CN109591397A - Frosted 3D special efficacy VCM clad steel plate and preparation method thereof - Google Patents
Frosted 3D special efficacy VCM clad steel plate and preparation method thereof Download PDFInfo
- Publication number
- CN109591397A CN109591397A CN201910063745.5A CN201910063745A CN109591397A CN 109591397 A CN109591397 A CN 109591397A CN 201910063745 A CN201910063745 A CN 201910063745A CN 109591397 A CN109591397 A CN 109591397A
- Authority
- CN
- China
- Prior art keywords
- layer
- chromium
- frosted
- free deactivation
- corona
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of frosted 3D special efficacy VCM clad steel plates and preparation method thereof, are related to composite decorative board technical field.Including substrate layer, the passivated processing in the two sides of the substrate layer is respectively formed the first chromium-free deactivation layer and the second chromium-free deactivation layer；The one side of the second chromium-free deactivation layer is coated with epoxy and carries on the back paint layer, and gum layer, adhesive phase, imitative wire drawing layer, 3D printing layer, pet layer, corona layer and 3D layers of frosted are successively arranged in the one side of the first chromium-free deactivation layer.The present invention is coated with to form frosted layer by using corona process formation corona layer on pet layer, then in corona layer, solves the problems, such as that existing abrasive material and PET directly fit poor performance.
Description
Technical field
The invention belongs to composite decorative board technical field, more particularly to a kind of frosted 3D special efficacy VCM clad steel plate and
Preparation method.
Background technique
The VCM product front used in household electric appliances be all it is smooth, it is without any processing because front be appearance contact
Face has during routine use and is easy to appear soft scuffing and problem of Cracking, and after front is destroyed, the entirety of product is weather-proof
Performance will decline, so will lead to product service life serious curtailment.Because the positive glossiness of PET is very high, can reach
300 degree, while also very light is net on surface, after this surface state reprocesses abrasive material, abrasive material and PET directly fit performance very
Difference, when by high temperature, particle is easy to fall off, and the performance of product is unable to satisfy requirement.
Summary of the invention
The purpose of the present invention is to provide a kind of frosted 3D special efficacy VCM clad steel plates, by using corona work on pet layer
Skill processing forms corona layer, then is coated with to form frosted layer in corona layer, solves existing abrasive material and PET directly fits performance
Very poor problem.
In order to solve the above technical problems, the present invention is achieved by the following technical solutions:
The present invention is a kind of frosted 3D special efficacy VCM clad steel plate, including substrate layer, the passivated place in the two sides of the substrate layer
Reason is respectively formed the first chromium-free deactivation layer and the second chromium-free deactivation layer；The one side of the second chromium-free deactivation layer is carried on the back coated with epoxy
Paint layer is successively arranged gum layer, adhesive phase, imitative wire drawing layer, 3D printing layer, PET in the one side of the first chromium-free deactivation layer
Layer, corona layer and 3D layers of frosted.
Further, the first chromium-free deactivation layer and the second chromium-free deactivation layer with a thickness of 2-10 μm.
A kind of preparation method of frosted 3D special efficacy VCM clad steel plate, comprising:
Step 1 forms the first chromium-free deactivation layer and the second chromium-free deactivation on the two sides of substrate layer respectively by Passivation Treatment
Layer；
Step 2, the second chromium-free deactivation layer one side be coated with epoxy carry on the back paint layer；
Step 3 sequentially forms gum layer, adhesive phase, imitative wire drawing layer, 3D printing in the upper surface of first chromium-free deactivation layer
Layer, pet layer；
Step 4 forms corona layer using corona process in the upper surface of pet layer, finally passes through dimple in corona layer again
Roller coating cloth, anilox roll or spary mode are coated with to form frosted layer.
The invention has the following advantages:
The present invention is coated with to form frosted by using corona process formation corona layer on pet layer, then in corona layer
Layer solves the problems, such as that existing abrasive material and PET directly fit poor performance；After can satisfy 240 degree of bakings 24 hours, use
Mightiness belt removing, frosted particle is without the problem of falling off.
Certainly, it implements any of the products of the present invention and does not necessarily require achieving all the advantages described above at the same time.
Detailed description of the invention
In order to illustrate the technical solution of the embodiments of the present invention more clearly, will be described below to embodiment required
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for ability
For the those of ordinary skill of domain, without creative efforts, it can also be obtained according to these attached drawings other attached
Figure.
Fig. 1 is frosted 3D special efficacy VCM clad steel plate structural schematic diagram of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts all other
Embodiment shall fall within the protection scope of the present invention.
In the description of the present invention, it is to be understood that, term " aperture ", "upper", "lower", " thickness ", "top", " in ",
Indicating positions or the positional relationship such as " length ", "inner", " surrounding ", are merely for convenience of description of the present invention and simplification of the description, without
It is that the component of indication or suggestion meaning or element must have a particular orientation, is constructed and operated in a specific orientation, therefore not
It can be interpreted as limitation of the present invention.
Refering to Figure 1, it is a kind of frosted 3D special efficacy VCM clad steel plate, including substrate layer 8 that the present invention, which is the present invention,
The passivated processing in the two sides of substrate layer 8 is respectively formed the first chromium-free deactivation layer 81 and the second chromium-free deactivation layer 82；Second Chrome-free is blunt
The one side for changing layer 82 is coated with epoxy and carries on the back paint layer 9, is successively arranged gum layer 7, adhesive in the one side of the first chromium-free deactivation layer 81
Layer 6, imitative wire drawing layer 5,3D printing layer 4, pet layer 3, corona layer 2 and frosted 3D layer 1.
Wherein, the first chromium-free deactivation layer 81 and the second chromium-free deactivation layer 82 with a thickness of 5 μm.
A kind of preparation method of frosted 3D special efficacy VCM clad steel plate, comprising:
Step 1, by Passivation Treatment respectively substrate layer 8 two sides formed the first chromium-free deactivation layer 81 and the second Chrome-free it is blunt
Change layer 82；
Step 2, the second chromium-free deactivation layer 82 one side be coated with epoxy carry on the back paint layer 9；
Step 3 sequentially forms gum layer 7, adhesive phase 6, imitative wire drawing layer 5,3D in the upper surface of first chromium-free deactivation layer 81
Printing layer 4, pet layer 3；
Step 4 forms corona layer 2 using corona process in the upper surface of pet layer 3, finally again in corona layer 2 by micro-
Gravure roller coating, anilox roll or spary mode are coated with to form frosted layer 1.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Particular features, structures, materials, or characteristics described in conjunction with this embodiment or example are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (3)
1. frosted 3D special efficacy VCM clad steel plate, including substrate layer (8), the passivated processing difference shape in the two sides of the substrate layer (8)
At the first chromium-free deactivation layer (81) and the second chromium-free deactivation layer (82)；It is characterized by: the second chromium-free deactivation layer (82)
It is coated with epoxy back paint layer (9) on one side, gum layer (7), bonding are successively arranged in the one side of the first chromium-free deactivation layer (81)
Oxidant layer (6), imitative wire drawing layer (5), 3D printing layer (4), pet layer (3), corona layer (2) and 3D layers of frosted (1).
2. a kind of frosted 3D special efficacy VCM clad steel plate according to claim 1, which is characterized in that first Chrome-free is blunt
Change layer (81) and the second chromium-free deactivation layer (82) with a thickness of 2-10 μm.
3. a kind of preparation method of frosted 3D special efficacy VCM clad steel plate as described in claim 1-2 is any one, feature exist
In, comprising:
Step 1, by Passivation Treatment respectively substrate layer (8) two sides formed the first chromium-free deactivation layer (81) and the second Chrome-free it is blunt
Change layer (82)；
Step 2, the second chromium-free deactivation layer (82) one side be coated with epoxy back paint layer (9)；
Step 3 sequentially forms gum layer (7), adhesive phase (6), imitative wire drawing layer in the upper surface of first chromium-free deactivation layer (81)
(5), 3D printing layer (4), pet layer (3)；
Step 4 forms corona layer (2) using corona process in the upper surface of pet layer (3), finally passes through in corona layer (2) again
Micro- gravure roller coating, anilox roll or spary mode are coated with to form frosted layer (1).