CN109705541A - A kind of plastic automotive accessory - Google Patents
A kind of plastic automotive accessory Download PDFInfo
- Publication number
- CN109705541A CN109705541A CN201711012885.7A CN201711012885A CN109705541A CN 109705541 A CN109705541 A CN 109705541A CN 201711012885 A CN201711012885 A CN 201711012885A CN 109705541 A CN109705541 A CN 109705541A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- wollastonite
- plastic automotive
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of plastic automotive accessories, are mainly made of the following component counted with mass fraction: 5-15 parts of polypropylene fire retardant master batch, 20-40 parts of polypropylene, 20-50 parts of poly butylene succinate, 15-20 parts of nylon -66, asbestos fibre 5-15 parts short, 5-15 parts of sisal fiber, 3-5 parts of wollastonite, 5-10 parts of polyimides, 0.3-0.5 parts of plasticizer, 0.5-1 parts of ethylene propylene diene rubber, 0.04 part of carbon black, 2-4 parts of antioxidant, 0.5-1.5 parts of Noryl.Automobile parts of the invention have good mechanical performance, being not easy to become fragile under high temperature environment is also unlikely to deform.
Description
Technical field
The present invention relates to technical field of automobile accessories more particularly to a kind of plastic automotive accessories.
Background technique
Existing plastic automotive accessory high temperature resistance is poor, is easy to become fragile with the part of engine close contact, fragmentation
And heat expansion deformation occurs.
Summary of the invention
In order to solve the above-mentioned technical problem, provide that a kind of high temperature resistance is good, plastic automotive accessory of high mechanical strength, this
Invention the following technical schemes are provided:
A kind of plastic automotive accessory, is made of the following component counted with mass fraction: 5-15 parts of polypropylene fire retardant master batch gathers
20-40 parts of propylene, 20-50 parts of poly butylene succinate, 15-20 parts of nylon -66, asbestos fibre 5-15 parts short, sisal fiber
5-15 parts, 3-5 parts of wollastonite, 5-10 parts of polyimides, 0.3-0.5 parts of plasticizer, 0.5-1 parts of ethylene propylene diene rubber, carbon black
0.04 part, 2-4 parts of antioxidant, 0.5-1.5 parts of Noryl.
Further, the wollastonite is replaced by silicon dioxide microsphere.
Further, be made of the following component counted with mass fraction: 10 parts of polypropylene fire retardant master batch, gathers 3 parts of polypropylene
35 parts of succinic acid-butanediol ester, 17.5 parts of nylon -66,10 parts of short asbestos fibre, 10 parts of sisal fiber, 4 parts of wollastonite, polyamides
8 parts of imines, 0.4 part of plasticizer, 0.75 part of ethylene propylene diene rubber, 0.04 part of carbon black, 3 parts of antioxidant, 1 part of Noryl.
Further, 5 parts of polypropylene fire retardant master batch, 20 parts of polypropylene, 20 parts of poly butylene succinate, nylon -66 15
Part, 5 parts of short asbestos fibre, 5 parts of sisal fiber, 3 parts of wollastonite, 5 parts of polyimides, 0.3 part of plasticizer, ethylene propylene diene rubber
0.5 part, 0.04 part of carbon black, 2 parts of antioxidant, 0.5 part of Noryl.
Further, 15 parts of polypropylene fire retardant master batch, 40 parts of polypropylene, 50 parts of poly butylene succinate, nylon -66
20 parts, 15 parts of short asbestos fibre, 15 parts of sisal fiber, 5 parts of wollastonite, 10 parts of polyimides, 0.5 part of plasticizer, EPDM
1 part of rubber, 0.04 part of carbon black, 4 parts of antioxidant, 1.5 parts of Noryl.
The beneficial effects of the present invention are: it is particularly suitable for the position close with engine, under the continuous high temperature of 120h
Embrittlement will not occur.
Specific embodiment
Embodiment 1,
A kind of plastic automotive accessory, is made of the following component counted with mass fraction: 10 parts of polypropylene fire retardant master batch, poly- third
3 parts of alkene, 35 parts of poly butylene succinate, 17.5 parts of nylon -66,10 parts of short asbestos fibre, 10 parts of sisal fiber, wollastonite 4
Part, 8 parts of polyimides, 0.4 part of plasticizer, 0.75 part of ethylene propylene diene rubber, 0.04 part of carbon black, 3 parts of antioxidant, modified polyphenyl
1 part of ether.
Embodiment 2,
A kind of plastic automotive accessory, 5 parts of polypropylene fire retardant master batch, 20 parts of polypropylene, 20 parts of poly butylene succinate, Buddhist nun
Imperial -66 15 parts, 5 parts of short asbestos fibre, 5 parts of sisal fiber, 3 parts of wollastonite, 5 parts of polyimides, 0.3 part of plasticizer, ternary second
Third 0.5 part of rubber, 0.04 part of carbon black, 2 parts of antioxidant, 0.5 part of Noryl.
Embodiment 3,
A kind of plastic automotive accessory, 15 parts of polypropylene fire retardant master batch, 40 parts of polypropylene, 50 parts of poly butylene succinate,
20 parts of nylon -66,15 parts of short asbestos fibre, 15 parts of sisal fiber, 5 parts of wollastonite, 10 parts of polyimides, 0.5 part of plasticizer,
1 part of ethylene propylene diene rubber, 0.04 part of carbon black, 4 parts of antioxidant, 1.5 parts of Noryl.
Claims (5)
1. a kind of plastic automotive accessory, it is characterised in that: be made of the following component counted with mass fraction: polypropylene fire retardant master batch
5-15 parts, 20-40 parts of polypropylene, 20-50 parts of poly butylene succinate, 15-20 parts of nylon -66, it is asbestos fibre 5-15 parts short,
5-15 parts of sisal fiber, 3-5 parts of wollastonite, 5-10 parts of polyimides, 0.3-0.5 parts of plasticizer, ethylene propylene diene rubber 0.5-1
Part, 0.04 part of carbon black, 2-4 parts of antioxidant, 0.5-1.5 parts of Noryl.
2. a kind of plastic automotive accessory as described in claim 1, it is characterised in that: the wollastonite is by silicon dioxide microsphere generation
It replaces.
3. a kind of plastic automotive accessory as described in claim 1, it is characterised in that: by the following component group in terms of mass fraction
At: 10 parts of polypropylene fire retardant master batch, 3 parts of polypropylene, 35 parts of poly butylene succinate, 17.5 parts of nylon -66, short asbestos are fine
Tie up 10 parts, 10 parts of sisal fiber, 4 parts of wollastonite, 8 parts of polyimides, 0.4 part of plasticizer, 0.75 part of ethylene propylene diene rubber, carbon black
0.04 part, 3 parts of antioxidant, 1 part of Noryl.
4. a kind of plastic automotive accessory as described in claim 1, it is characterised in that: 5 parts of polypropylene fire retardant master batch, polypropylene 20
Part, 20 parts of poly butylene succinate, 15 parts of nylon -66,5 parts of short asbestos fibre, 5 parts of sisal fiber, 3 parts of wollastonite, polyamides
5 parts of imines, 0.3 part of plasticizer, 0.5 part of ethylene propylene diene rubber, 0.04 part of carbon black, 2 parts of antioxidant, 0.5 part of Noryl.
5. a kind of plastic automotive accessory as described in claim 1, it is characterised in that: 15 parts of polypropylene fire retardant master batch, polypropylene
40 parts, 50 parts of poly butylene succinate, 20 parts of nylon -66,15 parts of short asbestos fibre, 15 parts of sisal fiber, 5 parts of wollastonite,
10 parts of polyimides, 0.5 part of plasticizer, 1 part of ethylene propylene diene rubber, 0.04 part of carbon black, 4 parts of antioxidant, Noryl 1.5
Part.