CN109535956A - One kind low solvent type high solid coating for automobile interiors and preparation method thereof - Google Patents
One kind low solvent type high solid coating for automobile interiors and preparation method thereof Download PDFInfo
- Publication number
- CN109535956A CN109535956A CN201710614229.8A CN201710614229A CN109535956A CN 109535956 A CN109535956 A CN 109535956A CN 201710614229 A CN201710614229 A CN 201710614229A CN 109535956 A CN109535956 A CN 109535956A
- Authority
- CN
- China
- Prior art keywords
- type high
- solvent type
- automobile interiors
- parts
- high solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low solvent type high solid coatings for automobile interiors, it is made by the raw material for including following parts by weight: 20-30 parts of Hydroxylated acrylic resin, 20-30 parts of low viscosity linear, crosslinkable resin, leveling auxiliary agent 3-6 parts of dispersion, 15-20 parts of toner, 10-12 parts of flatting silica, 20-30 parts of solvent, 20 parts of isocyanate curing agent and 10 parts of diluent, wherein, containing admittedly for the Hydroxylated acrylic resin is 49%-51%, and it is 1.8-2.3% that hydroxyl value, which accounts for solid component,.The route of Hydroxylated acrylic resin is largely used in coating of the invention product different from the past, but by being optimized to coating composition, low viscosity linear, crosslinkable resin is added, the resin participates in reaction, both the dosage of VOC had been greatly reduced, high solids content is still maintained again, ensure that the comprehensive performance of polyurethane, meets TL226-2016 test request.
Description
Technical field
The invention belongs to automobile interior decoration technical field of coatings, in particular to a kind of low solvent type high solid for automobile interiors
Coating and preparation method thereof may be directly applied to ABS, the substrates such as ABS/PC, or be applied indirectly to PP by other means, PC and
The acceptable substrates such as PA.
Background technique
Traditional solvent type automobile interior decoration coating in the construction process, must add opposite coating host agent mass fraction 20-
100% diluent is used for auxiliary construction, and in film forming procedure, which volatilizees immediately, thus guarantee coating application and at
Film quality.That is, under current techniques background, construction medium when organic solvent is only used as coating to spray, i.e. adjustment is viscous
Degree, therefore, volatile organic matter (VOC) dosage is big, and discharge amount is big, and environmental pollution is serious.
In recent years, this problem is being paid close attention in industry always, and is attempting to change this single function of organic solvent, to improve
The environmental friendliness of industry copes with the policy direction of energy-saving and emission-reduction.And for a long time, technology path is always to go out from thixotroping angle
Hair keeps stability with high finished product viscosity, the mobility under shearing force is provided with thixotropy, makes to reach and reduce diluent
The purpose of dosage, but the technical limitation is, high thixotropic is simultaneously unstable, while the thinking sheet of some offer high thixotropics
Body is also the product of the high VOC of high energy consumption, such as various organically-modified wax liquors.
Summary of the invention
The first object of the present invention is to provide a kind of low solvent type high solid coating for automobile interiors, by coating group
Divide and optimize, low viscosity linear, crosslinkable resin is added, had not only greatly reduced the dosage of VOC, but also still maintain large arch dam
Amount, in the case where not needing a large amount of extra diluent waters, construction is friendly, and volatile ingredient is few.
The second object of the present invention is to provide a kind of preparation side of above-mentioned low solvent type high solid coating for automobile interiors
Method, coating obtained had not only greatly reduced the dosage of VOC, but also still maintained high solids content, did not needed largely additionally to construct dilute
In the case where releasing agent, construction is friendly, and volatile ingredient is few.
Technical scheme is as follows:
A kind of low solvent type high solid coating for automobile interiors, is made by the raw material for including following parts by weight:
Wherein, the hydroxyl value of the Hydroxylated acrylic resin account for the resin itself can not the solid component of volatile ingredient be
1.8-2.3%, wherein the resin can not volatile component solid component be 49%-51%.
Preferably, the low viscosity linear, crosslinkable resin is the line containing the hydroxyl group that can be reacted with isocyanates
The low branched resins of property, solid component 100%.
Preferably, the dispersion leveling auxiliary agent is polyether modified siloxane, solid component 50%.
Preferably, the toner is goth black No. 4
Preferably, the flatting silica is Degussa OK412
Preferably, the solvent is the mixed solvent of the quality such as butyl acetate, diacetone alcohol and isopropyl acetate.
Preferably, the isocyanate curing agent is that N3390 curing agent is created in Cohan.
Preferably, the diluent is the mixture of the quality such as diacetone alcohol and isopropyl acetate.
The invention also discloses the preparation method of above-mentioned low solvent type high solid coating for automobile interiors, feature exists
In, comprising the following steps:
(1) raw material for taking each parts by weight described in claim 1 is added with stirring Hydroxylated acrylic resin, dispersion levelling agent
With appropriate solvent, 15-20min is stirred, carbon black toner is added and carries out high speed dispersion 30-45min, add low viscosity and linearly may be used
Crosslinked resin, flatting silica and residual solvent stir 15min, strainer filtering packed for standby use;
(2) before constructing, isocyanate curing agent and diluent are respectively after strainer filtering, and step (1) is obtained mixes
Liquid mixes, and obtains low solvent type high solid coating.
Compared with prior art, beneficial effects of the present invention are as follows:
The amount of the volatilizable component during coating application is greatly reduced in the present invention.
One kind low solvent type high solid coating for automobile interiors of the invention largely uses hydroxyl in product different from the past
The route of base acrylic resin, but by being optimized to coating composition, low viscosity linear, crosslinkable resin is added, this can be handed over
Join resin and participate in reaction, had not only greatly reduced the dosage of VOC, but also still maintain high solids content, and ensure that the synthesis of polyurethane
Performance meets TL226-2016 test request.
Certainly, it implements any of the products of the present invention and does not necessarily require achieving all the advantages described above at the same time.
Specific embodiment
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate this hair
It is bright, rather than limit the scope of protection of the present invention.What those skilled in the art made according to the present invention in practical applications changes
Into and adjustment, still fall within protection scope of the present invention.
The simple thinking for changing water from solvent different from the past for reducing VOC, the present invention had both guaranteed the long-term storage of product itself
Stability (better than aqueous product) is deposited, product itself large arch dam had both been ensure that, and had in turn ensured low viscosity, therefore, there is no need to a large amount of
In the case where additional construction diluent, construction is friendly, and volatile ingredient is few.In addition, automotive interior product uses poly- ammonia since tradition
Chemical constituent of the ester as coating, there is very high comprehensive performance.The present invention also different from previous product largely use hydroxyl
The route of acrylic resin, and the thinking of low viscosity linear, crosslinkable resin has been used, which participates in reaction, does not wave
Hair not only ensure that the comprehensive performance of polyurethane, but also reduce the discharge of VOC.
Comparative example 1
A kind of coating for automobile interiors of this comparative example 1 is made by the raw material for including following parts by weight:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method of the coating for automobile interiors of the comparative example, comprising the following steps:
(1) raw material for taking each parts by weight described in claim 1 is added with stirring the Hydroxylated acrylic resin, dispersion levelling
Agent and appropriate solvent stir 15-20min, add carbon black toner and carry out high speed dispersion 30-45min, add flatting silica and remain
Remaining solvent stirs 15min, strainer filtering packed for standby use;
(2) before constructing, isocyanate curing agent and diluent are respectively after strainer filtering, and step (1) is obtained mixes
Liquid mixes, and obtains coating.
Paint spraying method made from the comparative example are as follows: construction uses the air gun of 0.8-1.0 millimeters of bores, air pressure 3-
4bar, substrate are ABS plastic
Embodiment 1
One kind low solvent type high solid coating for automobile interiors of the present embodiment 1, mainly by including following parts by weight
Raw material is made:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method of the coating for automobile interiors of the embodiment, comprising the following steps:
(1) raw material for taking each parts by weight described in claim 1 is added with stirring Hydroxylated acrylic resin, dispersion levelling agent
With appropriate solvent, 15-20min is stirred, carbon black toner is added and carries out high speed dispersion 30-45min, add low viscosity and linearly may be used
Crosslinked resin, flatting silica and residual solvent stir 15min, strainer filtering packed for standby use;
(2) before constructing, isocyanate curing agent and diluent are respectively after strainer filtering, and step (1) is obtained mixes
Liquid mixes.
Paint spraying method made from the embodiment are as follows: construction uses the air gun of 0.8-1.0 millimeters of bores, air pressure 3-
4bar, substrate are ABS plastic.
Comparative example 2
A kind of coating for automobile interiors of this comparative example 2 is made by the raw material for including following parts by weight:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method and coating process of the coating are the same as comparative example 1.
Embodiment 2
One kind low solvent type high solid coating for automobile interiors of the present embodiment 2, mainly by including following parts by weight
Raw material is made:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method and coating process of the coating are the same as embodiment 1.
Comparative example 3
A kind of coating for automobile interiors of this comparative example 1 is made by the raw material for including following parts by weight:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method and coating process of the coating are the same as comparative example 2.
Embodiment 3
One kind low solvent type high solid coating for automobile interiors of the present embodiment 3, mainly by including following parts by weight
Raw material is made:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method and coating process of the coating are the same as embodiment 1.
Comparative example 4
A kind of coating for automobile interiors of this comparative example 4 is made by the raw material for including following parts by weight:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
The preparation method and coating process of the coating are the same as comparative example 1.
Embodiment 4
One kind low solvent type high solid coating for automobile interiors of the present embodiment 4, mainly by including following parts by weight
Raw material is made:
The preparation method and coating process of the coating are the same as embodiment 1.
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, and solid component contains
Amount is 50%.
Finally, by the result of comparative example 1~4 and Examples 1 to 4 statistics in table one.Wherein, VOC total amount is in table one
Volatilizable total amount of organic, that is, in the blends to be onstructed mixed, volatilizable quality accounts for the percentage of gross mass.Here
Volatilizable organic matter adjusted from the solvent of coating of the present invention, construction and glue diluent, and hydroxyl involved in coating of the present invention
Solvent in base acrylic resin and polyether modified siloxane.
Table one
It summarizes, according to some vehicle project monthly plan yield 20000, using coating host agent, (i.e. step 1 is made components
Mixed solution) amount to 720kg under the premise of, curing agent N3390 usage amount be host agent 20%, traditional product is needed using dilute
70% that dosage is host agent is released, and the formula of embodiment 1 is because of ontology large arch dam, the characteristic of low viscosity, diluent usage amount only accounts for
The 10% of host agent, therefore, total volatile ingredient can reduce 65%*720* (1+20%+70%) -42%*720* (1+20%+10%)
=4969.08kg.That is, corresponding every 1kg host agent, the VOC total amount of organic solvent drop to 0.546kg from 1.235kg, drop
Width is up to 54.6%.
In addition, also carrying out TL226-2016 test, as shown in Table 2, test result to the substrate after Examples 1 to 3 coating
Meet test request.
Table two
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (9)
1. a kind of low solvent type high solid coating for automobile interiors, which is characterized in that by the raw material system including following parts by weight
:
Wherein, it is 1.8-2.3% that the hydroxyl value of the Hydroxylated acrylic resin, which accounts for solid component, wherein solid component is
49%-51%.
2. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that described is low viscous
Degree linear, crosslinkable resin is the linear low branched resins containing the hydroxyl group reacted with isocyanates, and solid component is
100%.
3. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the dispersion
Leveling auxiliary agent is polyether modified siloxane, solid component 50%.
4. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the toner
It is goth black No. 4.
5. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the delustring
Powder is Degussa OK 412.
6. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the solvent
For the mixed solvent of the specific masses such as butyl acetate, diacetone alcohol and isopropyl acetate.
7. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the isocyanide
Acid esters curing agent is that N3390 curing agent is created in Cohan.
8. low solvent type high solid coating for automobile interiors according to claim 1, which is characterized in that the dilution
Agent adjusts spray viscosity use under Construction State, and the diluent is the mixed of the mass ratioes such as diacetone alcohol and isopropyl acetate
Close object.
9. a kind of preparation method of the low solvent type high solid coating for automobile interiors as described in claim 1~8, feature
It is, comprising the following steps:
(1) raw material for taking each parts by weight described in claim 1 is added with stirring Hydroxylated acrylic resin, dispersion levelling agent and fits
Solvent is measured, 15-20min is stirred, toner is added and carries out high speed dispersion 30-45min, add low viscosity linear, crosslinkable tree
Rouge, flatting silica and residual solvent, stir 15min, and strainer filtering is stand-by;
(2) isocyanate curing agent and diluent are mixed with mixed liquor made from step (1) respectively after strainer filtering, that is, are made
Obtain low solvent type high solid coating.