CN109705756A - A kind of printing foam tape and its production technology - Google Patents
A kind of printing foam tape and its production technology Download PDFInfo
- Publication number
- CN109705756A CN109705756A CN201811572183.9A CN201811572183A CN109705756A CN 109705756 A CN109705756 A CN 109705756A CN 201811572183 A CN201811572183 A CN 201811572183A CN 109705756 A CN109705756 A CN 109705756A
- Authority
- CN
- China
- Prior art keywords
- foam
- printing
- layer
- glue layer
- release film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of printing foam tape and its production technologies, a kind of printing foam tape, including adhesive tape ontology, the adhesive tape ontology is by transparent release film, first glue layer, printing layer, PE foam and the second glue layer composition, and the upper surface of transparent release film is provided with the first glue layer, the two sides up and down of the PE foam are respectively arranged with printing layer and the second glue layer, and PE foam is provided with the side of printing layer and is connected with each other by the first glue layer and transparent release film, a kind of production technology for printing foam tape, the following steps are included: PE foam spy processing → LOGO printing → wet glue film → sided corona treatment and compound → drying and winding → cutting；The printing foam tape and its production technology, foam tape peel force is high, reduces Local residues when adhesive tape is torn and pastes problem, while facilitating the printing of LOGO, and the foamed cotton layer and release film after not will cause LOGO printing are mutually disengaged.
Description
Technical field
The present invention relates to tape technology field, specially a kind of printing foam tape and its production technology.
Background technique
Adhesive tape is made of substrate and adhesive two parts, is connected to two or more disjunct objects by bonding
Together；One layer of sticker is coated on its surface, earliest sticker comes from animal and plant, according to the use purpose of adhesive tape and answers
With field, type and effect are also different, and foam tape just belongs to intravarietal one, adhesive tape.
However to there is use intensity when in use inadequate for existing foam tape, and it is de- that connection is easy to happen when pasting
It falls, easily causes peel force too low when pasting, Local residues occur when adhesive tape being caused to tear and continue to be pasted on product, simultaneously
The printing of existing foam tape LOGO is inconvenient, and it is light that LOGO prints trace, while being not easy to observe, be easy to happen foamed cotton layer and from
Stickup break-off between type film, influences the normal use of foam tape.
In view of the above-mentioned problems, being badly in need of carrying out innovative design on the basis of original foam tape.
Summary of the invention
The purpose of the present invention is to provide a kind of printing foam tape and its production technologies, are mentioned with solving above-mentioned background technique
The foam tape peel force having is too low, and Local residues easily occur when adhesive tape is torn and paste phenomenon, while the print of LOGO
The problem of system is inconvenient, and the foamed cotton layer and release film after be easy to causeing LOGO to print are mutually disengaged.
To achieve the above object, the invention provides the following technical scheme: a kind of printing foam tape, including adhesive tape ontology,
The adhesive tape ontology is made of transparent release film, the first glue layer, printing layer, PE foam and the second glue layer, and transparent release
The upper surface of film is provided with the first glue layer, and the two sides up and down of the PE foam are respectively arranged with printing layer and the second glue layer,
And PE foam is provided with the side of printing layer and is connected with each other by the first glue layer and transparent release film.
Preferably, the transparent release film is common release paper composition, and the release value in two sides of transparent release film is set as
30-45g。
Preferably, the material of first glue layer and the second glue layer is oiliness acrylate pressure sensitive adhesive, and the first glue
The thickness of water layer and the second glue layer is respectively arranged with 30um and 80um.
Preferably, the PE foam with a thickness of between 0.2-0.5mm, and the anti-wet look of PE foam is provided with printing
Layer, and printing layer is LOGO printing.
A kind of a kind of production technology for printing foam tape as described above, comprising the following steps: PE foam spy processing →
LOGO printing → wet glue film → sided corona treatment and compound → drying and winding → cutting；
(1) PE foam is chosen, special processing is carried out to the two sides of PE foam, retain PE foam is at least bright face on one side；
(2) LOGO printing is carried out in the bright face of PE foam, prevents the progress of corona operation when bright face is printed；
(3) it chooses transparent release film and carries out gluing in one side, the first glue layer of suitable thickness is coated, in PE foam
Other side dark face carries out gluing, coats the second glue layer；
(4) to the strong sided corona treatment of the bright face progress of the PE foam after LOGO prints has been carried out, the stickup in the bright face of PE foam is improved
Property, and PE foam and transparent release film paste compound；
(5) to after compound PE foam and transparent release film dry so that the gluing of the PE foam other side is gradually micro-
It is dry, adhesive tape is formed, winding storage then is carried out to the adhesive tape of formation；
(6) adhesive tape after winding is integrally cut according to the required width of adhesive tape, obtains the glue of suitable dimension size
Band volume.
Preferably, 6 sections that baking oven used is equal part are dried, and the length of every section baking oven is 4m, and the inside of baking oven is dried
Dry temperature is followed successively by 60 DEG C, 65 DEG C, 85 DEG C, 120 DEG C, 120 DEG C, 70 DEG C.
Preferably, adhesive tape unreels equal with the speed of winding, and the revolving speed of let off roll and wind-up roll is 10-15m/
min。
Compared with prior art, the beneficial effects of the present invention are: in the printing foam tape and its production technology, the first glue
The thickness of water layer and the second glue layer is respectively arranged with 30um and 80um, is being able to maintain that the good of transparent release film and PE foam
When being fixedly connected, the thickness problems of too of adhesive tape ontology not will cause, and the second glue layer of 80um, meeting market adhesive tape
Normal use when, avoid the dosage of the second glue layer from excessively causing the increasing of production cost, release value is set as 30-45g's
The transparent release film that common release paper is constituted plays the buffer action of product simultaneously, peeling force is big, improves glue moisture-proof, grease proofing
When the application intensity that band uses, when tearing adhesive tape, reduction adhesive tape, which is locally present, to be adhered on product, the behaviour that tears of Convenient adhesive tape
It carries out, the LOGO printing being arranged on the anti-wet look of PE foam facilitates the understanding of foam tape to weave, after LOGO printing
Strong sided corona treatment, being adhesively fixed between convenient glue, so that adhesive tape is integrally stronger, it, will not be because LOGO's using stabilization
Print the unstability for causing foam tape integrally to use.
Detailed description of the invention
Examples of the present invention will be described by way of reference to the accompanying drawings, in which:
Fig. 1 is adhesive tape ontology PE structural schematic diagram of the present invention；
Fig. 2 is present invention process flow diagram.
In figure: 1, adhesive tape ontology；2, transparent release film；3, the first glue layer；4, printing layer；5, PE foam；6, the second glue
Water layer.
Specific embodiment
In conjunction with the accompanying drawings, the present invention is further explained in detail.These attached drawings are simplified schematic diagram, only with
Illustration illustrates basic structure of the invention, therefore it only shows the composition relevant to the invention.
As shown in Figure 1, a kind of printing foam tape, including adhesive tape ontology 1, adhesive tape ontology 1 is by transparent release film 2, first
Glue layer 3, printing layer 4, PE foam 5 and the second glue layer 6 composition, and the upper surface of transparent release film 2 is provided with the first glue
The two sides up and down of 3, PE of layer foam 5 are respectively arranged with printing layer 4 and the second glue layer 6, and PE foam 5 is provided with printing layer 4
Side is connected with each other by the first glue layer 3 with transparent release film 2.
Embodiment 1:
A kind of printing foam tape, including adhesive tape ontology 1, adhesive tape ontology 1 is by transparent release film 2, the first glue layer 3, print
Brush layer 4, PE foam 5 and the second glue layer 6 composition, and the upper surface of transparent release film 2 is provided with the first glue layer 3, PE foam 5
Two sides up and down be respectively arranged with printing layer 4 and the second glue layer 6, and PE foam 5 is provided with the side of printing layer 4 by first
Glue layer 3 and transparent release film 2 are connected with each other；Transparent release film 2 is that common release paper is constituted, and the two sides of transparent release film 2
Release value is set as 30g；The material of first glue layer 3 and the second glue layer 6 is oiliness acrylate pressure sensitive adhesive, and the first glue
The thickness of layer 3 and the second glue layer 6 is respectively arranged with 30um and 80um；PE foam 5 with a thickness of 0.2mm, and PE foam 5 is anti-
Wet look is provided with printing layer 4, and printing layer 4 is LOGO printing.
A kind of production technology of printing foam tape as above, comprising the following steps:
Step 1: choosing PE foam 5, carries out special processing to the two sides of PE foam 5, and it is bright for retaining the minimum one side of PE foam 5
Face；
Step 2: LOGO printing is carried out in the bright face of PE foam 5, prevents the progress of corona operation when bright face is printed；
Step 3: transparent release film 2 is chosen in one side and carries out gluing, the first glue layer 3 of suitable thickness is coated, in PE
The other side dark face of foam 5 carries out gluing, coats the second glue layer 6；
Step 4: strong sided corona treatment is carried out to the bright face of PE foam 5 after LOGO prints has been carried out, improves the bright face of PE foam 5
Stickup, and PE foam 5 and transparent release film 2 paste compound；
Step 5: to after compound PE foam 5 and transparent release film 2 dry so that the gluing of 5 other side of PE foam
Gradually micro- drying forms adhesive tape, then carries out winding storage to the adhesive tape of formation；
Step 6: the adhesive tape after winding is integrally cut according to the required width of adhesive tape, obtains suitable dimension size
Tape roll；
Preferably, drying 6 sections that baking oven used is equal part, and the length of every section baking oven is 4m, and baking oven is interior
Portion's drying temperature is followed successively by 60 DEG C, 65 DEG C, 85 DEG C, 120 DEG C, 120 DEG C, 70 DEG C.
Preferably, unreeling for adhesive tape is equal with the speed of winding, and the revolving speed of let off roll and wind-up roll is 10m/
min。
Embodiment 2:
A kind of printing foam tape, including adhesive tape ontology 1, adhesive tape ontology 1 is by transparent release film 2, the first glue layer 3, print
Brush layer 4, PE foam 5 and the second glue layer 6 composition, and the upper surface of transparent release film 2 is provided with the first glue layer 3, PE foam 5
Two sides up and down be respectively arranged with printing layer 4 and the second glue layer 6, and PE foam 5 is provided with the side of printing layer 4 by first
Glue layer 3 and transparent release film 2 are connected with each other；Transparent release film 2 is that common release paper is constituted, and the two sides of transparent release film 2
Release value is set as 45g；The material of first glue layer 3 and the second glue layer 6 is oiliness acrylate pressure sensitive adhesive, and the first glue
The thickness of layer 3 and the second glue layer 6 is respectively arranged with 30um and 80um；PE foam 5 with a thickness of 0.5mm, and PE foam 5 is anti-
Wet look is provided with printing layer 4, and printing layer 4 is LOGO printing.
A kind of production technology of printing foam tape as above, comprising the following steps:
Step 1: choosing PE foam 5, carries out special processing to the two sides of PE foam 5, and it is bright for retaining the minimum one side of PE foam 5
Face；
Step 2: LOGO printing is carried out in the bright face of PE foam 5, prevents the progress of corona operation when bright face is printed；
Step 3: transparent release film 2 is chosen in one side and carries out gluing, the first glue layer 3 of suitable thickness is coated, in PE
The other side dark face of foam 5 carries out gluing, coats the second glue layer 6；
Step 4: strong sided corona treatment is carried out to the bright face of PE foam 5 after LOGO prints has been carried out, improves the bright face of PE foam 5
Stickup, and PE foam 5 and transparent release film 2 paste compound；
Step 5: to after compound PE foam 5 and transparent release film 2 dry so that the gluing of 5 other side of PE foam
Gradually micro- drying forms adhesive tape, then carries out winding storage to the adhesive tape of formation；
Step 6: the adhesive tape after winding is integrally cut according to the required width of adhesive tape, obtains suitable dimension size
Tape roll；
Preferably, drying 6 sections that baking oven used is equal part, and the length of every section baking oven is 4m, and baking oven is interior
Portion's drying temperature is followed successively by 60 DEG C, 65 DEG C, 85 DEG C, 120 DEG C, 120 DEG C, 70 DEG C.
Preferably, unreeling for adhesive tape is equal with the speed of winding, and the revolving speed of let off roll and wind-up roll is 15m/
min。
Embodiment 3:
A kind of printing foam tape, including adhesive tape ontology 1, adhesive tape ontology 1 is by transparent release film 2, the first glue layer 3, print
Brush layer 4, PE foam 5 and the second glue layer 6 composition, and the upper surface of transparent release film 2 is provided with the first glue layer 3, PE foam 5
Two sides up and down be respectively arranged with printing layer 4 and the second glue layer 6, and PE foam 5 is provided with the side of printing layer 4 by first
Glue layer 3 and transparent release film 2 are connected with each other；Transparent release film 2 is that common release paper is constituted, and the two sides of transparent release film 2
Release value is set as 45g；The material of first glue layer 3 and the second glue layer 6 is oiliness acrylate pressure sensitive adhesive, and the first glue
The thickness of layer 3 and the second glue layer 6 is respectively arranged with 30um and 80um；PE foam 5 with a thickness of 0.2mm, and PE foam 5 is anti-
Wet look is provided with printing layer 4, and printing layer 4 is LOGO printing.
A kind of production technology of printing foam tape as above, comprising the following steps:
Step 1: choosing PE foam 5, carries out special processing to the two sides of PE foam 5, and it is bright for retaining the minimum one side of PE foam 5
Face；
Step 2: LOGO printing is carried out in the bright face of PE foam 5, prevents the progress of corona operation when bright face is printed；
Step 3: transparent release film 2 is chosen in one side and carries out gluing, the first glue layer 3 of suitable thickness is coated, in PE
The other side dark face of foam 5 carries out gluing, coats the second glue layer 6；
Step 4: strong sided corona treatment is carried out to the bright face of PE foam 5 after LOGO prints has been carried out, improves the bright face of PE foam 5
Stickup, and PE foam 5 and transparent release film 2 paste compound；
Step 5: to after compound PE foam 5 and transparent release film 2 dry so that the gluing of 5 other side of PE foam
Gradually micro- drying forms adhesive tape, then carries out winding storage to the adhesive tape of formation；
Step 6: the adhesive tape after winding is integrally cut according to the required width of adhesive tape, obtains suitable dimension size
Tape roll；
Preferably, drying 6 sections that baking oven used is equal part, and the length of every section baking oven is 4m, and baking oven is interior
Portion's drying temperature is followed successively by 60 DEG C, 65 DEG C, 85 DEG C, 120 DEG C, 120 DEG C, 70 DEG C.
Preferably, unreeling for adhesive tape is equal with the speed of winding, and the revolving speed of let off roll and wind-up roll is 10m/
min。
It is above-mentioned according to the present invention for enlightenment, through the above description, relevant staff completely can without departing from
In the range of this invention technical idea, various changes and amendments are carried out.The technical scope of this invention is not limited to
In the content on specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (7)
1. a kind of printing foam tape, including adhesive tape ontology, transparent release film, the first glue layer, printing layer, PE foam, second
Glue layer, it is characterised in that: the adhesive tape ontology is by transparent release film, the first glue layer, printing layer, PE foam and the second glue
Layer composition, and the upper surface of transparent release film is provided with the first glue layer, the two sides up and down of the PE foam are respectively arranged with print
Brush layer and the second glue layer, and PE foam is provided with the side of printing layer and is mutually interconnected by the first glue layer with transparent release film
It connects.
2. a kind of printing foam tape according to claim 1, it is characterised in that: the transparent release film is common release
Paper is constituted, and the release value in two sides of transparent release film is set as 30-45g.
3. a kind of printing foam tape according to claim 1, it is characterised in that: first glue layer and the second glue
The material of layer is oiliness acrylate pressure sensitive adhesive, and the thickness of the first glue layer and the second glue layer be respectively arranged with 30um and
80um。
4. a kind of printing foam tape according to claim 1, it is characterised in that: the PE foam with a thickness of 0.2-
Between 0.5mm, and the anti-wet look of PE foam is provided with printing layer, and printing layer is LOGO printing.
5. a kind of production technology of printing foam tape according to claim 1-4, it is characterised in that: including with
Lower step: PE foam spy processing → LOGO printing → wet glue film → sided corona treatment and compound → drying and winding → cutting；
(1) PE foam is chosen, special processing is carried out to the two sides of PE foam, retain PE foam is at least bright face on one side；
(2) LOGO printing is carried out in the bright face of PE foam, prevents the progress of corona operation when bright face is printed；
(3) it chooses transparent release film and carries out gluing in one side, the first glue layer of suitable thickness is coated, in the another of PE foam
Side dark face carries out gluing, coats the second glue layer；
(4) to the strong sided corona treatment of the bright face progress of the PE foam after LOGO prints has been carried out, the stickup in the bright face of PE foam is improved, and
PE foam and transparent release film paste compound；
(5) to after compound PE foam and transparent release film dry so that the gradually micro- drying of the gluing of the PE foam other side,
Adhesive tape is formed, winding storage then is carried out to the adhesive tape of formation；
(6) adhesive tape after winding is integrally cut according to the required width of adhesive tape, obtains the tape roll of suitable dimension size.
6. a kind of production technology for printing foam tape according to claim 5, it is characterised in that: the drying is used to dry
Case is 6 sections of equal part, and the length of every section baking oven is 4m, and the inside drying temperature of baking oven is followed successively by 60 DEG C, 65 DEG C, 85
℃、120℃、120℃、70℃。
7. a kind of production technology for printing foam tape according to claim 5, it is characterised in that: the adhesive tape unreels
It is equal with the speed of winding, and the revolving speed of let off roll and wind-up roll is 10-15m/min.