CN109658113A - A kind of paper wrapper multiple anti-counterfeit label and preparation method thereof - Google Patents
A kind of paper wrapper multiple anti-counterfeit label and preparation method thereof Download PDFInfo
- Publication number
- CN109658113A CN109658113A CN201811553745.5A CN201811553745A CN109658113A CN 109658113 A CN109658113 A CN 109658113A CN 201811553745 A CN201811553745 A CN 201811553745A CN 109658113 A CN109658113 A CN 109658113A
- Authority
- CN
- China
- Prior art keywords
- background
- layer
- silane
- invisible
- printing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of anti-counterfeiting technologies, more particularly to a kind of paper wrapper multiple anti-counterfeit label and preparation method thereof, it includes background background color layer (1), it is printed on background background color layer (1) invisible two-dimensional codes layer (2), the printing material of invisible two-dimensional codes layer (2) includes the WO of the light color inks of 85-90wt%, the silane of 3-5wt% and 5-10wt% by weight percent3Photochromic material;The printing material of background background color layer (1) includes the Y of the light color inks of 85-90wt%, the silane of 3-5wt% and 5-10wt% by weight percent2O3: Eu nano-phosphor.The present invention has triple antifalse effects, includes invisible two-dimensional codes, and change colour two dimensional code and fluorescence background, while also having the advantages that low in cost, anti-counterfeit structure is complicated, good concealment, and common people are difficult to copy, and have broad application prospects in paper wrapper field.
Description
Technical field
The present invention relates to a kind of anti-counterfeiting technologies, more particularly to a kind of paper wrapper multiple anti-counterfeit label and its
Preparation method.
Background technique
In recent years, counterfeit and shoddy goods are becoming increasingly rampant, in order to protect brand names, protection market, protection the majority of consumers
Legitimate rights and interests, anti-counterfeiting technology both domestic and external rapidly develop.Currently, anti-counterfeiting technology product mainly have anti-counterfeiting mark, structure with
Package anti-counterfeiting technical products, anti-fake material (anti-counterfeiting paper, anti false film, anti-forgery ink, anti-counterfeiting stamp ink etc.), computer media are anti-fake
Technical products, biological characteristic anti-counterfeiting technology product and magnetic nuclear resonance radio frequency identification (MR) anti-counterfeiting technology etc..The selection of anti-counterfeiting technology
It is usually related to the added value of commodity and cost.
Ink anti-counterfeiting technology is low in cost, easy to operate, is in current packaging material using a kind of relatively more extensive anti-fake skill
Art.Mainly particular matter is added in this anti-counterfeiting technology in ink, is process by certain technique as special off-set oil
The technology of ink.Fluorescent material usually as fluorescent ink additive so that some region meeting under ultraviolet lighting of printed matter
Issue corresponding visible light, however single fluorescent ink anti-counterfeiting technology cannot for a long time effectively, it can only whithin a period of time can be with
Good antifalse effect is played, is easily copied by common fake producer, it is therefore, more in the specific printing zone setting of packaging material
Weight anti-counterfeiting technology is essential right-safeguarding guarantee.
Number of patent application 201721026142.0, patent name be it is a kind of can invisible two-dimensional codes mark Chinese utility model
A kind of two dimensional code mark that can be stealthy is disclosed in patent, electrochromic device is controlled by controller, two dimensional code is become
Color, under certain bias device show as with color similar in substrate, can not scan two dimensional code at this time, realize the stealthy of two dimensional code
Function;When conversion biases are to another state, device color changes, and shows two dimensional code, can carry out normal scan.
This kind of mode needs to carry out controller control biased device, and complicated operation, and typically only technical professional can
Rationally control, and ordinary consumer is difficult to control two dimensional code and shows hidden;Simultaneously in order to enable two dimensional code to be rapidly scanned, need
By two dimensional code adjustment as the biggish color of base color distinction, but base color there may be many kinds, thus can be into
The difficulty of one step increasing two dimensional code color adaptation;Finally this kind of technology is also only single is realized by scanning the two-dimensional code,
It can not play the role of multiple anti-fake.
Summary of the invention
The present invention anti-counterfeiting technology in the prior art there are aiming at the problem that, a kind of paper wrapper multiple anti-fake mark is provided
Know and preparation method thereof.
In order to solve the above-mentioned technical problem, the present invention is addressed by following technical proposals:
A kind of paper wrapper multiple anti-counterfeit label, including background background color layer are printed with stealth two on background background color layer
Code layer is tieed up, the printing material of invisible two-dimensional codes layer includes the silicon of the light color inks of 85-90wt%, 3-5wt% by weight percent
The WO of alkane and 5-10wt%3Photochromic material;The printing material of background background color layer includes 85-90wt%'s by weight percent
The Y of light color inks, the silane of 3-5wt% and 5-10wt%2O3: Eu nano-phosphor.
A method of preparing paper wrapper multiple anti-counterfeit label comprising following steps:
Step 1: weighing light color inks, silane and WO respectively by mass percentage3Photochromic material is as stealth two
Tie up the printing material of code layer;Weigh light color inks, silane and Y respectively by mass percentage2O3: Eu nano-phosphor is as back
The printing material of scape background color layer;
Step 2: material load weighted in step 1 to be prepared by mixing into the printing material of background background color layer;
Step 3: material load weighted in step 1 to be prepared by mixing into the printing material of invisible two-dimensional codes layer;
The printing material prepared in step 2 is first printed on packaging material by step 4, forms background background color layer, so
The printing material prepared in print steps three on background background color layer afterwards forms invisible two-dimensional codes layer.
Preferably, step 2 specifically includes the following steps:
Step 2.1, first by Y2O3: Eu nano-phosphor mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into
The Y of 0.05-0.1g/mL2O3: Eu suspension;
Then silane is added in step 2.2 in the suspension of step 2.1, continue ultrasound under the conditions of 200Hz and mix,
Silane-modified Y is obtained after reacting 5-8h at room temperature2O3: Eu nano-luminescent material;
Step 2.3, finally by silane-modified Y2O3: Eu, which is added in light color inks to be uniformly mixed, can be obtained background bottom
The printing material of chromatograph.
Preferably, step 3 specifically includes the following steps:
Step 3.1, first by WO3Photochromic powder mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into 0.1-
The WO of 0.2g/mL3Suspension;
Then silane is added in step 3.2 in the suspension of step 3.1, continue ultrasound under the conditions of 200Hz and mix,
Silane-modified WO is obtained after reacting 5-8h at room temperature3Photochromic material;
Step 3.3, finally by silane-modified WO3It is added in light color inks to be uniformly mixed and invisible two-dimensional codes can be obtained
The printing material of layer.
Preferably, the sequencing of step 2 and step 3 can be replaced.
Preferably, being used to prepare the light color inks of the printing material of invisible two-dimensional codes layer in step 1 and being used to prepare back
The light color inks of the printing material of scape background color layer are identical.
The present invention is due to using above technical scheme, with significant technical effect:
The present invention has triple antifalse effects, includes invisible two-dimensional codes, and change colour two dimensional code and fluorescence background, while also having
Low in cost, the advantages that anti-counterfeit structure is complicated, good concealment, common people are difficult to copy, and have in paper wrapper field wide
Wealthy application prospect.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the embodiment of the present invention 1.
The toponym that each number designation is referred in attached drawing is as follows: 1-background background color layer, 2-invisible two-dimensional codes layers.
Specific embodiment
Present invention is further described in detail with embodiment with reference to the accompanying drawing.
Embodiment 1
A kind of paper wrapper multiple anti-counterfeit label, as shown in Figure 1, including background background color layer 1, on background background color layer 1
It is printed with invisible two-dimensional codes layer 2, it is characterised in that: the printing material of invisible two-dimensional codes layer 2 includes 85- by weight percent
The WO of the light color inks of 90wt%, the silane of 3-5wt% and 5-10wt%3Photochromic material chooses light color in the present embodiment
85 parts of ink, 5 parts of silane, 10 parts of WO3 photochromic material;The printing material of background background color layer 1 includes 85- by weight percent
The Y of the light color inks of 90wt%, the silane of 3-5wt% and 5-10wt%2O3: Eu nano-phosphor chooses light color in the present embodiment
90 parts of ink, 3 parts of silane, Y2O3: 7 parts of Eu nano fluorescent.
Wherein specifically prepare the method for paper wrapper multiple anti-counterfeit label, comprising the following steps:
Step 1: weighing light color inks, silane and WO respectively by mass percentage3Photochromic material is as stealth two
Tie up the printing material of code layer 2;Weigh light color inks, silane and Y respectively by mass percentage2O3: Eu nano-phosphor is as back
The printing material of scape background color layer 1;
Step 2: material load weighted in step 1 to be prepared by mixing into the printing material of background background color layer 1;
Step 3: material load weighted in step 1 to be prepared by mixing into the printing material of invisible two-dimensional codes layer 2;
The printing material prepared in step 2 is first printed on packaging material by step 4, forms background background color layer 1, so
The printing material prepared in print steps three on background background color layer 1 afterwards forms invisible two-dimensional codes layer 2.
Wherein, step 2 specifically includes the following steps:
Step 2.1, first by Y2O3: Eu nano-phosphor mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into
The Y of 0.05g/mL2O3: Eu suspension;
Then silane is added in step 2.2 in the suspension of step 2.1, continue ultrasound under the conditions of 200Hz and mix,
The silane-modified Y of hydrophobic oleophilic oil is obtained after reacting 8h at room temperature2O3: Eu nano-luminescent material;
Step 2.3, finally by silane-modified Y2O3: Eu, which is added in light color inks to be uniformly mixed, can be obtained background bottom
The printing material of chromatograph 1.
Wherein, step 3 specifically includes the following steps:
Step 3.1, first by WO3Photochromic powder mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into 0.1g/
The WO of mL3Suspension;
Then silane is added in step 3.2 in the suspension of step 3.1, continue ultrasound under the conditions of 200Hz and mix,
The silane-modified WO of hydrophobic oleophilic oil is obtained after reacting 5h at room temperature3Photochromic material;
Step 3.3, finally by silane-modified WO3It is added in light color inks to be uniformly mixed and invisible two-dimensional codes can be obtained
The printing material of layer 2.
The light color inks of the printing material of invisible two-dimensional codes layer 2 are used to prepare in the present embodiment in step 1 and are used to prepare
The light color inks of the printing material of background background color layer 1 are identical.
WO3Photochromic material and Y2O3: Eu nano-luminescent material is hidden in printed matter, can not visually be observed, when ultraviolet
When light irradiation, invisible two-dimensional codes layer 2 will become blue, and the background background color layer 1 of two dimensional code can issue red fluorescence, show fresh
Gorgeous pattern in 2 D code, and after stopping ultraviolet light irradiation, blue two dimensional code will continue to keep, and background background color layer 1 is not
Red fluorescence is issued again, finally two-dimension code area is heated, two dimensional code can fade again, become colorless, and be hidden in printing
In product, multi-anti-counterfeit effect is played.
The specific working principle is as follows: the principle of invisible two-dimensional codes colour developing is the WO under ultraviolet lighting3Electronics is swashed in valence band
It is dealt into conduction band, hole is left in valence band, generates electron-hole pair, light induced electron times W6+Capture generates W5+, while photoproduction is empty
Cave and WO3The reduzate reaction of powder surface absorption, releases proton H+, the proton of releasing is internally spread along surface, through inside
Transmission and WO between different lattices3It is compounded to form tungsten bronze HxWO3, HxWO3In W5+The transition of electronic service guide band makes powder in valence band
Blue is presented.
The principle that two dimensional code fades is: two dimensional code is heated in air, so that HxWO3It is oxidized to WO again3, blue takes off,
Restore primary colors.
The principle that background background color layer 1 becomes red under ultraviolet lighting is: Y2O3: Eu fluorescent material can absorb certain form
Energy, and excitation photon is released the energy of absorption in the form of low visible light, to generate red fluorescence phenomenon.
The present invention has triple antifalse effects, includes invisible two-dimensional codes, and change colour two dimensional code and fluorescence background, in particular to the
Anti-fake one weight is so that invisible two-dimensional codes is developed the color by ultraviolet lighting, then carry out mobile phone scanning, checks the true and false, the second weight into official website
It is after two dimensional code colour developing, needing to heat could fade, and user can carry out second by way of heating to two dimensional code
Anti-counterfeit recognition again illustrates to belong to counterfeit and shoddy goods as colour-fast;Third is that two dimensional code background can be sent out under ultraviolet lighting again
Red visible light out, on the one hand which can form a sharp contrast with the two dimensional code of blue, so that two dimensional code
It can quickly be scanned, the anti-fake knowledge of third weight on the other hand can also be carried out by the color change of the background background color layer 1
Not, also explanation belongs to counterfeit and shoddy goods if background background color layer 1 is non-discolouring or non-red.Pass through triple anti-counterfeiting technology phases
In conjunction with keeping anti-counterfeit structure more complicated, good concealment, common people are difficult to copy.
Embodiment 2
With embodiment 1, except that in the present embodiment invisible two-dimensional codes layer 2 preparation: first by WO3Photochromic powder
Ultrasound is made into the WO of 0.1g/mL under the conditions of 200Hz after mixing with dehydrated alcohol3Then suspension is added in the suspension
Silane continues ultrasound under the conditions of 200Hz and mixes, obtains the silane-modified WO of hydrophobic oleophilic oil after reacting 5h at room temperature3It is photic
Off-color material, finally by silane-modified WO3It is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes.
Specifically, each material and mass fraction in invisible two-dimensional codes layer 2 are as follows: 90 parts of light color inks, 3 parts of silane, WO3Light
7 parts of off-color material of ratio is caused to be uniformly mixed.
The preparation of background background color layer 1: first by Y2O3: Eu nano-phosphor surpasses under the conditions of 200Hz after mixing with dehydrated alcohol
Sound is made into the Y of 0.1g/mL2O3: then silane is added in Eu suspension in the suspension, it is mixed to continue ultrasound under the conditions of 200Hz
It is even, the silane-modified Y of hydrophobic oleophilic oil is obtained after reacting 6h at room temperature2O3: Eu nano-luminescent material, it finally will be silane-modified
Y2O3: Eu is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes background background color.
Specifically, each material and mass fraction in background background color layer 1 are as follows: 88 parts of light color inks, 4 parts of silane, Y2O3:Eu
The ratio that 8 parts of nano fluorescent is uniformly mixed.
The performance of gained invisible two-dimensional codes layer 2 and its background background color layer 1 is similar to Example 1.
Embodiment 3
With embodiment 1, except that in the present embodiment invisible two-dimensional codes layer 2 preparation: first by WO3Photochromic powder
Ultrasound is made into the WO of 0.2g/mL under the conditions of 200Hz after mixing with dehydrated alcohol3Then suspension is added in the suspension
Silane continues ultrasound under the conditions of 200Hz and mixes, obtains the silane-modified WO of hydrophobic oleophilic oil after reacting 8h at room temperature3It is photic
Off-color material, finally by silane-modified WO3It is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes.
Specifically, each material and mass fraction in invisible two-dimensional codes layer 2 are as follows: 85 parts of light color inks, 5 parts of silane, WO3Light
10 parts of off-color material of ratio is caused to be uniformly mixed.
The preparation of background background color layer 1: first by Y2O3: Eu nano-phosphor surpasses under the conditions of 200Hz after mixing with dehydrated alcohol
Sound is made into the Y of 0.05g/mL2O3: then silane is added in Eu suspension in the suspension, it is mixed to continue ultrasound under the conditions of 200Hz
It is even, the silane-modified Y of hydrophobic oleophilic oil is obtained after reacting 7h at room temperature2O3: Eu nano-luminescent material, it finally will be silane-modified
Y2O3: Eu is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes background background color.
Specifically, each material and mass fraction in background background color layer 1 are as follows: 88 parts of light color inks, 4 parts of silane, Y2O3:Eu
The ratio that 8 parts of nano fluorescent is uniformly mixed.
The performance of gained invisible two-dimensional codes layer 2 and its background background color layer 1 is similar to Example 1.
Embodiment 4
With embodiment 1, except that in the present embodiment invisible two-dimensional codes layer 2 preparation: first by WO3Photochromic powder
Ultrasound is made into the WO of 0.1g/mL under the conditions of 200Hz after mixing with dehydrated alcohol3Then suspension is added in the suspension
Silane continues ultrasound under the conditions of 200Hz and mixes, obtains the silane-modified WO of hydrophobic oleophilic oil after reacting 6h at room temperature3It is photic
Off-color material, finally by silane-modified WO3It is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes.
Specifically, each material and mass fraction in invisible two-dimensional codes layer 2 are as follows: 87 parts of light color inks, 4 parts of silane, WO3Light
9 parts of off-color material of ratio is caused to be uniformly mixed.
The preparation of background background color layer 1: first by Y2O3: Eu nano-phosphor surpasses under the conditions of 200Hz after mixing with dehydrated alcohol
Sound is made into the Y of 0.1g/mL2O3: then silane is added in Eu suspension in the suspension, it is mixed to continue ultrasound under the conditions of 200Hz
It is even, the silane-modified Y of hydrophobic oleophilic oil is obtained after reacting 8h at room temperature2O3: Eu nano-luminescent material, it finally will be silane-modified
Y2O3: Eu is added in light color inks and is uniformly mixed, for printing invisible two-dimensional codes background background color.
Specifically, each material and mass fraction in background background color layer 1 are as follows: 86 parts of light color inks, 4 parts of silane, Y2O3:Eu
The ratio that 10 parts of nano fluorescent is uniformly mixed.
The performance of gained invisible two-dimensional codes layer 2 and its background background color layer 1 is similar to Example 1.
Embodiment 5
It is not both the sequencing of step 2 and step 3 in the present embodiment with any one embodiment of embodiment 1-4
It can replace, i.e., first prepare the printing material of invisible two-dimensional codes layer 2, then prepare the printing material of background background color layer 1, gained is stealthy
The performance of two dimensional code and its background background color is similar to Example 1.
In short, the foregoing is merely presently preferred embodiments of the present invention, it is all according to equalization made by scope of the present invention patent
Variation and modification, shall all be covered by the patent of the invention.
Claims (6)
1. a kind of paper wrapper multiple anti-counterfeit label, including background background color layer (1), it is printed on background background color layer (1) hidden
Shape two dimension code layer (2), it is characterised in that: the printing material of invisible two-dimensional codes layer (2) includes 85-90wt%'s by weight percent
The WO of light color inks, the silane of 3-5wt% and 5-10wt%3Photochromic material;The printing material of background background color layer (1) presses matter
Amount percentage includes the Y of the light color inks of 85-90wt%, the silane of 3-5wt% and 5-10wt%2O3: Eu nano-phosphor.
2. a kind of method for preparing paper wrapper multiple anti-counterfeit label described in claim 1, it is characterised in that it includes
Following steps:
Step 1: weighing light color inks, silane and WO respectively by mass percentage3Photochromic material is as invisible two-dimensional codes
The printing material of layer (2);Weigh light color inks, silane and Y respectively by mass percentage2O3: Eu nano-phosphor is as background
The printing material of background color layer (1);
Step 2: material load weighted in step 1 to be prepared by mixing into the printing material of background background color layer (1);
Step 3: material load weighted in step 1 to be prepared by mixing into the printing material of invisible two-dimensional codes layer (2);
The printing material prepared in step 2 is first printed on packaging material by step 4, is formed background background color layer (1), then
The printing material prepared in print steps three on background background color layer (1) is formed invisible two-dimensional codes layer (2).
3. a kind of preparation method of paper wrapper multiple anti-counterfeit label according to claim 2, it is characterised in that: step
Rapid two specifically includes the following steps:
Step 2.1, first by Y2O3: Eu nano-phosphor mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into 0.05-
The Y of 0.1g/mL2O3: Eu suspension;
Then silane is added in step 2.2 in the suspension of step 2.1, continue ultrasound under the conditions of 200Hz and mix, in room temperature
Silane-modified Y is obtained after lower reaction 5-8h2O3: Eu nano-luminescent material;
Step 2.3, finally by silane-modified Y2O3: Eu, which is added in light color inks to be uniformly mixed, can be obtained background background color layer
(1) printing material.
4. a kind of preparation method of paper wrapper multiple anti-counterfeit label according to claim 2, it is characterised in that: step
Rapid three specifically includes the following steps:
Step 3.1, first by WO3Photochromic powder mixed with dehydrated alcohol after under the conditions of 200Hz ultrasound be made into 0.1-0.2g/
The WO of mL3Suspension;
Then silane is added in step 3.2 in the suspension of step 3.1, continue ultrasound under the conditions of 200Hz and mix, in room temperature
Silane-modified WO is obtained after lower reaction 5-8h3Photochromic material;
Step 3.3, finally by silane-modified WO3It is added in light color inks to be uniformly mixed and invisible two-dimensional codes layer (2) can be obtained
Printing material.
5. a kind of preparation method of paper wrapper multiple anti-counterfeit label according to claim 2, it is characterised in that: step
Rapid two can replace with the sequencing of step 3.
6. a kind of preparation method of paper wrapper multiple anti-counterfeit label according to claim 2, it is characterised in that: step
It is used to prepare the light color inks of the printing material of invisible two-dimensional codes layer (2) in rapid one and is used to prepare the print of background background color layer (1)
The light color inks of brush material are identical.