CN109535862A - A kind of high intensity canvas - Google Patents

A kind of high intensity canvas Download PDF

Info

Publication number
CN109535862A
CN109535862A CN201710656851.5A CN201710656851A CN109535862A CN 109535862 A CN109535862 A CN 109535862A CN 201710656851 A CN201710656851 A CN 201710656851A CN 109535862 A CN109535862 A CN 109535862A
Authority
CN
China
Prior art keywords
parts
canvas
pvc
cotton yarn
pvc coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710656851.5A
Other languages
Chinese (zh)
Inventor
朱风振
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Leling Longbang Textile Co Ltd
Original Assignee
Leling Longbang Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Leling Longbang Textile Co Ltd filed Critical Leling Longbang Textile Co Ltd
Priority to CN201710656851.5A priority Critical patent/CN109535862A/en
Publication of CN109535862A publication Critical patent/CN109535862A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of high-intensitive canvas.The high intensity canvas is made of grid cloth double-coated PVC coating, and the composition of raw materials of the PVC coating includes following components according to parts by weight: 80 parts of PVC paste resin, 10~30 parts of haloflex, 40 ~ 85 parts of dioctyl phthalate, 1 ~ 8 part of anatase thpe white powder, 0.1~2 part of cotton yarn, 3 ~ 6 parts of stabilizer, 1 ~ 6 part of adhesive.High intensity canvas of the invention joined cotton yarn in PVC coating formula, its heat preservation and insulation that can not only increase high-intensitive canvas, and it can be with entanglement of formation between cotton yarn and the grid cloth of canvas, to increase the adhesive strength between coating and grid cloth, obtained PVC canvas is made to have the characteristics that high-strength and high ductility.

Description

A kind of high intensity canvas
Technical field
The present invention relates to a kind of high-intensitive canvas.
Background technique
PVC canvas is base fabric coated on both sides PVC paste resin.Compared with general PE tarpaulin, PVC tarpaulin rain proofness is much better than PP, PE paulin all have been widely used in fields such as paulin room, automobile, train, storages.In addition, PVC is at low cost, and abundance, nothing Poison is a kind of membrane material being worthy to be popularized.It is existing to have intensity low, poor toughness scarce in PVC canvas although inexpensive Point.
Summary of the invention
It is an object of the invention to overcome defect existing in the prior art, a kind of high-intensitive canvas is provided.
To achieve the purpose of the present invention, the technical scheme is that it is a kind of high intensity canvas, by the two-sided painting of grid cloth PVC coating composition is applied, the composition of raw materials of the PVC coating includes following components according to parts by weight: 80 parts of PVC paste resin, chlorine Change 10~30 parts of polyethylene, 40 ~ 85 parts of dioctyl phthalate, 1 ~ 8 part of anatase thpe white powder, 0.1~2 part of cotton yarn, stablize 3 ~ 6 parts of agent, 1 ~ 6 part of adhesive.
Preferred technical solution is that the length of the cotton yarn is 600 microns or less.
Preferred technical solution is that described adhesive is that vinylpyridine system adhesive or polyvinyl butyral bond Agent.
Preferred technical solution is, also comprising 0.1 ~ 0.8 part of anti-UV agent in the composition of raw materials of the PVC coating.
Preferred technical solution is, also comprising 1 ~ 10 part of antioxidant in the composition of raw materials of the PVC coating.
The prior art is compared, and present invention high intensity canvas joined cotton yarn in PVC coating formula, can not only be increased The heat preservation and insulation of high-intensitive canvas, and can be with entanglement of formation, to increase coating between cotton yarn and the grid cloth of canvas Adhesive strength between grid cloth makes obtained PVC canvas have the characteristics that high-strength and high ductility.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1
The present invention is a kind of high-intensitive canvas, is made of grid cloth double-coated PVC coating, the raw material of the PVC coating is matched Side according to parts by weight include following components: 80 parts of PVC paste resin, 20 parts of haloflex, 65 parts of dioctyl phthalate, 8 parts of anatase thpe white powder, 0.1 part of cotton yarn, 6 parts of epoxy soybean oil stabilizer, 1 part of polyvinyl butyral cementing agent.Wherein, cotton The length of yarn is 600 microns or less.
Embodiment 2
The present invention is a kind of high-intensitive canvas, is made of grid cloth double-coated PVC coating, the raw material of the PVC coating is matched Side according to parts by weight include following components: 80 parts of PVC paste resin, 30 parts of haloflex, 40 parts of dioctyl phthalate, 1 part of anatase thpe white powder, 2 parts of cotton yarn, 3 parts of epoxy soybean oil stabilizer, 5 parts of antioxidant, vinylpyridine system adhesive 4 Part.Wherein, the length of cotton yarn is 600 microns or less.
Embodiment 3
The present invention is a kind of high-intensitive canvas, is made of grid cloth double-coated PVC coating, the raw material of the PVC coating is matched Side according to parts by weight include following components: 80 parts of PVC paste resin, 10 parts of haloflex, 85 parts of dioctyl phthalate, 4 parts of anatase thpe white powder, 0.1 part of cotton yarn, 4 parts of epoxy soybean oil stabilizer, 10 parts of antioxidant, vinylpyridine system adhesive 6 parts, 0.1 part of anti-UV agent.Wherein, the length of cotton yarn is 600 microns or less.
Embodiment 4
The present invention is a kind of high-intensitive canvas, is made of grid cloth double-coated PVC coating, the raw material of the PVC coating is matched Side according to parts by weight include following components: 80 parts of PVC paste resin, 25 parts of haloflex, 70 parts of dioctyl phthalate, 6 parts of anatase thpe white powder, 1 part of cotton yarn, 3 parts of epoxy soybean oil stabilizer, 1 part of antioxidant, polyvinyl butyral cementing agent 5 Part, 0.8 part of anti-UV agent.Wherein, the length of cotton yarn is 600 microns or less.
Embodiment 5
The present invention is a kind of high-intensitive canvas, is made of grid cloth double-coated PVC coating, the raw material of the PVC coating is matched Side according to parts by weight include following components: 80 parts of PVC paste resin, 25 parts of haloflex, 70 parts of dioctyl phthalate, 4 parts of anatase thpe white powder, 1.5 parts of cotton yarn, 4 parts of epoxy soybean oil stabilizer, 2 parts of antioxidant, polyvinyl butyral bonding 4 parts of agent, 0.2 part of anti-UV agent.Wherein, the length of cotton yarn is 600 microns or less.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications Also it should be regarded as protection scope of the present invention.

Claims (5)

1. a kind of high intensity canvas, which is characterized in that be made of grid cloth double-coated PVC coating, the raw material of the PVC coating Formula includes following components according to parts by weight: 80 parts of PVC paste resin, 10~30 parts of haloflex, phthalic acid two are pungent 40 ~ 85 parts of ester, 1 ~ 8 part of anatase thpe white powder, 0.1~2 part of cotton yarn, 3 ~ 6 parts of stabilizer, 1 ~ 6 part of adhesive.
2. high intensity canvas as described in claim 1, which is characterized in that the length of the cotton yarn is 600 microns or less.
3. high intensity canvas as described in claim 1, which is characterized in that described adhesive be vinylpyridine system adhesive or Polyvinyl butyral cementing agent.
4. the high-intensitive canvas as described in claims 1 or 2 or 3, which is characterized in that in the composition of raw materials of the PVC coating also Include 0.1 ~ 0.8 part of anti-UV agent.
5. the high-intensitive canvas as described in claims 1 or 2 or 3, which is characterized in that in the composition of raw materials of the PVC coating also Include 1 ~ 10 part of antioxidant.
CN201710656851.5A 2017-08-03 2017-08-03 A kind of high intensity canvas Pending CN109535862A (en)