CN109536065A - A kind of medical adhesive tape and preparation method thereof - Google Patents
A kind of medical adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN109536065A CN109536065A CN201710617550.1A CN201710617550A CN109536065A CN 109536065 A CN109536065 A CN 109536065A CN 201710617550 A CN201710617550 A CN 201710617550A CN 109536065 A CN109536065 A CN 109536065A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive tape
- medical adhesive
- silicone polymer
- dimethyl silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of medical adhesive tapes, are prepared from the following parts by weight of the components: 7-45 parts of polysiloxanes, 4-15 parts of polyurethane, 0.1-0.4 parts of platinum catalyst, 6-40 parts of dimethyl silicone polymer, 5-15 parts of natural plant gum, 20-30 parts of water.Medical adhesive tape good permeability provided by the invention has preferable fitting effect to skin, mild, repeatable pastes.
Description
Technical field
The invention belongs to tape technology fields, and in particular to a kind of medical adhesive tape and preparation method thereof.
Background technique
The adhesive tape generally used in medicine and daily life at present is usually double-layer structure, and one layer is bottom cloth layer, and one layer is
Glue-line, this causes its airtight, and existing adhesive tape and skin to be bonded effect bad, when use, is easy degumming;Adhesive tape makes
After primary, it can not repeat to paste since sticking effect is bad, new adhesive tape, waste of energy can only be reused.
Summary of the invention
The invention reside in solving, adhesive tape in the prior art is airtight, with skin to be bonded effect bad, when use, is easy de-
Glue can not repeat the problem of pasting, and being to provide a kind of pair of skin has preferable fitting effect, mild, repeatable paste, is ventilative
The good medical adhesive tape and preparation method thereof of property.
The specific technical solution of the present invention is as follows:
A kind of medical adhesive tape, is prepared from the following parts by weight of the components:
7-45 parts of polysiloxanes
4-15 parts of polyurethane
0.1-0.4 parts of platinum catalyst
6-40 parts of dimethyl silicone polymer
5-15 parts of natural plant gum
20-30 parts of water.
Preferably, the medical adhesive tape is prepared from the following parts by weight of the components:
20-30 parts of polysiloxanes
8-12 parts of polyurethane
0.2-0.3 parts of platinum catalyst
2-30 parts of dimethyl silicone polymer
6-10 parts of natural plant gum
20-30 parts of water.
Preferably, the natural plant gum is guar gum or flax gum.
Preferably, the cloth substrate is PE film or TPU membrane or foam or PE film and non-woven fabric compounded cloth material.
The present invention also provides the preparation methods of the medical adhesive tape, include the following steps:
1) weigh polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and
Water;
2) polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and water are added
Enter into container, be uniformly mixed, forms glue;
3) gluing will prepare [U1] and is coated onto cloth substrate with glue spreader, and glue is with a thickness of 1-3mm.
Medical adhesive tape good permeability provided by the invention has preferable fitting effect, mild, repeatable viscous to skin
Patch.
Specific embodiment
The invention will be further described with reference to embodiments.
Embodiment 1
A kind of preparation method of medical adhesive tape, comprising the following steps:
1) first carry out ingredient by formula, the formula is as follows: 30 parts of polysiloxanes, 0.2 part of platinum catalyst, gathers 5 parts of polyurethane
40 parts of dimethyl siloxane, 10 parts of natural plant gum, 25 parts of water;
2) polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and water are added
Enter into container, be uniformly mixed, forms glue;
3) gluing will prepare [U2] and is coated onto cloth substrate with glue spreader, and glue is with a thickness of 1-3mm.
Embodiment 2
A kind of preparation method of medical adhesive tape, comprising the following steps:
1) first by formula carry out ingredient, it is described formula it is as follows: 10 parts of polysiloxanes, 12 parts of polyurethane, 0.3 part of platinum catalyst,
8 parts of dimethyl silicone polymer, 6 parts of natural plant gum, 20 parts of water;
2) polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and water are added
Enter into container, be uniformly mixed, forms glue;
3) gluing will prepare [U3] and is coated onto cloth substrate with glue spreader, and glue is with a thickness of 1-3mm.
Embodiment 3
A kind of preparation method of medical adhesive tape, comprising the following steps:
1) first by formula carry out ingredient, it is described formula it is as follows: 43 parts of polysiloxanes, 10 parts of polyurethane, 0.4 part of platinum catalyst,
25 parts of dimethyl silicone polymer, 15 parts of natural plant gum, 30 parts of water;
2) polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and water are added
Enter into container, be uniformly mixed, forms glue;
3) gluing will prepare [U4] and is coated onto cloth substrate with glue spreader, and glue is with a thickness of 1-3mm.
Medical adhesive tape good permeability provided by the invention has preferable fitting effect, mild, repeatable viscous to skin
Patch.
Claims (5)
1. a kind of medical adhesive tape, which is characterized in that be prepared from the following parts by weight of the components:
7-45 parts of polysiloxanes
4-15 parts of polyurethane
0.1-0.4 parts of platinum catalyst
6-40 parts of dimethyl silicone polymer
5-15 parts of natural plant gum
20-30 parts of water.
2. medical adhesive tape according to claim 1, which is characterized in that be prepared from the following parts by weight of the components:
20-30 parts of polysiloxanes
8-12 parts of polyurethane
0.2-0.3 parts of platinum catalyst
2-30 parts of dimethyl silicone polymer
6-10 parts of natural plant gum
20-30 parts of water.
3. medical adhesive tape according to claim 1 or 2, which is characterized in that the natural plant gum is guar gum or flax gum.
4. medical adhesive tape according to claim 3, which is characterized in that the cloth substrate is PE film or TPU membrane or foam
Or PE film and non-woven fabric compounded cloth material.
5. the preparation method of the described in any item medical adhesive tapes of Claims 1-4, it is characterised in that include the following steps:
1) weigh polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and
Water;
2) polysiloxanes, polyurethane, platinum catalyst, dimethyl silicone polymer, dimethyl silicone polymer, natural plant gum and water are added
Enter into container, be uniformly mixed, forms glue;
3) gluing will prepare [U1] and is coated onto cloth substrate with glue spreader, and glue is with a thickness of 1-3mm [U2].