CN109503932A - A kind of multi-layer co-extruded mold cleaning material - Google Patents
A kind of multi-layer co-extruded mold cleaning material Download PDFInfo
- Publication number
- CN109503932A CN109503932A CN201811392637.4A CN201811392637A CN109503932A CN 109503932 A CN109503932 A CN 109503932A CN 201811392637 A CN201811392637 A CN 201811392637A CN 109503932 A CN109503932 A CN 109503932A
- Authority
- CN
- China
- Prior art keywords
- layer
- cleaning material
- mold cleaning
- extruded mold
- polyolefin resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multi-layer co-extruded mold cleaning materials, are made of the component of following mass percentage: polyolefin resin is 90.0-99.5% as carrier, the mass percent of carrier;At least one of polyetheramine, polyisobutylene amine, polysuccinimide is selected to be used as detergent, the mass percent of detergent is 0.5-10%.The polyolefin resin is linear low density polyethylene.Multi-layer co-extruded mold cleaning material of the invention can improve existing mold cleaning material and be easy to damage mold and the problem bad to coking and carbonization cleaning effect, there is good effect in terms of cleaning coking and carbonization, it also has certain effect to the maintenance of mold simultaneously, mold cleaning and maintenance are carried out using the multi-layer co-extruded mold cleaning material, the time of mold dismantling cleaning can be made to extend 20-50%.
Description
Technical field
The invention belongs to mold cleaning material technical fields, specifically, it is clear to be related to a kind of novel multi-layer co-extruded mold
Clean material.
Background technique
The cleaning of multi-layer co-extruded mold is always industry difficult point, and mold clean-up performance can not enough bring various production problems,
Such as various problem of appearance of stain, crystal point, lines.Existing multi-layer co-extruded mold cleaning, typically uses high viscosity/extrusion
The material over time variable speed of pressure rinses, or is expected using proprietary cleaning to be cleaned.The principle of proprietary cleaning material are as follows: use
Very highly viscous resin carrier, the material comprising abrasiveness, foaming or non-foamed usage mode, by material shearing force with
Grinding agent cleans mold, generally require it is very long use the time, while can to mold, especially coated mold
Certain damage is generated, while cleaning material being removed from mold after cleaning finishes and is also required to long time.It is this
Mode is more effective to general gel, but the effect is relatively poor with carbonization to the coking in mold.
Therefore, it is badly in need of a kind of pair of good cleaning material of PP TYPE tool cleaning effect.
Summary of the invention
The first purpose of the invention is to provide a kind of multi-layer co-extruded mold cleaning materials.
A second object of the present invention is to provide a kind of preparation methods of multi-layer co-extruded mold cleaning material.
To achieve the goals above, The technical solution adopted by the invention is as follows:
The first aspect of the invention provides a kind of multi-layer co-extruded mold cleaning material, is by following mass percentage
Component be made:
Polyolefin resin is 90.0-99.5% as carrier, the mass percent of carrier;Select polyetheramine, polyisobutene
At least one of amine, polysuccinimide are used as detergent, and the mass percent of detergent is 0.5-10%.
The polyolefin resin is linear low density polyethylene (LLDPE), and melt index (MI) is between 0.3-50, preferably
It is 4.0, density 0.923g/cm3, the trade mark purchased from petrochemical industry Co., Ltd, Qatar is the polyolefin resin of FD0470.
The molecular weight of the polyetheramine is 1004, and molecular formula is (C3H6O)nC6H16N2O, n are 1~20, are purchased from Hensel gracefulization
Work Co., Ltd, model: FL1000.
The molecular weight of the polyisobutylene amine is 1300, viscosity 645Pa.s, model: PB1300, real purchased from South Korea great Lin
Industry Co., Ltd.
The polysuccinimide is T155 polyisobutylene-bis-succinimide, purchased from the limited public affairs of the holy big chemicals in Jinzhou
Department, kinematic viscosity (100 DEG C): 280-380mm2/ s, total base number (in terms of KOH): 15-25mg/g, flash-point (opening): > 180 DEG C,
Density (20 DEG C): 890-930g/mm3, coloration (dilution): 4.0, moisture: < 0.1%.
The second aspect of the invention provides a kind of preparation method of multi-layer co-extruded mold cleaning material, including with
Lower step:
According to the proportion, using the production method of auxiliary material bucket weighing mixing granulation, polyolefin resin carrier and clear is weighed
Clean dose, using dual-screw pelletizer extruding pelletization, obtain the multi-layer co-extruded mold cleaning material.
The dual-screw pelletizer screw diameter be 50mm, draw ratio 20:1, screw rod be incorgruous steering, extrusion temperature according to
Secondary is 150 DEG C, 170 DEG C, 200 DEG C, 200 DEG C, 200 DEG C, 200 DEG C.
Due to the adoption of the above technical scheme, the present invention has the following advantages and beneficial effects:
Multi-layer co-extruded mold cleaning material of the invention can improve existing mold cleaning material and be easy to damage mold and right
Coking and the bad problem of cleaning effect that is carbonized, have good effect, while to mold in terms of cleaning coking and carbonization
Maintenance also has certain effect, and carries out mold cleaning and maintenance using the multi-layer co-extruded mold cleaning material, can make
The time of mold dismantling cleaning extends 20-50%.
Specific embodiment
In order to illustrate more clearly of the present invention, below with reference to preferred embodiment, the present invention is described further.Ability
Field technique personnel should be appreciated that following specifically described content is illustrative and be not restrictive, this should not be limited with this
The protection scope of invention.
Embodiment 1
A kind of multi-layer co-extruded mold cleaning material is by the component system of following mass percentage (proportion is as shown in table 1)
At:
Polyolefin resin selects the conduct of at least one of polyetheramine, polyisobutylene amine, polysuccinimide as carrier
Detergent;The polyolefin resin is linear low density polyethylene (LLDPE), and melt index (MI) is between 0.3-50, preferably
It is 4.0, density 0.923g/cm3, the trade mark purchased from petrochemical industry Co., Ltd, Qatar is the polyolefin resin of FD0470;
The molecular weight of the polyetheramine is 1004, and molecular formula is (C3H6O)nC6H16N2O, n are 1~20, are purchased from the limited public affairs of the graceful chemical industry of Hensel
Department, model: FL1000;The molecular weight of the polyisobutylene amine is 1300, viscosity 645Pa.s, model, and: PB1300 is purchased from Korea Spro
Guo great woods Industrial Co., Ltd.;The polysuccinimide is T155 polyisobutylene-bis-succinimide, purchased from holy bigization in Jinzhou
Xue Pin Co., Ltd, kinematic viscosity (100 DEG C): 280-380mm2/ s, total base number (in terms of KOH): 15-25mg/g, flash-point (are opened
Mouthful): > 180 DEG C, density (20 DEG C): 890-930g/mm3, coloration (dilution): 4.0, moisture: < 0.1%.
A kind of preparation method of multi-layer co-extruded mold cleaning material, comprising the following steps:
According to the proportion, using the production method of auxiliary material bucket weighing mixing granulation, polyolefin resin carrier and clear is weighed
Clean dose, using dual-screw pelletizer extruding pelletization, the multi-layer co-extruded mold cleaning material is obtained, dual-screw pelletizer screw rod is straight
Diameter is 50mm, draw ratio 20:1, and screw rod is incorgruous steering, extrusion temperature be followed successively by 150 DEG C, 170 DEG C, 200 DEG C, 200 DEG C,
200℃、200℃。
Embodiment 2~20
Raw material proportioning is as shown in table 1, and the preparation method is the same as that of Example 1.
Comparative example 1
Polyolefin resin is linear low density polyethylene (LLDPE), and melt index (MI) is 4.0, is purchased from Qatar's petroleum
The trade mark of Chemical Co., Ltd. is the polyolefin resin of FD0470.
The proportion of Examples 1 to 20 and comparative example 1 is as shown in table 1, is mass percentage in table 1, of the invention is more
When layer co-extruding mould cleaning material is used for the cleaning of film blowing device, by the way of primary at interval of a cleaning in month, when cleaning
It was one bout every 10 minutes, cleaning three bouts terminates using variable speed " DISCO " cleaning way;Disassemble the survey in period
Examination: dismantling condition is to have obvious intermittent stain, stiff block etc. in finished films to influence the flaw of appearance, and can not pass through flushing
The modes such as machine are eliminated, and need to unpick and wash equipment at this time, and the data for disassembling the period are as shown in table 1, from table 1 it follows that this hair
The dismantling period of bright multi-layer co-extruded mold cleaning material is 7~15 months, and comparative example 1 is 6 months, it can be seen that, this
The product effect of invention is very good, carries out mold cleaning and maintenance using the multi-layer co-extruded mold cleaning material, can make mold
The time of dismantling cleaning extends 20-50%.
Table 1
The above is only presently preferred embodiments of the present invention, is not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this patent
Member without departing from the scope of the present invention, when the technology contents using above-mentioned prompt make it is a little change or be modified to
The equivalent embodiment of equivalent variations, but anything that does not depart from the technical scheme of the invention content, it is right according to the technical essence of the invention
Any simple modification, equivalent change and modification made by above embodiments, in the range of still falling within the present invention program.
Claims (8)
1. a kind of multi-layer co-extruded mold cleaning material, it is characterised in that: be made of the component of following mass percentage:
Polyolefin resin is 90.0-99.5% as carrier, the mass percent of carrier;It selects polyetheramine, polyisobutylene amine, gather
At least one of succimide is used as detergent, and the mass percent of detergent is 0.5-10%.
2. multi-layer co-extruded mold cleaning material according to claim 1, it is characterised in that: the polyolefin resin is linear
Low density polyethylene (LDPE), melt index is between 0.3-50, density 0.923g/cm3。
3. multi-layer co-extruded mold cleaning material according to claim 2, it is characterised in that: the melting of the polyolefin resin
Index is 4.0.
4. multi-layer co-extruded mold cleaning material according to claim 1, it is characterised in that: the molecular weight of the polyetheramine is
1004, molecular formula is (C3H6O)nC6H16N2O, n are 1~20.
5. multi-layer co-extruded mold cleaning material according to claim 1, it is characterised in that: the molecule of the polyisobutylene amine
Amount is 1300, viscosity 645Pa.s.
6. multi-layer co-extruded mold cleaning material according to claim 1, it is characterised in that: the polysuccinimide is
T155 polyisobutylene-bis-succinimide, kinematic viscosity: 280-380mm2/ s, total base number: 15-25mg/g, flash-point: > 180 DEG C,
Density: 890-930g/mm3, coloration: 4.0, moisture: < 0.1%.
7. a kind of preparation method of multi-layer co-extruded mold cleaning material as claimed in any one of claims 1 to 6, it is characterised in that:
The following steps are included:
Polyolefin resin carrier and detergent are weighed using the production method of auxiliary material bucket weighing mixing granulation according to the proportion,
Using dual-screw pelletizer extruding pelletization, the multi-layer co-extruded mold cleaning material is obtained.
8. the preparation method of multi-layer co-extruded mold cleaning material according to claim 7, it is characterised in that: the twin-screw
Pelletizer screw diameter be 50mm, draw ratio 20:1, screw rod be incorgruous steering, extrusion temperature be followed successively by 150 DEG C, 170 DEG C,
200℃、200℃、200℃、200℃。