CN109695646A - A kind of brake block of perfect heat-dissipating - Google Patents
A kind of brake block of perfect heat-dissipating Download PDFInfo
- Publication number
- CN109695646A CN109695646A CN201711002413.3A CN201711002413A CN109695646A CN 109695646 A CN109695646 A CN 109695646A CN 201711002413 A CN201711002413 A CN 201711002413A CN 109695646 A CN109695646 A CN 109695646A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel disc
- brake block
- dissipating
- perfect heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of brake blocks of perfect heat-dissipating, including steel disc, one layer of friction material layer is covered on steel disc, the steel disc upper end is equipped with the first installing port, lower end is equipped with the second installing port, steel disc is equipped with chip space, the friction material layer includes that each component of following parts by weight is prepared: 10-20 parts of phenolic resin, 0.5-2 parts of epoxy resin, 3-12 parts of nitrile rubber, 2-10 parts of butadiene rubber, 5-10 parts of carbon fiber, 3-8 parts of aramid fiber, 2-5 parts of glass fibre, 10-30 parts of magnesium titanate platelet, 5-20 parts of metatitanic acid ferrisodium platelet, 20-40 parts of barium sulfate, 2-5 parts of nano silica, 2-5 parts of sepiolite, 2-8 parts of alumina powder, 0.2-1.5 parts of diphenylguanidine, 0.1-0.5 parts of zinc oxide, 1-4 parts of vermiculite power , 2-5 parts of petroleum coke, 1-5 parts of artificial graphite, 3-10 parts of bamboo charcoal, 0.01-0.05 parts of promotor, 0.01-0.05 parts of anti-aging agent.The configuration of the present invention is simple, it is practical and convenient, the accumulation of dust is avoided, ensure that the stabilization of the coefficient of friction of brake block, the quality for improving brake block, improves security performance, reduces noise, service life is extended, the frequency and use cost of replacement is reduced, is conducive to application.
Description
Technical field
The present invention relates to a kind of brake block, in particular to a kind of brake block of perfect heat-dissipating.
Background technique
Brake block includes steel back and the friction material that is bonded in steel back.Currently, for the brake block friction material on vehicle
Material mostly uses asbestos brake lining, but the asbestos in asbestos brake lining have carcinogenesis, cause seriously to the physical and mental health of people
It influences.Brake block is easy to temperature and reaches 1000 degree or more when speed per hour reaches 300 kilometers or more after brake, it is therefore desirable to
Brake material wants high temperature resistant, indeformable etc.;And existing brake block is easy sedimentating dust, dust accumulation reduces rubbing for brake block
Coefficient is wiped, noise is bigger, while when in use, and the thickness of frictional layer has certain requirement on brake block, too thin to will affect brake
The sensitivity of vehicle, reduces security performance.
Summary of the invention
The object of the invention is that providing, a kind of structure is simple, and use is safe, and coefficient of friction is high, the brake of perfect heat-dissipating
Vehicle piece.
To achieve the goals above, the technical solution adopted by the present invention is that such: the brake of perfect heat-dissipating of the invention
Vehicle piece, including steel disc, are covered with one layer of friction material layer on steel disc, and the steel disc upper end is equipped with the first installing port, and lower end is equipped with the
Two installing ports, steel disc are equipped with chip space, and the friction material layer includes that each component of following parts by weight is prepared: phenolic aldehyde tree
10-20 parts of rouge, 0.5-2 parts of epoxy resin, 3-12 parts of nitrile rubber, 2-10 parts of butadiene rubber, 5-10 parts of carbon fiber, aramid fiber
3-8 parts, 2-5 parts of glass fibre, 10-30 parts of magnesium titanate platelet, 5-20 parts of metatitanic acid ferrisodium platelet, 20-40 parts of barium sulfate, nanometer
2-5 parts of silica, 2-5 parts of sepiolite, 2-8 parts of alumina powder, 0.2-1.5 parts of diphenylguanidine, 0.1-0.5 parts of zinc oxide, vermiculite
1-4 parts of powder, 2-5 parts of petroleum coke, 1-5 parts of artificial graphite, 3-10 parts of bamboo charcoal, 0.01-0.05 parts of promotor, anti-aging agent 0.01-
0.05 part.
Preferably, the promotor is promotor TT, Urotropinum or captax.
Preferably, the anti-aging agent is N- phenyl -2- naphthylamines.
Compared with the prior art, the advantages of the present invention are as follows: the configuration of the present invention is simple, it is practical and convenient, avoid dust
Accumulation, ensure that the stabilization of the coefficient of friction of brake block, improves the quality of brake block, improve security performance, reduce and make an uproar
Sound extends service life, reduces the frequency and use cost of replacement, is conducive to application.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
Specific embodiment
The present invention will be further described with reference to the accompanying drawings.
Referring to Fig. 1, the brake block of perfect heat-dissipating of the invention, including steel disc 1 is covered with one layer of friction material on steel disc 1
Layer 2,1 upper end of steel disc are equipped with the first installing port 3, and lower end is equipped with the second installing port 4, and steel disc 1 is equipped with chip space 5, described
Friction material layer 2 includes that each component of following parts by weight is prepared: 10-20 parts of phenolic resin, 0.5-2 parts of epoxy resin, fourth
3-12 parts of nitrile rubber, 2-10 parts of butadiene rubber, 5-10 parts of carbon fiber, 3-8 parts of aramid fiber, 2-5 parts of glass fibre, magnesium titanate
10-30 parts of platelet, 5-20 parts of metatitanic acid ferrisodium platelet, 20-40 parts of barium sulfate, 2-5 parts of nano silica, 2-5 parts of sepiolite, oxygen
Change aluminium powder 2-8 parts, 0.2-1.5 parts of diphenylguanidine, 0.1-0.5 parts of zinc oxide, 1-4 parts of vermiculite power, 2-5 parts of petroleum coke, artificial graphite
1-5 parts, 3-10 parts of bamboo charcoal, 0.01-0.05 parts of promotor, 0.01-0.05 parts of anti-aging agent, the promotor be promotor TT,
Urotropinum or captax, the anti-aging agent are N- phenyl -2- naphthylamines.
The configuration of the present invention is simple, it is practical and convenient, the accumulation of dust is avoided, ensure that the steady of the coefficient of friction of brake block
It is fixed, the quality of brake block is improved, security performance is improved, reduces noise, extends service life, reduces the frequency of replacement
Rate and use cost, are conducive to application.
Claims (3)
1. a kind of brake block of perfect heat-dissipating, including steel disc, one layer of friction material layer is covered on steel disc, it is characterised in that: institute
Steel disc upper end is stated equipped with the first installing port, lower end is equipped with the second installing port, and steel disc is equipped with chip space, the friction material layer packet
The each component for including following parts by weight is prepared: 10-20 parts of phenolic resin, 0.5-2 parts of epoxy resin, 3-12 parts of nitrile rubber,
2-10 parts of butadiene rubber, 5-10 parts of carbon fiber, 3-8 parts of aramid fiber, 2-5 parts of glass fibre, 10-30 parts of magnesium titanate platelet,
5-20 parts of metatitanic acid ferrisodium platelet, 20-40 parts of barium sulfate, 2-5 parts of nano silica, 2-5 parts of sepiolite, 2-8 parts of alumina powder,
0.2-1.5 parts of diphenylguanidine, 0.1-0.5 parts of zinc oxide, 1-4 parts of vermiculite power, 2-5 parts of petroleum coke, 1-5 parts of artificial graphite, bamboo charcoal 3-
10 parts, 0.01-0.05 parts of promotor, 0.01-0.05 parts of anti-aging agent.
2. the brake block of perfect heat-dissipating according to claim 1, it is characterised in that: the promotor be promotor TT,
Urotropinum or captax.
3. the brake block of perfect heat-dissipating according to claim 1, it is characterised in that: the anti-aging agent is N- phenyl-
2- naphthylamines.