CN109602106A - A kind of durable rubber gloves and preparation method thereof - Google Patents
A kind of durable rubber gloves and preparation method thereof Download PDFInfo
- Publication number
- CN109602106A CN109602106A CN201811484045.5A CN201811484045A CN109602106A CN 109602106 A CN109602106 A CN 109602106A CN 201811484045 A CN201811484045 A CN 201811484045A CN 109602106 A CN109602106 A CN 109602106A
- Authority
- CN
- China
- Prior art keywords
- rubber
- palm
- pad
- rubber gloves
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of durable rubber gloves and preparation method thereof, the rubber gloves ontology includes preventing rubber layer, gauze wearing layer, rubber adhesive layer, add cotton layer, the two sides of the rubber adhesive layer are bonded with gauze wearing layer respectively, add cotton layer, the preventing rubber layer is connected to gauze wearing layer and adds the side of cotton layer, the palm of the hand position of the rubber gloves ontology is connected with the first inserted link, the finger position side of the rubber gloves ontology is connected with the second inserted link, the palm of the hand position of the rubber gloves ontology is connected with centre of the palm pad, the finger position side of the rubber gloves ontology is connected with finger pad, reduce fretting wear, effectively extend the service life of rubber gloves ontology after finger pad and centre of the palm pad abrasion, it replaces finger pad and the centre of the palm is padded, the production of finger pad and centre of the palm pad and materials cost are respectively less than rubber Rubber gloves ontology, effectively reduces use cost, no replacement is required rubber gloves ontology, has saved use cost.
Description
Technical field
The invention belongs to rubber gloves technical fields, and in particular to a kind of durable rubber gloves, the invention further relates to
A kind of durable rubber gloves and preparation method thereof.
Background technique
Rubber gloves is one kind gloves made of rubber sheet or film.Divide latex hand by rubber raw materials or manufacturing process
Set and molding gloves etc..Acid and alkali-resistance gloves should be able to (density 1.19) makes in (density 1.32) or soda bath in sulfuric acid in 45 DEG C
With.Electrical isolation gloves are divided to high pressure and two kinds of low pressure.High pressure can use (test voltage is 12000 volts) at 6000 volts or less.It is low
Pressure can be used below at 1000 volts.
Safety of the rubber gloves due to barrier protection effect, can be good at protecting user, it is extensive
Applied in the production and living of people.After existing rubber gloves finger and palm portion generate abrasion, need whole gloves
It all throws away and more renews, cause the use cost of rubber gloves to increase.For this purpose, it is proposed that a kind of durable rubber gloves and
Preparation method, to solve the problems, such as to mention in above-mentioned background technique.
Summary of the invention
The purpose of the present invention is to provide a kind of durable rubber gloves and preparation method thereof, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme: a kind of durable rubber gloves, including rubber gloves
Ontology, the rubber gloves ontology include preventing rubber layer, gauze wearing layer, rubber adhesive layer plus cotton layer, the rubber adhesion
The two sides of layer are bonded with gauze wearing layer respectively plus cotton layer, the preventing rubber layer are connected to gauze wearing layer and plus cotton
The side of layer, the palm of the hand position of the rubber gloves ontology is connected with the first inserted link, the finger position of the rubber gloves ontology
Side is connected with the second inserted link, and the palm of the hand position of the rubber gloves ontology is connected with centre of the palm pad, the rubber gloves ontology
Finger position side is connected with finger pad.
Preferably, the side of the centre of the palm pad is equipped with the first jack for connecting the first inserted link, and the centre of the palm is padded another
Side is equipped with several groups anti-skid bulge.
Preferably, the side of the finger pad is equipped with for connecting the second jack of the second inserted link, the finger pad it is another
Side is equipped with the wear-resisting protrusion of several groups.
Preferably, the centre of the palm pad, finger pad are rubber pad, and first inserted link, the second inserted link are that one end is equipped with
The rubber inserted link of protrusion.
Preferably, the gauze wearing layer is cotton yarn wearing layer.
The present invention also provides a kind of preparation methods of durable rubber gloves, specifically includes the following steps:
S1: the sorting of rubber gloves ontology:
A: the sorting of preventing rubber layer, select 20-30 parts of nitrile rubber latex, 30-50 parts of polyethylene wax, 10-15 parts of nano silver,
It 3-5 parts of anti-aging agent, collects spare；
B: the sorting of gauze wearing layer selects the cotton gauze cloth with a thickness of 0.1-0.2mm, gauze wearing layer is cut into two
The shape of palm is collected spare；
C: the sorting of rubber adhesive layer selects silicon rubber 20-30 parts, collects spare；
D: adding the sorting of cotton layer, selects and adds cotton cloth with a thickness of the velveteen of 0.3-0.5mm, and cotton layer will be added to be cut into two palms
Shape is collected spare；
The sorting of S2, the centre of the palm pad, finger pad:
A: nano zine oxide 30-40 parts, 20-30 parts of isothiazolinone, 40-50 parts of fluorubber latex are selected in the sorting of centre of the palm pad,
It collects spare；
B: nano zine oxide 25-35 parts, 15-25 parts of isothiazolinone, 20-35 parts of fluorubber latex are selected in the sorting of finger pad,
It collects spare；
The production of S3, rubber gloves ontology:
A: the production of preventing rubber layer, select 20-30 parts of nitrile rubber latex, 30-50 parts of polyethylene wax, 10-15 parts of nano silver,
It 3-5 parts of anti-aging agent, being put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 130~180 DEG C, mixing time is 1~
2h takes the mixing latex solution of half to pour into glove model, is placed in baking oven dry, drying time 15-20min, together
When the gauze wearing layer cut is put into glove model again, the palm of the hand, the back of the hand two sides of gloves are adjacent to respectively, by rubber adhesion
Layer pours into glove model and covers gauze wearing layer, and cotton layer is then added in the covering of the side of rubber adhesive layer, finally will
The epoxy glue of remaining half pours into glove model in lotion, is placed in baking oven dry, drying time 15-20min,
After molding, demoulding obtains rubber gloves ontology, the slot for the first inserted link, the second inserted link is equipped in glove model；
The production of S4, centre of the palm pad: 30-40 parts of nano zine oxide, 20-30 parts of isothiazolinone, 40-50 parts of fluorubber latex are put
Enter in kneading machine and be kneaded, obtain epoxy glue, melting temperature is 130~180 DEG C, and mixing time is 1~2h, will mix latex solution
It pours into the pad model of the centre of the palm, is equipped with the nose bar for being used to form the first jack in the model of centre of the palm pad, be placed in baking oven dry, drying
Time is 15-20min, after molding, demoulding；
The production of S5, finger pad: 25-35 parts of nano zine oxide, 15-25 parts of isothiazolinone, 20-35 parts of fluorubber latex are put
Enter in kneading machine and be kneaded, obtain epoxy glue, melting temperature is 130~180 DEG C, and mixing time is 1~2h, will mix latex solution
It pours into the pad model of the centre of the palm, is equipped in the model of finger pad and is used for the molding nose bar of the second jack, be placed in baking oven dry, drying
Time is 15-20min, after molding, demoulding；
S6, combination installation:
Second jack of finger pad is plugged on the second inserted link of rubber gloves ontology, the first jack that the centre of the palm is padded is plugged on
On first inserted link of rubber gloves ontology, so that rubber gloves ontology and finger pad, the centre of the palm pad to form an entirety, complete durable
Rubber gloves production.
Compared with prior art, the beneficial effects of the present invention are: the durable rubber gloves of one kind provided by the invention and its
Gauze wearing layer is arranged by the inside of rubber gloves ontology in preparation method, the present invention, and the tension for reinforcing rubber gloves ontology is strong
Degree, wear-resistant strength make gauze wearing layer by rubber adhesive layer and add cotton layer steady by adding cotton layer to increase thermal effect
Waterproof anti-corrosion is played the role of by the setting of preventing rubber layer in the fixed inside for being connected to preventing rubber layer, by rubber
The palm of the hand position of Rubber gloves ontology is connected with the first inserted link, and the finger position side of rubber gloves ontology is connected with the second inserted link,
The palm of the hand position of rubber gloves ontology is connected with centre of the palm pad, and the finger position side of rubber gloves ontology is connected with finger pad, makes
The finger and palm part for obtaining rubber gloves ontology are protected, and effectively reduce rubber gloves ontology directly and by by the straight of article
Contact reduces fretting wear, effectively extends the service life of rubber gloves ontology after finger pad is worn with centre of the palm pad, replacement
Finger pad and the centre of the palm are padded, and the production of finger pad and centre of the palm pad and materials cost are respectively less than rubber gloves ontology, are effectively dropped
Low use cost, no replacement is required rubber gloves ontology have saved use cost.
Detailed description of the invention
Fig. 1 is positive structure diagram of the invention；
Fig. 2 is rubber gloves body interior structural schematic diagram of the invention；
Fig. 3 is that side structure schematic view is padded in the centre of the palm of the invention；
Fig. 4 is rubber gloves ontology side structure schematic view of the invention；
Fig. 5 is finger pad side structure schematic view of the invention.
In figure: 1 rubber gloves ontology, 2 finger pads, 3 wear-resisting protrusions, 4 centres of the palm pad, 5 anti-skid bulges, 6 first jacks, 7
One inserted link, 8 second inserted links, 9 preventing rubber layers, 10 gauze wearing layers, 11 rubber adhesive layers, 12 plus cotton layer, 13 second jacks.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
The present invention provides the durable rubber gloves of one kind of such as Fig. 1-5, including rubber gloves ontology 1, the rubber gloves sheets
Body 1 includes preventing rubber layer 9, gauze wearing layer 10, rubber adhesive layer 11 plus cotton layer 12, the two sides of the rubber adhesive layer 11
It is bonded with gauze wearing layer 10 plus cotton layer 12 respectively, the preventing rubber layer 9 is connected to gauze wearing layer 10 and plus cotton layer
12 side, the palm of the hand position of the rubber gloves ontology 1 are connected with the first inserted link 7, the finger section of the rubber gloves ontology 1
Position side is connected with the second inserted link 8, and the palm of the hand position of the rubber gloves ontology 1 is connected with centre of the palm pad 4, the rubber gloves sheet
The finger position side of body 1 is connected with finger pad 2.
Specifically, the side of the centre of the palm pad 4 is equipped with the first jack 6 for connecting the first inserted link 7, the centre of the palm pad 4
The other side be equipped with several groups anti-skid bulge 5.
Specifically, the side of the finger pad 2 is equipped with the second jack 13 for connecting the second inserted link 8, the finger pad 2
The other side be equipped with several groups wear-resisting raised 3.
Specifically, the centre of the palm pad 4, finger pad 2 are rubber pad, first inserted link 7, the second inserted link 8 are one end
Rubber inserted link equipped with protrusion.
Specifically, the gauze wearing layer 10 is cotton yarn wearing layer.
The present invention also provides a kind of durable rubber gloves and preparation method thereof, specifically includes the following steps:
S1: the sorting of rubber gloves ontology 1:
A: 20 parts of nitrile rubber latex, 30 parts of polyethylene wax, 10 parts of nano silver, anti-aging agent 3 are selected in the sorting of preventing rubber layer 9
Part, it collects spare；
B: the sorting of gauze wearing layer 10 selects the cotton gauze cloth with a thickness of 0.1mm, gauze wearing layer 10 is cut into two
The shape of palm is collected spare；
C: the sorting of rubber adhesive layer 11 selects 20 parts of silicon rubber, collects spare；
D: adding the sorting of cotton layer 12, select and add cotton cloth with a thickness of the velveteen of 0.3mm, and cotton layer 12 will be added to be cut into two palms
Shape is collected spare；
The sorting of S2, centre of the palm pad 4, finger pad 2；
A: 30 parts of nano zine oxide, 20 parts of isothiazolinone, 40 parts of fluorubber latex are selected in the sorting of centre of the palm pad 4, are collected standby
With；
B: 25 parts of nano zine oxide, 15 parts of isothiazolinone, 20 parts of fluorubber latex are selected in the sorting of finger pad 2, are collected standby
With；
The production of S3, rubber gloves ontology 1:
A: 20 parts of nitrile rubber latex, 30 parts of polyethylene wax, 10 parts of nano silver, anti-aging agent 3 are selected in the production of preventing rubber layer 9
Part, it is put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 130 DEG C, mixing time 1.5h, takes the mixed of half
It closes latex solution to pour into glove model, is placed in baking oven and does, drying time 15min, and meanwhile it is again that the gauze cut is wear-resisting
Layer 10 is put into glove model, is adjacent to the palm of the hand, the back of the hand two sides of gloves respectively, rubber adhesive layer 11 is poured into glove model simultaneously
And covering gauze wearing layer 10, then in the covering of the side of rubber adhesive layer 11 plus cotton layer 12, finally by remaining two/
One epoxy glue pours into glove model in lotion, is placed in drying in baking oven, drying time 15min, after molding, demoulding is obtained
The slot for the first inserted link 7, the second inserted link 8 is equipped with to rubber gloves ontology 1, in glove model；
The production of S4, centre of the palm pad 4: 30 parts of nano zine oxide, 20 parts of isothiazolinone, 40 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 1.5h, and mixing latex solution is poured into centre of the palm pad model
In, it is equipped with the nose bar for being used to form the first jack 6 in the model of centre of the palm pad 4, is placed in baking oven dry, drying time 15min,
After molding, demoulding；
The production of S5, finger pad 2: 25 parts of nano zine oxide, 15 parts of isothiazolinone, 20 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 1.5h, and mixing latex solution is poured into centre of the palm pad model
In, dry equipped with being placed in baking oven for the molding nose bar of the second jack 13 in the model of finger pad 2, drying time is
15min, after molding, demoulding；
S6, combination installation:
Second jack 13 of finger pad 2 is plugged on the second inserted link 8 of rubber gloves ontology 1, by the first jack of centre of the palm pad 4
6 are plugged on the first inserted link 7 of rubber gloves ontology 1, so that rubber gloves ontology 1 and finger pad 2, centre of the palm pad 4 form one
It is whole, complete the production of durable rubber gloves.
Embodiment 2
The present invention provides the durable rubber gloves of one kind of such as Fig. 1-5, including rubber gloves ontology 1, the rubber gloves sheets
Body 1 includes preventing rubber layer 9, gauze wearing layer 10, rubber adhesive layer 11 plus cotton layer 12, the two sides of the rubber adhesive layer 11
It is bonded with gauze wearing layer 10 plus cotton layer 12 respectively, the preventing rubber layer 9 is connected to gauze wearing layer 10 and plus cotton layer
12 side, the palm of the hand position of the rubber gloves ontology 1 are connected with the first inserted link 7, the finger section of the rubber gloves ontology 1
Position side is connected with the second inserted link 8, and the palm of the hand position of the rubber gloves ontology 1 is connected with centre of the palm pad 4, the rubber gloves sheet
The finger position side of body 1 is connected with finger pad 2.
Specifically, the side of the centre of the palm pad 4 is equipped with the first jack 6 for connecting the first inserted link 7, the centre of the palm pad 4
The other side be equipped with several groups anti-skid bulge 5.
Specifically, the side of the finger pad 2 is equipped with the second jack 13 for connecting the second inserted link 8, the finger pad 2
The other side be equipped with several groups wear-resisting raised 3.
Specifically, the centre of the palm pad 4, finger pad 2 are rubber pad, first inserted link 7, the second inserted link 8 are one end
Rubber inserted link equipped with protrusion.
Specifically, the gauze wearing layer 10 is cotton yarn wearing layer.
The present invention also provides a kind of durable rubber gloves and preparation method thereof, specifically includes the following steps:
S1: the sorting of rubber gloves ontology 1:
A: 25 parts of nitrile rubber latex, 40 parts of polyethylene wax, 12 parts of nano silver, anti-aging agent 4 are selected in the sorting of preventing rubber layer 9
Part, it collects spare；
B: the sorting of gauze wearing layer 10 selects the cotton gauze cloth with a thickness of 0.15mm, gauze wearing layer 10 is cut into two
The shape of palm is collected spare；
C: the sorting of rubber adhesive layer 11 selects 25 parts of silicon rubber, collects spare；
D: adding the sorting of cotton layer 12, select and add cotton cloth with a thickness of the velveteen of 0.4mm, and cotton layer 12 will be added to be cut into two palms
Shape is collected spare；
The sorting of S2, centre of the palm pad 4, finger pad 2；
A: 35 parts of nano zine oxide, 25 parts of isothiazolinone, 45 parts of fluorubber latex are selected in the sorting of centre of the palm pad 4, are collected standby
With；
B: 30 parts of nano zine oxide, 20 parts of isothiazolinone, 30 parts of fluorubber latex are selected in the sorting of finger pad 2, are collected standby
With；
The production of S3, rubber gloves ontology 1:
A: 25 parts of nitrile rubber latex, 40 parts of polyethylene wax, 12 parts of nano silver, anti-aging agent 4 are selected in the production of preventing rubber layer 9
Part, it is put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 180 DEG C, and mixing time 2h takes the mixing of half
Latex solution pours into glove model, is placed in baking oven dry, drying time 18min, while again that the gauze cut is wear-resisting
Layer 10 is put into glove model, is adjacent to the palm of the hand, the back of the hand two sides of gloves respectively, rubber adhesive layer 11 is poured into glove model simultaneously
And covering gauze wearing layer 10, then in the covering of the side of rubber adhesive layer 11 plus cotton layer 12, finally by remaining two/
One epoxy glue pours into glove model in lotion, is placed in drying in baking oven, drying time 18min, after molding, demoulding is obtained
The slot for the first inserted link 7, the second inserted link 8 is equipped with to rubber gloves ontology 1, in glove model；
The production of S4, centre of the palm pad 4: 35 parts of nano zine oxide, 25 parts of isothiazolinone, 45 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 1.5h, and mixing latex solution is poured into centre of the palm pad model
In, it is equipped with the nose bar for being used to form the first jack 6 in the model of centre of the palm pad 4, is placed in baking oven dry, drying time 18min,
After molding, demoulding；
The production of S5, finger pad 2: 30 parts of nano zine oxide, 20 parts of isothiazolinone, 30 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 1.5h, and mixing latex solution is poured into centre of the palm pad model
In, dry equipped with being placed in baking oven for the molding nose bar of the second jack 13 in the model of finger pad 2, drying time is
18min, after molding, demoulding；
S6, combination installation:
Second jack 13 of finger pad 2 is plugged on the second inserted link 8 of rubber gloves ontology 1, by the first jack of centre of the palm pad 4
6 are plugged on the first inserted link 7 of rubber gloves ontology 1, so that rubber gloves ontology 1 and finger pad 2, centre of the palm pad 4 form one
It is whole, complete the production of durable rubber gloves.
Embodiment 3
The present invention provides the durable rubber gloves of one kind of such as Fig. 1-5, including rubber gloves ontology 1, the rubber gloves sheets
Body 1 includes preventing rubber layer 9, gauze wearing layer 10, rubber adhesive layer 11 plus cotton layer 12, the two sides of the rubber adhesive layer 11
It is bonded with gauze wearing layer 10 plus cotton layer 12 respectively, the preventing rubber layer 9 is connected to gauze wearing layer 10 and plus cotton layer
12 side, the palm of the hand position of the rubber gloves ontology 1 are connected with the first inserted link 7, the finger section of the rubber gloves ontology 1
Position side is connected with the second inserted link 8, and the palm of the hand position of the rubber gloves ontology 1 is connected with centre of the palm pad 4, the rubber gloves sheet
The finger position side of body 1 is connected with finger pad 2.
Specifically, the side of the centre of the palm pad 4 is equipped with the first jack 6 for connecting the first inserted link 7, the centre of the palm pad 4
The other side be equipped with several groups anti-skid bulge 5.
Specifically, the side of the finger pad 2 is equipped with the second jack 13 for connecting the second inserted link 8, the finger pad 2
The other side be equipped with several groups wear-resisting raised 3.
Specifically, the centre of the palm pad 4, finger pad 2 are rubber pad, first inserted link 7, the second inserted link 8 are one end
Rubber inserted link equipped with protrusion.
Specifically, the gauze wearing layer 10 is cotton yarn wearing layer.
The present invention also provides a kind of durable rubber gloves and preparation method thereof, specifically includes the following steps:
S1: the sorting of rubber gloves ontology 1:
A: 30 parts of nitrile rubber latex, 50 parts of polyethylene wax, 15 parts of nano silver, anti-aging agent 5 are selected in the sorting of preventing rubber layer 9
Part, it collects spare；
B: the sorting of gauze wearing layer 10 selects the cotton gauze cloth with a thickness of 0.2mm, gauze wearing layer 10 is cut into two
The shape of palm is collected spare；
C: the sorting of rubber adhesive layer 11 selects 30 parts of silicon rubber, collects spare；
D: adding the sorting of cotton layer 12, select and add cotton cloth with a thickness of the velveteen of 0.5mm, and cotton layer 12 will be added to be cut into two palms
Shape is collected spare；
The sorting of S2, centre of the palm pad 4, finger pad 2:
A: 40 parts of nano zine oxide, 30 parts of isothiazolinone, 50 parts of fluorubber latex are selected in the sorting of centre of the palm pad 4, are collected standby
With；
B: 35 parts of nano zine oxide, 25 parts of isothiazolinone, 35 parts of fluorubber latex are selected in the sorting of finger pad 2, are collected standby
With；
The production of S3, rubber gloves ontology 1:
A: 30 parts of nitrile rubber latex, 50 parts of polyethylene wax, 15 parts of nano silver, anti-aging agent 5 are selected in the production of preventing rubber layer 9
Part, it is put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 180 DEG C, and mixing time 2h takes the mixing of half
Latex solution pours into glove model, is placed in baking oven dry, drying time 15-20min, while again that the gauze cut is resistance to
Mill layer 10 is put into glove model, is adjacent to the palm of the hand, the back of the hand two sides of gloves respectively, rubber adhesive layer 11 is poured into glove model
And gauze wearing layer 10 is covered, cotton layer 12 is then added in the covering of the side of rubber adhesive layer 11, finally by remaining two points
One of epoxy glue poured into glove model in lotion, be placed in baking oven dry, drying time 20min, after molding, demoulding,
Rubber gloves ontology 1 is obtained, the slot for the first inserted link 7, the second inserted link 8 is equipped in glove model；
The production of S4, centre of the palm pad 4: 40 parts of nano zine oxide, 30 parts of isothiazolinone, 50 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 2h, and mixing latex solution is poured into the pad model of the centre of the palm,
It is equipped with the nose bar for being used to form the first jack 6 in the model of centre of the palm pad 4, is placed in baking oven dry, drying time 20min, at
After type, demoulding；
The production of S5, finger pad 2: 35 parts of nano zine oxide, 25 parts of isothiazolinone, 35 parts of fluorubber latex are put into kneading machine
Middle mixing obtains epoxy glue, and melting temperature is 180 DEG C, mixing time 2h, and mixing latex solution is poured into the pad model of the centre of the palm,
It is equipped in the model of finger pad 2 and is used for the molding nose bar of the second jack 13, be placed in baking oven dry, drying time 20min, at
After type, demoulding；
S6, combination installation:
Second jack 13 of finger pad 2 is plugged on the second inserted link 8 of rubber gloves ontology 1, by the first jack of centre of the palm pad 4
6 are plugged on the first inserted link 7 of rubber gloves ontology 1, so that rubber gloves ontology 1 and finger pad 2, centre of the palm pad 4 form one
It is whole, complete the production of durable rubber gloves.
In conclusion compared with prior art, gauze wearing layer is arranged by the inside of rubber gloves ontology 1 in the present invention
10, reinforce the tensile strength of rubber gloves ontology 1, wear-resistant strength passes through rubber by adding cotton layer 12 to increase thermal effect
Adhesive layer 11 makes gauze wearing layer 10 and adds the 12 stable inside for being connected to preventing rubber layer 9 of cotton layer, passes through preventing rubber
The setting of layer 9, plays the role of waterproof anti-corrosion, is connected with the first inserted link 7 by the palm of the hand position in rubber gloves ontology 1,
The finger position side of rubber gloves ontology 1 is connected with the second inserted link 8, and the palm of the hand position of rubber gloves ontology 1 is connected with the centre of the palm
The finger position side of pad 4, rubber gloves ontology 1 is connected with finger pad 2, so that the finger and palmar hand of rubber gloves ontology 1
Position is protected, and is effectively reduced rubber gloves ontology 1 and is directly contacted with the direct of article is taken, reduces fretting wear, effectively prolong
The service life of long rubber gloves ontology 1 is after finger pad 2 and the abrasion of centre of the palm pad 4, replacement finger pad 2 and centre of the palm pad 4, hand
The production of thumb pad 2 and centre of the palm pad 4 and materials cost are respectively less than rubber gloves ontology 1, effectively reduce use cost, without more
Rubber gloves ontology 1 is changed, use cost has been saved.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (6)
1. a kind of durable rubber gloves, including rubber gloves ontology (1), it is characterised in that: rubber gloves ontology (1) packet
Preventing rubber layer (9), gauze wearing layer (10), rubber adhesive layer (11) plus cotton layer (12) are included, the rubber adhesive layer (11)
Two sides are bonded with gauze wearing layer (10) respectively plus cotton layer (12), the preventing rubber layer (9) are connected to gauze wearing layer
(10) and add cotton layer (12) side, the palm of the hand position of the rubber gloves ontology (1) is connected with the first inserted link (7), the rubber
The finger position side of Rubber gloves ontology (1) is connected with the second inserted link (8), and the palm of the hand position of the rubber gloves ontology (1) connects
It is connected to centre of the palm pad (4), the finger position side of the rubber gloves ontology (1) is connected with finger pad (2).
2. the durable rubber gloves of one kind according to claim 1, it is characterised in that: the side of the centre of the palm pad (4) is set
There is the first jack (6) for connecting the first inserted link (7), the other side of the centre of the palm pad (4) is equipped with several groups anti-skid bulge
(5).
3. the durable rubber gloves of one kind according to claim 1, it is characterised in that: the side of the finger pad (2) is set
There is the second jack (13) for connecting the second inserted link (8), the other side of the finger pad (2) is equipped with the wear-resisting protrusion of several groups
(3).
4. the durable rubber gloves of one kind according to claim 1, it is characterised in that: pad (4), finger pad in the centre of the palm
It (2) is rubber pad, first inserted link (7), the second inserted link (8) are the rubber inserted link that one end is equipped with protrusion.
5. the durable rubber gloves of one kind according to claim 1, it is characterised in that: the gauze wearing layer (10) is cotton
Yarn wearing layer.
6. the preparation method of durable rubber gloves described in a kind of claim 1-5, it is characterised in that: specifically include following step
It is rapid:
S1: the sorting of rubber gloves ontology (1):
A: 20-30 parts of nitrile rubber latex, 30-50 parts of polyethylene wax, nano silver 10-15 are selected in the sorting of preventing rubber layer (9)
Part, 3-5 parts of anti-aging agent are collected spare；
B: the cotton gauze cloth with a thickness of 0.1-0.2mm is selected in the sorting of gauze wearing layer (10), and gauze wearing layer (10) are cut out
It is cut into the shape of two palms, is collected spare；
C: the sorting of rubber adhesive layer (11) selects silicon rubber 20-30 parts, collects spare；
D: adding the sorting of cotton layer (12), selects and adds cotton cloth with a thickness of the velveteen of 0.3-0.5mm, and cotton layer (12) will be added to be cut into two
The shape of palm is collected spare；
The sorting of S2, the centre of the palm pad (4), finger pad (2):
A: the sorting of (4) is padded in the centre of the palm, selects nano zine oxide 30-40 parts, 20-30 parts of isothiazolinone, fluorubber latex 40-50
Part, it collects spare；
B: nano zine oxide 25-35 parts, 15-25 parts of isothiazolinone, fluorubber latex 20-35 are selected in the sorting of finger pad (2)
Part, it collects spare；
The production of S3, rubber gloves ontology (1):
A: 20-30 parts of nitrile rubber latex, 30-50 parts of polyethylene wax, nano silver 10-15 are selected in the production of preventing rubber layer (9)
Part, 3-5 parts of anti-aging agent, are put into kneading machine and are kneaded, and obtain epoxy glue, and melting temperature is 130~180 DEG C, mixing time 1
~2h takes the mixing latex solution of half to pour into glove model, is placed in baking oven dry, drying time 15-20min,
The gauze wearing layer (10) cut is put into glove model again simultaneously, the palm of the hand, the back of the hand two sides of gloves are adjacent to respectively, by rubber
Glue bond layer (11) pours into glove model and covers gauze wearing layer (10), then covers in the side of rubber adhesive layer (11)
It covers and adds cotton layer (12), finally pour into the epoxy glue of remaining half in glove model in lotion, be placed in baking oven and do
Dry, drying time 15-20min, after molding, demoulding is obtained rubber gloves ontology (1), is equipped in glove model and is used for first
The slot of inserted link (7), the second inserted link (8)；
The production of S4, centre of the palm pad (4): 30-40 parts of nano zine oxide, 20-30 parts of isothiazolinone, 40-50 parts of fluorubber latex,
It is put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 130~180 DEG C, and mixing time is 1~2h, will mix latex
Liquid pours into the pad model of the centre of the palm, and the nose bar for being used to form the first jack (6) is equipped in the model of centre of the palm pad (4), is placed in baking oven
It is dry, drying time 15-20min, after molding, demoulding；
The production of S5, finger pad (2): 25-35 parts of nano zine oxide, 15-25 parts of isothiazolinone, 20-35 parts of fluorubber latex,
It is put into kneading machine and is kneaded, obtain epoxy glue, melting temperature is 130~180 DEG C, and mixing time is 1~2h, will mix latex
Liquid pours into the pad model of the centre of the palm, is equipped in the model of finger pad (2) and is used for the second jack (13) molding nose bar, is placed in baking oven
It is dry, drying time 15-20min, after molding, demoulding；
S6, combination installation:
The second jack (13) of finger pad (2) is plugged on the second inserted link (8) of rubber gloves ontology (1), (4) are padded into the centre of the palm
The first jack (6) be plugged on the first inserted link (7) of rubber gloves ontology (1) so that rubber gloves ontology (1) and finger pad
(2), centre of the palm pad (4) forms an entirety, completes the production of durable rubber gloves.