:
The freeway guardrail composite material of the component preparation of 10 parts by weight of embodiment 1- embodiment according to the invention of table 1
Bending strength test
Bending strength (Mpa) | |
Embodiment 1 | 396 |
Embodiment 2 | 400 |
Embodiment 3 | 566 |
Embodiment 4 | 600 |
Embodiment 5 | 551 |
Embodiment 6 | 596 |
Embodiment 7 | 614 |
Embodiment 8 | 627 |
Embodiment 9 | 634 |
Embodiment 10 | 642 |
As it can be seen from table 1 freeway guardrail prepared by the component of 10 parts by weight of the embodiment of the present invention 1- embodiment
The bending strength of composite material is tested, it can be seen that the bending strength of freeway guardrail composite material of the invention is significantly larger than
The bending strength (270Mpa-350Mpa) of common freeway guardrail composite material, with freeway guardrail composite material
Middle resin, filler, curing agent, in ultraviolet absorbing agent is two or more mixtures and mixture quantity at infrared absorbent
More, bending strength numerical value is bigger, and impact strength increases.Further illustrate that freeway guardrail composite material of the invention has
Preferable toughness and impact resistance, not will receive destruction, the toughness of composite material is improved, mentioned when by external impacts
High application value.
The above is only section Examples of the invention, not do limitation in any form to the present invention, it is all according to
According to any simple modification that technical spirit of the invention makees above-described embodiment, equivalent variations and modification belong to the present invention
In technical proposal scope.
Claims (10)
1. a kind of freeway guardrail composite material, which is characterized in that the component including following parts by weight:
2. freeway guardrail composite material according to claim 1, it is characterised in that: the resin is vinyl tree
Rouge, adjacent one or more mixtures of benzene unsaturated-resin or isophthalic unsaturated-resin.
3. freeway guardrail composite material according to claim 1, it is characterised in that: the infrared absorbent is
One or more mixtures of ITO, ATO or GTO.
4. freeway guardrail composite material according to claim 1, it is characterised in that: the filler is calcium carbonate, cunning
One or more mixtures of mountain flour, kaolin, aluminium hydroxide or mica powder.
5. freeway guardrail composite material according to claim 1, it is characterised in that: the curing agent is peroxidating first
In ethyl ketone, benzoyl peroxide, cyclohexanone peroxide, t-butylperbenzoate, isopropyl benzene hydroperoxide or tert-butyl hydroperoxide
One or more kinds of mixtures.
6. freeway guardrail composite material according to claim 1, it is characterised in that: the ultraviolet absorbing agent is oxygen
Change one or more mixtures of zinc, iron oxide, titanium dioxide, UV-326 or UV-531.
7. freeway guardrail composite material according to claim 1, it is characterised in that: the Multiaxial Fiberglass Fabrics
For the mixing of one or more of the axial cloth of glass fibre two, the axial cloth of glass fibre three or the axial cloth of glass fibre four
Object.
8. freeway guardrail composite material according to claim 1, it is characterised in that: the Multiaxial Fiberglass Fabrics
It is axial for the axial cloth of glass fibre three, the axial cloth of glass fibre three, the glass fibre four of 4800tex of 4800tex of 2400tex
One or more mixtures of axial cloth of the glass fibre two of cloth or 9600tex.
9. freeway guardrail composite material according to claim 1, it is characterised in that: gram of the basalt fiber cloth
Weight is 30g/m2、40g/m2Or 60g/m2One or more mixtures of grammes per square metre.
10. a kind of preparation method of such as described in any item freeway guardrail composite materials of claim 1-9, feature exist
In including the following steps:
(1) it prepares high-strength composite material: sequentially adding resin, curing agent, infrared absorbent, filler, ultraviolet into stirred tank
Light absorbers are transferred in glue groove after stirring;
(2) impregnation: Multiaxial Fiberglass Fabrics and basalt fibre are arranged on warp thread plate, warp thread plate is put into glue groove impregnation;
(3) material after impregnation is then sequentially sent to preforming tool and molding die;
(4) curing molding at a temperature of 110 DEG C -180 DEG C draws depanning.