CN109679478A - A kind of high pressure resistant steam impringement metal material coating and preparation method thereof - Google Patents
A kind of high pressure resistant steam impringement metal material coating and preparation method thereof Download PDFInfo
- Publication number
- CN109679478A CN109679478A CN201811639259.5A CN201811639259A CN109679478A CN 109679478 A CN109679478 A CN 109679478A CN 201811639259 A CN201811639259 A CN 201811639259A CN 109679478 A CN109679478 A CN 109679478A
- Authority
- CN
- China
- Prior art keywords
- component
- metal material
- high pressure
- pressure resistant
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of high pressure resistant steam impringement metal material coating and preparation method thereof, the paint composite is by A) 10-40 parts of organosilicon modified crylic acid resin, B) hydroxy acrylic acid polyol resin 10-40 parts, C) there are 1-20 parts of organosiloxane resins of hydrolyzable, D) pigments and fillers 0-30 parts, E) 0.1-10 parts of organic phosphorus compound class stabilization agent, F) organic phenolic antioxidant 0.1-10 parts, G) 0.1-10 parts of the auxiliary agents such as moistening flatting agent, H) 1-40 parts of organic solvent and I) mating by weight percentage crosslinking agent forms.Compared with prior art, the present invention has the film forming physical property such as excellent adhesion, water resistance, high pressure resistant steam flush to metal material.According to the needs that vehicle designs, the glossiness of film is adjustable, and resistance to various chemicals performances are excellent, and has design appearance adjustability.Especially suitable for the automobile exterior part used in cold zone, has many advantages, such as corrosion resistance, heatproof is aqueous and high pressure resistant steam impringement.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of high pressure resistant steam impringement metal material coating and its
Preparation method.
Background technique
In American-European and China northeast cold district, carwash often is impacted with high-temperature steam when winter is to car detailing.
High steam can not only sterilize, but also can decontaminate, and have unique thermal decomposition function, can rapidly dissolve and freeze, silt and spot it is viscous
Stickiness matter allows it to be detached from the Automotive Paint Film Properties surface attached, achievees the purpose that cleaning.But due to what is used when high-temperature steam carwash
Vapor (steam) temperature is excessively high, and pressure crosses the impacting with high pressure burden resistant to high temperatures and anti-that conference additionally increases Automotive Paint Film Properties, prolonged high temperature
High steam impact carwash will cause protection paint film and become soft and deformed or even cause local shedding.
In addition, winter in order to prevent traffic freeze and when driving vehicle occur skidding accident, the part road surface road Hui You
Political affairs administrative department arranges road surface salting to effectively prevent road surface freezing by reducing the freezing point of ice water.But these salt content are high
Ice water when being splashed on the vehicle of walking, remaining salinity is easy to the vehicle body crossed to coating protection and forms corrosion, causes outer
Corrosion in the beautiful forfeiture of table and then formation structure.
In view of the above-mentioned problems, there is coating worker to start to develop the serial 2 liquid type paint composites of acroleic acid polyurethane, endeavour
Surface is set to be hardened in the degree of cross linking raising by film coated surface, to improve the water resistance and chemical resistance of paint film.However it is this kind of
The paint film of coating has just been formed at coating initial stage and its water resistance gradually successively decreases during use, can not be fully met and is used for
The high pressure resistant steam impringement carwash demand of automobile exterior paint.
On the other hand, there is producer to meet the high temperature steam impact of paint film, after completing paint spraying, then plus brush
One layer of high temperature resistant wax liquor protects paint film.Economic cost is caused to increase and as the film thickness increase of protective layer leads to paint film
Apparent visual aesthetics is impaired, and substantially there is no promotions largely for the high temperature steam impact of film.
Summary of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of high pressure resistant steam to rush
Hitting property metal material coating and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions: a kind of high pressure resistant steam impringement metal material use
Coating, the coating include component A and B component, and the component A includes the composition of following parts by weight:
The B component is crosslinking agent and organic solvent;
The mass ratio of crosslinking agent is 100:(25~50 in the component A and B component).
The present invention selects above-mentioned raw materials, under the premise of guaranteeing the compatibility between different types of resin, ensure that simultaneously
Adhesion between paint film and the metal base of difficult attachment, the appearance colour and water resistance of paint film, salt fog resistance and resistance to
High steam impact.
Preferably, the component A includes following parts by weight:
Preferably, the organosilicon modified crylic acid resin is organic silicon monomer and acrylic acid containing vinyl-functional
Esters monomer pass through Raolical polymerizable made of synthetic resin, the acrylic ester monomer include methacrylate,
One of acrylate or crylic acid hydroxy ester, the glass transition temperature of the organosilicon modified crylic acid resin are 20~90
℃.Acrylic resin side chain has polar carboxyl and hydroxyl group, can assign paint film good resistance to thermal oxide, weatherability, but
Its cold resistance, water resistance, resistance to steam impringement are poor.Organosilicon modified crylic acid resin has preferable curability, both can be with
Heating occurs with diisocyanates curing agent and reacts solidification, the alkoxy moisture that on the other hand can be completed again on silicon atom is solid
Change, improve solidfied material crosslink density, the paint film of completion of cure has good cold resistance, salt fog resistance, water resistance and resistance to steam
Impact etc..
Preferably, the hydroxy acrylic acid polyol resin is selected from commercially available hydroxyl value in the hydroxyl of 30-50mgKOH/g
Acrylic polyol resin.The hydroxyl of hydroxy acrylic acid polyol resin in dispersions is to be used as later period crosslinking on resin side chain
Active function groups, hydroxyl value is excellent to the adhesion of various metal bases in the interval range of 30-50mgKOH/g, meanwhile, with
Ricinate and dispersion pigment, the organic compatibility of filler is good, is easy to carry out the modulation of master grind.It is furthermore preferred that hydroxyl
Value is in the interval range of 35-45mgKOH/g, such as the LR-7602 of Mitsubishi Chemical.
Preferably, the organosiloxane resins are the organosiloxane resins with hydrolyzable, such as commercially available
The MKC MS-56 of Mitsubishi Chemical.Its composition is the oligomer of tetramethoxy-silicane part hydrolyzable, can pass through intramolecular Si-
The hydrolyzable of OR group forms Si-OH group to increase the hydrophily of film coated surface.Surface of the paint film is set to form organic-inorganic
Compound interface has high anti fouling performance and self-cleaning property to paint film.Paint film when high steam impacts, stick by surface of the paint film
It is dirty to be easier to fall off, cleaning time is saved, paint film is reduced by the adverse effect of high temperature impact, extends paint film service life.
The pigments and fillers are selected from rutile type titanium white, phthalocyanine blue, medium chrome yellow, everbright fast yellow, carbon black, calcium carbonate or sulfuric acid
One or more of barium;
The stabilization agent is organic phosphorus compound class stabilization agent, such as the IRGAFOS168 of commercially available BASF.Stabilization agent
The features such as IRGAFOS168 has high temperature resistant, and volatility is low, and hydrolytic resistance is prominent, can effectively prevent paint film when by high temperature impact
Chain rupture caused by the degradation of paint film oxidation polymer or the variation of dehydrogenation equimolecular quantity, can prevent paint film color appearance from being influenced by high temperature
And it changes;
The antioxidant is organic phenolic antioxidant, such as the IRGANOX 1010 of commercially available BASF.Antioxidant IRGANOX
1010 can be effectively prevented thermal oxidative degradation of paint film high molecular material during long-term ageing, while be also a kind of efficient
Processing stabilizers can improve discoloration-resistant of paint film high molecular material under the conditions of high temperature process;
The auxiliary agent is wetting agent and levelling agent, and the wetting agent, levelling agent are organically-modified siloxane solution;
The organic solvent is selected from commercially available esters, ketone, alcohols or hydrocarbon organic solvent.
Preferably, the crosslinking agent is selected from by commercially available diisocyanate type curing agent, such as the diisocyanate of BASF
Curing agent HI-190, the curing agent can be in film hot briquettings by containing hydroxyl in isocyanates and paint composite
Or the resin further occurrence cross-linking reaction of carboxyl, it can preferably increase the crosslink density of paint film, to improve resistance toization of paint film
Learn drug and water resistance.
A kind of preparation method of high pressure resistant steam impringement metal material coating as described above, comprising the following steps:
(1) hydroxy acrylic acid polyol resin and pigments and fillers are added into organic solvent, successively by stirring at low speed and
High-speed stirred, grinding, then sequentially add organosilicon modified crylic acid resin, organosiloxane resins, stabilization agent, antioxidant and
Auxiliary agent stirs at low speed, and adjusting viscosity to Saybolt viscosity is 60~80s, and filtering obtains component A;
(2) crosslinking agent is dissolved in organic solvent, high-speed stirred, B component is made;
(3) component A and B component are uniformly mixed to get the high pressure resistant steam impringement metal material coating.
Preferably, the rate stirred at low speed is 300~600rpm, and the rate of high-speed stirred is 1500~2500rpm;
The time stirred at low speed in step (1) is 20~30min, and the time of step (1) high speed stirring is 25~35min;Step (2)
The time of high speed stirring is 25~35min.
Preferably, described to be ground to 10 μm of fineness or less.
Compared with prior art, the beneficial effects of the present invention are embodied in following several respects:
1) present invention selects the organosilicon modified crylic acid resin from synthesis, which has as matrix film forming matter
Preferable curability both can occur heating with diisocyanates curing agent and react solidification, another aspect film forming matter at
When encountering high-temperature steam impact after type, and the alkoxy moisture solidification on silicon atom can be completed, improve solidfied material crosslink density,
The paint film of completion of cure has good cold resistance, salt fog resistance, water resistance and high pressure resistant steam impringement.
2) present invention selects the organosilicon modified crylic acid resin from synthesis, and collocation uses pigment dispersion good third
Olefin(e) acid polyol resin under the premise of guaranteeing the compatibility between different types of resin, while ensure that the appearance color of paint film
Coloured silk, adhesion and high-weatherability between paint film and the metal material of difficult attachment.
3) present invention selects the organosilicon modified crylic acid resin from synthesis, and collocation uses the organosilicon for having hydrolyzable
Oxygen alkane resin under the premise of guaranteeing the compatibility between different types of resin, while can increase the hydrophily of surface of the paint film.Make
Surface of the paint film forms organo-mineral complexing interface to have high anti fouling performance and self-cleaning property.Paint film is impacted in high steam
When, surface of the paint film stick it is dirty be easier to fall off, save cleaning time, reduce paint film by the adverse effect of high temperature impact, prolong
Long paint film service life.
4) present invention selects the organosilicon modified crylic acid resin from synthesis, and collocation uses organic phosphorus compound class stabilization agent
Paint film high score can be effectively prevented under the premise of guaranteeing the compatibility between different types of resin with organic phenolic antioxidant
Thermal oxidative degradation of sub- material during long-term ageing, increases the heat-resisting quantity of paint film, discoloration-resistant.
Specific embodiment
It elaborates below to the embodiment of the present invention, the present embodiment carries out under the premise of the technical scheme of the present invention
Implement, the detailed implementation method and specific operation process are given, but protection scope of the present invention is not limited to following implementation
Example.
Embodiment 1
A kind of high pressure resistant steam impringement metal material paint composite, is pressed by component A lacquer type organic coating with cross linking agent of component B
Weight ratio is composed for 100:25;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 1.
Wherein, organosilicon modified crylic acid resin 1 prepare it is as follows:
Organic silicon monomer model KBE-1003 containing vinyl-functional, purchased from Japanese SHIN-ETSU HANTOTAI's chemistry;Methacrylic acid
Methyl esters MMA and acrylic acid AA is purchased from Jilin Chemical Industrial Co. Ltd., hydroxyethyl methacrylate 2-HEMA purchased from Japan
Osaka organic chemistry.
Organic silicon monomer KBE-1003 and solvent acetic acid isobutyl containing vinyl-functional are successively added in four-hole boiling flask
Ester and diisobutyl ketone, and the air in reaction flask is excluded using nitrogen displacement, and use nitrogen protection, it is warming up to 60-90 DEG C.
At the uniform velocity 3 hours titration methyl methacrylate MMA, acrylic acid AA, hydroxyethyl methacrylate 2-HEMA, two isobutyls of azo simultaneously
Nitrile, solvent butanone and methyl iso-butyl ketone (MIBK);It is condensed back reaction 4-8 hours, obtains above-mentioned organosilicon modified crylic acid resin 1.
Wherein, the molar ratio of KBE-1003, MMA, AA, 2-HEMA are 0.1-0.4:1:0.1-0.2:0.4-0.8.Azodiisobutyronitrile is used
Amount is the 0.1-0.5% of above-mentioned monomer gross mass.The liquid acid value of organosilicon modified crylic acid resin 1 is 0.5KOHmg/g, liquid
State hydroxyl value is 30KOHmg/g, and the weight average molecular weight that GPC detects copolymer resin 1 is 48000.
Its molecular framework is as follows:
Embodiment 2
A kind of high pressure resistant steam impringement metal material paint composite, is pressed by component A lacquer type organic coating with cross linking agent of component B
Weight ratio is composed for 100:25;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 2, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 2.
Wherein, organosilicon modified crylic acid resin 2 prepare it is as follows:
Organic silicon monomer KBE-1003 and solvent acetic acid isobutyl containing vinyl-functional are successively added in four-hole boiling flask
Ester and diisobutyl ketone, and the air in reaction flask is excluded using nitrogen displacement, and use nitrogen protection, it is warming up to 60-90 DEG C.
At the uniform velocity 3 hours titration methyl methacrylate MMA, acrylic acid AA, hydroxyethyl methacrylate 2-HEMA, two isobutyls of azo simultaneously
Nitrile, solvent butanone and methyl iso-butyl ketone (MIBK);It is condensed back reaction 4-8 hours, obtains above-mentioned organosilicon modified crylic acid resin 2.
Wherein, the molar ratio of KBE-1003, MMA, AA, 2-HEMA are 0.1-0.8:1:0.1-0.2:0.1-0.4.Azodiisobutyronitrile is used
Amount is the 0.1-0.5% of above-mentioned monomer gross mass.The liquid acid value of organosilicon modified crylic acid resin 2 is 0.5KOHmg/g, liquid
State hydroxyl value is 18KOHmg/g, and the weight average molecular weight that GPC detects copolymer resin 2 is 56000.
Embodiment 3
A kind of high pressure resistant steam impringement metal material paint composite, is pressed by component A lacquer type organic coating with cross linking agent of component B
Weight ratio is composed for 100:25;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 3, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 3.
Wherein, organosilicon modified crylic acid resin 3 prepare it is as follows:
Organic silicon monomer KBE-1003 and solvent acetic acid isobutyl containing vinyl-functional are successively added in four-hole boiling flask
Ester and diisobutyl ketone, and the air in reaction flask is excluded using nitrogen displacement, and use nitrogen protection, it is warming up to 60-90 DEG C.
At the uniform velocity 3 hours titration methyl methacrylate MMA, acrylic acid AA, hydroxyethyl methacrylate 2-HEMA, two isobutyls of azo simultaneously
Nitrile, solvent butanone and methyl iso-butyl ketone (MIBK);It is condensed back reaction 4-8 hours, obtains above-mentioned organosilicon modified crylic acid resin 3.
Wherein, the molar ratio of KBE-1003, MMA, AA, 2-HEMA are 0.1-0.4:1:0.1-0.6:0.4-0.8.Azodiisobutyronitrile is used
Amount is the 0.1-0.5% of above-mentioned monomer gross mass.The liquid acid value of organosilicon modified crylic acid resin 3 is 1.0KOHmg/g, liquid
State hydroxyl value is 30KOHmg/g, and the weight average molecular weight that GPC detects copolymer resin 3 is 58000.
Embodiment 4
A kind of high pressure resistant steam impringement metal material paint composite, is pressed by component A lacquer type organic coating with cross linking agent of component B
Weight ratio is composed for 100:25;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 4.
Embodiment 5
A kind of high pressure resistant steam impringement metal material paint composite, is pressed by component A lacquer type organic coating with cross linking agent of component B
Weight ratio is composed for 100:25;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 5.
Comparative example 1
A kind of metal material paint composite of this comparative example is by weight with cross linking agent of component B by component A lacquer type organic coating
100:30 is composed;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
The preparation method of this comparative example material of resistance to metal paint composite a kind of specifically includes the following steps:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the metal
Material paint composite 6.
Comparative example 2
A kind of metal material paint composite of this comparative example is by weight with cross linking agent of component B by component A lacquer type organic coating
100:30 is composed;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of metal material paint composite of this comparative example specifically includes the following steps:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the metal
Material paint composite 7.
Comparative example 3
A kind of metal material paint composite of this comparative example is by weight with cross linking agent of component B by component A lacquer type organic coating
100:30 is composed;
Wherein, component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
A kind of preparation method of high pressure resistant steam impringement metal material paint composite of the present embodiment specifically include with
Lower step:
(1) by weight by the powders such as titanium dioxide, filler pigment and dispersing agent and acrylic polyol resin LR7602
It is added in dispersion tank, stirs evenly, related solvents are then added, stir at low speed 20~30min, then high-speed stirred 25~
35min is then introduced into and dispersion machine grinding distribution is sanded to fineness 10um hereinafter, adjusting viscosity to 60~80s, filtering is placed on
In reactor tank, by weight will from synthesizing organo-silicon acrylic resin modified 1, MKC MS56, IRGAFOS168,
IRGANOX1010, the auxiliary agents such as moistening flatting agent and organic solvent are added in reactor tank and stir evenly, and are added according to demand
Component A lacquer type organic coating is made in flatting silica 25~35min of high-speed stirred;
(2) crosslinking agent HI190 is added in related solvents by weight, 25~35min of high-speed stirred, component B is made
Crosslinking agent;
(3) when using component A lacquer type organic coating is uniformly mixed by weight with cross linking agent of component B, obtains the resistance to height
Press steam impringement metal material paint composite 8.
Spraying application paints paint composite obtained by above-described embodiment 1-5 and comparative example 1-3 on metal material simultaneously
The results are shown in Table 1 for film properties test.
1 paint film property test result of table
The physical property measurement method of each embodiment and comparative sample carries out in accordance with the following methods:
By the dry film coating of Examples 1 to 5 and comparative example 1~3 carry out material adhesive force, moisture-proof, oil resistant yogurt it is acid,
It can be carried out detection with chemical-resistant.
Adhesive force is according to GB9286-1998 standard testing.
Heatproof is aqueous according to NES M0141_2015 6.3.10 standard testing.
Resistance to thermal cycle is according to 1735 standard testing of GB/T.
Moisture-proof is according to daily output NES M0141_2015 6.3.1 standard testing.
Heat resistance is according to daily output NES M0141_2015 6.3.9 standard testing.
High pressure resistant steam impringement according to Q/JLY J7111122A-2018 5.13 standard testings.
Salt fog resistance is according to GB/T 10125-2012 standard testing.
Acid resistance is according to daily output NES M0141_2015 6.3.2 standard testing.
Alkali resistance is according to daily output NES M0141_2015 6.3.3 standard testing.
Resistance to suncream is according to Hyundai Motor MS-625-01_4.15 light resistance standard testing.
Resistance to hand lotion is according to Volkswagen's TL-226-2006PV3964 standard testing.
Alcohol resistance is according to Volkswagen's TL-226-2006_3.13 standard testing.
Seen from table 1, Examples 1 to 5 is coated on the paint composite coating on metal material, shows good element
Material adhesive force, heatproof be aqueous, moisture-proof, salt fog resistance, the performances such as high pressure resistant steam carwash.Wherein embodiment 1 is implemented
The comprehensive performance for the heat-curable coating being prepared in example 4 and embodiment 5 is optimal, is optimum embodiment of the present invention.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Embodiment 6
Using preparation step similar to Example 1, the difference is that each material composition ratio is different, it is specific as follows:
Component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
50 parts of HI190,
10 parts of n-butyl acetate,
60 parts of subtotal.
Through detecting, the coating be coated on metal material on paint composite coating, show good material adhesive force,
Heatproof is aqueous, moisture-proof, salt fog resistance, the performances such as high pressure resistant steam carwash.
Embodiment 7
Using preparation step similar to Example 1, the difference is that each material composition ratio is different, it is specific as follows:
Component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
30 parts of HI190,
8 parts of n-butyl acetate,
38 parts of subtotal.
Through detecting, the coating be coated on metal material on paint composite coating, show good material adhesive force,
Heatproof is aqueous, moisture-proof, salt fog resistance, the performances such as high pressure resistant steam carwash.
Embodiment 8
Using preparation step similar to Example 1, the difference is that each material composition ratio is different, it is specific as follows:
Component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
40 parts of HI190,
10 parts of n-butyl acetate,
50 parts of subtotal.
Through detecting, the coating be coated on metal material on paint composite coating, show good material adhesive force,
Heatproof is aqueous, moisture-proof, salt fog resistance, the performances such as high pressure resistant steam carwash.
Embodiment 9
Using preparation step similar to Example 1, the difference is that each material composition ratio is different, it is specific as follows:
Component A lacquer type organic coating includes following components and parts by weight content:
The component B includes following components and parts by weight content:
25 parts of HI190,
5 parts of n-butyl acetate,
30 parts of subtotal.
Through detecting, the coating be coated on metal material on paint composite coating, show good material adhesive force,
Heatproof is aqueous, moisture-proof, salt fog resistance, the performances such as high pressure resistant steam carwash.
Claims (10)
1. a kind of high pressure resistant steam impringement metal material coating, which is characterized in that the coating includes component A and B component, institute
State the composition that component A includes following parts by weight:
The B component is crosslinking agent and organic solvent;
The mass ratio of crosslinking agent is 100:(25~50 in the component A and B component).
2. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Component A includes following parts by weight:
3. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Organosilicon modified crylic acid resin is that the organic silicon monomer and acrylic ester monomer containing vinyl-functional pass through radical polymerization
Synthetic resin made of reaction is closed, the acrylic ester monomer includes methacrylate, acrylate or dihydroxypropyl
One of ester, the glass transition temperature of the organosilicon modified crylic acid resin are 20~90 DEG C.
4. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Hydroxy acrylic acid polyol resin is selected from commercially available hydroxyl value in the hydroxy acrylic acid polyol resin of 30-50mgKOH/g.
5. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Organosiloxane resins are the organosiloxane resins with hydrolyzable.
6. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Pigments and fillers are selected from one of rutile type titanium white, phthalocyanine blue, medium chrome yellow, everbright fast yellow, carbon black, calcium carbonate or barium sulfate or several
Kind;
The stabilization agent is organic phosphorus compound class stabilization agent;
The antioxidant is organic phenolic antioxidant;
The auxiliary agent includes wetting agent and levelling agent;
The organic solvent is selected from commercially available esters, ketone, alcohols or hydrocarbon organic solvent.
7. a kind of high pressure resistant steam impringement metal material coating according to claim 1, which is characterized in that described
Crosslinking agent is selected from by commercially available diisocyanate type curing agent.
8. a kind of preparation method of steam impringement metal material coating high pressure resistant as described in claim 1~7 is any, special
Sign is, comprising the following steps:
(1) hydroxy acrylic acid polyol resin and pigments and fillers are added into organic solvent, successively by stirring at low speed and at a high speed
Stirring, grinding, then sequentially adds organosilicon modified crylic acid resin, organosiloxane resins, stabilization agent, antioxidant and helps
Agent stirs at low speed, and adjusting viscosity to Saybolt viscosity is 60~80s, and filtering obtains component A;
(2) crosslinking agent is dissolved in organic solvent, high-speed stirred, B component is made;
(3) component A and B component are uniformly mixed to get the high pressure resistant steam impringement metal material coating.
9. a kind of preparation method of high pressure resistant steam impringement metal material coating according to claim 8, feature
It is, the rate stirred at low speed is 300~600rpm, and the rate of high-speed stirred is 1500~2500rpm;In step (1)
The time stirred at low speed is 20~30min, and the time of step (1) high speed stirring is 25~35min;Step (2) high speed is stirred
The time mixed is 25~35min.
10. a kind of preparation method of high pressure resistant steam impringement metal material coating according to claim 8, feature
It is, it is described to be ground to 10 μm of fineness or less.