CN109504147A - A kind of antirusting paint coated in mining machinery surface - Google Patents
A kind of antirusting paint coated in mining machinery surface Download PDFInfo
- Publication number
- CN109504147A CN109504147A CN201811203180.8A CN201811203180A CN109504147A CN 109504147 A CN109504147 A CN 109504147A CN 201811203180 A CN201811203180 A CN 201811203180A CN 109504147 A CN109504147 A CN 109504147A
- Authority
- CN
- China
- Prior art keywords
- parts
- mining machinery
- acrylate
- defoaming agent
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of antirusting paints coated in mining machinery surface, it is formed according to the parts by weight of following raw material: 65-83 parts of rosin modified alkyd resin, it is 42-51 parts acrylic resin modified, 28-36 parts of styrene-acrylic emulsion, 19-30 parts of epoxy soybean oil acrylate, 15-21 parts of acrylate, 3-9 parts of petroleum sodium sulfonate, 3-8 parts of phenyl salicylate, plough sugar alcohol ester 2-7 parts in mountain, 1-5 parts of trbasic zinc phosphate, 2-5 parts of organic polycarboxylic acid, 1-4 parts of lead naphthenate, 2-5 parts of calcium chloride, 1-4 parts of alumina powder, 3-7 parts of nano-silicon nitride, 1-5 parts of propylene glycol, 1-4 parts of hexone, 1-8 parts of vinyl benzene, 1-5 parts of micaceous iron oxide, 1-1.8 parts of azodiisobutyronitrile, 5-12 parts of silica sols, mica powder 3 - 8 parts, 4-10 parts of carbon fiber, 3-8 parts of quartz sand, 8-15 parts of active carbon, 6-14 parts of toughener, 1-4 parts of defoaming agent, 17-25 parts of castor oil, 29-48 parts of deionized water.Inventive formulation science, after mining machinery appearance is brushed, coating is closely knit, and adhesive force is strong, and has the abilities such as anti-corrosion, anti-corrosive properties, moisture resistance.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of antirusting paints coated in mining machinery surface.
Background technique
Mining machinery industry is to provide the important foundation industry of equipment for the exploitation and processing of solid material, material and fuel
One of, the important basic industries such as black and nonferrous metallurgy, coal, building materials, chemical industry, nuclear industry department is served, product is being handed over
Also there is extensive application in the capital construction of basic sectors such as logical, railway, building, water conservancy and hydropower.
China's mines machinery industry mainly has seven major class, the product of a kind and thousands of kinds of specifications about more than 300.From 2000
Start, at home under the pulling of basic industries and infrastructure great development, the products of mining machine market demand is vigorous, in 2010
State's mining machinery industry sales volume breaks through 400,000,000,000 yuan, and so far China has surmounted North America, Japan, West Europe, and it is maximum to become the whole world
Mining machinery market.Mining machinery industry occupies pillar status in national economy, and the effect and contribution in economic construction are good
It is more.Either from the market development status of Chinese mining machinery industry, or from the point of view of global industry operation situation, China's mines
Machinery industry is just being stayed in a historic window phase.The following 5-10 is China's mines machinery enterprise comprehensively or deeply melts
Enter the world, the important period with world's joint development, the development prospect of industry is preferable.
Currently, extending mining industry service life of equipment as the rapid mine of mining industry equipment use scope is big and also having become continuation
It solves the problems, such as.Internal temperature can be very high during the work time for current general mining industry equipment, and mining machinery device external is often
It cannot stand wind and weather, lead to rusty scale corrosion aggravation, antirusting paint and the associativity in rust face are poor, can endanger machine internal, cause
Serious economic loss.
Summary of the invention
The object of the invention is that providing a kind of antirust coated in mining machinery surface to solve the above-mentioned problems
Coating.
To achieve the goals above, the present invention is achieved by the following technical solutions: one kind being coated in mining machinery table
The antirusting paint in face forms: 65-83 parts of rosin modified alkyd resin, modified acroleic acid tree according to the parts by weight of following raw material
42-51 parts of rouge, 28-36 parts of styrene-acrylic emulsion, 19-30 parts of epoxy soybean oil acrylate, 15-21 parts of acrylate, mahogany acid
Sugar alcohol ester 2-7 parts, 1-5 parts of trbasic zinc phosphate, 2-5 parts of organic polycarboxylic acid, lead naphthenate are ploughed in 3-9 parts of sodium, 3-8 parts of phenyl salicylate, mountain
1-4 parts, 2-5 parts of calcium chloride, 1-4 parts of alumina powder, 3-7 parts of nano-silicon nitride, 1-5 parts of propylene glycol, hexone 1-4
Part, 1-8 parts of vinyl benzene, 1-5 parts of micaceous iron oxide, 1-1.8 parts of azodiisobutyronitrile, 5-12 parts of silica sols, mica powder
3-8 parts, 4-10 parts of carbon fiber, 3-8 parts of quartz sand, 8-15 parts of active carbon, 6-14 parts of toughener, 1-4 parts of defoaming agent, castor oil
17-25 parts, 29-48 parts of deionized water.
A kind of above-mentioned antirusting paint coated in mining machinery surface forms: pine according to the parts by weight of following raw material
Fragrant modified alkyd resin 65-78 parts, 42-49 parts acrylic resin modified, 28-33 parts of styrene-acrylic emulsion, epoxidized soybean oil acrylic acid
Sugar alcohol ester 2-6 parts, phosphorus are ploughed in 19-26 parts of ester, 15-20 parts of acrylate, 3-8 parts of petroleum sodium sulfonate, 3-7 parts of phenyl salicylate, mountain
Sour zinc 1-4 parts, 2-4 parts of organic polycarboxylic acid, 1-3 parts of lead naphthenate, 2-4 parts of calcium chloride, 1-3 parts of alumina powder, nano-silicon nitride
3-6 parts, 1-4 parts of propylene glycol, 1-3 parts of hexone, 1-6 parts of vinyl benzene, 1-4 parts of micaceous iron oxide, azo two it is different
1-1.5 parts of butyronitrile, 5-11 parts of silica sols, 3-7 parts of mica powder, 4-8 parts of carbon fiber, 3-7 parts of quartz sand, active carbon 8-13
Part, 6-12 parts of toughener, 1-3 parts of defoaming agent, 17-22 parts of castor oil, 29-45 parts of deionized water.
A kind of above-mentioned antirusting paint coated in mining machinery surface forms: pine according to the parts by weight of following raw material
71 parts of fragrant modified alkyd resin, 45 parts acrylic resin modified, 30 parts of styrene-acrylic emulsion, 22 parts of epoxy soybean oil acrylate, third
17 parts of olefin(e) acid ester, 5 parts of petroleum sodium sulfonate, 5 parts of phenyl salicylate, mountain plough 4 parts of sugar alcohol ester, 3 parts of trbasic zinc phosphate, 3 parts of organic polycarboxylic acid,
2 parts of lead naphthenate, 3 parts of calcium chloride, 2 parts of alumina powder, 5 parts of nano-silicon nitride, 2 parts of propylene glycol, 2 parts of hexone,
4 parts of vinyl benzene, 3 parts of micaceous iron oxide, 1.2 parts of azodiisobutyronitrile, 8 parts of silica sols, 5 parts of mica powder, carbon fiber 6
Part, 5 parts of quartz sand, 11 parts of active carbon, 9 parts of toughener, 2 parts of defoaming agent, 19 parts of castor oil, 34 parts of deionized water.
A kind of above-mentioned antirusting paint coated in mining machinery surface, the toughener are acetate.
A kind of above-mentioned antirusting paint coated in mining machinery surface, the defoaming agent are organosilicon ketone defoaming agent.
In summary the invention has the following advantages: inventive formulation is scientific, brushed in mining machinery appearance
Afterwards, coating is closely knit, and adhesive force is strong, and flatness is high, and has the abilities such as anti-corrosion, anti-corrosive properties, moisture resistance, it is not easy to break
Damage and part corrosion, and it overcomes the limitation for generally requiring higher derusting grade, can not do processing of rust removing in mechanical equipment
When directly coat, quickly can mutually be adsorbed on the mechanical equipment surface with rust, adhesive force is high, to reach the effect of lasting antirust
Fruit.
Specific embodiment
Specific embodiment 1:
A kind of antirusting paint coated in mining machinery surface forms: Abietyl modified alcohol according to the parts by weight of following raw material
78 parts of acid resin, 49 parts acrylic resin modified, 33 parts of styrene-acrylic emulsion, 26 parts of epoxy soybean oil acrylate, acrylate 19
6 parts of sugar alcohol ester, 4 parts of trbasic zinc phosphate, 4 parts of organic polycarboxylic acid, lead naphthenate are ploughed in part, 8 parts of petroleum sodium sulfonate, 7 parts of phenyl salicylate, mountain
3 parts, 4 parts of calcium chloride, 3 parts of alumina powder, 6 parts of nano-silicon nitride, 4 parts of propylene glycol, 3 parts of hexone, vinyl benzene 6
Part, 4 parts of micaceous iron oxide, 1.5 parts of azodiisobutyronitrile, 11 parts of silica sols, 7 parts of mica powder, 8 parts of carbon fiber, quartz sand 7
Part, 13 parts of active carbon, 12 parts of toughener, 3 parts of defoaming agent, 22 parts of castor oil, 45 parts of deionized water.
The toughener is acetate;The defoaming agent is organosilicon ketone defoaming agent.
Specific embodiment 2:
A kind of antirusting paint coated in mining machinery surface forms: Abietyl modified alcohol according to the parts by weight of following raw material
71 parts of acid resin, 45 parts acrylic resin modified, 30 parts of styrene-acrylic emulsion, 22 parts of epoxy soybean oil acrylate, acrylate 17
4 parts of sugar alcohol ester, 3 parts of trbasic zinc phosphate, 3 parts of organic polycarboxylic acid, lead naphthenate are ploughed in part, 5 parts of petroleum sodium sulfonate, 5 parts of phenyl salicylate, mountain
2 parts, 3 parts of calcium chloride, 2 parts of alumina powder, 5 parts of nano-silicon nitride, 2 parts of propylene glycol, 2 parts of hexone, vinyl benzene 4
Part, 3 parts of micaceous iron oxide, 1.2 parts of azodiisobutyronitrile, 8 parts of silica sols, 5 parts of mica powder, 6 parts of carbon fiber, quartz sand 5
Part, 11 parts of active carbon, 9 parts of toughener, 2 parts of defoaming agent, 19 parts of castor oil, 34 parts of deionized water.
The toughener is acetate;The defoaming agent is organosilicon ketone defoaming agent.
Specific embodiment 3:
A kind of antirusting paint coated in mining machinery surface forms: Abietyl modified alcohol according to the parts by weight of following raw material
65 parts of acid resin, 42 parts acrylic resin modified, 28 parts of styrene-acrylic emulsion, 19 parts of epoxy soybean oil acrylate, acrylate 15
2 parts of sugar alcohol ester, 1 part of trbasic zinc phosphate, 2 parts of organic polycarboxylic acid, lead naphthenate are ploughed in part, 3 parts of petroleum sodium sulfonate, 3 parts of phenyl salicylate, mountain
1 part, 2 parts of calcium chloride, 1 part of alumina powder, 3 parts of nano-silicon nitride, 2 parts of propylene glycol, 1 part of hexone, vinyl benzene 2
Part, 1 part of micaceous iron oxide, 1 part of azodiisobutyronitrile, 6 parts of silica sols, 3 parts of mica powder, 4 parts of carbon fiber, 3 parts of quartz sand,
8 parts of active carbon, 6 parts of toughener, 1 part of defoaming agent, 17 parts of castor oil, 29 parts of deionized water.
The toughener is acetate;The defoaming agent is organosilicon ketone defoaming agent.
Embodiment provided above is better embodiment of the invention, only is used to facilitate to illustrate the present invention, not to this hair
It is bright to make any form of restriction, any those of ordinary skill in the art, if not departing from the proposed skill of the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from technical feature content of the invention, in the range of still falling within the technology of the present invention feature.
Claims (5)
1. a kind of antirusting paint coated in mining machinery surface, which is characterized in that formed according to the parts by weight of following raw material:
65-83 parts of rosin modified alkyd resin, 42-51 parts acrylic resin modified, 28-36 parts of styrene-acrylic emulsion, epoxidized soybean oil propylene
19-30 parts of acid esters, 15-21 parts of acrylate, 3-9 parts of petroleum sodium sulfonate, 3-8 parts of phenyl salicylate, mountain plough sugar alcohol ester 2-7 parts,
1-5 parts of trbasic zinc phosphate, 2-5 parts of organic polycarboxylic acid, 1-4 parts of lead naphthenate, 2-5 parts of calcium chloride, 1-4 parts of alumina powder, nano silicon nitride
3-7 parts of silicon, 1-5 parts of propylene glycol, 1-4 parts of hexone, 1-8 parts of vinyl benzene, 1-5 parts of micaceous iron oxide, azo two
1-1.8 parts of isobutyronitrile, 5-12 parts of silica sols, 3-8 parts of mica powder, 4-10 parts of carbon fiber, 3-8 parts of quartz sand, active carbon 8-
15 parts, 6-14 parts of toughener, 1-4 parts of defoaming agent, 17-25 parts of castor oil, 29-48 parts of deionized water.
2. a kind of antirusting paint coated in mining machinery surface according to claim 1, which is characterized in that according to following
The parts by weight of raw material form: 65-78 parts of rosin modified alkyd resin, 42-49 parts acrylic resin modified, styrene-acrylic emulsion 28-
33 parts, 19-26 parts of epoxy soybean oil acrylate, 15-20 parts of acrylate, 3-8 parts of petroleum sodium sulfonate, phenyl salicylate 3-7
Part, mountain plough sugar alcohol ester 2-6 parts, 1-4 parts of trbasic zinc phosphate, 2-4 parts of organic polycarboxylic acid, 1-3 parts of lead naphthenate, 2-4 parts of calcium chloride, oxidation
1-3 parts of aluminium powder, 3-6 parts of nano-silicon nitride, 1-4 parts of propylene glycol, 1-3 parts of hexone, 1-6 parts of vinyl benzene, mica
1-4 parts of iron oxide, 1-1.5 parts of azodiisobutyronitrile, 5-11 parts of silica sols, 3-7 parts of mica powder, 4-8 parts of carbon fiber, quartz
3-7 parts of sand, 8-13 parts of active carbon, 6-12 parts of toughener, 1-3 parts of defoaming agent, 17-22 parts of castor oil, 29-45 parts of deionized water.
3. a kind of antirusting paint coated in mining machinery surface according to claim 1, which is characterized in that according to following
The parts by weight of raw material form: 71 parts of rosin modified alkyd resin, 45 parts acrylic resin modified, 30 parts of styrene-acrylic emulsion, epoxy
4 parts of sugar alcohol ester, phosphorus are ploughed in 22 parts of soybean oil acrylate, 17 parts of acrylate, 5 parts of petroleum sodium sulfonate, 5 parts of phenyl salicylate, mountain
3 parts of sour zinc, 3 parts of organic polycarboxylic acid, 2 parts of lead naphthenate, 3 parts of calcium chloride, 2 parts of alumina powder, 5 parts of nano-silicon nitride, propylene glycol 2
Part, 2 parts of hexone, 4 parts of vinyl benzene, 3 parts of micaceous iron oxide, 1.2 parts of azodiisobutyronitrile, silica sols 8
Part, 19 parts of castor oil, is gone 5 parts of mica powder, 6 parts of carbon fiber, 5 parts of quartz sand, 11 parts of active carbon, 9 parts of toughener, 2 parts of defoaming agent
34 parts of ionized water.
4. a kind of antirusting paint coated in mining machinery surface according to claim 1 to 3, it is characterised in that: institute
Stating toughener is acetate.
5. a kind of antirusting paint coated in mining machinery surface according to claim 1 to 3, it is characterised in that: institute
Stating defoaming agent is organosilicon ketone defoaming agent.