CN109577586A - Inorganic flame-retarded light composite interior wallboard of assembled and preparation method thereof - Google Patents
Inorganic flame-retarded light composite interior wallboard of assembled and preparation method thereof Download PDFInfo
- Publication number
- CN109577586A CN109577586A CN201811589855.7A CN201811589855A CN109577586A CN 109577586 A CN109577586 A CN 109577586A CN 201811589855 A CN201811589855 A CN 201811589855A CN 109577586 A CN109577586 A CN 109577586A
- Authority
- CN
- China
- Prior art keywords
- back side
- inorganic flame
- composite interior
- interior wallboard
- substrate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses inorganic flame-retarded light composite interior wallboards of a kind of assembled and preparation method thereof, including one piece of substrate layer made of diatomite plate and two pieces by decorative plies made of HPL plate, it towards the back side of wall and one is in front positioned opposite with the back side that the substrate layer, which has one, and two pieces of decorative plies are corresponding to be pasted on the back side for being fixed on the substrate layer and front；The effect of by raw material Optimal improvements, the fire protecting performance of composite interior wallboard of the present invention is greatly promoted, and reaches A grades of fire protection requirements, and can be effectively reduced the weight of the composite interior wallboard, is realized lightweight Reduction of Students' Study Load, is conducive to installation；In addition, composite interior wallboard of the present invention can be installed on wall by mounting structures such as fastener, setscrew, expansion tubes, not only simple installation, quick, and can random dismounting and change, meet the demand in current house ornamentation market well.
Description
Technical field
The present invention relates to building material technical fields, specifically provide a kind of inorganic flame-retarded light composite interior wallboard of assembled and
Its production method.
Background technique
With assembled architecture increasingly rise and country is to the demand for development of assembled architecture, in speed of application and
In terms of whole economic efficiency, especially in assembled fine fitment the commercial house field, the integrated assembled composite interior wallboard of wall cabinet
With apparent advantage, this will greatly push and realize that room policy requirements are handed in domestic full room customization and scale fine fitment.
But the generally existing flameproof effect of assembled composite interior wallboard is not good enough on the market at present, heavier mass, is not easy to pacify
Dress, wall sense are empty, can not clothes-hook the deficiencies of, especially can fire-proof and water-proof but also be used for the lightweight non-metallic of Furniture manufacture without
Pole decoration material field or a blank, thus it is not well positioned to meet current house ornamentation market to safe and environment-friendly, energy saving, peace
Fill convenient and fast family's reload request.
In view of this, the present invention is specifically proposed.
Summary of the invention
In order to overcome drawbacks described above, the present invention provides a kind of inorganic flame-retarded light composite interior wallboard of assembled and its production
Method, with light, fire protecting performance is good, simple installation, quick, and can arbitrarily dismounting and change, can clothes-hook the advantages that, well
Meet the demand in house ornamentation market.
The present invention is to solve technical solution used by its technical problem: a kind of inorganic flame-retarded light of assembled is compound
Lining, including one piece of substrate layer made of diatomite plate and two pieces are by decorative plies made of HPL plate, the base
Plate layer is in front positioned opposite with the back side towards the back side of wall and one with one, and two pieces of decorative plies are right respectively
The stickup answered is fixed on the back side and front of the substrate layer.
As a further improvement of the present invention, two pieces of decorative plies are respectively pasted by an adhesive layer accordingly respectively
It is fixed on the back side and front of the substrate layer, and the adhesive layer uses monocomponent polyurethane adhesive.
As a further improvement of the present invention, the substrate layer is with a thickness of 4~20mm, width 1220mm, length
1830~3050mm；
The decorative plies are 1830~3050mm with a thickness of 0.4~1.0mm, width 1220mm, length.
As a further improvement of the present invention, the decorative plies corresponding with the back side of the substrate layer are defined
For back side decorative plies, it is equipped on the back side decorative plies for by the inorganic flame-retarded light composite inner wall of the assembled
Installation component in plate integral installation to wall.
The present invention also provides a kind of production method of inorganic flame-retarded light composite interior wallboard of assembled, including it is following
Making step:
Step 1) chooses one block of diatomite plate as substrate layer, and it is spare to be cut out suitable size；
Two blocks of HPL plates are chosen as decorative plies, and it is spare to be cut out suitable size respectively；
Step 2) is pasted two pieces of decorative plies are corresponding on the back side and front of being fixed on the substrate layer,
Then it recycles cold press to be pressed together two pieces of decorative plies being pasted together and the substrate layer, obtains
The inorganic flame-retarded light composite interior wallboard of the assembled.
As a further improvement of the present invention, in above-mentioned steps 2) in, first respectively at the back side and front of the substrate layer
Upper each even spread has one layer of adhesive layer, and corresponding tile of two pieces of decorative plies is then covered on two layers of gluing again
On layer, and then be pasted together two pieces of decorative plies and the substrate layer are put into cold press again, and is working
Pressure can be prepared by the inorganic flame-retarded light composite inner wall of the assembled be pressed together 4~8 hours under conditions of 15 megapascal
Plate.
As a further improvement of the present invention, the adhesive layer uses monocomponent polyurethane adhesive, and the adhesive layer
Coating weight be 100~250g/m2。
As a further improvement of the present invention, it after the completion of being pressed together, also needs to two pieces of decorative plies and the base
Plate layer carries out deburring processing.
As a further improvement of the present invention, the decorative plies corresponding with the back side of the substrate layer are defined
For back side decorative plies；
After the completion of being pressed together, also it is equipped on the back side decorative plies for the assembled is inorganic non-ignitable light
Installation component in matter composite interior wallboard integral installation to wall.
The beneficial effects of the present invention are: on the one hand, the present invention is optimized by the raw material to the composite interior wallboard
It improves, it may be assumed that diatomite plate is selected to make as substrate layer, HPL plate as decorative plies and monocomponent polyurethane adhesive
Reach A grades of fire protection requirements, again so that the fire protecting performance of the composite interior wallboard can either be enable to greatly promote for adhesive layer
The effect of can be effectively reduced the weight of the composite interior wallboard, realizing lightweight Reduction of Students' Study Load, be conducive to installation.On the other hand, originally
Inventing the composite interior wallboard can be installed on wall by mounting structures such as fastener, setscrew, expansion tubes, not only
It is simple installation, quick, and can random dismounting and change, meet the demand in current house ornamentation market well.
Detailed description of the invention
Fig. 1 is the schematic diagram of the section structure of the inorganic flame-retarded light composite interior wallboard of assembled of the present invention；
Fig. 2 is installed to centre keel by installation component for the inorganic flame-retarded light composite interior wallboard A of assembled of the present invention
On decomposition texture schematic diagram.
In conjunction with attached drawing, make the following instructions:
1 --- substrate layer 2 --- decorative plies
3 --- adhesive layer 40 --- fasteners
41 --- setscrew 42 --- expansion tubes
5 --- centre keel
Specific embodiment
Referring to figure to a preferred embodiment of the present invention will be described in detail.
Embodiment 1:
The present embodiment 1 is used to illustrate the specific structure of the inorganic flame-retarded light composite interior wallboard of assembled of the present invention.
It please refers to shown in attached drawing 1, is the cross-section structure of the inorganic flame-retarded light composite interior wallboard of assembled of the present invention
Schematic diagram.The inorganic flame-retarded light composite interior wallboard of assembled includes one piece of substrate layer 1 and two made of diatomite plate
By decorative plies 2 made of HPL plate, the substrate layer 1 has one is in block with the back side towards the back side of wall and one
Front positioned opposite, two pieces of decorative plies 2 are corresponding to paste the back side and front for being fixed on the substrate layer 1
On.
In the present embodiment, it is preferred that two pieces of decorative plies 2 are respectively pasted by an adhesive layer 3 accordingly respectively
It is fixed on the back side and front of the substrate layer 1, and the adhesive layer 3 uses monocomponent polyurethane adhesive.
In the present embodiment, it is preferred that the substrate layer 1 is with a thickness of 4~20mm, width 1220mm, length
1830~3050mm；
The decorative plies 2 are 1830~3050mm with a thickness of 0.4~1.0mm, width 1220mm, length.
In the present embodiment, it is preferred that define the decorative plies 2 corresponding with the back side of the substrate layer 1
For back side decorative plies, it is equipped on the back side decorative plies for by the inorganic flame-retarded light composite inner wall of the assembled
Installation component in plate integral installation to wall (or other installing components), wherein fastener, swollen can be used in the installation component
Swollen screw, expansion tube etc..
Embodiment 2:
The present embodiment 2 is used to illustrate the specific production side of the inorganic flame-retarded light composite interior wallboard of assembled of the present invention
Method.
The production method of the inorganic flame-retarded light composite interior wallboard of assembled, comprises the following steps that:
Step 1) chooses one block of diatomite plate as substrate layer 1, and it is spare to be cut out suitable size；
Two blocks of HPL plates are chosen as decorative plies 2, and it is spare to be cut out suitable size respectively；
Corresponding paste of two pieces of decorative plies 2 is fixed on the back side and front of the substrate layer 1 by step 2)
On, then cold press is recycled to be pressed together the two pieces of decorative plies 2 and the substrate layer 1 that are pasted together,
Obtain the inorganic flame-retarded light composite interior wallboard of the assembled.
In in the present embodiment, it is preferred that in above-mentioned steps 2), first respectively on the back side of the substrate layer 1 and front
Each even spread has one layer of adhesive layer 3, and the adhesive layer 3 uses monocomponent polyurethane adhesive, and the coating of the adhesive layer 3
Amount is 100~250g/m2；Then corresponding tile of two pieces of decorative plies 2 is covered on two layers of adhesive layer 3 again,
And then be pasted together two pieces of decorative plies 2 and the substrate layer 1 are put into cold press again, and in operating pressure
To carry out being pressed together 4~8 hours under conditions of 15 megapascal, the inorganic flame-retarded light composite interior wallboard of the assembled can be prepared by.
In the present embodiment, it is preferred that after the completion of being pressed together, also need to two pieces of decorative plies 2 and the substrate
Layer 1 carries out deburring processing.
In the present embodiment, it is preferred that define the decorative plies 2 corresponding with the back side of the substrate layer 1
For back side decorative plies；
After the completion of being pressed together, also it is equipped on the back side decorative plies for the assembled is inorganic non-ignitable light
Button can be used in installation component in matter composite interior wallboard integral installation to wall (or other installing components), the installation component
Part, setscrew, expansion tube etc. (are seen shown in attached drawing 2).
In conclusion the present invention is optimized by the raw material to the composite interior wallboard, it may be assumed that select diatomite
Plate as substrate layer, HPL plate as decorative plies and monocomponent polyurethane adhesive as adhesive layer, thus can
So that the fire protecting performance of the composite interior wallboard is greatly promoted, reach A grades of fire protection requirements, and can be effectively reduced described multiple
The effect of closing the weight of lining, realizing lightweight Reduction of Students' Study Load, be conducive to installation.In addition, composite interior wallboard of the present invention can lead to
The mounting structures such as fastener, setscrew, expansion tube are crossed to be installed on wall, not only simple installation, quick, and can be random
Dismounting and change meets the demand in current house ornamentation market well.
The above is only a preferred embodiment of the present invention, it but is not intended to restrict the invention, it is noted that for this
For the those of ordinary skill of technical field, without departing from the technical principles of the invention, several improvement can also be made
And modification, these improvements and modifications also should be regarded as within the scope of the present invention.
Claims (9)
1. a kind of inorganic flame-retarded light composite interior wallboard of assembled, it is characterised in that: including one piece made of diatomite plate
Substrate layer (1) and two pieces have the back side towards wall by decorative plies (2) made of HPL plate, the substrate layer (1)
It is in front positioned opposite with one and the back side, corresponding paste of two pieces of decorative plies (2) is fixed on the base
On the back side and front of plate layer (1).
2. the inorganic flame-retarded light composite interior wallboard of assembled according to claim 1, it is characterised in that: two pieces of decorations
Plate layer (2) is each to be pasted on the back side and front of being fixed on the substrate layer (1) by an adhesive layer (3) accordingly respectively, and
The adhesive layer (3) uses monocomponent polyurethane adhesive.
3. the inorganic flame-retarded light composite interior wallboard of assembled according to claim 1, it is characterised in that: the substrate layer
(1) be 1830~3050mm with a thickness of 4~20mm, width 1220mm, length；
The decorative plies (2) are 1830~3050mm with a thickness of 0.4~1.0mm, width 1220mm, length.
4. the inorganic flame-retarded light composite interior wallboard of assembled according to claim 1, it is characterised in that: will be with the substrate
The corresponding decorative plies (2) in the back side of layer (1) are defined as back side decorative plies, pacify on the back side decorative plies
Equipped with for by the installation component in the inorganic flame-retarded light composite interior wallboard integral installation to wall of the assembled.
5. a kind of production method of such as inorganic flame-retarded light composite interior wallboard of assembled of any of claims 1-4,
It is characterized by comprising following making steps:
Step 1) chooses one block of diatomite plate as substrate layer (1), and it is spare to be cut out suitable size；
Two blocks of HPL plates are chosen as decorative plies (2), and it is spare to be cut out suitable size respectively；
Corresponding paste of two pieces of decorative plies (2) is fixed on the back side and front of the substrate layer (1) by step 2)
On, then cold press is recycled to carry out at pressing the two pieces of decorative plies (2) and the substrate layer (1) that are pasted together
Reason, obtains the inorganic flame-retarded light composite interior wallboard of the assembled.
6. the production method of the inorganic flame-retarded light composite interior wallboard of assembled according to claim 5, it is characterised in that:
Above-mentioned steps 2) in, first at the back side of the substrate layer (1) and front, upper each even spread has one layer of adhesive layer (3) respectively, so
Corresponding tile of two pieces of decorative plies (2) is covered on two layers of adhesive layer (3) again afterwards, and then will be pasted onto again
The decorative plies (2) of two pieces together and the substrate layer (1) are put into cold press, and in the item that operating pressure is 15 megapascal
It carries out being pressed together 4~8 hours under part, can be prepared by the inorganic flame-retarded light composite interior wallboard of the assembled.
7. the production method of the inorganic flame-retarded light composite interior wallboard of assembled according to claim 6, it is characterised in that: institute
Adhesive layer (3) are stated using monocomponent polyurethane adhesive, and the coating weight of the adhesive layer (3) is 100~250g/m2。
8. the production method of the inorganic flame-retarded light composite interior wallboard of assembled according to claim 6, it is characterised in that: pressure
After the completion of conjunction processing, also need to carry out deburring processing to two pieces of decorative plies (2) and the substrate layer (1).
9. the production method of the inorganic flame-retarded light composite interior wallboard of assembled according to claim 6, it is characterised in that: will
The decorative plies (2) corresponding with the back side of the substrate layer (1) are defined as back side decorative plies；
After the completion of being pressed together, also it is equipped on the back side decorative plies for answering the inorganic flame-retarded light of the assembled
Close the installation component in lining integral installation to wall.