CN109627594A - The corrosion-resistant PP material of high resiliency and preparation method for lash curler - Google Patents
The corrosion-resistant PP material of high resiliency and preparation method for lash curler Download PDFInfo
- Publication number
- CN109627594A CN109627594A CN201910000411.3A CN201910000411A CN109627594A CN 109627594 A CN109627594 A CN 109627594A CN 201910000411 A CN201910000411 A CN 201910000411A CN 109627594 A CN109627594 A CN 109627594A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- resistant
- preparation
- high resiliency
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to artificial cosmetic technical fields, and the invention discloses the corrosion-resistant PP materials of high resiliency and preparation method for lash curler, including the following raw material: the Preparation equipment of 60 parts of polypropylene, 15 parts of butadiene rubber, 1 part of antioxidant, 0.5 part of silane coupling agent, 15 parts of glass fibre, 8 parts of talcum powder, pigment, the quartz plate includes weighing apparatus, high-speed mixer, double screw extruder.This is used for the corrosion-resistant PP material of high resiliency and preparation method of lash curler, the necessary material prepared by reasonable PP material, utilize the effect of butadiene rubber, so that PP material has high resiliency and wearability, the antioxidant effect of antioxidant, talcum powder significantly improves the tensile strength and flexural strength of PP material, raw material function is different, so that the advantages of having for the corrosion-resistant PP material of high resiliency of lash curler is increased, it is single to avoid plurality of raw materials ingredient, leads to increased costs.
Description
Technical field
The present invention relates to cosmetic technical fields, particularly for the corrosion-resistant PP material of high resiliency of lash curler and preparation side
Method.
Background technique
PP also known as polypropylene are a kind of semi-crystalline materials, it is harder than polythene material and has higher fusing point,
PP resin all has excellent resistance to water soak, antiacid caustic corrosion, antilysis, due to PP material have it is light, do not corrode, absolutely
The advantages that edge is good is widely used in fields such as chemical industry, building materials, household electrical appliances, automobile, cosmetics.
It is also higher and higher to the use feeling requirement of lash curler as effect requirements of the makeups person of having deep love for beauty are constantly promoted,
The elasticity of existing lash curler PP material is lower and corrosion resistance is poor, the using effect of user is reduced, simultaneously because city
The demand of lash curler is more and more right on field, and the preparation flow of existing lash curler PP material is more complex, so that being used for lash curler PP material
The production efficiency of material reduces, and the effect of part material is overlapped, so that cost of material is higher, to increase lash curler PP material
Production cost.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides for lash curler the corrosion-resistant PP material of high resiliency and preparation side
Method, the elasticity for solving existing lash curler PP material is lower poor with corrosion resistance, reduces the using effect of user, together
When due to the demand of lash curler in the market it is more and more right, the preparation flow of existing lash curler PP material is more complex, so that being used for eyelash
The production efficiency of hairbrush PP material reduces, and the effect of part material is overlapped, so that cost of material is higher, to increase eyelashes
The problem of brushing the production cost of PP material.
To achieve the above object, the invention provides the following technical scheme: being used for the corrosion-resistant PP material of high resiliency of lash curler
And preparation method, including the following raw material: 60 parts of polypropylene, 15 parts of butadiene rubber, 1 part of antioxidant, 0.5 part of silane coupling agent, glass
15 parts of glass fiber, 8 parts of talcum powder, pigment；
The Preparation equipment of the quartz plate includes weighing apparatus, high-speed mixer, double screw extruder.
Preferably, the raw material parts is measured in parts by weight.
Preferably, the antioxidant be one of antioxidant such as antioxidant CA, antioxidant 1010, antioxidant 1076 or
Numerous compositions.
Preferably, the talcum powder also has the function of nucleating agent.
Preferably, the pigment be artificial synthetic dyestuff, including titanium white, lithopone, lead chromate yellow, barba hispanica, iron oxide red, red lead,
One of pigment such as pigment scarlet powder, azophosphine, phthalocyanine blue are a variety of.
Preferably, the forming temperature of the double screw extruder is 160-220 DEG C, and the maximum screw rod of double screw extruder
Velocity interval is 300-600r/min.
Preferably, the corrosion-resistant PP material of the high resiliency for lash curler and the preparation method is as follows:
The first step, ingredient carries out sorting as needed, and is weighed by weighing apparatus；
Silane coupling agent and talcum powder are added in high-speed mixer by second step, and stirring 10-20min keeps silane even
Join agent and talcum powder is uniformly mixed；
Polypropylene, butadiene rubber, anti-is added in the mixture of silane coupling agent and talcum powder that will be uniformly mixed for third step
Oxygen agent, glass fibre carry out uniform stirring and stirring 20-30min, so that the mixture of silane coupling agent and talcum powder and poly- third
Alkene, butadiene rubber, antioxidant, glass fibre are sufficiently mixed, then pigment is added to silane coupling agent, talcum powder, polypropylene, suitable
Buna, antioxidant, glass fibre mixture in, stir evenly；
4th step, adds mixture into double screw extruder, is granulated through melting extrusion on double screw extruder, cold
But to get the corrosion-resistant PP material of high resiliency arrived for lash curler.
It has the beneficial effect that:
1, the corrosion-resistant PP material of high resiliency and preparation method that are used for lash curler, by reasonable PP material prepare must
Material is wanted, using the effect of butadiene rubber, so that PP material has high resiliency and wearability, the antioxidant effect of antioxidant, talcum
Powder significantly improves the tensile strength and flexural strength of PP material, and raw material function is different, so that the high resiliency for lash curler is resistance to
Corrosion PP material the advantages of having, increases, and it is single to avoid plurality of raw materials ingredient, leads to increased costs.
2, the corrosion-resistant PP material of high resiliency and preparation method that are used for lash curler are mixed by selection weighing, raw material, are double
Screw extruder extrusion molding prepares and makes entire operation process simply clear for the corrosion-resistant PP material of high resiliency of lash curler
It is clear, a large amount of time and manpower and material resources are saved, simultaneously because while high-speed mixer and double screw extruder and uninterrupted
Work, improve the preparation efficiency of the corrosion-resistant PP material of high resiliency.
Specific embodiment
Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without making creative work
The every other embodiment obtained, shall fall within the protection scope of the present invention.
The present invention provides a kind of technical solution: the corrosion-resistant PP material of high resiliency and preparation method for lash curler, including
The following raw material: 60 parts of polypropylene, 15 parts of butadiene rubber, 1 part of antioxidant, 0.5 part of silane coupling agent, 15 parts of glass fibre, talcum
8 parts of powder, pigment, talcum powder also have the function of that nucleating agent, antioxidant are antioxidant CA, antioxidant 1010, antioxidant 1076 etc.
One or more of antioxidant composition, pigment be artificial synthetic dyestuff, including titanium white, lithopone, lead chromate yellow, barba hispanica,
One of pigment such as iron oxide red, red lead, pigment scarlet powder, azophosphine, phthalocyanine blue are a variety of, and raw material parts is measured in parts by weight；
The Preparation equipment of quartzy plate includes weighing apparatus, high-speed mixer, double screw extruder, the forming temperature of double screw extruder
It is 160-220 DEG C, and the maximum screw speed range of double screw extruder is 300-600r/min.
The corrosion-resistant PP material of high resiliency for lash curler and the preparation method is as follows:
The first step, ingredient carries out sorting as needed, and is weighed by weighing apparatus；
Silane coupling agent and talcum powder are added in high-speed mixer by second step, and stirring 10-20min keeps silane even
Join agent and talcum powder is uniformly mixed；
Polypropylene, butadiene rubber, anti-is added in the mixture of silane coupling agent and talcum powder that will be uniformly mixed for third step
Oxygen agent, glass fibre carry out uniform stirring and stirring 20-30min, so that the mixture of silane coupling agent and talcum powder and poly- third
Alkene, butadiene rubber, antioxidant, glass fibre are sufficiently mixed, then pigment is added to silane coupling agent, talcum powder, polypropylene, suitable
Buna, antioxidant, glass fibre mixture in, stir evenly；
4th step, adds mixture into double screw extruder, is granulated through melting extrusion on double screw extruder, cold
But to get the corrosion-resistant PP material of high resiliency arrived for lash curler.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. being used for the corrosion-resistant PP material of high resiliency and preparation method of lash curler, it is characterised in that: including the following raw material: polypropylene
60 parts, 15 parts of butadiene rubber, 1 part of antioxidant, 0.5 part of silane coupling agent, 15 parts of glass fibre, 8 parts of talcum powder, pigment；
The Preparation equipment of the quartz plate includes weighing apparatus, high-speed mixer, double screw extruder.
2. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The raw material parts is measured in parts by weight.
3. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The antioxidant is one or more of the antioxidant such as antioxidant CA, antioxidant 1010, antioxidant 1076 composition.
4. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The talcum powder also has the function of nucleating agent.
5. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The pigment is artificial synthetic dyestuff, including titanium white, lithopone, lead chromate yellow, barba hispanica, iron oxide red, red lead, pigment scarlet powder, azophosphine, phthalein
One of pigment such as cyanines indigo plant are a variety of.
6. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The forming temperature of the double screw extruder is 160-220 DEG C, and the maximum screw speed range of double screw extruder is 300-
600r/min。
7. the corrosion-resistant PP material of the high resiliency according to claim 1 for lash curler and preparation method, it is characterised in that:
The corrosion-resistant PP material of the high resiliency for lash curler and the preparation method is as follows:
The first step, ingredient carries out sorting as needed, and is weighed by weighing apparatus；
Silane coupling agent and talcum powder are added in high-speed mixer by second step, and stirring 10-20min makes silane coupling agent
It is uniformly mixed with talcum powder；
Polypropylene, butadiene rubber, antioxygen will be added in the mixture of uniformly mixed silane coupling agent and talcum powder in third step
Agent, glass fibre carry out uniform stirring and stirring 20-30min, so that the mixture of silane coupling agent and talcum powder and poly- third
Alkene, butadiene rubber, antioxidant, glass fibre are sufficiently mixed, then by pigment be added to silane coupling agent, talcum powder, polypropylene,
Butadiene rubber, antioxidant, glass fibre mixture in, stir evenly；
4th step, adds mixture into double screw extruder, is granulated through melting extrusion on double screw extruder, cooling, i.e.,
Obtain the corrosion-resistant PP material of high resiliency for lash curler.