CN109721917A - A kind of poly methyl methacrylate plastic lens and preparation method thereof - Google Patents
A kind of poly methyl methacrylate plastic lens and preparation method thereof Download PDFInfo
- Publication number
- CN109721917A CN109721917A CN201811607981.0A CN201811607981A CN109721917A CN 109721917 A CN109721917 A CN 109721917A CN 201811607981 A CN201811607981 A CN 201811607981A CN 109721917 A CN109721917 A CN 109721917A
- Authority
- CN
- China
- Prior art keywords
- plastic lens
- methyl methacrylate
- parts
- poly
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to automobile lamp technical fields, and in particular to a kind of poly methyl methacrylate plastic lens include: 60-80 parts of polymethyl methacrylate by parts by weight of raw materials;10-20 parts of vinylsiloxane rubber;2-5 parts of radical initiator;0.5-1 parts of ultraviolet absorbing agent, plastic lens has that refractive index is good, transparency is high, light transmittance is high, the benefit performances such as ageing-resistant.
Description
Technical field
The invention belongs to automobile lamp technical fields, especially lens of car light, and in particular to a kind of car headlamp
Poly methyl methacrylate plastic lens and preparation method thereof.
Background technique
In automotive lighting field, using lens the object for being placed in its focus, focal plane or attachment can be carried out at
The characteristic of picture, realize dipped beam, distance light lighting pattern optical plan, be a kind of relatively common form, not only in traditional halogen
Plain light source, the occasion of high-pressure discharge light source are common, recently as the rise of LED light source, are also commonly used for LED light source
Closely, in the scheme of distance light automotive lighting.
With the continuous maturation of LED light source, the case where being conventionally used to brake lamp modulating signal lamps and lanterns, just towards being applied to head lamp
The occasion of illumination constantly promotes.After LED light source is applied to headlamps, one benefit of bring is exactly, relative to traditional
Halogen and gas photoelectricity light source can deserve to be called cold light source, the remote traditional light lower than with power of external heat radiation
Source, therefore heatproof plastic material lens more very different than glass just have ample scope for abilities, plastic material lens are light-weight with its
The characteristics of, promotion rate is quickly under the background of energy-saving and emission-reduction.But the refractive index of existing plastic lens is generally 1.3 or so,
Light transmittance is 90% or so, and refractive index, resistance to ag(e)ing and transparency are still undesirable, it is difficult to meet the needs of market.
Summary of the invention
One of the objects of the present invention is to provide a kind of poly methyl methacrylate plastic lens, have refractive index good, saturating
Lightness is high, light transmittance is high, the benefit performances such as ageing-resistant.
The second object of the present invention is to provide a kind of preparation method of poly methyl methacrylate plastic lens, this method
The plastic lens of preparation has that refractive index is good, transparency is high, light transmittance is high, the benefit performances such as ageing-resistant.
Specifically, first technical solution of the invention is as follows
A kind of poly methyl methacrylate plastic lens include: by parts by weight of raw materials
Further, further include,
5-8 parts of glass fibre;
8-10 parts of tantalum pentoxide.
Another technical solution of the invention is as follows:
A kind of preparation method of poly methyl methacrylate plastic lens, comprising the following steps:
Polymethyl methacrylate is dried into 4h in the blast drier of sealing, obtains dry poly-methyl methacrylate
Ester;
Dry polymethyl methacrylate is heated to molten condition, is added with stirring tantalum pentoxide, free radical draws
Agent and vinylsiloxane rubber are sent out, continues insulated and stirred 30-45min, obtains modified poly (methyl methacrylate);
Ultraviolet absorbing agent and glass fibre are added in modified poly (methyl methacrylate), continuation insulated and stirred is uniform,
Obtain mixed raw material;
To in the mold of mixed raw material injected plastic lens, is demoulded after cooling and solidifying, obtain plastic lens.
It is further, described that by polymethyl methacrylate, dry 4h, drying temperature are in the blast drier of sealing
90℃。
Further, described that dry polymethyl methacrylate is heated to molten condition, heating temperature is 220 DEG C.
In conclusion the invention has the following advantages:
1. vinylsiloxane rubber is added in polymethyl methacrylate and is modified to it by the present invention, strand is improved
Rigidity, to improve modified poly (methyl methacrylate) anti-aging property;
2. the present invention in polymethyl methacrylate be added tantalum pentoxide it is modified, improve its refractive index and
Transparency;
3. glass fibre is added in polymethyl methacrylate and is modified to it by the present invention, optimization modeling is further increased
Expect the anti-aging property of lens.
Specific embodiment
Technical solution of the present invention is further illustrated below by way of specific embodiment, and specific embodiment does not represent to this hair
The limitation of bright protection scope.Other people according to the present invention theory made it is some it is nonessential modification and adjustment still fall within this hair
Bright protection scope.
Main raw material(s):
PMMA:HW55 9V913 wins wound Degussa;
Vinylsiloxane rubber: A board;
Tantalum pentoxide: Taizhou City Ai Tesi optical material Co., Ltd;
Embodiment 1
A kind of poly methyl methacrylate plastic lens, raw material include: by weight
In the embodiment poly methyl methacrylate plastic lens preparation method the following steps are included:
S11 dry 4h in the blast drier of 90 DEG C of constant temperature of sealing by polymethyl methacrylate, obtains drying
Polymethyl methacrylate;
65 parts of dry polymethyl methacrylates are heated to molten condition at 220 DEG C by S12, are added with stirring 8 parts
Tantalum pentoxide, 3 parts of radical initiators and 10 parts of vinylsiloxane rubbers continue insulated and stirred 30-45min, obtain modified poly-
Methyl methacrylate;
0.5 part of ultraviolet absorbing agent and 6 parts of glass fibres is added in S13 in modified poly (methyl methacrylate), after continuation of insurance
Temperature stirs evenly, and obtains mixed raw material;
S14 demoulds after cooling and solidifying in the mold of mixed raw material injected plastic lens, obtains plastic lens.
Embodiment 2
A kind of poly methyl methacrylate plastic lens include: by parts by weight of raw materials
The preparation method of poly methyl methacrylate plastic lens in the embodiment, comprising the following steps:
S21 dry 4h in 90 DEG C of sealing of blast drier by polymethyl methacrylate, obtains dry poly- first
Base methyl acrylate;
76 parts of dry polymethyl methacrylates are heated to molten condition at 220 DEG C by S22, are added with stirring 10 parts
Tantalum pentoxide, 3 parts of radical initiators and 15 parts of vinylsiloxane rubbers continue insulated and stirred 30-45min, obtain modified poly-
Methyl methacrylate;
0.8 part of ultraviolet absorbing agent and 8 parts of glass fibres is added in S23 in modified poly (methyl methacrylate), after continuation of insurance
Temperature stirs evenly, and obtains mixed raw material;
S24 demoulds after cooling and solidifying in the mold of mixed raw material injected plastic lens, obtains plastic lens.
Embodiment 3
A kind of poly methyl methacrylate plastic lens include: by parts by weight of raw materials
The preparation method of poly methyl methacrylate plastic lens in the embodiment, comprising the following steps:
S21 dry 4h in 90 DEG C of sealing of blast drier by polymethyl methacrylate, obtains dry poly- first
Base methyl acrylate;
68 parts of dry polymethyl methacrylates are heated to molten condition at 220 DEG C by S22, are added with stirring 8.3
Part tantalum pentoxide, 4 parts of radical initiators and 16 parts of vinylsiloxane rubbers, continue insulated and stirred 30-45min, are modified
Polymethyl methacrylate;
0.7 part of ultraviolet absorbing agent and 8 parts of glass fibres is added in S23 in modified poly (methyl methacrylate), after continuation of insurance
Temperature stirs evenly, and obtains mixed raw material;
S24 demoulds after cooling and solidifying in the mold of mixed raw material injected plastic lens, obtains plastic lens.
Test example
Anti-cracking performance, ageing-resistant performance, light transmittance are carried out to plastic lens obtained in embodiment 1 and embodiment 2 respectively
Test:
Test result table
Glass fibre that as can be seen from the above table, the present invention uses,.Vinylsiloxane rubber, tantalum pentoxide can be significant
Improve the cracking of lens, ageing resistance and light transmittance.
The above, the specific embodiment of foot prop only of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept, which is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of poly methyl methacrylate plastic lens, which is characterized in that it includes: by parts by weight of raw materials
2. poly methyl methacrylate plastic lens as described in claim 1, which is characterized in that further include glass fibre 5-8
Part;
8-10 parts of tantalum pentoxide.
3. a kind of preparation method of the poly methyl methacrylate plastic lens as described in claim 1-2 is any, feature exist
In, comprising the following steps:
Polymethyl methacrylate is dried into 4h in the blast drier of sealing, obtains dry polymethyl methacrylate;
Dry polymethyl methacrylate is heated to molten condition, is added with stirring tantalum pentoxide, radical initiator
And vinylsiloxane rubber, continue insulated and stirred 30-45min, obtains modified poly (methyl methacrylate);
Ultraviolet absorbing agent and glass fibre are added in modified poly (methyl methacrylate), continuation insulated and stirred is uniform, obtains
Mixed raw material;
To in the mold of mixed raw material injected plastic lens, is demoulded after cooling and solidifying, obtain plastic lens.
4. the preparation method of poly methyl methacrylate plastic lens as claimed in claim 3, which is characterized in that described to gather
Methyl methacrylate dry 4h in the blast drier of sealing, drying temperature are 90 DEG C.
5. the preparation method of poly methyl methacrylate plastic lens as claimed in claim 3, which is characterized in that described to do
Dry polymethyl methacrylate is heated to molten condition, and heating temperature is 220 DEG C.