CN109503895A - A kind of oil resistant low temperature resistant rubber and preparation method thereof - Google Patents
A kind of oil resistant low temperature resistant rubber and preparation method thereof Download PDFInfo
- Publication number
- CN109503895A CN109503895A CN201811344517.7A CN201811344517A CN109503895A CN 109503895 A CN109503895 A CN 109503895A CN 201811344517 A CN201811344517 A CN 201811344517A CN 109503895 A CN109503895 A CN 109503895A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- low temperature
- oil resistant
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of oil resistant low temperature resistant rubber and preparation method thereof, which is made of following composition by weight: 50-80 parts of natural rubber, 20-50 parts of nitrile rubber, 40-80 parts of carbon black, 5-20 parts of plasticizer, 2-20 parts of zinc oxide, 1-5 parts of stearic acid, 1-10 parts of anti-aging agent, 1-8 parts of sulphur, 1-8 parts of vulcanization accelerator, 1-4 parts of processing aid.Rubber of the invention oil resistant and resistance to low temperature compared with General Purpose Rubber is prominent, and has good physical mechanical property, and rubber preparation method of the invention is simple, and at low cost, sizing material processing performance is good, easy to industrialized production.
Description
Technical field
The invention belongs to field of rubber materials, more particularly to a kind of oil resistant low temperature resistant rubber and preparation method thereof.
Technical background
With extensive use of the rubber material in the heavy industry and new industry such as digging, traffic, building, machinery, electronics,
To the performance of rubber material, more stringent requirements are proposed, especially the oil resistant low temperature resistant performance of rubber, and low temperature resistant and oil resistivity
It can be a pair of contradictory body, according to similar compatibility principle, rubber molecule polarity is stronger, and small molecule oil product is poorer to its permeability,
Oil resistivity is better, and molecular polarity more force it is intermolecular interaction it is bigger, to the binding force of the movement of strand and segment
Also bigger, so that glass transition temperature Tg increases, to make rubber keep elastic reduced capability under certain low temperature, i.e.,
Resistance to low temperature is deteriorated.Therefore single rubber base material is no longer satisfied use demand.
The performance of rubber product also has close ties, rubber in addition to related with the property of rubber matrix itself with balanced constant
The locomitivity that the cold resistance of glue is mainly reflected in strand is stronger, and intermolecular movement is relatively easy, the energy of molecule cohesion
Opposite is low.Presently most used solution first is that the selection and use of plasticizer, plasticizer can be such that rubber molecule moves
It becomes easy, reduces the active force between rubber molecule, to reduce the glass transition temperature of rubber, improve rubber plasticity and flowing
Property, convenient for calendering, the forming operations such as extrude, while certain physical mechanical properties of vulcanizate can also be improved, such as reduce hardness and
Stress at definite elongation assigns higher elasticity and lower heat, raising cold resistance etc..
Summary of the invention
The purpose of the present invention is to provide a kind of oil resistant and resistance to low temperature balance are preferable, while having both good physical machine
Tool performance, production method is simple, oil resistant low temperature resistant rubber easy to industrialized production, to meet the use need of people's production and living
It asks.
To achieve this purpose, the present invention adopts the following technical scheme:
A kind of oil resistant low temperature resistant rubber of the present invention, the raw material composition of following components by weight percent: 50-80 parts of natural rubber, butyronitrile
20-50 parts of rubber, 40-80 parts of carbon black, 5-20 parts of plasticizer, 2-20 parts of zinc oxide, 1-5 parts of stearic acid, 1-10 parts of anti-aging agent, sulphur
1-8 parts of sulphur, 1-8 parts of vulcanization accelerator, L-181-4 parts of processing aid.
The natural rubber is any one of pimpled rubber, smoke sheet rubber, air dried sheet glue, crepe rubber.
The nitrile rubber is nitrile rubber 1052, and wherein acrylonitrile content is 31%-35%.
The carbon black is high abrasion furnace carbon black N330, general purpose furnace black N660, spray carbon black, one in semi-reinforcing carbon black N774
Kind or several combinations.
The plasticizer is one of polyethers plasticizer TP-90B and Etheric ester type plasticizer TP-95.
The anti-aging agent is the two kinds of arbitrary proportion mixing of anti-aging agent RD and antioxidant BLE.
The vulcanization accelerator is one of sulfenamide accelerator CZ and accelerator D TDM or two
Kind combination.
A kind of preparation method of oil resistant low temperature resistant rubber, including following operating procedure:
(1) take natural rubber on a mill it is thin it is logical beat after triangle bag plasticates 5 times, add nitrile rubber together it is thin lead to beat
Triangle bag is plasticated 20 times, and temperature is controlled at≤60 DEG C, after plasticating, broken-down rubber is obtained after bin aging 8h, and can detecte door
Buddhist nun's viscosity examines Mooney viscosity result to be no more than 40, and relatively low Mooney viscosity is conducive to improve the dispersibility of sizing material.
(2) broken-down rubber and carbon black, zinc oxide, stearic acid, plasticizer, processing aid step (1) plasticated are thrown in succession
Enter in the banburying chamber of mixer, mixing room temperature is no more than 50 DEG C when throwing glue, and mixing time 12-18min, mixing room temperature reaches
To 100 DEG C of dumping blowings, 8 hours are parked for use.
(3) sizing material and anti-aging agent, sulphur, vulcanization accelerator that are kneaded in step (2) are put into mixer be kneaded together
6-10min, mixing room temperature is no more than 35 DEG C when throwing glue, and mixing room temperature reaches 70 DEG C of dumping blowings, after parking 8 hours to obtain the final product
Oil resistant low temperature resistant rubber.
Beneficial effects of the present invention: rubbery system of the present invention is used in combination using natural rubber with nitrile rubber, and natural rubber is
Most widely used general purpose rubber, because of its elasticity with higher, slightly band plasticity, cold resistance has extraordinary machinery after reinforcement
Intensity, but natural rubber main chain contains double bond, is easy under attack, not ageing-resistant, oil resistivity, chemicals-resistant (in addition to alkali) performance
It is bad, therefore application is restricted.Nitrile rubber is a kind of synthetic rubber as prepared by butadiene and acrylonitrile compolymer, is
Oil resistant (especially alkane oil), the preferable synthetic rubber of ageing-resistant performance, mainly for the manufacture of oil resistant rubber product, acrylonitrile contains
Amount is more, and oil resistivity is better, but cold resistance then accordingly declines.The two is used in combination, the oil resistant that can not only improve rubbery system is resistance to
Low temperature properties can also be effectively improved processing performance.
Rubbery system of the invention is used in the excellent natural rubber of resistance to low temperature and the excellent butyronitrile rubber of oil resistance
Glue 1052 simultaneously uses and uses TP-90B or TP-95 as rubber plastizing agent, compared with common natural rubber, rubber of the invention
Glue is with oil resistant, resistance to low temperature, and suitable for the use of the continuous duration under cryogenic conditions, and rubber preparation method is simple
Single, at low cost, sizing material processing performance is good, easy to industrialized production.
Specific embodiment
The following describes the present invention in detail with reference to examples, but embodiment of the present invention is without being limited thereto.
Embodiment 1
A kind of oil resistant low temperature resistant rubber, is made of the raw material of following components by weight percent: 60 parts of natural rubber WF, nitrile rubber
1052 40 parts, 60 parts of carbon black N330,15 parts of carbon black N660,15 parts of TP-90B, 5 parts of zinc oxide, 1.5 parts of stearic acid, prevent old
2 parts of agent RD, 2 parts of antioxidant BLE, 1.5 parts of sulphur, 1.2 parts of CZ, 1.8 parts of DTDM, 1.5 parts of processing aid L-18.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is such as
Under:
(1) take natural rubber on a mill it is thin it is logical beat after triangle bag plasticates 5 times, add nitrile rubber together it is thin lead to beat
Triangle bag is plasticated 20 times, and temperature is controlled at≤60 DEG C, after plasticating, broken-down rubber is obtained after bin aging 8h, and can detecte door
Buddhist nun's viscosity examines Mooney viscosity result to be no more than 40, and relatively low Mooney viscosity is conducive to improve the dispersibility of sizing material.
(2) raw rubber and carbon black, zinc oxide, stearic acid, plasticizer, processing aid that step (1) has been plasticated are put into succession
In the banburying chamber of mixer, mixing room temperature is no more than 50 DEG C when throwing glue, and mixing time 12-18min, mixing room temperature reaches
100 DEG C of dumping blowings park 8 hours for use.
(3) sizing material and anti-aging agent, sulphur, vulcanization accelerator that are kneaded in step (2) are put into mixer be kneaded together
6-10min, mixing room temperature is no more than 35 DEG C when throwing glue, and mixing room temperature reaches 70 DEG C of dumping blowings, after parking 8 hours to obtain the final product
Oil resistant low temperature resistant rubber, detection physical mechanical property are as shown in table 1 below:
Embodiment 2
A kind of oil resistant low temperature resistant rubber, is made of the raw material of following components by weight percent: 70 parts of natural rubber WF, nitrile rubber
1052 30 parts, 60 parts of carbon black N330,15 parts of carbon black N660,10 parts of TP-90B, 5 parts of zinc oxide, 1.5 parts of stearic acid, prevent old
2 parts of agent RD, 2 parts of antioxidant BLE, 1.5 parts of sulphur, 1.2 parts of CZ, 1.8 parts of DTDM, 1.5 parts of processing aid L-18.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is same
Embodiment 1 is identical, and detection physical mechanical property is as shown in table 1 below:
Embodiment 3
A kind of oil resistant low temperature resistant rubber, is made of the raw material of following components by weight percent: WF80 parts of natural rubber, nitrile rubber
1052 20 parts, 60 parts of carbon black N330,15 parts of carbon black N660,10 parts of TP-90B, 5 parts of zinc oxide, 1.5 parts of stearic acid, prevent old
2 parts of agent RD, 2 parts of antioxidant BLE, 1.5 parts of sulphur, 1.2 parts of CZ, 1.8 parts of DTDM, 1.5 parts of processing aid L-18.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is same
Embodiment 1 is identical, and detection physical mechanical property is as shown in table 1 below:
Embodiment 4
A kind of oil resistant low temperature resistant rubber, the raw material composition of following components by weight percent: WF50 parts of natural rubber, nitrile rubber 1052
50 parts, 60 parts of carbon black N330,20 parts of carbon black N660,5 parts of TP-95,2 parts of zinc oxide, 1 part of stearic acid, 5 parts of anti-aging agent RD,
5 parts of antioxidant BLE, 1 part of sulphur, 1 part of CZ, L-181 parts of processing aid.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is same
Embodiment 1 is identical, and detection physical mechanical property is as shown in table 1 below:
Embodiment 5
A kind of oil resistant low temperature resistant rubber, the raw material composition of following components by weight percent: WF80 parts of natural rubber, nitrile rubber 1052
20 parts, 30 parts of carbon black N330,10 parts of carbon black N660,20 parts of TP-95,20 parts of zinc oxide, 5 parts of stearic acid, anti-aging agent RD 0.5
Part, 0.5 part of antioxidant BLE, 8 parts of sulphur, 8 parts of CZ, 4 parts of processing aid L-18.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is same
Embodiment 1 is identical, and detection physical mechanical property is as shown in table 1 below:
Embodiment 6
A kind of oil resistant low temperature resistant rubber, the raw material composition of following components by weight percent: WF60 parts of natural rubber, nitrile rubber 1052
40 parts, 60 parts of carbon black N330,15 parts of carbon black N660,5 parts of TP-95,5 parts of zinc oxide, 1.5 parts of stearic acid, anti-aging agent RD 2
Part, 2 parts of antioxidant BLE, 1.5 parts of sulphur, 3 parts of DTDM, 1.5 parts of processing aid L-18.
Rubber compound oil resistant low temperature resistant rubber is made in raw material open mill and mixer according to above-mentioned formula, operating procedure is same
Embodiment 1 is identical, and detection physical mechanical property is as shown in table 1 below:
Table 1
The foregoing is only a preferred embodiment of the present invention, but hold in range of the invention be not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the scope of protection of the present invention.
Claims (8)
1. a kind of oil resistant low temperature resistant rubber, it is characterised in that: the oil resistant low temperature resistant rubber by following composition by weight raw material
Composition: 50-80 part of natural rubber, 20-50 parts of nitrile rubber, 40-80 parts of carbon black, 5-20 parts of plasticizer, 2-20 parts of zinc oxide, firmly
1-5 parts of resin acid, 1-10 parts of anti-aging agent, 1-8 parts of sulphur, 1-8 parts of vulcanization accelerator, L-181-4 parts of processing aid.
2. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the natural rubber is particle
Any one of glue, smoke sheet rubber, air dried sheet glue, crepe rubber.
3. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the nitrile rubber is butyronitrile rubber
Glue 1052, wherein acrylonitrile content is 31%-35%.
4. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the carbon black is high wear-resistant carbon black
One or more of N330, general purpose furnace black N660, spray carbon black, semi-reinforcing carbon black N774 combination.
5. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the plasticizer is polyethers increasing
Mould one of agent TP-90B and Etheric ester type plasticizer TP-95.
6. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the anti-aging agent is anti-aging agent RD
With two kinds of arbitrary proportion mixing of antioxidant BLE.
7. a kind of oil resistant low temperature resistant rubber according to claim 1, it is characterised in that: the vulcanization accelerator is time sulphur
One or two kinds of combinations in amides accelerator CZ and accelerator D TDM.
8. a kind of preparation method of oil resistant low temperature resistant rubber described according to claim 1 or 2 or 3 or 4 or 5 or 6 or 7, special
Sign is: including following operating procedure:
(1) take natural rubber on a mill it is thin it is logical beat after triangle bag plasticates 5 times, add nitrile rubber together it is thin lead to beat triangle
Plastic refining 20 times, temperature is controlled at≤60 DEG C, after plasticating, broken-down rubber is obtained after bin aging 8h, and detect Mooney viscosity, examined
Mooney viscosity result is tested no more than 40, relatively low Mooney viscosity is conducive to improve the dispersibility of sizing material;
(2) broken-down rubber and carbon black, zinc oxide, stearic acid, plasticizer, processing aid step (1) plasticated, put into close in succession
In the banburying chamber of mill, mixing room temperature is no more than 50 DEG C when throwing glue, and mixing time 12-18min, mixing room temperature reaches
100 DEG C of dumping blowings park 8 hours for use;
(3) sizing material and anti-aging agent, sulphur, vulcanization accelerator that are kneaded in step (2) are put into be kneaded 6- in mixer together
10min, mixing room temperature is no more than 35 DEG C when throwing glue, and mixing room temperature reaches 70 DEG C of dumping blowings, up to resistance to after parking 8 hours
Oily cold resistant rubber.