CN109594349A - A kind of basalt fibre filtering cloth - Google Patents

A kind of basalt fibre filtering cloth Download PDF

Info

Publication number
CN109594349A
CN109594349A CN201811496524.9A CN201811496524A CN109594349A CN 109594349 A CN109594349 A CN 109594349A CN 201811496524 A CN201811496524 A CN 201811496524A CN 109594349 A CN109594349 A CN 109594349A
Authority
CN
China
Prior art keywords
parts
basalt fibre
fiber cloth
cloth
coupling agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811496524.9A
Other languages
Chinese (zh)
Inventor
宋奇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Michimori Bag Co Ltd
Original Assignee
Jiangsu Michimori Bag Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Michimori Bag Co Ltd filed Critical Jiangsu Michimori Bag Co Ltd
Priority to CN201811496524.9A priority Critical patent/CN109594349A/en
Publication of CN109594349A publication Critical patent/CN109594349A/en
Pending legal-status Critical Current

Abstract

The invention proposes a kind of basalt fibres to filter cloth, on fiber cloth surface, even spread protective coating glue, glass fibre accounts for 20%-70% in the fiber cloth, and basalt fibre accounts for 30%-80% in the fiber cloth.A kind of basalt fibre that the present invention points out filters cloth, has merged the speciality of glass fibre and basalt fibre, and manufactured fabric fire insulation performance is good, and surface is coated with fire resistant coating, soft, and various firefighter uniforms or decoration is suitble to use.

Description

A kind of basalt fibre filtering cloth
Technical field
The present invention relates to filtering cloth technical fields, and in particular to a kind of basalt fibre filtering cloth.
Background technique
In various disasters, fire be most frequently, most generally threaten public security and social development major casualty it One.The reason of fire occurs has plenty of natural phenomena, but caused by more or human factor, we should grasp fire The rule of generation is reduced as far as fire and its harm caused by the mankind.
80% or more coal-burning power plant, developed country uses electric precipitator in the world, and soot emissions are dense after electric precipitator is handled Degree is generally lower than 30mg/m3.The Large-scale machine set electric precipitator that coal-burning power plant, China has put into operation also have largely lower than 50mg/m3 and The real case of 30mg/m3.Obviously, electric precipitator is to can satisfy a kind of high-efficiency energy-saving dust-removing of China's New emission standard to set It is standby, while there is good comparative advantages and Technical Economy.In recent years, dust collection filter bag electric precipitator is still that coal-burning power plant is preferential The mainstream cleaner of selection.
Different dedusters uses different modes of gathering dust.And whether the different modes of gathering dust is directly related to Technical investment Economical rationality.The original mode of gathering dust is to beat cloth bag progress deashing in work drilling dust-precipitator to gather dust.But allow worker in height The in-house operation of the irritant gas of Wen Duochen, it is clear that be it is very worthless, the equipment some of improved mode of gathering dust is designed to Mechanical vibrator, some wind blowbacks, some compressed airs make pulse jet, and some carries out deashing to cloth bag with back-blowing.It is right For user, ideal dust collection device is exactly to require structure optimization, and filter bag is convenient, the filter bag longevity for good operational environment, inspection and replacement Length, high temperature resistant, antistatic are ordered, dust-collecting efficiency is high, and power facility is few, and low energy consumption.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of basalt fibre filtering cloth, and the present invention merges The speciality of glass fibre and basalt fibre, manufactured fabric fire insulation performance is good, and surface is coated with fire resistant coating, matter Ground is soft, and various firefighter uniforms or decoration is suitble to use.
The present invention provides a kind of basalt fibre filtering cloth, on fiber cloth surface, even spread protective coating glue.
As further improvement of the invention, glass fibre is accounted in the fiber cloth 20%-70%。
As further improvement of the invention, basalt fibre is accounted in the fiber cloth 30%-80%。
As further improvement of the invention, the fiber cloth is with a thickness of 0.5-1mm.
As further improvement of the invention, the protective coating glue is made of following raw material: organic silicon rubber 30-50 Part, polyvinyl chloride fibre 20-40 parts fire-retardant, 5-10 parts of coupling agent, 2-5 parts of curing agent, 2-10 parts of polyethylene glycol, 3-7 parts of triethanolamine, prevent it is quiet Electric agent 3-7 parts.
As further improvement of the invention, the protective coating glue is made of following raw material: organic silicon rubber 35-45 Part, polyvinyl chloride fibre 25-35 parts fire-retardant, 6-9 parts of coupling agent, 3-5 parts of curing agent, 4-8 parts of polyethylene glycol, 4-6 parts of triethanolamine, antistatic 4-6 parts of agent.
As further improvement of the invention, the protective coating glue is made of following raw material: 40 parts of organic silicon rubber, resistance Fire 20 parts of polyvinyl chloride fibre, 7 parts of coupling agent, 4 parts of curing agent, 6 parts of polyethylene glycol, 5 parts of triethanolamine, 5 parts of antistatic agent.
As further improvement of the invention, the coupling agent is silane coupling agent.
A kind of basalt fibre pointed out the invention has the following beneficial effects: the present invention filters cloth, has merged glass The speciality of fiber and basalt fibre, manufactured fabric fire insulation performance is good, and surface is coated with fire resistant coating, and quality is soft It is soft, it is suitble to various firefighter uniforms or decoration to use.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the invention is clearly and completely described, Obviously, the embodiment described is the embodiment of part of representative of the invention, rather than whole embodiments, this field are general Other all embodiments obtained belong to protection of the invention to logical technical staff without making creative work Range.
A kind of basalt fibre filtering cloth, on fiber cloth surface, even spread protective coating glue.
Glass fibre accounts for 20%-70% in the fiber cloth.Glass fibre is a kind of performance Excellent inorganic non-metallic material, many kinds of, advantage is good insulating, heat resistance is strong, corrosion resistance is good, high mechanical strength.
Basalt fibre accounts for 30%-80% in the fiber cloth.Basalt fibre is not only steady It is qualitative good, but also there are a variety of excellent properties such as electrical insulating property, anticorrosive, flame resistant, high temperature resistant.
The fiber cloth is with a thickness of 0.5-1mm.
The protective coating glue is made of following raw material: 30-50 parts of organic silicon rubber, polyvinyl chloride fibre 20-40 parts fire-retardant, coupling agent 5-10 parts, 2-5 parts of curing agent, 2-10 parts of polyethylene glycol, 3-7 parts of triethanolamine, 3-7 parts of antistatic agent.
The coupling agent is silane coupling agent.
Embodiment 1
A kind of basalt fibre filtering cloth, on fiber cloth surface, even spread protective coating glue.
Glass fibre accounts for 20% in the fiber cloth.
Basalt fibre accounts for 30% in the fiber cloth
The fiber cloth is with a thickness of 0.5mm.
The protective coating glue is made of following raw material: 30 parts of organic silicon rubber, 5 parts of coupling agent, is consolidated 20 parts of fire-retardant polyvinyl chloride fibre 2 parts of agent, 2 parts of polyethylene glycol, 3 parts of triethanolamine, 3 parts of antistatic agent.
The coupling agent is silane coupling agent.
Embodiment 2
A kind of basalt fibre filtering cloth, on fiber cloth surface, even spread protective coating glue.
Glass fibre accounts for 70% in the fiber cloth.Glass fibre is that one kind is had excellent performance Inorganic non-metallic material, many kinds of, advantage is good insulating, heat resistance is strong, corrosion resistance is good, high mechanical strength.
Basalt fibre accounts for 80% in the fiber cloth.Basalt fibre not only stability It is good, but also there are a variety of excellent properties such as electrical insulating property, anticorrosive, flame resistant, high temperature resistant.
The fiber cloth is with a thickness of 1mm.
The protective coating glue is made of following raw material: 50 parts of organic silicon rubber, 40 parts of fire-retardant polyvinyl chloride fibre, 10 parts of coupling agent, 5 parts of curing agent, 10 parts of polyethylene glycol, 7 parts of triethanolamine, 7 parts of antistatic agent.
The coupling agent is silane coupling agent.
Embodiment 3
A kind of basalt fibre filtering cloth, on fiber cloth surface, even spread protective coating glue.
Glass fibre accounts for 50% in the fiber cloth.Glass fibre is that one kind is had excellent performance Inorganic non-metallic material, many kinds of, advantage is good insulating, heat resistance is strong, corrosion resistance is good, high mechanical strength.
Basalt fibre accounts for 60% in the fiber cloth.Basalt fibre not only stability It is good, but also there are a variety of excellent properties such as electrical insulating property, anticorrosive, flame resistant, high temperature resistant.
The fiber cloth is with a thickness of 0.7mm.
The protective coating glue is made of following raw material: 40 parts of organic silicon rubber, 7 parts of coupling agent, is consolidated 20 parts of fire-retardant polyvinyl chloride fibre 4 parts of agent, 6 parts of polyethylene glycol, 5 parts of triethanolamine, 5 parts of antistatic agent.
The coupling agent is silane coupling agent.
In conclusion a kind of basalt fibre filtering cloth that the present invention points out, has selected glass fibre and basalt fine Dimension is used as cloth raw material, and design on fabric surface smooth pliable, fire protecting performance is excellent, applied widely.
Those skilled in the art is not under conditions of departing from the spirit and scope of the present invention that claims determine, also Various modifications can be carried out to the above content.Therefore the scope of the present invention is not limited in above explanation, but by The range of claims determines.

Claims (8)

1. a kind of basalt fibre filters cloth, which is characterized in that on fiber cloth surface, even spread protective coating glue.
2. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that in the fiber cloth Glass fibre accounts for 20%-70%.
3. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that in the fiber cloth Basalt fibre accounts for 30%-80%.
4. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that the fiber cloth thickness For 0.5-1mm.
5. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that the protective coating glue by Following raw material composition: 30-50 parts of organic silicon rubber, polyvinyl chloride fibre 20-40 parts fire-retardant, 5-10 parts of coupling agent, 2-5 parts of curing agent, poly- second 2-10 parts of glycol, 3-7 parts of triethanolamine, 3-7 parts of antistatic agent.
6. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that the protective coating glue by Following raw material composition: 35-45 parts of organic silicon rubber, polyvinyl chloride fibre 25-35 parts fire-retardant, 6-9 parts of coupling agent, 3-5 parts of curing agent, poly- second two 4-8 parts of alcohol, 4-6 parts of triethanolamine, 4-6 parts of antistatic agent.
7. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that the protective coating glue by Following raw material composition: 40 parts of organic silicon rubber, 20 parts of fire-retardant polyvinyl chloride fibre, 7 parts of coupling agent, 4 parts of curing agent, 6 parts of polyethylene glycol, three second 5 parts of hydramine, 5 parts of antistatic agent.
8. a kind of basalt fibre filters cloth according to claim 1, which is characterized in that the coupling agent is silane Coupling agent.
CN201811496524.9A 2018-12-07 2018-12-07 A kind of basalt fibre filtering cloth Pending CN109594349A (en)